3,3''''-二羟基4,4''''-联苯二甲酸的合成和表征

联苯二甲酸类化合物是很好的刚性桥联配体,可用于制备纳米多孔材料.设计了一条制备联苯二甲酸类新配体的合成路线,以4氨基水杨酸为原料,经过4步反应最终合成了新配体3,3'-二羟基4,4'-联苯二甲酸,并通过红外光谱、核磁共振氢谱和元素分析进行了表征.     

杂化材料[Mn(H2O)(2,2''''-bipy)V2O6]的合成与表征

合成并表征了新化合物[Mn(H2O)(2,2'-bipy)V2O6],且对化合物进行了相应的红外、热重分析.结果表明:该化合物的空间群是Pca2(1),其晶胞参数为a=9.170 2(2),b=10.477 3(8),c=14.523 1(3)(A),V=1 393.54(10) (A)3且Z=4;该化合物的结构特征是钒氧四面体[VO4]以共顶点构成的钒氧链,[MnN2O4]八面体将钒氧链连成层;配体2,2'-联吡啶则分布于层的上下两侧,并以π-π相互作用将层与层之间连接起来.     

新型有机-无机杂化材料固载烯烃环氧化催化剂

本文以新型有机-无机杂化材料"低聚苯乙烯基膦酸-磷酸氢锆(ZSPP)"为载体,设计合成了四种多胺配体钼配合物多相催化剂,并用红外、拉曼、XPS、XRD及元素分析等方法对催化剂进行了表征.以TBHP为氧源,考察了所制备催化剂催化环己烯环氧化的催化活性,结果表明,所制备的固载催化剂催化环己烯环氧化时具有较高的催化活性、选择性和重复使用性,但随着配体中N原子数的增加,转化率和选择性会逐渐降低.     

SiAlON材料的氧化行为

SiAlON材料在高温氧化气氛下的氧化行为和氧化机理一直是材料科学领域关注的焦点.本文综述了SiAlON材料氧化的相关研究,分析对比了单相和复相SiAlON材料的氧化行为,讨论了SiAlON材料的氧化影响因素以及氧化机理,指出了SiAlON材料氧化研究存在的问题.     

电镀Zn-Fe-SiO2复合材料的性能研究

镀锌与Zn-Fe合金广泛用于钢铁零件的防护,但是仍存在钝化液毒性大、环境污染严重、耐蚀性低、氢脆高等不足。本文采用无氰电镀技术制备了Zn-Fe-SiO2复合材料,并测试了Zn-Fe-SiO2复合材料的耐蚀性、孔隙率和氢脆性等综合性能,同时与电镀Zn及Zn-Fe合金进行了对比。实验结果表明:电镀Zn-Fe-SiO2复合材料的耐蚀性及其它综合性能均优于镀锌与Zn-Fe合金,无需钝化处理,环境友好,应用前景广阔。     

相似模拟实验中光纤光栅传感测试的温度补偿

为了提高光纤光栅的测试水平，研究了相似模拟实验中光纤光栅传感测试的温度补偿方法。采用了不受力温度补偿法。将温度补偿光栅埋设于模型外的相似材料模块中。模型开采过程中模块仅感受温度的变化，不受任何外力；模型内的测试光栅同时感受温度和应变的变化。实验表明，在外界温度变化的情况下，温度的影响作用明显，因此，剔除温度的影响很有必要。使用不受力法可以消除温度的影响，解决了相似模拟实验中光栅测试的交叉敏感问题，提高了测试的精度。     

提高英语听说的重要途径——运用语境理论分析真实语言材料

通过对雅思考试听力部分的分析,探讨了选择真实语言听力材料的必要性,以及应用语境理论,特别是情景文化语境分析真实语言材料在帮助学生充分理解材料过程中的重要作用。     

Preparation of 3-D porous fibroin scaffolds by freeze drying with treatment of methanol solutions

In this study, silk scaffolds with appropriate porous structures were prepared by adjusting solution concentrations and providing treatment with methanol solutions in the way of freeze drying. The effects of the preparation conditions on the microstructures and properties of the scaffolds were discussed. Fibroin solutions with different concentrations of 4, 6, 8, 10 wt% were used respectively to prepare the scaffolds. The effects of the addition of 20 vol% methanol before or after freeze drying to the 4 wt% fibroin solution were investigated. As demonstrated by Scanning Electron Microscope (SEM), the fib-roin scaffolds prepared without methanol had porous microstructures composed of thin sheets, and the sizes of the pores decreased with the increase of the fibroin solution concentrations, while the scaffolds prepared in the presence of methanol showed porous microstructures formed by fine-particle aggregates. The porosities and mechanical properties of the prepared fibroin scaffolds under different conditions were tested. The crystalline structures and conformations of the fibroin scaffolds were detected by Fourier transform infrared spectroscopy (FT-IR) and X-ray diffraction (XRD).     

用真空温压技术制备纳米金属铜块体材料

采用自悬浮-真空温压法制备纳米金属Cu块体材料。通过X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、正电子湮没(PAS)实验、HMV-2型显微硬度计和用Arechimedes原理等测试手段研究压制压力、保压时间、温度等工艺参数对样品密度的影响;考察其热稳定性和微结构。研究结果表明:纳米金属Cu块体材料的密度随压制压力、保压时间和温度的增加而提高,最高相对密度为96.15%;纳米金属Cu块体材料具有较好的热稳定性;在1.5 GPa和200℃压制的样品的平均晶粒度为25.3 nm,微应变为0.047%。     

超高压力下通电烧结制备钼铜合金

采用超高压力下通电烧结技术制备了铜体积分数25%～75%的钼铜合金材料. 烧结压力2～10 Gpa,通电功率15 kW,通电时间65 s. 分析了不同成分和制备工艺参数的钼铜合金显微形貌及力学性能. 结果表明,所制备的钼铜合金材料结构致密,力学性能优越,而且超高压力下通电烧结技术能有效地避免晶粒长大和组织偏析.