Preparation and Mechanical Properties of a Novel Textile Pad for Wound Debridement

Various types of wound debridement approaches are currently available in clinical practice such as autolytie, enzymatic. biodebridement, mechanical, and surgical debridemenl techniques. A critical look at these various options can explain their potential but also their limitations. In this study, a novel textile pad, which is composed of polyester filaments on the fleecy side and a bioeompatible coating on the opposite side, was made to provide a safe, inexpensive, easier and especially more efficient debridement process that can be used in all healthcare settings by all healthcare practitioners. Eighteen kinds of samples were prepared with different pile density, ground yarn count and coating amount. Dimensional morphology, stitch density, mass per unit area and mechanical properties were investigated to study the intrinsic relationship of structure and properties of textile pad for wound debridement. Results showed that tensile strength and suturing strength at piped site increased obviously with the increment of ground yarn count, while the amount of coating could also have a slight impact on these two properties. However, compressive load was mainly affected by pile density, with no obvious relation to ground yarn count and coating amount.     

水热法制备Li_(4-3x)Eu_x(WO_4)_2微晶及其发光性能

采用水热法制备了Li_(4-3x)Eu_x(WO_4)_2系列红色荧光粉.通过荧光分析(FL)、扫描电镜(SEM)和X射线衍射(XRD)对所得粉体的发光性能、颗粒大小及形貌和物相进行表征分析.XRD分析结果表明,制备的Li_(4-3x)Eu_x(WO_4)_2微晶均为白钨矿四方结构.SEM结果表明,Li_(4-3x)Eu_x(WO_4)_2颗粒度为2.0μm×0.2μm~12μm×1.0μm,且随x的增大而增大.荧光分析结果表明,该荧光粉可被近紫外光(395nm)有效激发,最大发射波长位于614nm,即为纯正的红光.随着x的增大,样品中Eu~(3+)的593nm和614nm两个特征发射峰的强度先增大后减小,当x=1.0时达到最大.     

离子液体[C2mim]NO3与[C2mim][MetSO4]的热力学性能研究

采用MDY-2型密度仪在常压、一定温度范围内对离子液体1-乙基-3-甲基咪唑硝酸盐(简写为[C2mim]NO3)和1-乙基-3-甲基咪唑硫酸甲酯盐(简写为[C2mim][MetSO4])的密度进行了测定.结果表明,离子液体的密度随温度升高呈线性下降的趋势.由离子液体的密度值计算得到离子液体[C2mim]NO3和[C2m...     

新型微生物源天然食品防腐剂及其抑菌性能

天然食品防腐剂按其来源不同可分为植物源天然防腐剂、动物源天然防腐剂以及微生物源天然防腐剂等类型。天然微生物源食品防腐剂由于其本身的优越性,越来越受到人们的青睐。主要对5种新型微生物源天然食品防腐剂(即乳球菌肽、溶菌酶、聚赖氨酸、苯乳酸及曲酸)的理化特性、抑菌机制和抑菌特性等进行了概括和论述,旨在为我国新型、安全、高效微生物源天然食品防腐剂的研究和开发提供参考。     

Enhanced mechanical properties of AZ31 magnesium alloy sheets by continuous bending process after V-bending

The effects of V-bending process, continuous bending process and combination process on the microstructure and mechanical properties and formability of an AZ31 magnesium alloy sheet were investigated. The experimental results showed that no twins were found in the microstructure of all samples after processes due to the fine grain. The V-bending and continuous bending processes were proved to be an effective approach to modify the mechanical properties and formability. While the samples after the combination process exhibited better mechanical properties and formability than the single processed sample. The yield strength significantly decreased with the value of 100 MPa and the fracture elongation enhanced to 18.3% at room temperature. The Erichsen value was 5.0 mm which was significantly increased by 117% compared with as-received sample. The superior formability of combination processed samples was mainly attributed to the smaller r-value and n-value.     

Microstructure and properties of in-situ synthesized Cu-1 wt%TiC alloy followed by ECAP and post-annealing

A dispersion-strengthened copper alloy with 1 wt% TiC for commercial electrical-contact wires was prepared by in-situ reaction casting, grain-ultrafining by equal-channel angular pressing (ECAP) and subsequent annealing with aim to obtain excellent comprehensive performance. The results showed that fine TiC particles were in-situ synthesized in the as-cast Cu matrix and aggregated in clusters, and thus mechanical properties of the as-cast alloy deemed insufficient. Continued ECAP at 473 K significantly refined the grains of the as-cast alloy and improved the distribution of TiC particles. Due to multiple strengthening mechanisms, the ECAP-processed alloys maintained good conductivity with obviously enhanced tensile strength and hardness values. After post-ECAP annealing, the elongation and conductivity of the fine-grained copper alloy increased with the adequate tensile strength. The novel combined process endows the alloy appropriate performance to serve current high-frequency electrification railway systems.     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

采用双等离子体制备非晶态碳膜的研究

采用直流金属磁过滤阴极真空弧(FCVA)制造出Ti和乙炔(C2H2)气体的双等离子体在单晶硅(100)上制备非晶态碳膜.重点研究了乙炔气体和过滤线圈电流对非晶态碳膜的结构、形貌和机械性能的影响.研究结果表明,薄膜中主要成分是TiC,并以(111)作为主晶向;随着过滤线圈电流的增大,薄膜的晶粒度越来越小;薄膜表面的粗糙度逐渐减小,变得更加平整;薄膜的应力减小,可以下降到2.5 GPa.薄膜的显微硬度和弹性模量随着C2H2体积流qV(C2H2)的增大而降低,硬度和弹性模量分别可以达到33.9 GPa和237.6 GPa.非晶态碳膜的摩擦因数在0.1～0.25之间,大大低于衬底材料单晶硅片的摩擦因数0.6.随着过滤线圈电流增大,摩擦因数减小.     

掺铝氧化锌ZAO(ZnO:Al)薄膜研究

描述ZAO(ZnO:Al)薄膜的晶体结构,论述ZAO薄膜的光学、电学性质与其结构的关系,介绍了掺铝氧化锌ZAO薄膜的各种制备方法,并总结了ZAO薄膜在各种领域中的应用.提出了薄膜材料研究的关键问题以及今后的发展方向.     

消除7A05铝合金板材各向异性的热处理工艺

为提高7A05铝合金热轧板材的综合力学性能并减少各向异性,对7A05铝合金固溶、预时效、时效和形变处理等工艺对性能的影响进行了系统的研究. 比较了供货态、形变态、回归(RRA)态和采用预时效形变热处理的优化态热处理工艺对综合力学性能的影响. 结果表明:固溶的最佳温度为480 ℃,单级时效最佳工艺为120 ℃,24 h,双级时效中第一级时效最佳工艺为90 ℃,8 h,最佳形变为25%. 通过金相组织和力学性能测试结果表明:由于预时效析出促进形变热处理时亚晶等轴化,优化态强度高,进一步改善了合金性能,减少了轧制板材纵横向力学性能各向异性倾向.