Dielectric properties, electrical modulus and current transport mechanisms of Au/ZnO/n-Si structures

Au/Zn O/n-Si(MIS)structures were fabricated by using the RF sputtering method and their complex dielectric constant(ε~*=ε’-jε’’),electric modulus(M~*=M′+j M’’)and electrical conductivity(σ=σ_(dc)+σ_(ac))values were investigated as a function of frequency(0.7 k Hz-1 MHz)and voltage(-6–(+6 V))by capacitance-voltage(C-V)and conductance-voltage(G/ω-V)measurements to get more information on the conduction mechanisms and formation of barrier height between Au and n-Si.The lnσ-Lnf plots have two different regions corresponding to low-intermediate and high frequencies.Such behavior of lnσ-lnf plots shows that the existence of two different conduction mechanisms(CMs)at low-intermediate and high frequencies.Moreover,the reverse bias saturation current(I_o),ideality factor(n),barrier height(Φ_(Bo))were determined from the forward bias I-V data and they were found as a strong function of temperature.The value of n especially at low temperature is considerably higher than unity.The values ofΦ_(B0)and standard deviation(σ_s)were found from the intercept and slope ofΦ_(Bo)-q/2k T plots as 0.551 e V and 0.075 V for the region I(80–220 K)and 1.126 e V and 0.053 V for the region II(220–400 K),respectively.The values ofΦ_(Bo)and effective Richardson constant(A~*)were found from slope and intercept of activation energy plots as 0.564 e V and 101.084 Acm~(-2)K~(-2)for the region I and 1.136 e V and41.87 Acm~(-2)K~(-2)for the region II,respectively.These results confirm that the current-voltage-temperature(I-V-T)characteristics of the fabricated Au/Zn O/n-Si SBDs can satisfactorily be explained on the basis of TE theory with double GD of the BHs.     

基于饱和沉淀Ca（DBS）2及结合 MBFGA1絮凝沉降去除罗丹明b

通过提高溶液中十二烷基苯磺酸钙(Ca(DBS)2)沉淀的析出,结合微生物絮凝剂GA1(MBFGA1)对Ca(DBS)2的絮凝作用,将阳性染料罗丹明b(RB)从溶液中絮凝去除.在整个絮凝过程中,十二烷基苯磺酸钠(SDBS)增溶RB分子,然后在过量Ca~(2+)的影响下,增溶了RB分子的Ca(DBS)2悬浮物充分析出,最后被MBFGA1絮凝沉淀.为了提高RB的去除效率,采用响应面分析法(RSM)对Ca~(2+)、SDBS及MBFGA1初始浓度进行优化.实验结果表明,最优条件下(SDBS:2.67 mmol/L、Ca~(2+):5.61 mmol/L、MBFGA1:4.34 mL/L),RB和SDBS去除率达到99.80%和90.03%,其出水COD值为89.69 mg/L,低于国家工业废水排放标准,无需进行后续处理.同时,采用环境扫描电镜(ESEM)来探讨RB的絮凝去除机理以及SDBS和Ca~(2+)之间的相互作用.当Ca~(2+)初始浓度相对SDBS初始浓度过量时,增溶RB分子的SDBS胶团(SDBSRB胶团)会与Ca~(2+)反应生成被RB分子附着的Ca(DBS)2颗粒(Ca(DBS)2-RB颗粒),最后Ca(DBS)2颗粒被MBFGA1絮凝沉降;而当SDBS初始浓度相对Ca~(2+)初始浓度过量时,Ca(DBS)2颗粒会逐渐复溶并生成大量的附着Ca~(2+)的SDBS胶团.     

Distribution and ecology of freshwater Ostracoda (Crustacea) collected from springs of Nevada, Idaho, and Oregon: a preliminary study

Fourteen freshwater ostracod species collected from 24 springs in Nevada, Idaho, and Oregon between 1991 and 1994 were classified. Their ecology, based on major water parameters (i.e., temperature, dissolved oxygen, pH, conductivity), and biogeographical distribution in North America were studied. Among these 14 species, 9 ( Ilyocypris bradyi , I. gibba , Darwinula stevensoni , Candona candida , Heterocypris incongruens , Herpetocypris reptans , H. chevreuxi , Prionocypris canadensis , P. longiforma ) are new records for Nevadas ostracod fauna, while 3 ( H. reptans , P. canadensis , and Cypria turneri ) are new species for Oregon. H. reptans , P. canadensis , and Heterocypris salina are also recorded as new for the ostracod literature of Idaho. Scottia pseudobrowniana , collected from Nevada, is a new ostracod species for the United States. The occurrence of 5 Holarctic species in the northern Great Basin area may suggest a possible historical relationship with the European ostracod fauna.     

串列双方柱的风压特性及其流场机理

为了研究干扰条件下方柱的风压特性及其流场机理,以串列双方柱为研究对象,采用大涡模拟方法,在雷诺数Re=8×104、间距比P/B=1.1～5的条件下,研究了两个方柱的风压系数、气动力系数、风压非高斯特性、风压相关性随间距比的变化规律,重点探讨了双方柱流场特性及其与风压非高斯特性的内在联系.研究结果表明:随着间距比的增大,串列双方柱依次表现为3种流态,即单一钝体、剪切层再附和双涡脱流态,风压特性与流态密切相关.风压的非高斯特性和风压相关性随流态变化呈现为3种类型:在单一钝体流态下,柱间回流区附近的表面风压呈现明显的非高斯特性且风压相关性较强;在剪切层再附流态下,方柱尾流的涡脱强度低,风压相关性弱,但风压非高斯区域大;在双涡脱流态下,受上游方柱尾流旋涡的作用,方柱侧风面的风压相关性较强,下游方柱的侧风面和背风面出现大范围的风压非高斯区域.     

不同气候下海峡两岸建筑抗风标准之基本风速比较

为明确闽台两地基本风速的合理取值,以台北市某气象站1961-2015年的实测风速数据为研究对象,基于两岸现行建筑结构抗风标准,分别选用年最大风速法和台风风速法取样,采用极值I型分布模型,对不同气候模式下的基本风速进行了比较研究.结果表明:对于相同的风速观测数据,根据台湾建筑抗风标准TB2015获得的极值风速略小于现行建筑抗风标准GB50009获得的极值风速(福建),而基本风速正好相反,但是两者之间的差别均很小;台风气候模式下的极值风速/基本风速预测值要大于混合气候模式下的对应值,且与实测极值/基本风速最为接近,误差均小于0.5％;对于受台风影响严重的海峡两岸地区,建议采用以台风风速法取样的台风气候模式下的基本风速.     

斜拉桥多索-浅拱-弹性约束模型及面内自由振动

考虑斜拉桥的初始构型和支座刚度,建立了竖向弹性约束下的多索-浅拱动力学模型.首先基于索和浅拱的经典动力学方程,将浅拱在索-拱耦合处分段,推导了竖向弹性约束多索-浅拱的面内自由振动理论.然后采用分离变量法对其面内特征值问题进行了求解.同时以双索-浅拱模型为例,建立了相应的有限元模型,并将论文方法算出的频率和模态与有限元结果进行对比,从而验证了论文方法和模型的正确性.最后,对竖向弹性约束双索-浅拱的动力学特性进行了系统的参数化分析.结果表明:竖向刚度对系统的动力学特性有着明显的影响.     

钢纤维再生混凝土抗折强度尺寸效应试验研究

通过5组再生骨料取代率和4组钢纤维体积掺量小梁试件的四点弯曲试验,研究了再生骨料取代率和钢纤维掺量对再生混凝土抗折强度及尺寸效应的影响.结果表明:各规格小梁试件的抗折强度均存在尺寸效应,随再生骨料取代率的增加,再生混凝土抗折强度尺寸效应呈先增大后降低的规律,取代率为75％小梁试件抗折强度尺寸效应约分别为取代率为0和100％试件的1.32倍和1.09倍.钢纤维掺量对再生混凝土抗折强度尺寸效应有一定影响,当掺量为0～0.75％时,钢纤维掺量越大,尺寸效应越明显,钢纤维掺量分别为0、0.25％和0.50％时,试件抗折强度尺寸效应约分别为钢纤维掺量0.75％试件的77％、85％和94％.钢纤维掺量较大时,钢纤维掺量对尺寸效应的影响较弱,钢纤维掺量为0.75％试件抗折强度尺寸效应度约为1.00％掺量试件的99％.提出了再生混凝土抗折强度尺寸效应律计算公式,可用于再生混凝土抗折强度的分析计算.     

正前角金刚石磨粒磨削钛合金仿真与试验研究

为研究正前角金刚石磨粒磨削加工的机理,论证正前角磨削的可行性,采用有限元仿真软件ABAQUS建立单颗金刚石磨粒磨削Ti6Al4V钛合金过程的模型,对比研究不同工艺条件下具有正、负前角的单颗金刚石磨粒磨削过程中磨削力的变化规律.在此基础上,分别针对飞秒激光加工的正前角金刚石磨粒和原始的负前角金刚石磨粒开展钛合金磨削试验,采用测力仪测量磨削力,并将测得的磨削力与仿真结果进行对比;观测磨削加工表面形貌,测量表面粗糙度,将正、负前角磨削时的磨削力、磨削加工表面形貌和表面粗糙度进行对比.结果表明,在单颗金刚石磨粒磨削中,磨削力随着磨削速度的增大而减小,随着磨削深度的增加而增大,随着磨粒前角由负到正而逐渐减小,仿真得到的磨削力与试验结果的变化趋势基本吻合.相比于传统的负前角磨削,正前角金刚石磨粒具备良好的耐磨性,磨削表面磨痕较浅、加工缺陷少,表面粗糙度值降低58％～66％,可有效提高磨削加工表面质量.     

聚苯胺基气凝胶衍生纳米碳的电化学性能研究

采用树枝状聚苯胺,长纤维聚苯胺,树枝状聚苯胺-石墨烯以及长纤维聚苯胺-氮掺杂石墨烯4种气凝胶作为前驱体,经直接碳化后获得了氮掺杂连续的纳米碳.研究了聚苯胺基气凝胶衍生纳米碳的微观形貌结构、元素组成以及电化学性能.结果表明,树枝状聚苯胺,长纤维聚苯胺,树枝状聚苯胺-石墨烯以及长纤维聚苯胺-氮掺杂石墨烯气凝胶衍生的纳米碳具有连续的多级孔结构,其比表面积分别为273.9、487.7、241.4和295.9 m2·g-1,氮的摩尔分数分别高达7.82％、9.62％、7.91％和10.17％,在0.5 A·g-1的电流密度下分别具有高达268、311、280和362 F·g-1的质量比电容,且倍率性能和循环稳定性能优异.     

Al-Cu-Li合金轧制厚板的 疲劳性能及断裂机理研究

利用疲劳试验机、扫描电子显微镜(SEM)和透射电子显微镜(TEM)等设备研究了95 mm厚的Al-Cu-Li合金热轧板材不同方向的组织特征、疲劳性能和断裂机理.结果表明:Al-Cu-Li合金热轧厚板的力学性能和疲劳性能均存在各向异性.LT向(横向)的力学性能和疲劳性能均优于L向(纵向)和ST向(高向),L向(纵向)的力学性能较ST向更好,但疲劳性能较ST向更差.Al-Cu-Li合金厚板的疲劳裂纹源主要出现在试样表面、近表面的夹杂物和晶界处.裂纹扩展过程中,LT向裂纹扩展路径较L向更曲折,ST向具有典型的解理特征,瞬断区形貌与静态拉伸断口相似.晶界越多,裂纹扩展阻力越大,LT向和ST向的未溶第二相能够有效阻碍裂纹扩展,导致其疲劳性能优于L向.