相干测风激光雷达带通采样方法的仿真研究

根据相干测风雷达回波信号载频高、带宽窄的特点,尤其星载相干测风雷达回波信号数千兆赫兹,采用传统采样方式对采集卡的采样率要求很高.鉴于采集卡的采样率和分辨力互相制约,提出将带通采样引入到相干测风雷达系统.本文以1.5 μm全光纤相干测风激光雷达的实测数据作为仿真输入,经Simulink滤波、带通采样,结果表明,在对探测距离影响不大的情况下,与低通采样方式相比径向风速反演结果最大相差0.5 μm/s;数据处理的时间复杂度降低,其下降值是带通采样频率与低通采样频率的比值;但信噪比会恶化,其下降值介于1~3 dB.      

Effect of minor Sc on the microstructure and mechanical properties of AZ91 Magnesium Alloy

The as-cast and heat-treated microstructures and mechanical properties of the AZ91 magnesium alloys with and without minor Sc addition were investigated and compared in this paper. The results indicated that adding0.15–0.45 wt% Sc to the as-cast AZ91 alloy not only could modify and refine the Mg_(17)Al_(12) phase but also suppress the formation of the Mg_(17)Al_(12) phase. At the same time, the grains of the Sc-containing as-cast AZ91 alloys were also effectively refined. As a result, the mechanical properties at room temperature(RT) for the Sccontaining as-cast AZ91 alloys were effectively improved. In addition, adding 0.15–0.45 wt%Sc to the AZ91 alloy promoted the formation of the continuous precipitates(CP) during the aging treatment in spite of that the formation of the discontinuous precipitates(DP) was simultaneously suppressed. Accordingly, the Sc-containing as-aged AZ91 alloys obtained the relatively higher mechanical properties at RT than the as-aged AZ91 alloy.     

基于RSM和FEM的辊锻件长度控制技术

以某钩尾框精密辊锻工艺为研究对象,首次应用响应面法(RSM)和有限元数值模拟法(FEM)对精密辊锻件的长度控制问题进行了研究.首先以满足辊锻件长度和降低轧辊最大扭矩为目标,采用FORGE3有限元软件建立了RSM与FEM相结合的二阶分析模型,研究了轧辊间隙、摩擦因子、轧辊转速和坯料温度对辊锻件的长度和轧辊最大扭矩的显著性和影响规律;其次采用优化后的工艺参数对该辊锻工艺进行了再模拟,提出了辊锻件长度的调试原则,利用该原则和点的反追踪技术对辊锻模具进行了再设计,同时分析了设计、模拟和生产辊锻件的长度和辊锻过程的功率耗散和分布.研究结果表明:应用RSM和FEM可准确有效地掌握精密辊锻件的长度控制技术.     

An efficient identity-based key agreement protocol in a multiple PKG environment

Identity-based key agreement protocol affords a natural way to combine the participant’s identity with its public key.However,most of them just consider the key agreement in a single private key generator(PKG)environment.In addition,the existing key agreement protocols have a great computing overhead for mobile computing which is more and more popular today.This paper proposes a new identity based key agreement protocol.With the help of mathematical tools,we make our protocol applied in multiple PKG environment.It also satisfies all the security properties which is set for key agreement protocol.Moreover,some of its time-consuming operations can be delivered to untrusted public computation resources,so its computing complexity can be greatly reduced.     

河北省高校区域创新体系服务调查研究

高校是区域创新体系的重要主体要素。近年来,高校凭借其雄厚的科研基础和集聚的科研人才,迅速成为推动区域经济和社会发展的主要生长点和辐射源。研究通过对河北省高校为区域创新体系发展提供人才培养培训服务、平台服务和资源保障的实际情况,总结高校服务取得的成绩和存在的问题,并提出相关发展对策和建议。     

Effect of Ce addition on hot tearing behavior of AZ91 alloy

A small amount of cerium (below 1.0 wt%) addition to AZ91 alloy have been investigated on the hot tearing susceptibility (HTS) at a cooling rate of 1.5Ks^?1. The HTS increased to a maximum value with a cerium addition of 0.6 wt% and then decreased to a stable status as cerium was gradually added. Due to high chemical activity, cerium into the melts can react with aluminum to form an Al₁₁Ce₃ intermetallic compound. X–ray diffraction results also confirmed the existence of Al₁₁Ce₃. The Al₁₁Ce₃ increased with the presence of the needle-like and block morphology. As cerium levels increased, the amount of Mg₁₇Al₁₂ decreased. The variations between Mg₁₇Al₁₂ and Al₁₁Ce₃ resulted in a similar normal distribution of the HTS in AZ91 alloy. The findings were further verified through the microstructure evolution and the surface morphology of fracture.     

基于广义出行成本的出行方案优化

为了使出行成本更加符合出行者的认知规律,运用结构方程建模方法模拟出行成本,个体特征及出行决策之间的影响关系.引入敏感系数调整服务属性在出行成本中的贡献率,利用出行意愿调查数据对敏感系数进行标定.考虑出行者对抵达时刻的选择偏好,假设行程时间服从正态分布条件下,对最佳出发时刻及期望出行成本进行寻优求解,结果表明它取决于期望到达时刻,行程时间的期望值及方差,出行者对早到损失及晚到延误损失时间成本的相对大小.研究成果可为制定个性化及最优化出行决策方案提供依据.     

基于树状分子及炭黑复合纳米材料修饰电极的Cr(VI)电化学检测

用树状分子及炭黑纳米复合材料修饰玻碳电极,并对六价铬Cr(VI)进行电化学测定.采用X射线光电子能谱(XPS)、循环伏安法(CV)、交流阻抗法(EIS)、方波溶出伏安法(SWSV)等方法对修饰电极进行了表征.研究发现多种其他离子如Ni~(2+)、Co~(2+)、Pb~(2+)、Cu~(2+)、Cd~(2+)、NO_3~-、SO_4~(2-)、Cl~-等对六价铬离子的测定没有明显干扰,且Cr(VI)的还原峰电流与Cr(VI)的物质的量浓度在4~60 nmol/L和0.06~500μmol/L范围内呈线性关系,检测限达1 nmol/L.该法具有简便快速,选择性好,线性范围宽,灵敏度高等优点.     

苯并[1，2-b：4，5-b’]二噻吩-thieno[3，4-易]thiadiazole导电性的理论研究

采用密度泛函理论，在B3LYP／6—31G（d）水平下，对苯并[1，2-b：4，5-b’]二噻吩（BDT）-thieno[3，4-b]thiadiaz01e（TD）的低聚物和聚合物进行了理论计算．其中，BDT为电子供体，TD为电子受体，以1：2的方式结合形成化合物，并计算了二面角、分子内的电荷传输、桥键键长和中心键电荷密度．结果显示：随着聚合链增长，共轭程度增加．NICSs值显示：中心环比边环的共轭程度更大．聚合物的能带结构表明：该聚合物的带隙比较低（0．87eV），故其可以作为潜在的导电材料．     

Cobalt doped titanate nanotubes: Synthesis and properties

Cobalt oxide doped titanate nanotubes are synthesized with a simple hydrothermal treatment of mixed Co_3O_4 and TiO_2 powders. The formed tubular nanostructure, chemical composition,and the elemental distribution are analyzed using TEM, BET, FTIR, XRD, and XPS. The electrocatalytic activity towards oxygen evolution reactions and photodegradation against Rhodamine B are investigated. It has been found out that the oxygen evolutions starts at 0.8 V and reaches 0.98 mA ·cm~(–1) at 1.4 V vs. SCE. For photodegradation of Rhodamine B, the concentration decreased to 24% after 1 h irradiation using the sample with a mass percentage of 5% cobalt. The results demonstrate that the cobalt oxide doped titanate nanotubes are good candidates as electrocatalysts and photocatalytic materials.