壳聚糖改性微球的微波制备及其吸附性能-1

采用微波辐射法制备了戊二醛交联壳聚糖水杨醛希夫碱微球吸附剂,使用红外光谱和热重分析表征了吸附剂的结构,研究了其对金属离子的吸附性能,同时与采用常规水浴加热制备的微球吸附剂进行了比较.结果表明,微波辐射法能加快反应的进行,制得的吸附剂微球较为均匀,同时增大了对Pb2+、Cd2+的吸附量.     

微波辐射下交联壳聚糖树脂的制备及其吸附性能

在稀醋酸溶液中，微波辐射下壳聚糖与Zn^2＋反应制备了壳聚糖Zn^2＋配合物，然后将制得的配合物与环氧氯丙烷在微波辐射下进行交联反应后，用稀酸除去Zn^2＋，合成了具有Zn^2＋孔穴的交联壳聚糖树脂，实验考察了该树脂对一些金属离子的吸附性能，并对影响树脂吸附性能的因素进行了研究。     

香草醛接枝壳聚糖的微波辐射制备及其吸附性能

用微波辐射制备了香草醛接枝壳聚糖 ,并用IR、XRD表征了产物的结构 ,同时研究了接枝壳聚糖的吸附性能 .实验结果表明 ,用微波辐射作为加热手段 ,壳聚糖的接枝反应速度远远大于传统加热手段 .所制得的香草醛接枝壳聚糖对金属离子的吸附容量和吸附速度要优于壳聚糖 .在常温下 ,它对Cu2 + 、Ni2 + 、Zn2 + 、Pb2 + 的吸附容量分别达到1 95 5 ,1 0 7.7,1 4 3.7,97.5mg·g- 1,并且对金属离子的吸附在 2h内即可达到饱和     

微波辐射下甲醛交联壳聚糖香草醛希夫碱的制备及吸附性能

利用微波辐射法合成了甲醛交联壳聚糖香草醛希夫碱,用IR和XRD对其结构进行了表征,并用UV吸收光谱比较了甲醛交联前后壳聚糖香草醛希夫碱在酸中的溶解性能.吸附实验表明,该壳聚糖改性产物对一些金属离子的吸附性能与壳聚糖香草醛希夫碱和甲醛交联的壳聚糖有所不同,对Cu2 具有良好的吸附选择性,并且在酸性环境中几乎不溶解,因此可用作Cu2 的选择性吸附剂.     

微波辐射下模板交联壳聚糖的制备及其对Cu2+吸附性能的研究

微波辐射下,用壳聚糖在稀醋酸介质中与Cu2+制得壳聚糖Cu2+络合物, 然后使壳聚糖铜络合物与戊二醛进行交联, 用稀酸洗去Cu2+, 制得具有Cu2+模板离子孔穴的交联壳聚糖树脂, 考察了该树脂对Cu2+的吸附性能. 实验表明, 微波加热所得的交联壳聚糖, 在酸性条件下不会发生软化和溶解, 重复使用性能亦好, 且比水浴加热制得的具有Cu2+模板离子孔穴的交联壳聚糖对铜有较大的吸附量.     

季铵化壳聚糖微球的制备及其对酸性媒介黑PV的吸附性能研究

本文采用反相悬浮交联法制备了壳聚糖微球,并以3-氯-2-羟基丙基三甲基氯化铵为改性剂在微球上引入了季铵盐基团．考察了改性后的微球对染料酸性媒介黑PV（PV）的吸附性能．实验结果表明季铵化壳聚糖微球对偶氮染料PV有较好的吸附能力．实验条件下,最大平衡吸附量为1759mg／g,等温吸附很好地符合Langmuir等温方程,表明为单分子层吸附．吸附量受染料初始浓度、温度和溶液pH等因素影响．负载染料的微球容易洗脱,洗脱再生后的微球可重复使用．     

微波辐射下交联壳聚糖树脂的制备及其吸附性能

在稀醋酸溶液中，微波辐射下壳聚糖与Zn^2 反应制备了壳聚糖Zn^2 配合物，然后将制得的配合物与环氧氯丙烷在微波辐射下进行交联反应后，用稀酸除去Zn^2 ，合成了具有Zn^2 离子孔穴的交联壳聚糖树脂。实验考察了该树脂对一些金属离子的吸附性能，并对影响树脂吸附性能的因素进行了研究。     

微波辐射氯丙酸改性壳聚糖的制备研究

通过微波辐射,研究了3-氯丙酸与壳聚糖的接枝共聚反应,探讨了加料方式、微波辐射时间、微波功率、加热方式、单体浓度等因素对聚合反应的影响.结果显示,微波辐射可以得到较高接枝率的氯丙酸-壳聚糖共聚物.     

微波辐射下模板交联壳聚糖的制备及其对Cu^2＋吸附 …

微波辐射下,用壳聚在烯醋酸介质中与Ｃｕ＾２＋制得壳聚糖Ｃｕ＾２＋络合物,然后使壳聚糖铜络合物与戊二醛进行交联,用稀酸洗去Ｃｕ＾２＋,制得具有Ｃｕ＾２＋模板离子孔穴的壳聚糖树脂,考虑了该树脂对Ｃｕ＾２＋的吸附性能。实验表明,微波加热所得的交联壳聚糖,在酸性条件下不会发生软化和溶解,重复使用性能亦好,且比水浴加热制得的具有Ｃｕ＾２＋模板离子孔穴的交联壳聚糖对铜有较大的吸附量。     

壳聚糖磁性微球对偶氮品红的吸附

利用反相悬浮交联法,以Fe3O4为核,制备了壳聚糖磁性微球.将其用于水中偶氮品红的吸附,研究了溶液酸度、吸附时间、偶氮品红初始浓度、温度、离子强度对吸附的影响.结果表明:在40℃,pH 4.0,无盐条件下吸附效果最佳,壳聚糖磁性微球对偶氮品红的饱和吸附量达到357.1 mg/g.运用相关数学模型拟合实验数据得出,该吸附同时符合Freundlich和Langmuir模型(均R2>0.96).经3次重复使用再生后壳聚糖磁性微球对偶氮品红的吸附率仍高于90%.该种新型吸附剂吸附能力强、速度快且易分离和可再生.     

Preparation and Adsorption Ability of Polysulfone Microcapsules Containing Modified Chitosan Gel

Chemically modified chitosan beads containing polyethyleneimine （PEI） were prepared to improve the metal ion adsorption capacity of the chitosan beads and their mechanical stability and to limit their biodegradability. The modified beads were encapsulated with the polymer material polysulfone by a novel surface coating method named the emulsion phase inversion method. The adsorption properties of the modified beads and the microstructures of the polysulfone coating layer were then analyzed. The experimental results showed that the PEI was successfully linked onto the chitosan beads. The density of the -NH2 groups in the modified beads was significantly increased, while the water content was reduced. The coating layer thickness was about 200 pm. The modified chitosan gel beads had excellent Cu（ll） adsorption capacity, with a maximum Cu（ll） adsorption capacity 1.34 times higher than that of the unmodified beads. The results show that even with the polysulfone coating the adsorption kinetics of the modified beads is still better than those of the unmodified beads. The modifications improve the mass transfer performance of the chitosan beads as well as the bead stability.     

壳聚糖/壳聚糖季铵盐共混微球吸附五氯酚钠

以乳化-化学交联法制备了壳聚糖/壳聚糖季铵盐共混微球,质量比为1:1的壳聚糖/壳聚糖季铵盐共混微球粒度均匀,平均粒径大约200μm,对农药五氯酚钠具有较好的吸附性能,其静态饱和吸附量大约为0.6mmol/g.     

壳聚糖载药微球的制备和体外释放研究

以壳聚糖(CS)和盐酸左氧氟沙星(LVFX)为原料,通过乳化交联法制备CS载药微球,应用显微镜、扫描电镜考察载药微球微观形态,建立恒温恒速流动药物溶出系统检测微球中药物体外释放特性和影响因素.结果发现:微球理化特性受壳聚糖脱乙酰度、壳聚糖醋酸溶液浓度、交联剂用量等工艺条件影响,微球载药量与壳聚糖降解程度、CS与LVDX...     

蚯蚓纤溶酶壳聚糖微球的制备及性质

以蚯蚓纤溶酶为生物大分子模式药物,研究壳聚糖载药微球的制备方法及对药物活性和稳定性 的影响.以壳聚糖为原料,采用超声乳化交联法制备壳聚糖微球,分别吸附和包埋蚯蚓纤溶酶.在油水体积比 15/1,搅拌转速800 r/min,1 mL戊二醛作为交联剂,超声处理5 min条件下乳化交联制备微球,包埋法具有 较高的栽药率和...     

改性壳聚糖对苯酚吸附条件筛选

开发新型低成本苯酚吸附剂是处理含酚废水的研究重点.将苯酚采用吸附法固定在戊二醛交联的壳聚糖(CTS)上,研究改性壳聚糖对苯酚的吸附效果,并对影响吸附率的主 要因素pH值,吸附时间等进行了研究.结果表明,改性后的壳聚糖对苯酚的吸附能力增强,在pH=5.8,吸附时间为2h时,对苯酚的吸附效果最佳,能够达到52mg/g.改性壳聚糖微球的洗脱和重吸附试验表明:重复使用的微球对苯酚的吸附量保持不变,重复性能良好,因此由戊二醛交联的改性壳聚糖是含酚废水较好的苯酚吸附剂.     

丙酮酸壳聚糖衍生物的制备及其吸附性能研究

利用壳聚糖C2位上活泼氨基与丙酮酸进行大分子反应,采用正交试验法优化合成条件,合成了带有高取代羧基、能溶于水的功能聚合物－丙酮酸改性壳聚糖（简称PCTS）,研究了PCTS对Cu^2 ,Zn^2 ,Co2 等重金属离子的吸附性能,其对低浓度金属离子去除率分别达到100％,99．8％和40．5％,与壳聚糖、水杨醋改性壳聚糖相比,溶解性能和吸附性能有较大提高。     

壳低聚糖硫酸盐的制备及其特性研究

壳低聚糖具有优越的生理活性,但其在长期的保存过程中容易变质。为了便于长期保存,将其制备成壳低聚糖硫酸盐。用高效液相色谱测定其分子量,用酸碱滴定法确定壳低聚糖硫酸盐的组成。以壳低聚糖为参照,研究壳低聚糖硫酸盐的吸湿、保湿性及其在不同时间、温度、pH值的稳定性。结果表明:样品中主要成分是壳低聚糖硫酸盐;壳低聚糖硫酸盐的保湿能力比壳低聚糖强;在不同时间、温度、pH值的条件下比壳低聚糖稳定。     

壳聚糖交联酸改性粉煤灰的制备及对Mn~(2+)的吸附性能研究

以壳聚糖和酸改性粉煤灰为原料,制备壳聚糖交联酸改性粉煤灰吸附剂.利用SEM、XRD、FTIR对其结构进行表征,考察其制备及吸附条件对Mn2+去除率的影响.结果表明:制备时,当壳聚糖与酸改性粉煤灰的质量比为1∶10,交联剂用量为2 mL/g;吸附时,废水pH为9,吸附时间为90 min,吸附剂用量为10 g/L时,Mn2+去除率为98.7%.