锂离子电池正极材料Li[Li0.2Mn0.54Ni0.13Co0.13]O2的碳包覆研究

以过渡金属乙酸盐和氢氧化锂为原料,采用共沉淀方法制备了锂离子电池富锂正极材料Li[Li0.2Mn0.54Ni0.13Co0.13]O2并对该材料进行表面包碳.X射线衍射技术(XRD)、扫描电子显微技术(SEM)实验数据表明,该材料具有层状α-NaFeO2 结构.包碳后材料结构没有变化,表面覆盖上一层纳米级别的颗粒.电化学性能测试结果表明该材料包碳后在0.1 C (1 C＝180 mA/g),2.0 ～ 4.8 V电位范围内首次放电比容量高达259.0 mAh/g.包碳后首次放电比容量,倍率性能,循环性能均得到提高.采用电化学阻抗谱(EIS)研究包碳前后该材料的传荷阻抗,结果显示碳包覆材料的传荷阻抗明显减小,电子电导率得到提高,从而提高电化学性能.     

碳纳米管内包覆Fe/Co粒子的磁性能

采用自制的装置,通过阳极弧光放电法制备了内包覆Fe/Co磁性纳米粒子的碳纳米管(CNTs).利用透射电子显微镜(TEM)、拉曼散射光谱和X射线衍射(XRD)对其进行表征,用振动样品磁强计(VSM)检测得到其磁学性能参数.TEM测试表明,CNTs杂质少,管径均匀一致,CNTs内包覆的物质均匀、连续,且为Fe/Co粒子.磁学性质的测量表明, CNTs的磁学性能较包覆前有了很大的改善,其比饱和磁化强度ós为17.30A·m2·kg-1,比剩余磁化强度ór为3.96A·m2·kg-1,矫顽力Hc为31521.60A·m-1.     

热处理对H13钢组织性能的影响

H13是一种新型热作模具钢,它常用作了挤压模、铝合金压铸模和塑料膜,使用温度≤600℃时期寿命远高于3Cr2W8V,还可用于冷挤凹模、冷挤钢管环形模,是冷热皆宜的模具钢。H13(4Cr5MoSiV1)的韧性和塑性明显优于其它H型钢,本文利用扫描电镜及透射电子显微镜研究了锻造退火后淬火、回火工艺对钢组织和性能的影响。     

20Cr圆销热处理淬火软点形成原因及防止措施

20Cr热处理淬火后常规检查方法,以洛氏硬度进行抽样检测,也可根据技术要求的不同和实际所发生的情况采用金相检验来解决热处理淬火发生的缺陷,结果表明改进加热工装,提高碳氮共渗效果,增强冷却介质的搅动程度可有效地防止软点发生,经多炉次生产试验,现已达到技术要求并装车使用。     

挤压轮转速对铝护套连续挤压包覆过程的影响

基于Deform-3D模拟分析铝护套连续包覆成形过程,挤压轮转速的增加不利于导流模处金属流动的均匀性,随着挤压轮转速的提高,可能会造成模腔的失效,不考虑其它因素下,提高挤压轮的转速有利于连续挤压包覆生产率的提高。综合考虑连续挤压包覆工模具的使用寿命和生产效率的提高,挤压轮的转速为4~6 rpm较为合适。     

新型合金铸铁对汽车冲压模具质量的影响

优质的模具材料是提高模具质量、延长模具寿命和降低生产成本的关键。以生铁为主要原料,以Cr、Sb等为辅料,改变材料配比以及在孕育剂里面加入特种合金,进行拉深和冲击试验,研究了MoCr及GGG70L两种合金铸铁材质性能提升对冲压模具淬火质量的影响。结果表明:MoCr中,设定渗碳体碳含量为6.69%,基体中转变的碳总量为1.2%～1.4%,可获得更高的淬火硬度;GGG70L中,增加Cr合金,珠光体稳定在80%～90%,可获得较高的淬火硬度和强度,提高模具质量。     

锂离子电池正极材料LiMn2O4的Al2O3包覆研究

文章采用高温固相法合成尖晶石LiMn2O4,并采用液相包覆的方法对其进行改性处理。采用XRD、SEM、XPS以及电池测试系统等,研究了所制备材料的结构、组成、性能和包覆机理。实验结果表明:表面处理后的LiMn2O4循环性能显著提高,以A12O3对尖晶石LiMn2O4进行表面包覆,使LiMn2O4颗粒不与电解液直接接触,可以防止锰离子溶解在电解液中,获得结构稳定、循环性能优异的锂离子电池正极材料;同时Al2O3会和电解液中微量的HF反应,减小了HF对锰离子溶解的加速作用。     

Element distribution and diffusion behavior in Q&P steel during partitioning

Carbon, manganese, and silicon distribution in quenching and partitioning （Q＆P） steel during partitioning process was investigated to reveal the diffusion behavior. The microstructure and chemical composition were analyzed by means of scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and three-dimensional atom probe. It is shown that the studied Q＆P steel consisted of martensite laths and thin, film-like retained austenite showing extraordinary phase transformation stability. Carbon atoms mostly diffused to the retained austenite from martensite at a higher partitioning temperature. In the experimental steel partitioned at 400℃ for 10-60 s, carbides or cementite formed through carbon segregation along martensite boundaries or within the martensite matrix. As a result of carbon atom diffusion from martensite to austenite, the carbon content in martensite could be ignored. When the partitioning process completed, the constrained carbon equilibrium （CCE） could be simplified. Results calculated by the simplified CCE model were similar to those of CCE, and the difference between the two optimum quenching temperatures, where the maximum volume fraction of the retained austenite can be obtained by the Q＆P process, was little.     

包覆涂层的可溶性微针的制备及性能测试

近年来,可溶性微针因其优势引起了科学家的广泛关注,但由于可溶性高分子材料快速溶解的特性,较难实现药物的缓控释.笔者提出了一种在可溶性微针针体上包覆一层涂层的方法,以实现对药物释放行为的控制.采用自制的旋涂机在微针针体上包覆一层缓释涂层,以透皮扩散试验探究高分子涂层材料的种类和浓度、旋涂机的转速、包覆的次数等参数对药物释放的影响规律;采用力学强度测试和皮肤穿刺试验考察微针的穿刺行为和效率,最后通过经皮水分流失测试和皮肤恢复情况来评估微针的安全性.通过上述方法,成功制备了可实现缓控释的微针,优选的高分子涂层材料为聚苯乙烯,优选浓度为3％,旋涂机转速为600 r·m in-1,包覆次数1次为宜;4种不同的药物均可用上述包覆的方法实现药物的缓控释.研究结果表明,包覆涂层的微针每根能承受至少0.21 N·tip-1,能够有效地刺入皮肤,穿刺皮肤效率达到97.20％.经皮水分流失测试结果显示,微针刚处理后经皮水分流失值升高至(54.03±3.85)g·m-2·h-1,6h后便下降到正常水平((13.80±1.37)g·m-2·h-1)(与对照组无显著性差异),表明皮肤已恢复屏障作用.笔者所制备的微针可以实现多种药物的缓控释,具有足够的机械强度,而且相对安全,是一种具有较大潜力的新型药物载体.     

特厚钢板阵列射流淬火的表面换热

采用特厚钢板专用辊式射流淬火试验装置和多通道钢板温度记录仪,测试出射流速度3.39~26.8 m·s-1、雷诺数12808~117340、水流密度978.7~6751.5 L·(m2·min)-1条件下,84 mm厚钢板淬火冷却曲线;进而基于反传热修正方法计算高温钢板淬火过程壁面温度和热流密度,描绘出沸腾曲线,分析多束圆孔阵列射流对特厚钢板淬火表面换热的影响.结果表明:射流速度、水流密度等参数影响钢板表面射流滞止区和平行流区换热机制,进而影响最大热流密度分布.射流速度较低时,壁面平行流区观察到混合换热和"热流密度肩"现象;随射流速度增大,膜沸腾换热机制消失,最大热流密度移至较低壁面过热度处.相关研究将对特厚钢板淬火过程温度场计算和组织性能调控提供有益的帮助.