新型锆质不定形耐火材料的研制

以废旧电熔锆刚玉为主要原料,采用合理的粒度级配,应用复合结合剂和外加剂以凝聚结合的方式研制成功具有高荷重软化温度、高强度、低气孔率、低烧结线变化的新型锆质不定形耐火材料。图4,表4,参3。     

WATER-BASED BINDERS USED IN PROCESS FORMAKING AUTOMOBLE FILTER PAPER

INTRODUTIONThe paper used as the filtration medium for automotbile filters has been traditionally treated with alcohol solution of phenolic resins. This has been done to improve the paper's strength properties and allow it to be pleated in an accordion-like shape and to hold the shape when the paper composite is cured.[1]With the onset of greater concern for environmental quality, the filter manufactures have requested paper suppliers to provide a free or lower formaldehyde-containing impr…     

对采用有机粘结剂球团生产DRI产品的评价

以氧化铁皮为原料,采用有机粘结剂“CC”和以皂土为粘结剂,生产球团作对比试验。结果表明:有机粘结剂“CC”和皂土均可降低生球长大速度,提高生球、干球落下和抗压强度,但生产同样质量的球团矿,“CC”的用量只有皂土用量的1/10。且其直接还原铁(DIR)产品质量优于皂土球团。     

新型粘合剂、增稠剂的印染性能

通过对单体、乳化剂及工艺过程的选择,合成了丙烯酸酯类新型粘合剂PBAMM(Ⅰ)和增稠剂PMAEE(Ⅰ)及增稠剂PMAOE(Ⅱ)。所合成的粘合剂Ⅰ具有优良的配伍性能,且印花织物的牢度、色光、强度、手感等优良。增稠剂Ⅰ及Ⅱ既具有优良的增稠性能又有较强的耐电解质性,应用时少剂量即达要求,且能减少印花浆中的火油耗用量。尤其,当粘合剂Ⅰ与增稠剂Ⅰ或Ⅱ配套使用时,更具优越的加和应用性能。     

黏结剂对RDX/Al复合含能材料的性能影响

为了研究不同黏结剂对RDX/Al复合含能材料性能的影响,分别以氟橡胶(F_(2602))、热塑性聚氨酯(Estane5703)和硝化棉(NC)为黏结剂,利用喷雾干燥法制备了3种含有不同黏结剂成分的黑索今(RDX)/Al复合含能材料。采用扫描电子显微镜(scanning electron microscope, SEM)、X射线光电子能谱仪(X-ray photoelectron spectroscopy, XPS)、X射线衍射仪(X-ray diffraction, XRD)和差示扫描量热仪(differential scanning calorimeter, DSC)对样品的形貌、表面元素、结构和热分解特性进行了表征;采用12型工具法测试了样品的撞击感度。结果表明:以F_(2602)为黏结剂制备的样品表面光滑,颗粒密实,表面有大量F元素且Al元素含量最少,包覆黏结效果最好;使用3种黏结剂制备的样品晶型未发生改变;使用F_(2602)、Estane5703和NC制备的样品热爆炸临界温度较RDX分别降低了6.17、0.81、6.24 K,说明铝粉的加入提高了RDX的热分解活性;以F_(2602)为黏结剂制备的样品特性落高较RDX提高了68.3 cm,撞击感度最低。     

全砂土固结充填材料的性能研究

对全砂土固结充填材料的性能进行了试验研究.结果表明全砂土固结充填材料的强度标号达到525#普通水泥标准,抗折抗压比高于425#普通水泥.在充填料配比相同的条件下,全砂土固结体的强度是水泥胶结体强度的3～4倍,与普通水泥的水化产物相比,全砂土固结充填材料的水化产物有更多的钙矾石晶体和无定形物质.在相同的碳化条件下,全砂土固结体的残余强度是水泥胶结体残余强度的1.5倍.图4,表6,参4.     

MHA黏结剂在钒钛磁铁矿氧化球团制备中的应用

应用已发明的MHA黏结剂替代膨润土制备钒钛磁铁矿氧化球团,获得质量优良的高炉冶炼原料。研究表明:当MHA用量为0.25%,在预热温度950℃,预热时间10 min,焙烧温度1 250℃,焙烧时间10 min的条件下,获得的预热球团抗压强度为522 N/个,焙烧球团抗压强度为3 702 N/个。与2.0%膨润土球团矿比较,MHA成品球团的抗压强度略低,而TFe品位明显提高1.11%。2种黏结剂球团矿的还原性能指标接近。MHA球团黏结剂在氧化球团矿生产中具有良好的应用前景。     

Effect of Polyvinylpyrrolidone on the Morphologies of Latex Films and Air Permeability of the Latex Finished Fabrics

Low air permeability is a common problem happening to the coating finished and pigment dyed fabrics.To tackle the problem,styrene and butyl acrylate copolymer latex was prepared and used as substitute for the binder.Then,polyvinylpyrrolidone(PVP)was fed into the latex.It was expected that pores could form in the resulting latex film after being rinsed.The morphologies of the latex films were analysized by scanning electric microscope(SEM).It was found that the continuity of the latex films decreased greatly...     

GAP基热塑性聚氨酯弹性体溶解性能的研究

用作火药黏结剂的聚氨酯弹性体溶解效果将直接影响火药组分的混合及火药的力学性能。采用八种不同溶剂溶解聚氨酯弹性体,并对其溶解现象、溶解程度及黏度进行初步研究。根据极性相似原则和溶度参数相近原则选择与配制多组溶剂,由乌氏黏度计测量同一温度下相同浓度待测液的黏度,得出溶解最好的实验方案是极性相似且溶度参数相差不大的丙酮/THF(1∶1)。     

高温养护对钢渣复合胶凝材料早期水化性能的影响

为了探讨高温养护时钢渣复合胶凝材料的早期水化性能,采用了化学结合水的测定、浆体显微观察、X射线衍射分析和孔隙分析等手段进行了研究。结果表明:高温养护能明显缩短复合胶凝材料的水化诱导期,加快其早期反应速率;能够同时促进水泥和钢渣的水化,提高钢渣复合胶凝材料的水化程度。高温养护能改善复合胶凝材料浆体在水化早期形成的孔结构,降低孔隙率,减小粗孔比例;但对水化产物种类的影响很小。