ZTA—SiCw—TiC复相陶瓷材料强韧化机理研究

四方氧化锆相变增韧、碳化硅晶须补强、碳化钛粒子弥散强化，同时引入一个新的陶瓷基复合材料系统中产生了叠加的强韧化效果。热压ＺＴＡ－ＳｉＣｗ－ＴｉＣ复相陶瓷材料与Ａｌ２Ｏ３－ＳｉＣｗ－ＴｉＣ相比具有更高的综合机械性能。碳化钛在基体中形成连续的骨架阻碍晶粒的长大，随着碳化钛含量的增加，基体的硬度明显增加。主要强韧化机理有相变增韧、晶须拔出、载荷转移、裂纹偏转等。基体的主要断裂方式为穿晶解理断裂。     

TiC原位增强块状Cu47Ti34Zr11Ni8非品合金复合材料

在电弧炉中利用吸铸法制备了直径1～4mm的原位生成TiC和β-Ti枝晶联合增强的块状Cu47Ti34Zr11Ni8非晶合金复合材料．DSC热分析结果表明、原位生成TiC颗粒的引入，没有影响基体合金的非晶形成能力．用OM，XRD，SEM，EDS等方法研究了复合材料的相组成、微观组织以及成分分布、结果表明．TiC颗粒怍为异质形核中心促进了β-Ti枝晶的形成、形成了TiC颗粒和β-Ti枝晶联合增强的块状Cu47Ti34Zr11Ni8非晶合金复合材料、而且β-Ti枝晶的尺寸和数量与TiC颗粒的多少以及试样的尺寸有关．室温压缩试验表明，同单相非晶合金相比，块状Cu47Ti34Zr11Ni8非晶合金复合材料提高了抗压强度及塑性。     

前驱体碳化复合等离子熔覆涂层

以钛铁粉、铬粉、铁粉和碳的前驱体（蔗糖）等为原料,通过前驱体碳化复合技术制备了碳化复合粉,并利用等离子熔覆技术在Q235钢表面制备了Fe-Cr-C和Fe-Cr-C-Ti涂层.采用X射线衍射和扫描电镜对涂层的相组成和显微组织结构进行了分析.结果表明:Fe-Cr-C涂层由（Cr,Fe）₇C₃初生碳化物和菊花瓣状分布共晶碳化物（Cr,Fe）₇C₃与奥氏体组织组成;Fe-Cr-C-Ti涂层由原位合成的TiC相和（Cr,Fe）₇C₃共晶相与奥氏体相构成.这两种涂层与基体之间都是冶金结合.涂层中碳化物TiC的体积分数呈现梯度分布,并且涂层的熔合区和中部区域TiC颗粒形状多为等轴状颗粒,涂层的表层区域部分TiC颗粒多为树枝晶颗粒.与Fe-Cr-C涂层相比较,Fe-Cr-C-Ti涂层的抗开裂性更好.Fe-Cr-C和Fe-Cr-C-Ti两涂层的平均显微硬度约是750HV_0.2,是基体金属的3.2倍,从涂层表面到熔合区相差不大.     

MXene终端基团改性研究与应用进展

新型二维过渡金属碳化物/氮化物/碳氮化物MXene因其优异的结构特征和性能,逐渐成为当前低维材料的研究热点.MXene表面丰富的终端基团结构为其后续的改性研究提供了基础.在MXene片层表面通过改性去除或引入某些官能团,可实现MXene结构的可控调节,增加离子输运通道,扩大电荷存储容量,增强材料某项特性或获得其他特殊性...     

金属有机化合物化学气相淀积含钛硬质涂层的性能研究

在用文题淀积方法制备出氮化钛、碳氮化钛和碳氮氧化钛硬质涂层的基础上,用表面分析手段分别进行了成分、结构分析、形貌观察和硬度测定。结果表明:以二乙胺基钛为原料可分别在773K和973K淀积氮化钛和碳氮化钛涂层;用钛酸异丙酯和钛酸丁酯可分别在973K和1073K获得碳氮氧化钛涂层。所得的涂层表面光洁度高、与基体附着性好、硬度满足实用要求。相比于普通化学气相淀积方法,本法在制备硬质涂层上有两大优点:(1)淀积温度降低,扩大了基体的选用范围;(2)固溶体涂层的获得扩大了涂层的适用范围。     

合金元素对TiC与钢润湿性的影响

本文用静滴法测定了TiC与45钢的润涅角。发现合金元素Mo、Ti均有改善其润涅性的作用,尤以钼的效果最为明显。     

<Emphasis Type="Italic">In situ</Emphasis> synthesis of TiC reinforced Cu<Subscript>47</Subscript>Ti<Subscript>34</Subscript>Zr<Subscript>11</Subscript>Ni<Subscript>8</Subscript> bulk metallic glass composites

In situ synthesized TiC particles and β-Ti dendrites reinforced Cu47Ti34Zr11Ni8 bulk metallic glass (BMG) composite ingots were prepared by the suction casting method.The ingots with diameters from 1 up to 4mm were successfully obtained. It was shown that introducing TiC micro-sized particles into the amorphous matrix did not disturb the glass forming ability (GFA) of the matrix,while the yield strength and ductility could be well improved.The phase constitution, microstructure and elements distribution in the composites were studied by OM, XRD, SEM and EDS.It was shown that the in situ synthesized TiC particles acting as heterogeneous nucleation sites promoted the precipitation of β-Ti dendrites, resulting in the formation of the TiC particles and β-Ti dendrites co-reinforced BMG composites. The compressive tests were employed to probe the yield strength and ductility of BMG composites.     

AgNWs/MXene增强的柔性多孔压阻传感器的制备与性能研究

随着物联网、人工智能等技术的兴起,柔性压阻传感器在人工触觉、健康监测、仿生电子皮肤等领域具有广阔的应用前景.目前柔性压阻传感器的灵敏度和稳定性与实际应用还存在一定的差距.本文中以AgNWs和MXene为导电材料,以具有良好生物兼容性的明胶为聚合物基体,采用冷冻干燥法制备一种多孔蜂窝状的AgNWs-MXene/明胶压阻传感器.测试结果表明所制备的柔性压阻传感器在0～14 kPa压强范围内具有3个线性响应区,在4～9 kPa压强范围内灵敏度最高,为116 kPa^-1.该传感器的响应时间最快可达1.79 s,且对人体脉搏跳动及肢体的运动状态具有良好的压阻敏感特性,表明实验所制备的柔性压阻传感器在柔性可穿戴电子器件领域具有良好的应用前景.     

固体粉末法渗覆氮化钛和碳化钛

用含钛和氮的化合物作渗剂，采用化学热处理方法，对20钢、45钢及W18Cr4V钢分别加热到850～950℃，保温6～8h，可以在试样表面得到TiN-TiC化合物层，层深0.3～2.2μm，显微硬度1894～1991HV，试验结果表明，在同一保温时间情况下，化合物层随加热温度升高而加深，在同一加热温度情况下，化合物层随保温时间延长而变厚。     

多孔Ti3C2Tx/SnSe复合材料的制备及其储钾性能

采用原位氧化-刻蚀法和水热合成法制备了多孔MXene复合材料(Ti₃C₂T_x/SnSe),并对所制备的材料进行了结构表征与电化学性能测试. 结果表明:在0.05 A/g的电流密度下,多孔Ti₃C₂T_x/SnSe电极具有381.9 mA ·h/g的储钾容量,而相同情况下SnSe电极的比容量仅为119.2 mA ·h/g. 在1 A/g的电流密度下,多孔Ti₃C₂T_x /SnSe电极的初始可逆比容量为118.5 mA ·h/g,循环500次的比容量仍保持在35.4 mA ·h/g. 多孔Ti₃C₂T_x/SnSe电极材料优异的电化学性能得益于多孔Ti₃C₂T_x材料的高导电性,它不仅缓解了SnSe的体积膨胀,而且为离子的转移提供了良好的通路.