偏高岭土对高性能水泥砂浆性能的影响

研究了偏高岭土的火山灰活性,考察了不同偏高岭土掺量对高性能水泥砂浆的流动度、抗折强度、抗压强度和氯离子渗透性的影响.试验结果表明:偏高岭土的火山灰活性高于硅灰;偏高岭土颗粒形貌的不规则性会降低新拌砂浆的流动度;偏高岭土的掺入使砂浆的抗折强度降低,90d养护龄期时偏高岭土掺量为10%的砂浆抗折强度高于偏高岭土掺量为6%,14%的砂浆抗折强度.偏高岭土掺量为10%的砂浆的后期抗压强度最高,90 d养护龄期时可达96.3 MPa;56 d龄期时偏高岭土掺量为0%,6%,10%,14%的砂浆的氯离子渗透性都较低,电通量分别为165,221,191,158 C.     

颜料对聚合物水泥砂浆性能影响的实验研究

向聚合物水泥砂浆中掺入氧化铁颜料制备彩色聚合物水泥砂浆。研究了不同颜料及其掺量的变化对聚合物水泥砂浆力学性能、工作性能和粘结强度的影响;并借助扫描电镜(SEM)表征了彩色聚合物水泥砂浆的微观组织形貌。结果表明:颜料会一定程度降低聚合物砂浆的抗折、抗压强度;且颜料掺量为5%时,对聚合物砂浆的抗折、抗压强度影响显著;随着颜料掺量的逐渐增加,聚合物砂浆的抗折、抗压强度呈现先增加后平缓的趋势;聚合物砂浆的流动度和粘结强度随颜料掺量的增加而减小。SEM测试结果表明颜料一方面会包裹水泥颗粒,阻碍水泥水化,降低彩色聚合物砂浆的抗折、抗压强度;另一方面颜料能有效填充聚合物砂浆空隙,改善密实度,又提高彩色聚合物砂浆的抗折、抗压强度。     

颜料对聚合物水泥砂浆性能的影响

向聚合物水泥砂浆中掺入氧化铁颜料制备彩色聚合物水泥砂浆,研究了不同颜料及其掺量的变化对聚合物水泥砂浆力学性能、工作性能和粘结强度的影响,并借助扫描电镜(SEM)表征了彩色聚合物水泥砂浆的微观组织形貌。结果表明：颜料会一定程度降低聚合物砂浆的抗折、抗压强度,且颜料掺量为5%时,对聚合物砂浆的抗折、抗压强度影响显著,随着颜料掺量的逐渐增加,聚合物砂浆的抗折、抗压强度呈现先增加后平缓的趋势;聚合物砂浆的流动度和粘结强度随颜料掺量的增加而减小;SEM测试结果表明颜料一方面会包裹水泥颗粒,阻碍水泥水化,降低彩色聚合物砂浆的抗折、抗压强度,但另一方面颜料能有效填充聚合物砂浆空隙,改善密实度,提高聚合物砂浆的抗折、抗压强度。     

硫铝酸盐水泥基修补砂浆的力学性能

采用可再分散乳胶粉改性硫铝酸盐水泥制备修补砂浆,分别测试其抗折强度、抗压强度、折压比和黏结强度,并结合电子扫描显微镜(SEM)分析水泥砂浆微观结构以及可再分散乳胶粉对硫铝酸盐水泥砂浆的影响机理,研究不同掺量的可再分散乳胶粉对硫铝酸盐水泥砂浆力学性能的影响。试验结果表明:当可再分散乳胶粉质量分数掺量为3%时,水泥砂浆28 d抗折、抗压强度可分别达到8.1 MPa和45.5 MPa,14 d黏结强度可达4.78 MPa;掺入可再分散乳胶粉后,砂浆力学性能改性效果明显。随着可再分散乳胶粉掺量的增加,砂浆的抗折强度大幅度提高,抗压强度降低,折压比增大,黏结强度增大。     

机制砂取代率及石粉掺量对人工砂砂浆流动度与力学性能的影响

通过使用不同机制砂取代率的人工砂、采用掺入石粉部分替代水泥的方法,研究人工砂砂浆流动度及力学性能的变化规律.研究表明:随着机制砂取代率的增大,人工砂砂浆的流动度优于天然砂砂浆,且其7、28 d抗压和抗折强度随着机制砂取代率的增大而增大.掺入5%的石粉可以提高人工砂砂浆的流动度及7 d抗压和抗折强度,28 d抗压和抗折强度降低幅度在10%之内.综合考虑人工砂砂浆的流动度及力学性能,建议采用机制砂取代率为66.7%及石粉掺量为5%的人工砂.     

水性环氧树脂改性水泥基材料应用于彩色路面的研究

通过水性环氧树脂改性水泥基彩色砂浆,制备一种力学性能优异且经济的彩色路面铺装材料,并通过抗折强度试验、抗压强度试验、粘结强度试验、抗滑性能试验、色彩耐久性试验研究了复合材料的最佳配合比和路用性能,通过扫描电子显微镜(scanning electron microscope, SEM)试验分析了水性环氧树脂和粉煤灰对水泥水化产物的影响。结果表明：粉煤灰掺量10%,水性环氧树脂掺量10%,改性砂浆力学性能最优;改性砂浆的摆式摩擦系数BPN基本保持在55～80,抗滑性能良好;水性环氧树脂的掺入增加了水泥砂浆的粘结性、耐酸腐蚀性和后期抗折强度,但降低了其抗压强度;适量粉煤灰可以增加水泥砂浆的后期抗折和抗压强度。     

粉煤灰对砂浆力学性能与孔结构参数的影响

贵州II级粉煤灰排放量多且分布广。为了明确各地区II级粉煤灰的差异性及对砂浆力学性能和孔结构参数的影响,采用都匀粉煤灰、大方粉煤灰、鸭溪粉煤灰和六盘水粉煤灰等质量替代水泥,探讨粉煤灰掺量对砂浆力学性能、吸水量和孔结构参数的影响,并分析其作用机理。结果表明:粉煤灰的掺入显著降低砂浆的抗折强度和抗压强度,掺量以20%为宜,但抗折强度与抗压强度之比不断增长,抗折强度为抗压强度的1/4~1/5.8。粉煤灰种类和掺量对砂浆吸水量、孔径均匀性和平均孔径的影响规律不同,但粉煤灰砂浆的吸水量高于纯水泥砂浆。粉煤灰在砂浆中的作用可简述为形态作用、填充作用和火山灰效应,文中4种II级粉煤灰的活性较低,在砂浆中主要以填充作用为主。     

纳米CaCO_3对砂浆强度和微观结构的影响

为了解不同纳米CaCO_3粉末掺量对水泥砂浆力学性能和微观结构形貌的影响和发展规律,试验取纳米CaCO_3的掺量分别为0,0.4%,1.2%,1.8%,2.2%,3.0%,对不同掺量下砂浆的力学性能和微观结构进行比较分析。结果表明:纳米CaCO_3可明显提高砂浆的抗折强度和抗压强度,掺量为2.2%时,3,7,28 d龄期的砂浆抗折强度比基准提高了17.1%,18.4%,43.6%,抗压强度比基准提高了32.3%,26.8%,28.9%;同时该掺量下7 d的水泥砂浆,其微观结构的水化硅酸钙凝胶最多,孔隙率和裂隙最低,Ca(OH)_2的取向程度最低,结构最为致密。     

粉煤灰基地聚合物砂浆组成设计与性能研究

以粉煤灰为主要原材料,矿粉为添加剂,水玻璃和氢氧化钠为复合激发剂,标准砂为细集料,制备地聚合物砂浆。运用三维图与等值线作图分析的方法,探究水胶比与胶砂比这两个组成设计参数对粉煤灰基地聚合物砂浆的流动度、抗压强度、抗折强度的影响规律。试验结果表明水胶比与胶砂比均对粉煤灰基地聚合物砂浆流动度与力学强度影响较大。水胶比在0.4~0.42,胶砂比在0.45~0.5时,制备出的地聚合物砂浆工作性能和力学性能较优。基于地聚合物砂浆脆性较大的特点,应用长度为8 mm与12 mm的PVA纤维进行增韧改性。结果表明,掺量为0.5%的PVA纤维对地聚合物砂浆抗压强度影响不大,但是抗折强度显著提高,延性增强,因此压折比下降,弯曲韧性增强。     

超细矿渣在硫铝酸盐水泥砂浆中的应用

在硫铝酸盐水泥砂浆中加入超细矿渣,研究不同掺量的超细矿渣对水泥浆体凝结时间及胶砂流动度、强度的影响.采用电子扫描显微镜(SEM)分析水泥砂浆微观结构以及超细矿渣在砂浆中的影响机理.实验结果表明:随着掺量的提高,水泥浆体的初凝时间延长,终凝时间缩短;胶砂流动度随超细矿渣掺量的增大而减小; 随超细矿渣掺量的增大,水泥胶砂的3d和28d强度提高,当掺量质量分数为20%时,水泥砂浆28d的抗折、抗压强度达到最大,分别达到7.3Mpa和46.93Mpa.     

助磨剂对普通硅酸盐水泥性能的影响及作用机理

研究了助磨剂对普通硅酸盐水泥的流动性、颗粒分散度及其砂浆性能的影响并对作用机理进行了探讨。结果表明,助磨剂加强了水泥的流动性、提高了水泥细度、增加了细粉量、对勃氏比表面积无明显改变、增加了水泥3d、28d强度;助磨剂的作用机理是减小了粉碎阻力、防止团聚和糊磨、提高流动性而加强了料和球的作用频率和效率,从而提高了粉磨效率。     

Effect of grinding on chemical and physical properties of rice husk ash

The effect of grinding on the chemical and physical properties of rice husk ash was studied. Four rice husk ashes with different finenesses, i.e. coarse original rice husk ash (RHA0), RHA1, RHA2, and RHA3 were used for the study. Ordinary Portland cement (OPC) was partially replaced with rice husk ash at 20% by weight of binder. The water to binder ratio (W/B) of the mortar was maintained at 110%±5% with flow table test. Specific gravity, fineness, chemical properties, compressive strength, and porosity test of mortars were determined. The differences in chemical composition of the rice husk ashes with different finenesses from the same batch are small. The use of RHA3 produces the mortars with good strength and low porosity. The strength of the mortar improves with partial replacement of RHA3 in comparison with normal coarse rice husk ash. The use of RHA3 results in a strong and dense mortar, which is due to the better dispersion and filling effect, as well as an increase in the pozzolanic reaction.     

水泥中S/Al比和外渗硫酸盐对氯离子临界浓度影响研究

采用线性极化法、压汞法和X射线衍射分析等方法研究了外渗氯盐条件下水泥中S/Al比及外渗硫酸盐对氯离子临界浓度的影响,研究结果表明：氯离子临界浓度随水泥中S/Al比提高先增大后减少,而氯离子的结合量随S/Al比提高而降低,氯离子临界浓度最大值时的S/Al比随水泥中Al2O3含量的提高而降低,S/Al比和Al2O3含量对氯离子临界浓度的影响实质上是对砂浆孔隙结构的影响。在SO42-和Cl-含量与华南地区海水相近的复合渗透液中,氯离子临界浓度随水泥中的S/Al比提高而先增大后减少,且临界浓度约为NaCl溶液浸泡试件的70%。复合渗透液中的SO42-渗透进砂浆先会使砂浆结构变致密,然后才引起体积膨胀,提高水泥中的S//Al比可提高水泥中AFm的生成量,从而相对降低由于生成滞后钙矾石引起的体积膨胀。     

养护条件对改性水泥砂浆力学性能的影响

通过对齐鲁石化生产的水泥改性专用丁苯乳胶乳液聚合物改性水泥砂浆的试验研究,考察了养护条件对聚合物改性水泥砂浆力学性能的影响,试验证明：乳液的掺量越小,试件所需在水中养护的天数越多,乳液的掺量越大,试件所需在水中养护的天数越少;当乳液的掺量达到一定值时,就无需在水中养护,只需在空气中养护即可,提出了应用该种乳液改性不泥砂浆时的最佳乳胶渗量及不同掺量时的最佳养护条件。     

纤维增强磷酸钾镁水泥砂浆力学性能研究

研究了PVA纤维、PP纤维、玻璃纤维三种纤维在不同的w_(S/C)下对磷酸钾镁水泥砂浆力学性能的影响.结果表明:三种纤维都能在一定程度上增强磷酸钾镁水泥砂浆的力学性能,对磷酸钾镁水泥砂浆早期力学性能的影响比较大,后期力学性能的影响会有所降低.其中,PVA的增强效果最为明显,PP纤维次之,玻璃纤维增强效果最弱.同时得出,在同种纤维条件下,w_(S/C)不是磷酸钾镁水泥砂浆抗折强度的主要影响因素,但是其抗压强度均随着w_(S/C)的增大而增大.     

高岭土细粉碎过程中的机械化学效应

研究了高岭土的细粉碎过程与机械化学效应。实验结果表明,粉碎过程能使物料发生粒径变小、比表面积增大,并且产生晶体结构畸变、热效应温度降低等一系列机械化学变化。以KB(a)-192 h试样为例,代表性粒径从3.2 μm降至0.95μm,比表面积从1.27 m~2/g增至3.38 m~2/g,脱去结构水的温度降低28℃。液相介质和助磨剂对粉体的机械化学变化都有很大影响。就热效应温度而言,粉碎处理192h后,KE系列试样降低12℃,KB系列试样降低17℃,可见丙酮比乙醇更有利于机械化学变化。KB(a)试样降低28℃,比KB系列试样降得更低,说明引入三乙醇胺作助磨剂,能促进机械化学反应。     

聚合物干粉改性水泥砂浆力学性能的研究

研究了掺羟乙基甲基纤维素醚和乙烯-醋酸乙烯酯共聚物乳胶粉的水泥砂浆的力学性能.试验结果表明,聚合物的掺入对砂浆的力学性能影响较大,砂浆的抗压、抗折强度有所下降,但砂浆的韧性、抗收缩等变形力学性能得到改善,不同基层上的抗拉粘结强度大大提高并具有较好的温度稳定性和耐水性.聚合物的种类、掺量对砂浆的各项性能有很大的影响,复掺能充分发挥不同聚合物对砂浆的改性作用.     

刚玉质自流浇注料流变性和流动性的关系

采用浇注料流变仪、L型流动性测试装置和自流值测定装置,测定了加水量、分散剂(FS10)、纯铝酸钙水泥和α-Al2O3微粉对刚玉质自流浇注料的流变性和流动性的影响,并分析了流变性和流动性之间的关系.实验结果表明:随加水量增加(质量分数4.9%～5.3%),相对屈服应力、相对塑性黏度和相对平均黏度均逐渐减小,自流值和流动速度逐渐增大.随分散剂FS10加入量的增加(质量分数0.16%～0.20%),相对屈服应力、相对塑性黏度和相对平均黏度逐渐减小,自流值和流动速度逐渐增大;分散剂FS10加入量继续增大时(0.20%～0.22%),相对屈服应力、相对塑性黏度和相对平均黏度显著增大,而自流值和流动速度大幅下降.随纯铝酸钙水泥加入量增加(质量分数1%～4%),流变参数和流动参数有一定的变化,但变化不明显.随α-Al2O3微粉加入量的增加(质量分数9%～12%),相对屈服应力和相对平均黏度均减小,相对塑性黏度变化不大,自流值变化不大,流动速度加快.刚玉质自流浇注料流变参数和流动参数之间的关系为:自流值和相对屈服应力有较好的相关性,而流动速度和相对平均黏度有较好的相关性.     

保温时间对铝厂废渣研制的氧化铝磨介微观结构及性能影响

以铝型材厂废渣为主要原料,通过添加少量粘土,滑石及碳酸钡复合助烧剂研制刚玉耐磨瓷球.探讨不同保温时间对瓷球微观结构及各项性能指标的影响.采用XRD和SEM等测试手段探讨其晶相结构和显微结构并测试抗弯强度、硬度、磨损率和气孔率等性能指标.结果表明:最佳保温时间为3 h,此时样品由4种晶相组成,其中刚玉为主晶相,含量约75%,其各项性能分别为:吸水率为0.032%,气孔率为0.105%,体积密度为3.289 g/cm3,抗弯强度为136 MPa,显微硬度为8.25 GPa,磨损率为0.044 1%/h.     

石墨导电混凝土的制备与性能

为研究石墨混凝土的力学及电学特性,以C30混凝土为基准分别制备不同石墨掺量的石墨导电混凝土,分析石墨对混凝土拌合物和易性的影响,以及石墨混凝土在不同养护龄期时抗压强度及电阻率的变化.结果表明：加入石墨后混凝土的流动性明显变差,坍落度下降约25％,黏聚性和保水性下降明显.掺加5％和10％石墨的混凝土养护28 d时抗压强度分别下降了约50％和77％.加入石墨的混凝土导电性有所提高,掺加5％和10％石墨的混凝土养护28 d时电阻率分别为未加石墨混凝土的千分之一和五千分之一.该研究为混凝土改性提供了借鉴.