钢-半固态Al-7石墨复合界面特性

为了开发高温钢铝轴瓦材料,采用铸轧技术进行了钢板与Al-7石墨半固态浆料的复合实验,得到了不同于常规钢铝复合产品的界面结构。结果表明:在钢板预热温度为510℃、Al-7石墨半固态浆料固相率(体积分数)为32%的条件下,随着扩散时间的增加,复合界面上生成的铁铝化合物逐渐增多;当扩散时间大于35s时,复合界面完全由铁铝化合物构成;当扩散时间为22.5s时,可形成由铁铝化合物和铁铝固溶体交替构成的新型结构,其界面力学性能较好。     

Semi-solid Processing of Al-7Graghite Composite

Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f_s = 591.5-0.897 t (where f_s is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.     

超声焊接的研究和工艺模型

为了能进行超声焊接工艺的线检测，必须了解超声焊接的机制。本文对这个问题作了研究。在本实验所用的焊机中，用一块压电晶体作为换能器产生超声振动。在通常的焊接过程中，研究了换能器驱动信号和从机械振动测出的信号这二者的变动情况，同时还研究了这二种信号的各次谐波信号。     

膨胀石墨导电改性技术研究

未加特殊工艺修饰的膨胀石墨电阻率较高,通过开展膨胀石墨导电改性技术研究,在可膨胀石墨中加入高导电率的改性添加剂来降低膨胀石墨的电阻率,使其具有良好的导电性能,为拓展膨胀石墨的应用范围奠定了基础。     

镀铜膨胀石墨的制备

为改善铜与石墨的表面性能,采用化学镀铜工艺对膨胀石墨粉体进行表面镀覆,制备镀铜膨胀石墨,并利用TG-DTA、XRD、SEM分析方法对其进行表征.结果表明：在400～600 ℃范围内,镀铜膨胀石墨因膨胀石墨及镀铜层的氧化而增重,600 ℃后膨胀石墨烧蚀严重;镀铜膨胀石墨有明显的Cu衍射峰;铜颗粒均匀镀覆在膨胀石墨表面.该研究为膨胀石墨改性提供了借鉴.     

聚丙烯棒在混凝土中的黏结性能试验研究

在新型地下粮仓中防水防潮是一大难题,现采用内衬塑料构件解决该难题。利用聚丙烯(PP)棒连接混凝土与聚丙烯板,通过中心拉拔试验研究了PP棒在混凝土中的黏结应力分布曲线及破坏形态,结果表明:PP棒与混凝土黏结滑移曲线包括弹性阶段、局部开裂阶段以及下降阶段;影响PP棒在混凝土中的平均黏结应力的因素有PP棒表面形式、PP棒直径和混凝土强度,其中,PP棒表面形式影响最大;在不同荷载作用下,试件自由端的黏结应力总是小于加载端的黏结应力且黏结应力峰值出现在加载端附近。     

石墨矿渣在高速公路底基层中应用

探讨采用石墨矿渣作为高速公路填筑材料的可行性。通过对石墨矿渣及其水泥稳定后材料的水温稳定性、抗压强度、劈裂强度、回弹模量等物理力学性能的试验分析,探讨了水泥稳定石墨矿渣的可行性,提出了水泥稳定石墨矿渣用作高速公路底基层的施工压实控制标准,指出了合理的水泥剂量为6％。     

基于镍钯金PCB的数字声传感器键合工艺研究

本文介绍了数字传声器的关键结构,并基于其焊接及键合工艺的特点引入了镍钯金PCB,实现了其高可靠性的连接;并根据键合工艺的的要求,进行了一系列引线键合实验,取得了相关数据,得出了相匹配的皮膜厚度参数。     

水泥混凝土桥面铺装层间黏结性能研究

研究了水泥混凝土桥面铺装层间黏结性能随温度的变化规律,同时探究了黏结层的温度性能以及直剪与斜剪剪切强度之间的关系. 对比分析了4种涂膜黏结层（SBS改性沥青、WTR改性沥青、WTR/APAO改性沥青、AMP-100二阶反应型黏结涂料）和3种改性沥青碎石黏结层（SBS改性沥青碎石、WTR改性沥青碎石、WTR/APAO改性沥青碎石）的拉拔及剪切强度差异. 采用回归分析法获得层间强度随温度的变化规律;计算不同温度下层间强度与常温（20 ℃）下层间强度的比值,用于黏结层剪切强度和拉拔强度的温度敏感性对比分析;分析不同温度下斜剪强度与直剪强度的比值关系. 结果表明：层间拉拔强度、层间剪切强度与温度均满足单指数函数关系,拟合优度R2达0.970以上. WTR/APAO改性沥青黏结层及WTR/APAO改性沥青碎石黏结层力学性能优良,在不同温度下的拉拔和剪切强度值均高于同类型黏结层. AMP-100黏结层拉拔和剪切强度对温度的敏感性最低. 建立了20~45 ℃的层间强度比值表,用于层间强度预估. 斜剪强度显著高于直剪强度,同时斜剪强度对温度的敏感性低于直剪强度,当温度处于20~45 ℃时,斜剪强度与直剪强度比值范围为1.165~2.990.     

热喷涂底层处理工艺的研究

火焰线材喷涂是基本的热喷涂方法之一，至今仍被广泛采用．在喷涂工艺中，界面底层的处理对涂层的结合强度有重要影响．采用低、中、高碳钢、黄铜及自制的镍合金在几种底层处理条件下进行试验，发现Ｎｉ拉毛和Ｎｉ／Ａｌ打底，对涂层结合强度有明显的强化效果     

Modifying agent selection for Al-7Si alloy by Miedema model

To determine the modifying agents for Al-7Si alloys, microstructure observation and mixing enthalpy analysis using Miedema model for Al-7Si alloy with additions of different rare earth elements were performed, and the effects of rare earth elements on the modification of eutectic silicon morphology were investigated. The results of mixing enthalpy analysis show that these four rare earth elements, La, Sm, Pr, and Ce, which have the large negative mixing enthalpies with Si, can be selected as modifying agents for eutectic silicon morphology. The element with the largest negative mixing enthalpy is Ce. Furthermore, the microstructures indicate that these four elements can effectively modify the eutectic (α)Al-Si crystals in Al-7Si alloy, and the most effective one is also Ce. Differential scanning calorimetry (DSC) results show that the eutectic temperature depressions due to the additions of modifying agents are the important reasons for the modification of eutectic (α)Al-Si crystals.     

石墨薄膜热导率的研究

通过对90K~350K温度下石墨薄膜热导率的数据进行拟合分析,从理论上预测了石墨薄膜热导率随温度的变化趋势.结果表明,当薄膜厚度可与声子平均自由程比拟时,石墨薄膜热导率的尺寸效应比较明显.该尺寸效应归因于薄膜的边界对载热声子散射作用的增强.     

层状粘接结构中粘弹类表面波传播特性的研究

对金属下基底 -胶粘层 -金属上基底结构中的类Rayleigh(瑞利 )波传播特性进行了研究 .从粘弹的基本理论出发 ,通过Laplace Hankel(拉普拉斯 -汗克尔 )变换及转移矩阵技术建立起类Rayleigh波的频率方程 ,将粘接层视为Kelvin(开尔文 )体计算 ,分析了其粘弹模量对波频散关系的影响 .理论计算发现 ,粘弹体的粘滞项对频散低频段影响不大 ,但随着粘滞的增大对高频可产生影响 .最后 ,计算了粘滞对Sezawa(塞扎瓦 )模式及Saw(表面声波 )模式的衰减影响 .     

热超声键合过程中键合力波动特性仿真研究

利用有限元分析方法研究了在铜金属化晶片上进行金引线热超声键合过程中的键合力变化情况,建立了基于率相关材料特性的热超声键合有限元模型,对键合中的碰撞和超声两个过程进行了仿真分析,并引入平均键合力、键合力标准差值等统计参量来判定键合力的波动变化,从而更加准确地揭示了各键合参数对键合力波动的影响规律.研究结果表明:碰撞初速度(v0)、超声时间或键合温度的增加,均会使得键合力的波动加剧,不利于键合力的控制;对于v1/v0(v1为劈刀速度)则存在一个合适的值,可以使得键合力的波动变化最小.     

单基包覆火药界面粘结强度研究

该文提出了一种改善单基包覆火药界面粘结强度的方法，其工艺过程如下：（１）将单基火药吸收增塑剂进行表面预处理；（２０进行包覆，制备了用增塑剂ＮＧ和ＤＢＰ进行表面预处理的２种单基包覆火药，与直接包覆的单克包覆火药作对比，进行老化和落锤冲击试验，测试其界面粘结强度。     

玻纤织物增强混凝土界面黏结性能的试验研究

利用MTS万能试验机进行了纤维束的静态拔出试验,分别研究了不同的埋置深度、温度及纤维织物表面改性对耐碱玻璃纤维织物与水泥基体间黏结性能的影响.试验结果表明:玻璃纤维织物与水泥基体的黏结性能与纤维束埋深、纤维织物改性及温度条件存在一定的相关性.在常温条件25℃时,随着纤维束埋置深度的增大(15～25 mm),纤维束的拔出刚度、极限拔出力和拔出功不断增大,等效黏结强度反而呈现减小趋势.在相同的埋置深度(15 mm)下,随着温度的升高,纤维束的拔出刚度和极限拔出力不断降低.温度在25℃至300℃范围时,浸渍环氧树脂或者黏砂处理均能提高纤维束的极限拉拔承载力,且表面黏砂相比浸渍环氧树脂具有更好的增强效果.然而,当温度在400℃和500℃范围变化时,表面浸渍环氧树脂和黏砂对提高玻璃纤维束的极限拔出力影响不太显著,而在一定程度上降低了极限拔出力.     

Ekonol-PTFE-石墨自润滑复合材料的磨损性能研究

研究了聚苯酯 (Ekonol)的含量对Ekonol-PTFE -石墨自润滑复合材料的磨损性能的影响 ,用扫描电子显微镜观察了此复合材料磨损前和磨损后的表面形貌 ,进而对其磨损机理进行了探讨 结果表明 :当Ekonol含量较少时 ,结晶体仍以带状结构存在 ,磨损中易发生带状破坏导致其耐磨性仍较差 ,磨损机理为严重粘着磨损 ;当Ekonol含量适中时 ,其结晶体以连续网状结构存在 ,其可有效地阻止PTFE基体的带状破坏 ,从而可极大地提高此复合材料的耐磨性 ,磨损机理为疲劳磨损和轻微粘着磨损 ;当Ekonol含量较多时 ,其结晶体以分散状存在 ,磨损机理为晶体剥落 图 7,表 1 ,参 9     

钴基结合剂对金刚石把持力的研究

概述金刚石锯片的工作机理，指出钴基结合剂的致密度、硬度与金刚石把持力的关系，且以加入与不加入金刚石的结块的抗弯强度损失率的对比试验为主要依据，提出并论证增强钴基结合剂对金刚石把持力的两个可行途径──部分液相烧结与加入强碳化合物形成元素．     

钢板-型钢双剪试件的界面粘结性能试验研究

为验证粘贴钢板的不同厚度、层数及宽度等因素对钢–钢界面粘结性能的影响,通过改进的双剪试验装置,对钢板–型钢双剪试件进行了轴向拉伸试验研究,分析在各因素影响下,粘结界面上的应力分布特点、粘结剪切破坏过程、破坏特征、钢板应变发展及分布规律,得出钢板与型钢的粘结应力分布规律和粘结剪应力-滑移曲线,提出钢板型钢界面粘结承载力的计算公式,且计算结果与试验结果吻合良好,研究成果为粘钢法加固钢结构计算理论建立及加固设计提供了试验依据。     

植生带建坪中几种粘合材料应用效果的研究

选用 Ｄ Ｅ２３、 Ｆ２ 、 Ｆ３、 Ｗ １ 的几种粘合材料,研究其在黑麦草植生带制作中的应用效果．结果表明,各粘合材料进行植生带建坪效果差异较大． 其中以 Ｆ２ 和 Ｗ１ 两种粘合材料在植生带建坪应用中表现出更为良好的性能