分级多孔纳米炭纤维的结构及电容性能

以酚醛树脂为碳源、PVP为纺丝助剂、纳米MgO颗粒为模板剂,通过静电纺丝法制得酚醛树脂基纳米炭纤维,经过炭化、KOH活化、酸洗后得到分级多孔纳米炭纤维,利用SEM、XRD、XPS、拉曼光谱仪及氮气吸脱附实验,对所制多孔纳米炭纤维的结构和形貌进行表征,并将其作为模拟电容器的电极,利用循环伏安、恒电流充放电及交流阻抗方法测试了材料的电化学性能。结果表明,KOH活化引入了数量可观的微孔,所得纳米炭纤维表现出明显的"微孔-中孔-大孔"分级孔分布的特点,其比表面积达到1058.4m~2/g,总孔容为1.64cm~3/g。电化学测试结果表明,所制分级多孔纳米炭纤维在6mol/L KOH电解液中显示出优异的电容性能,在0.2A/g的电流密度下,其放电比容量达到198F/g,在20A/g电流密度下,电容保持率达到65%。     

Nb微合金化对低合金高强钢耐海水腐蚀性能的影响

利用室内模拟海水加速腐蚀试验及电化学分析,研究了Nb微合金化对Cu-Cr-Ni-P系低合金高强钢耐海水腐蚀性能的影响。结果表明,含Nb钢与不含Nb钢组织均由铁素体和珠光体构成,但Nb微合金化后钢中珠光体组织减少且晶粒细化明显,其在模拟海水介质中的平均腐蚀速率与不含Nb钢相比,降低了约12%,阳极腐蚀电流密度也有所降低。由此可见,在Cu-Cr-Ni-P系低合金高强钢中加入Nb元素有助于提高其耐海水腐蚀性能。     

Effects of Zn content on the microstructure and the mechanical and corrosion properties of as-cast low-alloyed Mg–Zn–Ca alloys

The effects of Zn content on the microstructure and the mechanical and corrosion properties of as-cast low-alloyed Mg–xZn–0.2Ca alloys (x=0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively) are investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstructure of the 0.6Zn alloy is composed of α-Mg, Mg₂Ca, and Ca₂Mg₆Zn₃ phases, whereas 2.0Zn and 2.5Zn alloys only contain α-Mg and Ca₂Mg₆Zn₃ phases, as revealed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analyses. Moreover, with increasing Zn content, both the ultimate tensile strength (UTS) and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS (178 MPa) and the highest elongation to fracture (6.5%) are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides an updated investigation of the alloy composition–microstructure–property relationships of different Zn-containing Mg–Zn–Ca alloys.     

假塑性流体液滴撞击壁面上的铺展的格子Boltzmann模拟

流体液滴在壁面上的铺展与沉积在工业应用中存在广泛应用,研究非牛顿流体特性对液滴铺展的影响具有重要的实际意义。基于相场法建立了非牛顿幂律流体与牛顿流体的两相流格子Boltzmann模型,引入包括接触角影响的边界条件,模拟了假塑性流体在幂律指数（n）0.5~1.0以及韦伯数（We）5~45时液滴撞击壁面的铺展过程。结果表明：相对于牛顿流体,幂律流体的非牛顿特性会抑制液滴的铺展,且n越小,越有利于液滴沉积。此外,韦伯数越大,液滴越快地达到稳定。     

Effect of particle size distribution on the microstructure,texture,and mechanical properties of Al–Mg–Si–Cu alloy

The effect of particle size distribution on the microstructure,texture,and mechanical properties of Al–Mg–Si–Cu alloy was investigated on the basis of the mechanical properties,microstructure,and texture of the alloy.The results show that the particle size distribution influences the microstructure and the final mechanical properties but only slightly influences the recrystallization texture.After the pre-aging treatment and natural aging treatment(T4 P treatment),in contrast to the sheet with a uniform particle size distribution,the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids exhibits higher strength and a somewhat lower plastic strain ratio(r) and strain hardening exponent(n).After solution treatment,the sheet with a bimodal particle size distribution of large constituent particles and small dispersoids possesses a finer and slightly elongated grain structure compared with the sheet with a uniform particle size distribution.Additionally,they possess almost identical weak recrystallization textures,and their textures are dominated by CubeND {001}310 and P {011}122 orientations.     

Morphology and quantitative analysis of O phase during heat treatment of hot-deformed Ti_2AlNb-based alloy

A 1040°C-hot-deformed Ti_2AlNb-based alloy solution-treated at 950°C and aged at different temperatures was quantitatively investigated. The microstructure, size of the phase, and microhardness of the deformed alloys were measured. The results indicated that the microstructure of the deformed Ti_2AlNb-based alloy specimens comprise coarse O lath, fine O lath, equiaxed O/α_2, and acicular O phase. More O phase was generated in the deformed alloy after heat treatment because the acicular O phase was more likely to nucleate and grow along the deformation-induced crystal defects such as dislocations and subgrain boundaries. After deformation and subsequent heat treatment, the acicular O phase of the resultant alloy became finer compared to that of the undeformed alloy, and the acicular O phase became coarser and longer with the elevated aging temperature, while the width of the O lath exhibited unobvious variations. The hot deformation facilitated the dissolution of the O lath but accelerated the precipitation of the acicular O phase. When the 950°C-solution-treated deformed Ti_2AlNb-based alloy was then aged at 750°C for different periods, the phase content was nearly invariable, O and B2 phases eventually reached equilibrium, and the microstructure became stable and homogeneous.     

Developing anti-neoplastic biotherapeutics against eIF4F

Biotherapeutics have revolutionized modern medicine by providing medicines that would not have been possible with small molecules. With respect to cancer therapies, this represents the current sector of the pharmaceutical industry having the largest therapeutic impact, as exemplified by the development of recombinant antibodies and cell-based therapies. In cancer, one of the most common regulatory alterations is the perturbation of translational control. Among these, changes in eukaryotic initiation factor 4F (eIF4F) are associated with tumor initiation, progression, and drug resistance in a number of settings. This, coupled with the fact that systemic suppression of eIF4F appears well tolerated, indicates that therapeutic agents targeting eIF4F hold much therapeutic potential. Here, we discuss opportunities offered by biologicals for this purpose.     

基于CF-PCCs模型的维西县滑坡致灾因子敏感性分析

为了深入了解滑坡的成灾背景，减少灾害造成的生命财产损失，以云南省维西县为研究区，选取了高程、坡度、坡向、降水量、距河流距离、工程地质岩组、距断层距离、植被归一化指数（Normalized Difference Vegetation Index,NDVI）和道路密度9项致灾因子，利用确定性系数（Certainty Factor,CF）-皮尔逊积矩相关系数（Pearson Product-moment Correlation Coefficient,PCCs）模型对致灾因子进行敏感性分析，并对分析结果的准确性进行了验证.结果表明：(1)因子敏感性由高到低分别为坡向、河流、高程、降水量、断层、道路、坡度、工程地质岩组和NDVI；(2)敏感性最大的因子类别包括：高程为1 486～2 600 m，坡度为0°～20°，坡向为半阳坡，降水量为782～1 178 mm，距河流距离为0～300 m，工程地质岩组为极软岩，距断层距离为2 400～3 200 m,NDVI为-0.169～0.039，道路密度为80～117 km/km2；(3)CF-PCCs模型精度高，数据分析结果可靠，该方法可为滑坡敏感性分...     

不同冲击间隔分布下经典δ冲击模型的参数估计1

通过极大似然估计方法,对冲击时间间隔服从[0, b]上均匀分布、参数为λ的指数分布以及一般更新过程的经典δ冲击模型的参数δ、λ和b进行估计,得到了其相应的估计量。     

Deep cleaning of a metallurgical zinc leaching residue and recovery of valuable metals

Huge quantities of zinc leaching residues (ZLRs) generated from zinc production are dumped continuously around the world and pose a potential environmental threat because of their considerable amounts of entrained heavy metals (mainly lead). Most ZLRs have not been properly treated and the valuable metals in them have not yet been effectively recovered. Herein, the deep cleaning of a ZLR and recovery of valuable metals via a hydrometallurgical route were investigated. The cleaning process consists of two essential stages:acid leaching followed by calcium chloride leaching. The optimum conditions for extracting zinc, copper, and indium by acid leaching were a sulfuric acid concentration of 200 g·L-1, a liquid/solid ratio of 4:1 (mL/g), a leaching time of 2 h, and a temperature of 90℃. For lead and silver extractions, the optimum conditions were a calcium chloride concentration of 400 g·L-1, a pH value of 1.0, a leaching time of 1 h, and a temperature of 30℃. After calcium chloride leaching, silver and lead were extracted out and the lead was finally recovered as electrolytic lead by electrowinning. The anglesite phase, which poses the greatest potential environmental hazard, was removed from the ZLR after deep cleaning, thus reducing the cost of environmental management of ZLRs. The treatment of chlorine and spent electrolyte generated in the process was discussed.