一种超弹性SMA复合阻尼器的设计与试验

根据形状记忆合金(SMA)的超弹性特性,设计、制造了一种SMA复合摩擦阻尼器,该阻尼器利用SMA超弹性阻尼与SMA丝的约束作用使阻尼器内部产生摩擦来共同耗散振动能量.介绍了阻尼器的结构构造及工作原理.通过试验研究了加载频率、位移幅值对阻尼器力学性能的影响.试验结果表明,在试验频率范围内,阻尼器的刚度、输出力、耗能等主要力学参数随加载频率的改变而变化较小;位移幅值是影响这些力学参数的主要因素,当阻尼器在小位移的情况下,其刚度变化较小,而输出力和耗能与位移基本成线性关系.但在大位移的情况下,阻尼器的输出力变化较小,而其割线刚度减小,耗能有大幅度的增加.分析表明,该SMA复合阻尼器是一种位移相关性的变刚度阻尼器.     

Cr和Mn元素强化的α钛合金的制备及其组织性能

在前人已经优化评估的Ti-Al-Cr-Mn四元热力学数据库的基础上,设计了一种新型α钛合金Ti-6Al-3Cr-1Mn,并利用分瓣式水冷铜坩埚成功制得了该合金。该合金在770℃下经轧机轧制成6mm厚的板材,然后于750℃保温90min进行真空退火热处理,出炉后置于空气中冷却。通过组织观察,发现无论是铸锭还是退火后的板材,室温下均为α型钛合金,与设计相符。室温力学性能试验表明,Ti-6Al-3Cr-1Mn合金的力学性能良好,平均屈服强度为894.9MPa,抗拉强度为926.7MPa,断后延伸率为15.2%。Ti-6Al-3Cr-1Mn合金与典型的α型钛合金TA15相比,室温强度相当,但塑性更好,成本更低。Ti-6Al-3Cr-1Mn合金的自腐蚀电位为-0.21V,自腐蚀电流密度为7.7×10-7 A·cm-2,耐腐蚀性能良好。     

高压成型（PrNd）_xAl_（0.7）Nb_（0.6）Cu_（0.1）B_（1.05）Fe_（97.55-x）合金的超精细结构分析

采用高压和常压方式制备出（PrNd）xAl0.7Nb0.6Cu0.1B1.05Fe97.55-x（质量百分比）合金,由扫描电子显微镜、振动样品磁强计、穆斯堡尔谱仪和电子自旋共振谱仪对比研究了两种压制方式对样品微观结构、磁性能和超精细结构的影响.结果发现：与常规压制方式制备的样品相比,采用1.8GPa成型得到的样品Hcj（内禀矫顽力）和（BH）max（最大磁能积）分别提高了133kAm-1和0.6kJm-3;而采用3.6GPa成型样品的Hcj和（BH）max分别提高了120.3kAm-1和3.2kJm-3.高压成型样品的R-rich相、富B相和α-Fe相较少,围绕铁原子的其他原子固有的对称性被改变,g因子增大.0.2,1.8和3.6GPa成型得到样品的内磁场Hin分别为2.206×104,2.205×104和2.194×104kA/m.     

含镍磁黄铁矿硝酸浸出液中硝酸镁与硫酸镁的分离

硝酸催化浸出是处理金属硫化物的有效方法。用这种方法在较低温度和氧压下成功地处理了含镍磁黄铁,但矿石中的氧化镁与硫酸和硝酸反应生成硫酸镁和硝酸镁,后者消耗了大量硝酸;因而需要分离硫酸镁,返回使用硝酸镁才能保证浸出过程经济地进行。本研究测定了Mg(NO_3)_2-MgSO_4-H_2O系在343K,308K,以及Mg(NO_3)_2-MgSO_4-C_2H_5OH-H_2O系在298K的平衡相图。结果表明,蒸发结晶法及乙醇结晶法均能有效地分离出硫酸镁,但后者更为节能。加10％乙醇即可使硫酸镁与硝酸镁较好分离。     

N+离子注入Ti-4Al-2V合金的表面分析研究

作者采用3×1017/cm2和8×1017cm2两种注量对Ti-4Al-2V合金样品进行了N+离子注入,N离子能量75keV,在注入过程中样品温度控制在200℃以下.对注入前后的样品进行了X射线衍射(XRD)以及光电子能谱(XPS)分析.由XRD衍射谱表明,离子注入后有新相TiN和TiO2生成.由XPS宽程扫描谱表明,注入后样品表面主要为Ti,C,N和O.对Ti2p和N1s的XPS窄程扫描谱也证明,离子注入后致使合金近表面形成了TiN和TiO2.     

Preparing Ca-P coating on biodegradable magnesium alloy by hydrothermal method: In vitro degradation behavior

Magnesium alloys are potentially attractive biodegradable materials.However,their rapid corrosion rate limits their biomedical application.To slow down the rate of biodegradation,a protective calcium-phosphate coating was formed on a magnesium alloy substrate by a hydrothermal method.Scanning electron microscope results showed that the coating consisted of two layers with different crystalline characteristics.The loose outer layer showed a prism-like crystal structure,while the compact inner layer is a dense ultra-fine regular di-pyramid-like structure with an average grain dimension of ～200 nm.The compositions of the inner layer and outer layer were calcium-deficient hydroxyapatite (Ca-def HA) and dicalcium phosphate (DCPa),respectively.The coating adhered well to the substrate with a thickness of about 15 m.Immersion in Hank’s solution indicated that the coating could significantly improve the degradation properties of magnesium alloy.The pH of the solution containing the coated samples increased much more slowly than the untreated control.After 8 d immersion,the uncoated sample had corroded seriously while the coated sample was much less corroded.The Ca/P atom ratio in both the layers of the coating increased and the coating was still protecting the substrate.The two layers of the coating corroded differently because of differences in solubility.The outer layer was more severely attacked and many holes were formed on the surface,the inner layer suffered less attack.In addition,a growth of precipitate on the inner layer was observed,indicating that surface bioactivity was improved by the coating.Thus,magnesium alloys coated with a Ca-P coating prepared by a hydrothermal method are promising candidate biodegradable biomaterials,and further investigation of in vivo degradation behavior is suggested.     

低合金钢过冷奥氏体转变曲线CAD

用计算机对低合金钢的过冷奥氏体转变动力学进行了数学模拟，综合考 虑了冷却速度、合金化学成分和晶粒度等因素对过冷奥氏体转变的影响。利 用ｄＢＡＳＥ Ⅲ程序设计语言和ＢＡＳＩＣＡ程序设计语言建立了合金钢数据库， 并在ＩＢＭ－ＰＣ机上绘出了ＴＴＴ曲线及ＣＣＴ曲线。     

微量Co对Cu-0.2Be合金组织性能的影响

采用大气熔铸工艺制备不同Co含量的Cu-0.2Be-XCo合金（X=0、0.5%、1.0%,质量分数）,采用维氏硬度计、金属电导率测试仪及金相显微镜对合金的性能及组织进行测试.结果表明：随着Co含量的增加,铸态Cu-0.2Be-XCo合金的中心等轴晶区域逐渐扩大、粗大柱状晶区域减小,晶粒明显细化;Co的添加提高了铸态合金硬度,但同时降低了导电率,Cu-0.2Be-1.0Co合金的硬度较Cu-0.2Be合金增加23.5%,而导电率降低39.9%.合金经950℃×1 h固溶+460℃不同时间时效后,Cu-0.2Be合金导电率及硬度随时效时间基本不发生变化,Cu-0.2Be-0.5Co合金及Cu-0.2Be-1.0Co合金导电率及硬度在时效初期（0~2 h）急剧升高,中期（2~4 h）缓慢增加,后期（4~8 h）趋于稳定.时效态Cu-0.2Be-0.5Co合金的综合性能较佳,经460℃×2 h时效,导电率为57.1%IACS,硬度（HV）为243.     

ZL102表面直接化学复合镀Ni-P-SiC镀层的结构与性能

采用直接化学复合镀法在铸铝102合金表面制备Ni-P-SiC复合镀层,利用XRD、扫描电镜等对镀态复合镀层的结构和形貌进行分析,并对镀层的显微硬度、结合力及耐蚀性进行测试.结果表明:镀层表面平整均匀;复合镀层中SiC微粒分布均匀且复合量较高,镀层厚度均匀、致密;复合镀层相结构更类似于非晶态;镀层镀态显微硬度可达823.8HV;镀层与基体结合较好,且复合镀层极大地改善了基体的耐蚀性.     

添加Al_2O_3对95W-Ni-Fe合金微观组织与力学性能的影响

针对钨合金作为预制破片战斗部穿甲后的易碎性,研究了添加不同粒径Al2O3对95W合金微观组织与性能的影响.结果表明,随着添加的Al2O3粒径的减小,钨合金中钨颗粒的平均直径尺寸减小 获得的新型95W合金的静态抗拉强度和延伸率均低于传统95W合金,并且新型95W合金的强度和延伸率随着添加Al2O3初始粉末粒径的降低而增加 添加Al2O3初始粉末粒径的减小增大了新型95W合金的抗压强度 新型钨合金由于Al2O3的存在引发了大量初始裂纹并在承受冲击载荷时导致应力集中,微裂纹迅速连结并扩展后形成裂纹.