The Development of Materials for the Production of Hydrogen from Bio-ethanol

1 Results There is an increased interest in the hydrogen production from renewable sources. In this context, recently, numerous studies which use ethanol for hydrogen production have appeared. Ethanol is easily handled, non-toxic, and it can be obtained from biomass. The steam-reforming of bioethanol has been shown to beeffective for hydrogen production:C2H5OH 3 H2O  6 H2 2 CO2. Six moles of hydrogen can be yielded for each mole of ethanol reacted. However, depending on the catalyst used, other und...     

尖晶石型LiMn2O4的制备及结构研究

将LiNO3和以沉淀法制备的Mn3O4按一定比例混合制成样品，在空气气氛中分别以不同温度（300℃，400℃，500℃和700℃）进行烧结合成。利用差热－热重分析、X射线衍射、电子能谱及Raman光谱等测试手段对材料的结构及其随烧结温度变化情况进行了研究。首次观察到尖晶石型LiMn2O4的Raman特征峰。研究表明，低温烧结得到的样品为富氧的尖晶石型LiMn2O4；随着烧结温度的升高，结构中多余的氧逐渐放出，晶胞参数增大，晶体的结合能和晶格振动能增强。     

ZAO透明导电纳米薄膜中Al元素分布对其性能的影响

主要对直流反应磁控溅射法制备ZAO纳米薄膜中Al元素的相对含量进行了分析,对其作了EDS,XRD测试,并研究了Al质量分数与ZAO薄膜的光、电性能的关系·得出ZAO薄膜中成分是均匀的,具有ZnO晶体结构;Al元素的掺杂没有形成新的化合物(Al2O3),Al对Zn的掺杂替换是提高ZAO薄膜导电性能的关键因素,对薄膜在可见光区的透射性影响不大·制备的薄膜最低电阻率为4 5×10-4Ω·cm,可见光透射率达到80%以上·     

合肥盆地东部朱巷组X射线衍射分析及其油气意义

对取自合肥盆地大桥凹陷内下白垩统朱巷组(K1Z)21个泥岩样粘土矿物进行X射线衍射分析,定量研究表明,伊利石结晶度值均大于0.42,一般为0.42～0.75。伊利石/蒙皂石混层比有5个样品小于50.00%,其余为50.20%～70.10%,蒙皂石转化从无序间层到部分有序间层,反映地表处朱巷组处于成岩作用中-早期阶段,有机质成熟度处于成熟-未成熟阶段,没有进入埋藏变质。结合钻井Ro资料及地球物理资料,揭示朱巷组埋深大于3000m,预测深埋地下的朱巷组烃源岩已进入生油门限。     

分子筛结构和无定形结构中Ti-O-SiO_3键的IR特性

在对用ＸＲＤ表征确证分属于ＴＳ－２分子筛和无定形ＴＳ氧化物（简称ＡＴＳ）结构的一系列样品进行红外表征时，首次发现在分子筛骨架与无定形表面都存在Ｔｉ－Ｏ－ＳｉＯ３健，但这两者在红外上是可区分的，前者作为骨架钛振动带出现在９６２．５～９６６．７ｃｍ－１处，而后者作为非骨架钛振动带则出现在９４５～９５６ｃｍ－１处，即后者明显发生了红移．分子筛骨架振动带（１２２６，５５６ｃｍ－１）强弱对其Ｔｉ－Ｏ－ＳｉＯ３带的位置影响不大，比较而言骨架带弱的约有２．０ｃｍ－１的红移．苯酚羟基化结果表明在分子筛骨架上的Ｔｉ－Ｏ－ＳｉＯ３活性位上苯酚羟基化生成邻苯二酚和对苯二酚；而处于无定形表面的非骨架Ｔｉ－Ｏ－ＳｉＯ３活性位上只生成邻苯二酚     

Preparation and characterization of doubly substituted microwave absorbing material by sol-gel technique for super high frequency applications

Rare earth Dy~(3+)and divalent Mn~(2+)elements substituting W-type hexagonal ferrites Ba_(1-x)Dy_xZn_2Fe_(16-y)Mn_yO_(27)(x=0,0.02,0.06,0.1 and y=0,0.1,0.3,0.5)were prepared by sol-gel method.The thermo-gravimetric analysis(TGA)and differential scanning calorimetry(DSC)was carried out to find the temperature at which single phase can be obtained.XRD patterns indicate the presence of the single phase for all the synthesized samples with the absence of any extra peak due to unreacted material and secondary phases.The occurrence of absorption bands at low wave numbers(563 and 446 cm~(-1)),can be assigned to the stretching vibration of metal and oxygen ions in FTIR spectra,which also confirms the single hexagonal phase for prepared material.The grains are of platelet like structure,which enhances the microwave absorption properties of hexagonal ferrites.The synthesized material exhibits the minimum reflection loss of-20.9 dB at 11.8 GHz frequency,which reflects the applications of this material in super high frequency devices.The microwave conductivity of the material increases with frequency.     

过饱和Al-Zn-Mg-Cu-Mn合金热分解的XRD研究

利用雾化及高能低温球磨的方法制备了过饱和的Al-Zn-Mg-Cu-Mn合金粉,并利用XRD方法,研究了所得过饱和铝合金粉的热分解过程.研究结果表明,在350℃以下热分解时,过饱和固溶体析出的平衡相为η(MgZn2),XRD未检测出含锰相的存在.含锰铝合金粉在高于350℃分解时,除η(MgZn2)相外,析出相中还有Al6Mn,但未发现其他任何类型的亚稳含锰相,说明Al6Mn直接从过饱和的α-Al中析出,而非是先析出含锰的亚稳过渡相,由中间相转变为平衡相.     

溶剂热法实现ZnS晶体相变的反应条件研究

以去离子水和乙二胺作为溶剂,采用溶剂热法制备了ZnS晶体,探讨了反应时间、反应温度、溶剂配比等条件对ZnS晶体晶型转变的影响。采用X射线衍射仪、扫描电镜等手段进行了ZnS晶体物相结构及表征的分析。结果表明,通过简单调节反应参数可以实现ZnS晶体由立方闪锌矿到六方钎锌矿的相变;当反应时间大于10h,反应温度高于140℃,去离子水与乙二胺溶剂配比大于1的实验条件下所得样品为纯度较高的六方钎锌矿型ZnS;立方闪锌矿ZnS均为直径约3μm的单分散微球体,而六方钎锌矿ZnS是由许多纳米纤维缠绕而成的大小不一的球形颗粒。     

溅射于NiMnCo上的TiO2薄膜的结构与相变

利用射频磁控溅射方法以纯金属钛做靶材在氩氧混合气 体中制备了TiO₂薄膜. X射线衍射结果表明, 在NiMnCo合金基底上成功地沉积了 具有金红石、 金红石/锐钛矿和锐钛矿结构的TiO₂薄膜, 工作气压从0.2 Pa变 化到2 Pa, TiO₂薄膜的结构由金红石相变到锐钛矿相. 低于600 nm时, 厚度对T iO₂薄膜结构没有明显影响.     

Ni_(100-x)P_x合金的X射线谱学研究

利用X射线吸收精细结构(XAFS)和X射线衍射(XRD)研究了化学还原法制备的不同磷含量的Ni_(100-x)P_x合金的原子和电子结构.结果表明,当x=10时,磷元素的掺入导致了NiP样品中fcc结构的镍晶格扭曲和膨胀,Ni-Ni第一近邻配位的键长约增加0.03 A.随着磷含量的增加,膨胀和扭曲加剧,当x达到14左右时,样品的fcc-Ni晶格被完全破坏,从而形成非晶态NiP合金.X射线吸收近边结构(XANES)的结果表明,低磷含量(x≤10)时NiP样品的电子结构没有明显的变化,随着磷含量的增加,Ni4p态的分布变得宽化和越来越弥散.而当x达到26时,有大量电荷从Ni原子转移到P原子.