Al_2O_3对钼合金组织与性能的影响

以二氧化钼和硝酸铝为原料,用液-固掺入法制备了Al2O3体积分数分别为3%、5%、7%和10%的钼合金。测定了混合钼粉的粒度、钼基体的显微硬度、钼合金的密度及磨损性能,用SEM观察了混合钼粉的形貌与钼合金的显微组织,用XRD分析了钼合金的相组成。结果表明:钼合金由Mo和Al2O3组成;随Al2O3体积分数增加,钼合金晶粒细化,钼基体显微硬度增加,钼合金密度先增加后减小;钼合金摩擦因数受Al2O3体积分数的影响较小,摩擦因数的值在0.47～0.57之间波动;随Al2O3体积分数增加,磨损量不断减少,磨损类型主要以滑动磨损为主,磨损表面有明显的犁沟和磨屑。     

石墨、铝电极低压脉冲电解含油废水效果对比

对铝、石墨电极-低压脉冲电解含油废水影响因素:时间、电压、频率、占空比、电解质进行了对比试验.结果表明:石墨电极和铝电极电解效果与支持电解质Na2SO4用量有较为明显的关系,当Na2SO4用量小于0.7%时,石墨电极的油去除率高于铝电极;大于0.7%时,铝电极的油去除率高于石墨电极.在支持电解质Na2SO4用量较高的条件下,石墨电极油去除率受电压、占空比、频率因素影响较大,随频率增加而增加,随电压、占空比增加油去除率先增加而后下降;当电压大于6 V,频率高于500 Hz,占空比大于30%时,改变参数对铝电极的油去除率影响不显著.     

Al掺杂TiO_2的制备及酸化处理对其光催化活性的影响

锐钛矿相TiO2的光催化活性高于金红石相。采用化学溶液分解法制备了Al掺杂锐钛矿TiO2,并用硝酸对其进行酸化处理。利用TG-DTA、XRD、FTIR、BET和UV-vis等手段对样品进行了表征,通过对甲基橙的降解分析了酸化处理对Al掺杂TiO2光催化活性的影响。结果表明:掺杂Al能有效抑制TiO2由锐钛矿向金红石转变。酸化处理因能增大Al掺杂TiO2的比表面积而使其光催化活性提高。Al/Ti掺杂比为1∶4的样品在酸化处理后具有的光催化活性最高,60min后对甲基橙的降解达到100%。     

枇杷酒中总黄酮的测定

采用可见分光光度法进行测定,确定枇杷酒中总黄酮的含量,并通过单因素实验和正交实验优化了测定条件。确定了NaNO2、Al（NO3）3和NaOH浓度分别为4%、0.5%和6%（质量分数）时最适合用于枇杷酒中总黄酮含量的测定。最后,通过芦丁标准曲线确定总黄酮含量。以上方法简便、稳定、可靠,容易操作,可以作为总黄酮含量的测定方法之一。     

ZL102铸造铝合金炊具防粘涂层鼓泡原因的研究

用金相显微镜和电子探针研究了ZL102铸造铝合金炊具防粘涂层部分产品在使用过程中逐渐产生鼓泡的原因.结果表明:产生鼓泡的产品是由于浇注前精炼、变质处理不充分,残留在合金缺陷(如气孔、疏松等)中的杂质,在高温使用过程中,逐渐扩散至表面,在防粘涂层下面产生一定的压力而引起的.     

制备方法对Pt在氧化铝上分布状态的影响

以不同的浸渍方式制备了Pt/γ -Al2 O3 催化剂 ,通过体视显微镜观察其分布型式 ,用 5 %CO/He脉冲化学吸附法研究了Pt在催化剂颗粒中的分散度 .研究结果表明 :浸渍液的pH值、浸渍时间、竞争吸附剂的性质对Pt在γ -Al2 O3 球上的径向分布影响较大 ,以Pt溶胶为前驱物比以氯铂酸溶液为前驱物制得样品的分散度略高 .     

桑色素-铝离子-核酸三元体系的研究及其分析应用

用分光光度法研究了桑色素-铝离子-核酸三元体系。在pH 3.25的Britton-Robinson介质中, 桑色素在250,300和350nm处有吸收峰。铝离子的加入使桑色素350nm处的吸收峰下降, 在419nm处出现桑色素-铝络合物的吸收峰。再往桑色素-铝离子二元体系中加入核糖核酸或脱氧核糖核酸, 则进一步引起桑色素350nm吸收峰的降低,419nm处的吸收大大加强, 同时在370nm处有一等色点。419nm处吸光度的增加值与加入的核酸量在一定范围内成正比, 基于此建立了在较宽范围内测定核酸的方法。其线性范围分别为：ρ(ct DNA), 0.71～35.4μg/mL;ρ(fs DNA), 0.64～25.6μg/mL;ρ(y RNA), 0.94～28.4μg/mL。     

Cu-Zn-Al-Cr催化剂还原行为的热分析研究

通过共沉淀法制备了不同组分的Cu-Zn-Al-Cr催化剂,并采用热重法分析了催化剂的还原失重,由失重数据推算出,不同组成Cu-Zn-Al-Cr催化剂还原后,CuO均还原为零价,Al2O3,ZnO未被还原,Cr则随引入时价态和催化剂组成的不同分别还原为＋4价和＋2价,催化剂用于1,4－丁二醇脱氢制γ－丁内酯的活性比较数据表面,Cu^0是活性中心,ZnO和CrO2可使催化剂的选择性明显提高。     

Formation of nanocrystalline during flash welding of 0Cr16Ni22Mo2Ti steel

A nanocrystalline layer was fabricated in bond area of 0Cr16Ni22Mo2Ti austenite steel using flash welding. The mean grain size near bond line is about 20 nm, and the farther the distance from bond line, the larger the size of the nanocrystalline. The thickness of the nanocrystalline layer is about 50 -m. The formation mechanism of the nanocry- stalline may be that the metal in semisolid state is deformed severely and its solid grains are fragmented.     

Study on ZnO:Al (ZAO) films by DC reaction magnetron sputtering

The high quality ZnO: A1 films were successfully produced by DC reaction magnetron sputtering technology. The Al-doping effect on electrical and optical properties and its scattering mechanism are discussed in detail. The analyses of X-ray diffractometer (XRD), X-ray photoelectron spectroscopy(XPS) and high resolution Auger electron spectroscopy (AES) show that Al2O3 could be effectively removed by controlling oxygen flow and Al-doping concentration during deposition of ZnO: Al films. Zn, Al and oxygen elements are well distributed through the films. For highly degenerated ZnO:A1 semi-conductive thin films, the theoretical and experimental results reveal that the ionized impurity. scattering dominates the Hall mobility in the films in the low-temperature range, while the lattice vibration scattering becomes a major scattering mechanism in the high-temperature range. The grain boundary scattering only plays a major role in the ZAO films with small grain size (as compared to the electron mean free path). The photoelectric properties of ZAO films show that it has low resistivity ( ～ 5 × 10-4 Ωcm), and the transmittance in visible range and the reflectance in IR region are above 80% and 60%, respectively.