Effect of Ce addition on microstructures and mechanical properties of A380 aluminum alloy prepared by squeeze-casting

The effect of cerium (Ce) addition on the eutectic Si, β-Al₅FeSi phase, and the tensile properties of A380 alloy specimens prepared by squeeze-casting were studied by optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The experimental results showed that Ce more effectively modified the eutectic Si and refined the β-Al₅FeSi. The refinement effect significantly increased under a specific pressure of 100 MPa with the addition of Ce from 0.1wt% to 0.9wt%. In contrast, the average length and the aspect ratio of the eutectic Si and β-Al₅FeSi exhibited their optimal values when the content of the added Ce was greater than 0.5wt%. Needle-like Al8Cu4Ce was precipitated with the addition of excessive Ce; hence, the mechanical properties of A380 gradually decreased with increasing Ce content in the range from 0.3wt% to 0.9wt%.     

New testing methodology for the quantification of rock crushability: Compressive crushing value (CCV)

Crushing is a size reduction process that plays a key role in both mineral processing and crushing-screening plant design. Investigations on rock crushability have become an important issue in mining operations and the manufacture of industrial crusher equipment. The main objective of this research is to quantify the crushability of hard rocks based on their mineralogical and mechanical properties. For this purpose, the mineralogical, physical, and mechanical properties of various hard rocks were determined. A new compressive crushing value (CCV) testing methodology was proposed. The results obtained from CCV tests were compared with those from mineralogical inspections, rock strength as well as mechanical aggregate tests. Strong correlations were found between CCV and several rock and aggregate properties such as uniaxial compressive strength (UCS), the brittleness index (S₂₀), and aggregate impact value (AIV). Furthermore, the relationship between the mineralogical properties of the rocks and their CCVs were established. It is concluded that the proposed testing methodology is simple and highly repeatable and could be utilized as a pre-design tool in the design stage of the crushing process for rock quarries.     

Complementation in the composition of steel slag and red mud for preparation of novel ceramics

A method for preparing novel ceramics was developed in this study. Different ratios red muds were added to steel slags to optimize the preparation of novel ceramics by a traditional ceramic preparation process. The sintering mechanism, microstructure, and performance were studied by X-ray diffraction techniques, scanning electron microscopy, and combined experiments of linear shrinkage, water absorption, and flexural strength. The results confirmed that red mud can reduce the volumetric instabilities through the complementarity of red mud and ferroalloy slag. The crystal phases in the ceramics are all pyroxene group minerals, including diopside ferrian, augite, and diopside. The flexural strength of the ceramic that contains 40wt% red mud and was prepared at the optimal sintering temperature (1140℃) is greater than 93 MPa; its corresponding water absorption is less than 0.05%.     

Leaching behavior of V,Pb, Cd,Cr, and As from stone coal waste rock with different particle sizes

This paper investigates the leaching behavior of heavy metals (V, Pb, Cd, Cr, and As) from stone coal waste rocks with various particle sizes using dynamic leaching experiments. The results show that the dissolved concentrations of V and As initially increased and then slightly decreased as time progressed and that the dissolved concentrations of Pb, Cd, and Cr were high in the early stage before decreasing. The particle size of the stone coal waste rocks strongly influenced the heavy metal concentration in the leaching solutions. The effects of the particle size of the stone coal waste rocks on the dissolved concentrations of V, Pb, and As decreased in the order fine fraction > medium fraction > coarse fraction, and the effects of particle size on the dissolved concentrations of Cr and Cd decreased in the order medium fraction > coarse fraction > fine fraction and coarse fraction > medium fraction > fine fraction, respectively. The quantities of heavy metals dissolved from the stone coal waste rock with fine particle sizes were observed to decrease in the order V (17104.36 μg/kg) > As (609.41 μg/kg) > Pb (469.24 μg/kg) > Cr (56.35 μg/kg) > Cd (27.52 μg/kg), and the dissolution rates decreased in the order As (2.96%) > Pb (0.93%) > V (0.35%) > Cd (0.25%) > Cr (0.01%). The specific surface area, pore size of the stone coal waste rocks, and chemical forms of heavy metals also influenced the release of heavy metals from the stone coal waste rocks. Kinetic analysis showed that the dissolution of heavy metals fundamentally agreed with the rate equation controlled by the shrinking core model. The results of this study are expected to serve as a reference for the evaluation of heavy metals contamination from stone coal waste rocks.     

Microstructural characterization and oxidation resistance of multicomponent equiatomic CoCrCuFeNi-TiO high-entropy alloy

CoCrCuFeNi-TiO was prepared by arc melting of the pure elements and Ti₂CO powder under an Ar atmosphere. Both CoCrCuFeNi and CoCrCuFeNi-TiO alloys are composed of a face-centered cubic (fcc) solid solution, whereas the alloys of CoCrCuFeNi-TiO are basically composed of an fcc solid solution and TiO crystals. The microstructures of CoCrCuFeNi-TiO are identified as dendrite and interdendrite structures such as CoCrCuFeNi. The morphology of TiO is identified as an equiaxed crystal with a small amount of added Ti₂CO. By increasing the amount of Ti₂CO added, the TiO content was dramatically increased and part of the equiaxed crystals changed to a dendrite structure. A test of the oxidation resistance demonstrates that the oxidation resistance of CoCrCuFeNi-TiO is better than that of CoCrCuFeNi. However, as the TiO content increases further, a corresponding decrease is observed in the oxidation resistance.     

Effect of melting temperature on microstructural evolutions,behavior and corrosion morphology of Hadfield austenitic manganese steel in the casting process

In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium silicate/CO₂ method, using a blind riser, and then the desired molten steel was obtained using a coreless induction furnace. The casting was performed at melting temperatures of 1350, 1400, 1450, and 1500℃, and the cast blocks were immediately quenched in water. Optical microscopy was used to analyze the microstructure, and scanning electron microscopy (SEM) and X-ray diffractrometry (XRD) were used to analyze the corrosion morphology and phase formation in the microstructure, respectively. The corrosion behavior of the samples was analyzed using a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS) in 3.5wt% NaCl. The optical microscopy observations and XRD patterns show that the increase in melting temperature led to a decrease of carbides and an increase in the austenite grain size in the Hadfield steel microstructure. The corrosion tests results show that with increasing melting temperature in the casting process, Hadfield steel shows a higher corrosion resistance. The SEM images of the corrosion morphologies show that the reduction of melting temperature in the Hadfield steel casting process induced micro-galvanic corrosion conditions.     

Mineral-phase evolution and sintering behavior of MO-SiO2-Al2O3-B2O3 (M=Ca,Ba) glass-ceramics by low-temperature liquid-phase sintering

In this work, network former SiO₂ and network intermediate Al₂O₃ were introduced into typical low-melting binary compositions CaO·B₂O₃, CaO·2B₂O₃, and BaO·B₂O₃ via an aqueous solid-state suspension milling route. Accordingly, multiple-phase aluminosilicate glass-ceramics were directly obtained via liquid-phase sintering at temperatures below 950℃. On the basis of liquid-phase sintering theory, mineral-phase evolutions and glass-phase formations were systematically investigated in a wide MO-SiO₂-Al₂O₃-B₂O₃ (M=Ca, Ba) composition range. The results indicate that major mineral phases of the aluminosilicate glass-ceramics are Al₂₀B₄O₃₆, CaAl₂Si₂O₈, and BaAl₂Si₂O₈ and that the glass-ceramic materials are characterized by dense microstructures and excellent dielectric properties.     

Urban Transport and Sustainable Transport Strategies： A Case Study of Karachi, Pakistan

The uncontrolled growth in urbanization and motorization generally contributes to an urban land use and transportation system that is socially, economically, and environmentally unsustainable. This paper uses Karachi as a case study, which is the largest urban and economic centre of Pakistan, passing through an uncontrolled phase of rapid urbanization and motorization. The paper first reviews research related to sustainable transportation systems to comprehend the concept of sustainable development and transporta-tion. The paper then evaluates the existing transportation and infrastructure system, national transportation policies, and urban transportation projects to determine if the current paradigm is moving toward or away from sustainable transportation. Furthermore, the principles for sustainable urban transportation are devel-oped to see what significance national transportation policies have given to urban transportation from a sus-tainable transportation point of view. Finally some strategies are suggested, adoption of which may lead to a sustainable urban development and transportation system in Karachi.     

40-Gb/s all-optical digital 4-bit priority encoder employing cross-gain modulation in semiconductor optical amplifiers

High-speed all-optical logic circuits have attracted much attention because of their important roles in signal processing in next-generation optical networks.The digital encoder is widely used in binary calculation,multiplexing,demultiplexing,address recognition and data encryption.A priority encoder allows the existence of multiple valid inputs simultaneously,identifies the priority of the request signals and encodes the priority.We propose and experimentally demonstrate an all-optical 4-bit priority encoder for return-to-zero signals at 40 Gbit/s based on cross-gain modulation in semiconductor optical amplifiers.Detuning fil-ters after semiconductor optical amplifiers are employed to improve the output performance.Correct logic bit sequences and clear open eye patterns with extinction ratios exceeding 10 dB are achieved.     

Measurement of laminar burning velocities of iso-butanol-air mixtures

The laminar burning velocity of iso-butanol-air mixtures was measured under different initial pressures, initial temperatures and equivalence ratios using high-speed schlieren photography and outwardly propagation flame in a constant volume combustion bomb. Based on the analysis of stretched flame propagation speed and stretch rate, the laminar burning velocities and Markstein lengths of iso-butanol-air flames are obtained. In accordance, with photos of flame, an analysis of flame stability and the influencing factors is carried out. The results show that the laminar burning velocity is decreased with the increase of initial pressure and is increased with the increase of initial temperature. The maximum value of laminar burning velocity is presented at the equivalence ratio of 1.2. The Markstein length is decreased with the increase of equivalence ratio. For specified equivalence ratio, the Markstein length is decreased with the increase of initial temperature and initial pressure. Thus, the flame instability is increased with the increase of equivalence ratio, initial temperature and initial pressure.