二甲基丙烯酸乙二醇酯的催化合成研究

用固体超强酸SO24–/TiO2为催化剂,以乙二醇和甲基丙烯酸为原料合成二甲基丙烯酸乙二醇酯（EGDMA）。探讨了催化剂制备条件、原料配比、反应时间、催化剂用量等工艺参数对酯收率的影响,在适宜的工艺条件下酯收率达88.5。     

马来酸酐/丙烯酸水凝胶对亚甲基蓝染料的吸附

以马来酸酐(MA)、丙烯酸(AA)和丙烯酰胺(AM)为原料,采用水溶液聚合法制备P(MA-co-AA-co-AM)水凝胶,并考察不同因素对水凝胶吸附亚甲基蓝染料效果的影响.实验结果表明:当亚甲基蓝染料初始质量浓度为1g/L,吸附剂用量为1g/L,溶液pH=9,环境温度为20~25℃时,P(MA-co-AA-co-AM)水凝胶对亚甲基蓝染料的吸附效果最佳,最大吸附量为985.98mg/L,去除率达98.60%;水凝胶对亚甲基蓝的吸附行为符合准二级反应动力学方程和Langmuir吸附等温式.     

水性自交联丙烯酸金属防腐底漆的制备研究

本文研究了水性自交联丙烯酸金属防腐底漆的设计与应用,探讨了成膜物质、颜料体积浓度、防锈颜料、抗闪锈助剂等对水性金属防腐漆性能的影响。结果表明:树脂的玻璃化温度(Tg)为30 o C,用量占防腐底漆的40%;颜料体积浓度(PVC)为40%;防锈颜料选用改性磷酸锌且占底漆的20%;抗闪锈助剂选用RAYBO 60,占防腐底漆的0.3%;水性自交联丙烯酸金属防腐底漆的性能达到最优。该金属防腐底漆具有耐酸碱、耐盐水、附着力佳等性能。是一种综合性能优异、性价比高的水性自交联丙烯酸金属防腐底漆。     

链转移剂与极性单体对基于双向拉伸聚丙烯用压敏胶性能的影响

本文以丙烯酸酯类单体为主要原料,采用种子半连续乳液聚合工艺,制备了一款性能良好用于双向拉伸聚丙烯(BOPP)薄膜的水性丙烯酸酯乳液压敏胶。主要研究了链转移剂硫醇和极性单体丙烯酸(AA)、丙烯酸羟乙酯(HEA)、丙烯酸羟丙酯(HPA)用量及链转移试剂和极性单体(AA、HPA)的不同加入方式对压敏胶性能的影响。结果表明:当硫醇用量为0.5%,AA用量(占总单体量,下同)为5.6%,HPA为5.1%,HEA为4.2%,其中硫醇部分分批加入,AA和HPA以方式3加入时,可显著提高压敏胶的粘结性能。     

丙烯酸叔丁酯与丙烯酰胺基偶氮苯共聚竞聚率的研究

以丙烯酸叔丁酯(tBA)和丙烯酰胺基偶氮苯(AAAB)为单体,偶氮二异丁腈(AIBN)为引发剂,四氢呋喃(THF)为溶剂,在60℃下,利用自由基聚合法合成tBA-AAAB无规共聚物。利用FT-IR方法测定共聚物的组成,通过Yezreielv-Brokhina-Roskin法(简称YBR法)计算了共聚反应的竞聚率。结果表明,tBA与AAAB的竞聚率分别为r1=2.20,r2=0.34,说明tBA的均聚反应的倾向大于共聚反应的倾向,而AAAB则相反。     

Ce:LuAG粉体的溶胶-凝胶燃烧法制备和发光性能

以尿素、甘氨酸为燃烧助剂,采用低温溶胶-凝胶燃烧法制备多晶Ce离子掺杂Lu3Al5O12(Ce:LuAG)粉体.X射线衍射(XRD)检测结果表明,前驱体在700℃条件下开始出现弱的晶化峰,850℃时晶化逐步完全,1 000℃时晶粒发育完善,得到单相Ce:LuAG粉体,一次粒径约40nm.紫外激发条件下,Ce掺杂LuAG粉体表现出涵盖480~700nm的宽带发射,中心位置位于530nm左右.随着煅烧温度的提高,两种燃烧助剂所得Ce:LuAG粉体的发光强度明显增强,甘氨酸法所得粉体的分散性和发光强度均优于尿素法.     

Preparation and optical properties of waterborne acrylic-based cool white coatings

Cool coatings （solar reflective coatings） possess a high total solar reflectance and a high thermal emittance, and they have potential applications in building surfaces, pavements, and oil tanks. By decreasing the accumulation of heat, these coatings can reduce the urban heat island effect to increase thermal comfort and to decrease energy consumption in hot zones. In this work, a cool white coating based on waterborne acrylic was prepared. The reflectance and thermal emittance were measured using an ultraviolet- visible-near-infrared spectrophotometer and the steady- state calorimetric technique, respectively. The cool coating possessed a total solar reflectance of 0.887 and a thermal emittance of 0.85. The linear fitting results indicated that the thickness of the dry film is an important factor that affects the reflectance and that the physical limit of total solar reflectance in practical cool coatings is 0.91. A homemade device developed according to military specification MIL-E-46096C was used to measure insulation temperature differences, and an insulation temperature difference of 29 ℃ was obtained. The above results demonstrated that the cool coating can be applied to buildings.     

微乳液聚合制备含氟丙烯酸酯共聚物

以十二烷基磺酸钠和十三异构醇聚氧乙烯醚为复合乳化剂,采用半连续滴加预乳化单体与引发剂,微乳液聚合的方法制备了丙烯酸全氟己基乙基酯(PFEA)、丙烯酸丁酯和甲基丙烯酸甲酯共聚物.考察了PFEA、乳化剂的质量分数和温度等因素对微乳液聚合及共聚物性能的影响.研究结果表明,当乳化剂质量分数在2%～3%,PFEA质量分数在12%～20%,聚合温度在75～80℃时,聚合反应稳定,且制得的共聚物憎水性优异.     

二元共聚物P(MA-AA)的合成工艺研究

介绍了马来酸酐(MA)与丙烯酸(AA)共聚的基本原理.探讨了共聚物P(MA-AA)的聚合反应中引发剂用量、聚合温度、单体配比、聚合时间等因素对螯合性能及分散性能的影响,通过改变引发剂滴加方式和氮气保护等工艺提升聚合物的皂洗能力.     

单纯形法合成耐盐高吸水树脂

以丙烯酸和丙烯酰胺为单体,N,N’-亚甲基双丙烯酰胺为交联剂,以过硫酸铵和亚硫酸氢钠体系为引发剂,采用水溶液聚合法合成耐盐高吸水树脂。运用单纯形优化法获得了单体配比、丙烯酸中和度、引发剂用量、交联剂用量的优化条件组合,树脂在0.9%NaCl溶液中的最高吸盐水率达143.9 g.g-1。还考察了溶液盐浓度、pH值和温度等对树脂吸液性能的影响。