Effect of Al on microstructure and mechanical properties of as-extruded Mg–1Mn alloy sheet

The effect of Al addition on microstructure and mechanical properties of hot extruded Mg–1 Mn alloy sheet was investigated. The results revealed that the dynamic recrystallization was promoted by increasing Al content. The ultimate tensile strength and yield strength of the alloy increased with the increase of Al content. The Mg–9 Al–1 Mn alloy exhibited the highest strength, with tensile strength of 308 MPa, 307 MPa, 319 MPa, yield strength of 199 MPa, 207 MPa, 220 MPa and the elongation of 20.9%, 20.1%, 19.2% in 0°, 45°, 90°, respectively.The high strength was mainly attributed to the formation of fine dynamically recrystallized grains and large amounts of the second phase. The strengthening mechanism of the alloys was explained.     

Microstructure,mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.     

浅谈铁和碱反应

文献［１～６］报道：“铁同强碱不发生作用”．我们用干燥的铁粉和氢氧化钠进行实验．实验证明：铁能跟强碱反应，反应的化学方程式为     

铝合金加工用刀具的使用研究（三）

当前我国各机械加工生产厂家引进国外进口设备及生产线较多，实现引进设备及生产线上刀具的国产化以降低生产成本，成为当前国内整个机械加工领域亟待解决的问题。     

气相Lys分子体系捕获双电子单重激发态的特性

采用密度泛函理论（DFT）中的B3LYP方法, 在6-311+G(2df)基组水平上, 对气相赖氨酸（Lys）分子和Lys^2-的基态稳定构型进行优化, 并用含时密度泛函理论（TD DFT)方法考察气相Lys分子和带电离子体系单重激发态的特性. 结果表明： Lys分子体系捕获双电子时, 其体系能量有所增加； S1单重激发态与S0基态能量差值变小； 分子体系的荧光波长增加； S7单重激发态跃迁轨道数减少.     

Influence of Microstructure and Sintering Routes on Transport Properties of Apatite Materials for Fuel Cells

1 Results Oxy-apatite materials are thought as zirconia-substitutes in Solid Oxide Fuel Cells due to their fast ionic conduction. However, the well known difficulties related to their densification prevent them from being used as such. This study presents strategies to obtain oxy-apatite dense materials and the influence of elaboration route on transport properties. Particular emphasis is put on the microstructure effect on ion conduction. By the combined use of freeze-drying and conventional or spark p...     

羧基淀粉的制备及其吸附性能的研究

本文研究羧基淀粉的制备条件与吸附重金属离子的容量关系,并研究它的使用条件和性能。     

Zn^2＋在电解还原铕（Ⅲ）过程中的催化行为研究

本文报道微量Zn~(2+)在电解还原铕(Ⅲ)离子过程中的催化作用,研究结果表明:当阴极中含Zn~(2+)时,铕(Ⅲ)离子将缩短到达定量还原的时间,用循环伏安法监控电极过程的结果表明:电极过程是准一级的催化过程。     

离子交换树脂非均相催化酯化合成丙烯酸丁酯

研究了在间歇搅拌釜中以阳离子交换树脂为催化剂，由丙烯酸和丁醇合成丙烯酸丁酯。分别考察了不同类型离子交换树脂的催化酯化作用，并且研究了搅拌速度、催化剂用量以及反应温度对酯化反应的影响。研究结果表明以KNC9型离子交换树脂在373.15-393.15K温度下具有最好的催化酯化作用。     

电磁相分离法制备自生表层复合材料

采用电磁相分离法制备出以初生富铁相（AlSiFeMn复杂金属间化合物）为增强相，表层硬度为HB62．25，基体硬度为HB59．00的Al-11.70%Si-1.20?-1.50%Mn合金自生表层复合材料，增强相的显微硬度为HV 842。87，大小为20－80μm，该表层复合材料同基体材料相比，耐磨性提高了57．41％，所用方法工艺过程简单，成本低，为解决材料在服役环境中不同部位，不同性能的问题提供了新途径。