Microstructure and electrolysis behavior of self-healing Cu-Ni-Fe composite inert anodes for aluminum electrowinning

The microstructure evolution and electrolysis behavior of (Cu₅₂Ni₃₀Fe₁₈)-xNiFe₂O₄ (x=40wt%, 50wt%, 60wt%, and 70wt%) composite inert anodes for aluminum electrowinning were studied. NiFe₂O₄ was synthesized by solid-state reaction at 950℃. The dense anode blocks were prepared by ball-milling followed by sintering under a N₂ atmosphere. The phase evolution of the anodes after sintering was determined by scanning electron microscopy and energy-dispersive X-ray spectroscopy. The results indicate that a substitution reaction between Fe in the alloy phase and Ni in the oxide phase occurs during the sintering process. The samples were also examined as inert anodes for aluminum electrowinning in the low-temperature KF-NaF-AlF₃ molten electrolyte for 24 h. The cell voltage during electrolysis and the corrosion scale on the anodes were analyzed. The results confirm that the scale has a self-repairing function because of the synergistic reaction between the alloy phase with Fe added and the oxide phase. The estimated wear rate of the (Cu₅₂Ni₃₀Fe₁₈)-50NiFe₂O₄ composite anode is 2.02 cm·a-1.     

Complementation in the composition of steel slag and red mud for preparation of novel ceramics

A method for preparing novel ceramics was developed in this study. Different ratios red muds were added to steel slags to optimize the preparation of novel ceramics by a traditional ceramic preparation process. The sintering mechanism, microstructure, and performance were studied by X-ray diffraction techniques, scanning electron microscopy, and combined experiments of linear shrinkage, water absorption, and flexural strength. The results confirmed that red mud can reduce the volumetric instabilities through the complementarity of red mud and ferroalloy slag. The crystal phases in the ceramics are all pyroxene group minerals, including diopside ferrian, augite, and diopside. The flexural strength of the ceramic that contains 40wt% red mud and was prepared at the optimal sintering temperature (1140℃) is greater than 93 MPa; its corresponding water absorption is less than 0.05%.     

Leaching behavior of V,Pb, Cd,Cr, and As from stone coal waste rock with different particle sizes

This paper investigates the leaching behavior of heavy metals (V, Pb, Cd, Cr, and As) from stone coal waste rocks with various particle sizes using dynamic leaching experiments. The results show that the dissolved concentrations of V and As initially increased and then slightly decreased as time progressed and that the dissolved concentrations of Pb, Cd, and Cr were high in the early stage before decreasing. The particle size of the stone coal waste rocks strongly influenced the heavy metal concentration in the leaching solutions. The effects of the particle size of the stone coal waste rocks on the dissolved concentrations of V, Pb, and As decreased in the order fine fraction > medium fraction > coarse fraction, and the effects of particle size on the dissolved concentrations of Cr and Cd decreased in the order medium fraction > coarse fraction > fine fraction and coarse fraction > medium fraction > fine fraction, respectively. The quantities of heavy metals dissolved from the stone coal waste rock with fine particle sizes were observed to decrease in the order V (17104.36 μg/kg) > As (609.41 μg/kg) > Pb (469.24 μg/kg) > Cr (56.35 μg/kg) > Cd (27.52 μg/kg), and the dissolution rates decreased in the order As (2.96%) > Pb (0.93%) > V (0.35%) > Cd (0.25%) > Cr (0.01%). The specific surface area, pore size of the stone coal waste rocks, and chemical forms of heavy metals also influenced the release of heavy metals from the stone coal waste rocks. Kinetic analysis showed that the dissolution of heavy metals fundamentally agreed with the rate equation controlled by the shrinking core model. The results of this study are expected to serve as a reference for the evaluation of heavy metals contamination from stone coal waste rocks.     

Microstructural characterization and oxidation resistance of multicomponent equiatomic CoCrCuFeNi-TiO high-entropy alloy

CoCrCuFeNi-TiO was prepared by arc melting of the pure elements and Ti₂CO powder under an Ar atmosphere. Both CoCrCuFeNi and CoCrCuFeNi-TiO alloys are composed of a face-centered cubic (fcc) solid solution, whereas the alloys of CoCrCuFeNi-TiO are basically composed of an fcc solid solution and TiO crystals. The microstructures of CoCrCuFeNi-TiO are identified as dendrite and interdendrite structures such as CoCrCuFeNi. The morphology of TiO is identified as an equiaxed crystal with a small amount of added Ti₂CO. By increasing the amount of Ti₂CO added, the TiO content was dramatically increased and part of the equiaxed crystals changed to a dendrite structure. A test of the oxidation resistance demonstrates that the oxidation resistance of CoCrCuFeNi-TiO is better than that of CoCrCuFeNi. However, as the TiO content increases further, a corresponding decrease is observed in the oxidation resistance.     

南图尔盖盆地SA区块河道砂体演化及定量刻画

针对河道砂体横向变化快而难以有效刻画评价的问题,综合应用分频检测、相位调整、地层切片及地质体雕刻等技术对南图尔盖盆地SA区块上侏罗统阿克萨布拉克组河道发育特征及期次进行了研究。首先,利用分频方法检测出目的层段可能存在的两期调谐厚度不同的河道沉积体;然后,采用波阻抗分析和90°相位转换,揭示目的层段地震负振幅与河道砂岩具有较好的对应关系;最后,在高频层序地层格架内制作等时地层切片的基础上,通过河道沉积特征及典型地层切片振幅的单井标定分析,识别并分期刻画出两期不同类型的河道砂体。结合河道弯度、宽厚比及储集体积等参数综合分析认为,早期河道具有低弯度曲流河特征,晚期河道为具有平直河特征的三角洲平原分流河道,且早期河道储集体积明显高于晚期河道。     

Improved hemimorphite flotation using xanthate as a collector with S(Ⅱ) and Pb(Ⅱ) activation

The flotation of hemimorphite using the S(Ⅱ)–Pb(Ⅱ)–xanthate process, which includes sulfidization with sodium sulfide, activation by lead cations, and subsequent flotation with xanthate, was investigated. The flotation results indicated that hemimorphite floats when the S(Ⅱ)–Pb(Ⅱ)–xanthate process is used; a maximum recovery of approximately 90% was obtained. Zeta-potential, contact-angle, scanning electron microscopy–energy-dispersive spectrometry (SEM–EDS), and diffuse-reflectance infrared Fourier transform spectroscopy (DRIFTS) measurements were used to characterize the activation products on the hemimorphite surface and their subsequent interaction with sodium butyl xanthate (SBX). The results showed that a ZnS coating formed on the hemimorphite surface after the sample was conditioned in an Na₂S solution. However, the formation of a ZnS coating on the hemimorphite surface did not improve hemimorphite flotation. With the subsequent addition of lead cations, PbS species formed on the mineral surface. The formation of the PbS species on the surface of hemimorphite significantly increased the adsorption capacity of SBX, forming lead xanthate (referred to as chemical adsorption) and leading to a substantial improvement in hemimorphite flotation. Our results indicate that the addition of lead cations is a critical step in the successful flotation of hemimorphite using the sulfidization–lead ion activation–xanthate process.     

Effect of melting temperature on microstructural evolutions,behavior and corrosion morphology of Hadfield austenitic manganese steel in the casting process

In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium silicate/CO₂ method, using a blind riser, and then the desired molten steel was obtained using a coreless induction furnace. The casting was performed at melting temperatures of 1350, 1400, 1450, and 1500℃, and the cast blocks were immediately quenched in water. Optical microscopy was used to analyze the microstructure, and scanning electron microscopy (SEM) and X-ray diffractrometry (XRD) were used to analyze the corrosion morphology and phase formation in the microstructure, respectively. The corrosion behavior of the samples was analyzed using a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS) in 3.5wt% NaCl. The optical microscopy observations and XRD patterns show that the increase in melting temperature led to a decrease of carbides and an increase in the austenite grain size in the Hadfield steel microstructure. The corrosion tests results show that with increasing melting temperature in the casting process, Hadfield steel shows a higher corrosion resistance. The SEM images of the corrosion morphologies show that the reduction of melting temperature in the Hadfield steel casting process induced micro-galvanic corrosion conditions.     

Mineral-phase evolution and sintering behavior of MO-SiO2-Al2O3-B2O3 (M=Ca,Ba) glass-ceramics by low-temperature liquid-phase sintering

In this work, network former SiO₂ and network intermediate Al₂O₃ were introduced into typical low-melting binary compositions CaO·B₂O₃, CaO·2B₂O₃, and BaO·B₂O₃ via an aqueous solid-state suspension milling route. Accordingly, multiple-phase aluminosilicate glass-ceramics were directly obtained via liquid-phase sintering at temperatures below 950℃. On the basis of liquid-phase sintering theory, mineral-phase evolutions and glass-phase formations were systematically investigated in a wide MO-SiO₂-Al₂O₃-B₂O₃ (M=Ca, Ba) composition range. The results indicate that major mineral phases of the aluminosilicate glass-ceramics are Al₂₀B₄O₃₆, CaAl₂Si₂O₈, and BaAl₂Si₂O₈ and that the glass-ceramic materials are characterized by dense microstructures and excellent dielectric properties.     

DARPA持续推动科技创新的挑战赛模式分析

 国防高级研究计划局（DARPA）是引领美军科技创新的"技术引擎"。为总结DARPA在推动科技创新方面的成功经验,回顾了DARPA代表性挑战赛的有关情况,分析了DARPA挑战赛模式的成功经验。研究表明,DARPA挑战赛模式充分利用了美国乃至世界的技术研发力量,取得了显著成效,目前已成为DARPA推动科技创新发展的重要途径,并引起美国其他创新机构和世界各国的广泛关注与纷纷效仿。     

基于ICA变量分组的集成软测量方法研究

提出了一种基于独立主成分分析（independent component analysis,ICA）变量分组和集成学习的软测量建模方法.该方法首先运用ICA对输入过程变量进行分组,建立多个变量组子空间.然后在各变量组子空间内提取子样本集,降低变量和变量组之间的耦合性,并基于核偏最小二乘法（KPLS）建立预测子模型.最后,采用贝叶斯方法对子模型的输出进行集成,给出最终预测结果.运用该方法对工业橡胶密炼过程的数据进行了预测,并与其它软测量方法的结果进行比较分析,实验结果表明,本文提出的方法具有更好的预测性能.