Kinetics of discontinuous precipitation in Cu–20Ni–20Mn alloy

The morphology and growth kinetics of discontinuous precipitation (DP) in a Cu–20Ni–20Mn alloy were investigated in the temperature range of 523–673 K by optical microscopy, scanning electron microscopy, and transmission electron microscopy. A lamellar mixed structure consisting of alternating lamellae of a matrix and NiMn phase was observed in DP colonies. The volume fraction of regions formed by a DP reaction was determined by quantitative metallographic measurements. The kinetics of DP was evaluated on the basis of the Johnson–Mehl–Avrami–Kolmogorov equation, which resulted in a time exponent of approximately 1.5. We confirmed that the nucleation of the discontinuous precipitate was confined to grain edges or boundaries at an early stage of the reaction. The activation energy of DP process was determined to be approximately (72.7 ±7.2) kJ/mol based on the Arrhenius equation; this result suggests that DP is controlled by grain boundary diffusion. The hardness values exhibited good correlation with the volume fraction of DP; this correlation was attributed to the presence of the ordered NiMn phase.     

Enhanced photocatalytic activity of electrochemically synthesized aluminum oxide nanoparticles

In this study, aluminum oxide (Al₂O₃) nanoparticles (NPs) were synthesized via an electrochemical method. The effects of reaction parameters such as supporting electrolytes, solvent, current and electrolysis time on the shape and size of the resulting NPs were investigated. The Al₂O₃ NPs were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, transmission electron microscopy, thermogravimetric analysis/differential thermal analysis, energy-dispersive X-ray analysis, and ultraviolet–visible spectroscopy. Moreover, the Al₂O₃ NPs were explored for photocatalytic degradation of malachite green (MG) dye under sunlight irradiation via two processes: adsorption followed by photocatalysis; coupled adsorption and photocatalysis. The coupled process exhibited a higher photodegradation efficiency (45%) compared to adsorption followed by photocatalysis (32%). The obtained kinetic data was well fitted using a pseudo-first-order model for MG degradation.     

Effect of shot peening on hydrogen embrittlement of high strength steel

The effect of shot peening (SP) on hydrogen embrittlement of high strength steel was investigated by electrochemical hydrogen charging, slow strain rate tensile tests, and hydrogen permeation tests. Microstructure observation, microhardness, and X-ray diffraction residual stress studies were also conducted on the steel. The results show that the shot peening specimens exhibit a higher resistance to hydrogen embrittlement in comparison with the no shot peening (NSP) specimens under the same hydrogen-charging current density. In addition, SP treatment sharply decreases the apparent hydrogen diffusivity and increases the subsurface hydrogen concentration. These findings are attributed to the changes in microstructure and compressive residual stress in the surface layer by SP. Scanning electron microscope fractographs reveal that the fracture surface of the NSP specimen exhibits the intergranular and quasi-cleavage mixed fracture modes, whereas the SP specimen shows only the quasi-cleavage fractures under the same hydrogen charging conditions, implying that the SP treatment delays the onset of intergranular fracture.     

Effects of sphere size on the microstructure and mechanical properties of ductile iron–steel hollow sphere syntactic foams

The effects of sphere size on the microstructural and mechanical properties of ductile iron–steel hollow sphere (DI–SHS) syntactic foams were investigated in this study. The SHSs were manufactured by fluidized-bed coating via the Fe-based commercial powder–binder suspension onto expanded polystyrene spheres (EPSs). Afterwards, the DI–SHS syntactic foams were produced via a sand-mold casting process. The microstructures of specimens were investigated by optical microscopy, scanning electron microscopy (SEM), and energy- dispersive X-ray spectroscopy (EDS). The microscopic evaluations of specimens reveal distinct regions composed of the DI matrix, SHS shells, and compatible interface. As a result, the microstructures and graphite morphologies of the DI matrix depend on sphere size. When the sphere size decreases, the area fractions of cementite and graphite phases are observed to increase and decrease, respectively. Compression tests were subsequently conducted at ambient temperature on the DI–SHS syntactic foams. The results reveal that the compression behavior of the syntactic foams is enhanced with increasing sphere size. Furthermore, the compressed specimens demonstrate that microcracks start and grow from the interface region.     

Conductive and corrosion behaviors of silver-doped carbon-coated stainless steel as PEMFC bipolar plates

Ni–Cr enrichment on stainless steel SS316L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316L substrate. The corrosion resistance of this film in 0.5 mol·L-1 H₂SO₄ solution containing 5 ppm F- at 80℃ was investigated using polarization tests. The results showed that the surface treatment of the SS316L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316L, the Ag-doped carbon-coated SS316L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell (PEMFC) and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 mΩ·cm2 to 21.6 mΩ·cm2 at a compaction pressure of 1.2 MPa.     

Preparation of ultrafine silica from potash feldspar using sodium carbonate roasting technology

A novel process was developed for the preparation of ultrafine silica from potash feldspar. In the first step, potash feldspar was roasted with Na₂CO₃ and was followed by leaching using NaOH solution to increase the levels of potassium, sodium, and aluminum in the solid residue. The leaching solution was then carbonated to yield ultrafine silica. The optimized reaction conditions in the roasting process were as follows: an Na₂CO₃-to-potash feldspar molar ratio of 1.1, a reaction temperature of 875°C, and a reaction time of 1.5 h. Under these conditions, the extraction rate of SiO₂ was 98.13%. The optimized carbonation conditions included a final solution pH value of 9.0, a temperature of 40°C, a CO₂ flow rate of 6 mL/min, a stirring intensity of 600 r/min, and an ethanol-to-water volume ratio of 1:9. The precipitation rate and granularity of the SiO₂ particles were 99.63% and 200 nm, respectively. We confirmed the quality of the obtained ultrafine silica by comparing the recorded indexes with those specified in Chinese National Standard GB 25576―2010.     

Precipitation of flaky moolooite and its thermal decomposition

Moolooite particles with flaky morphology were synthesized by mixing dilute solutions of copper nitrate and sodium oxalate in the presence of citric acid. Solution pH value, citric acid concentration, and stirring were found to have large effect on the shape of the precipitated particles. Under the stirring, the radial area of flaky moolooite particles was enlarged and extended to become a thinner and larger flake. This is ascribed to growth promotion caused by the selective absorption of citric ligands onto a particular crystalline surface of the moolooite particles. Flaky shape of the moolooite particles tended to become spherical and disappeared completely when decomposed under an Ar atmosphere, leading to the formation of large porous aggregated particles composed of many tiny nanosized copper crystals.     

Fracture behavior and microstructure analysis of Al2O3–MgO–CaO castables for steel-ladle purging plugs

Three different castables based on the Al₂O₃–MgO–CaO system were prepared as steel-ladle purging plug refractories: corundum- based low-cement castable (C-LCC), corundum-spinel-based low-cement castable (C-S-LCC), and corundum-spinel no-cement castable (C-S-NCC) (hydratable alumina (ρ-Al₂O₃) bonded). The fracture behavior at room temperature was tested by the method of “wedge-splitting” on samples pre-fired at different temperatures; the specific fracture energy G′_f and notched tensile strength σ_NT were obtained from these tests. In addition, the Young’s modulus E was measured by the method of resonance frequency of damping analysis (RFDA). The thermal stress resistance parameter R′′′′ calculated using the values of G′_f, σ_NT, and E was used to evaluate the thermal shock resistance of the materials. According to the microstructure analysis results, the sintering effect and the bonding type of the matrix material were different among these three castables, which explains their different fracture behaviors.     

Microstructure evolution and thixoforming behavior of 7075 aluminum alloy in the semi-solid state prepared by RAP method

The effects of isothermal treatments on the microstructural evolution and coarsening rate of semi-solid 7075 aluminum alloy produced via the recrystallization and partial remelting (RAP) process were investigated. Samples of 7075 aluminum alloy were subjected to cold extrusion, and semi-solid treatment was carried out for 5–30 min at temperatures ranging from 580 to 605°C. A backward-extrusion experiment was conducted to investigate liquid segregation during the thixoforming process. The results revealed that obvious grain coarsening and spheroidization occurred during prolonged isothermal treatments. In addition, higher soaking temperatures promoted the spheroidization and coarsening process because of the increased liquid fraction and the melting of second phases. Segregation of the liquid phase caused by the difference in fluidity between the liquid and the solid phases was observed in different regions of the thixoformed specimens.     

Thermodynamic simulation of the effect of slag chemistry on the corrosion behavior of alumina–chromia refractory

The corrosion behavior of alumina–chromia refractory against two kinds of industrial slags (coal slag and iron smelting slag) at 1550°C was investigated via thermodynamic simulations. In the proposed simulation model, the initial slag first attacks the matrix and surface aggregates and subsequently attacks the inner aggregates. The simulation results indicate that the slag chemistry strongly affects the phase formation and corrosion behavior of the refractory brick. Greater amounts of alumina were dissolved and spinel solid phases formed when the brick interacted with iron smelting slag. These phenomena, as well as the calculated lower viscosity, may lead to much deeper penetration than that exhibited by coal slag and to more severe corrosion compared to that induced by coal slag. The thermodynamic calculations well match the experimental observations, demonstrating the efficiency of the proposed simulation model for evaluating the corrosion behavior of alumina–chromia refractory.