Gold telluride ores are important gold refractory ores due to the presence of sulfides and other gangue materials. The classification and main physical properties of gold telluride ores were described, and possible treatment methods including flotation, leaching, and oxidation were reviewed. The results show that flotation procedures are much easier for gold tellurides compared to other refractory gold-bearing ores. For the conventional cyanide leaching process, pretreatment such as oxidation is required to achieve high gold recovery. Roasting is a relatively simple but not environment-friendly method; bio-oxidation technology seems to be more suitable for the oxidation of flotation concentrate. Other treatment methods involve cyanide leaching, thiourea leaching, ammoniacal thiosulfate leaching, carbon-in-pulp, and resin-in-pulp, all of which are less commonly utilized.     

硫酸镁还原热解制备高纯氧化镁

用菱镁矿和工业纯硫酸来制备七水硫酸镁,进一步脱水得到无水硫酸镁。以无水硫酸镁和木炭粉为原料,经高温煅烧制备高纯氧化镁。研究反应物的配比、煅烧温度、煅烧时间以及粒径对产品纯度的影响。采用X线衍射和扫描电镜对样品进行表征。通过单因素实验确定的最佳工艺条件为:硫酸镁和炭粉的最佳配比8:1,煅烧时间2 h,煅烧温度800℃,粒径109μm。研究结果表明:在最佳工艺下,样品纯度达到99%,粒径分布介于109～700μm之间,单分子表面为多孔蓬松高比表面。     

镁橄榄石合成反应动力学研究

以分析纯氧化镁、高纯熔融石英以及电熔镁砂颗粒为原料,研究了固相法合成镁橄榄石的反应动力学.利用X射线衍射和扫描电子显微镜等手段,研究了合成温度和保温时间对镁橄榄石生成速率的影响,分析了MgO与SiO2的反应机理.根据实验结果,建立了1100~1300℃下MgO与SiO2反应的动力学方程,并求出了表观反应活化能.研究结果表明,随着合成温度的提高和保温时间的延长,镁橄榄石生成率逐渐增加.在反应初期,MgO与SiO2反应生成了镁橄榄石和顽火辉石,在合成反应中后期时Mg2+通过产物层扩散而进一步反应,MgO与SiO2反应合成镁橄榄石的反应过程由Mg2+扩散所控制,反应的表观活化能为(220±20)kJ/mol.     

轻烧粉-氢氧化钠法制备氢氧化镁的研究

以轻烧粉经酸化、氧化除铁等精制过程得到的氯化镁溶液为原料,以氢氧化钠为沉淀剂制备氢氧化镁。研究了pH值对轻烧粉酸化除铁的影响,考察了原料的物质的量比、反应温度、加料时间、陈化时间等因素对产品质量的影响,得到了轻烧粉精制和反应制备氢氧化镁的最佳工艺条件。采用扫描电子显微镜（SEM）、X射线粉末衍射仪（XRD）和激光粒度分布测试仪等对实验产品进行表征。结果表明,该工艺制备的氢氧化镁纯度达到98%以上,CaO质量分数低于0.1%,颗粒呈片状结构,粒度分布均匀,形貌规则。     

含钛电炉熔分渣碱熔过程中 Ti元素的选择性富集及MgAl2O4的物相转化规律

以KOH为改性剂,利用渣碱共熔反应对攀钢含钛电炉熔分渣进行改性处理,成功地将炉渣中Ti元素从原来的重钛酸镁选择性地富集到偏钛酸钾中,同时渣中镁铝尖晶石和镁橄榄石转化为易溶于水的铝酸盐和硅酸盐.采用X射线衍射技术研究了共熔反应中煅烧温度、渣碱比(含钛电炉熔分渣的质量与KOH质量之比)、保温时间等对Ti元素迁移富集和镁铝尖晶石转化的影响.当渣碱比为1：2.1、煅烧温度700℃及保温时间1 h时,生成的偏钛酸钾衍射峰达到最强,镁铝尖晶石的衍射峰最弱,有效地实现了Ti元素的选择性富集及镁铝尖晶石的物相转化.实验证实了较高K/Ti比( K2 O与TiO2的摩尔比)是生成偏钛酸钾的主要原因.以最佳碱熔条件下得到的共熔渣为原料,经过后续处理,在850℃的条件下合成了六钛酸钾纳米晶须.     

一种难选铁矿石磁选精矿直接反浮选的分散特征

介绍了一种处理难选铁矿石磁选精矿的直接反浮选工艺.采用XRD,SEM和EDS等手段对原矿、精矿和尾矿的形貌及矿物组成进行了表征,重点探讨了分离过程中矿物的分散特征,为含碳酸盐难选铁矿石磁选精矿的直接反浮选技术提供理论基础.研究结果表明,采用添加分散剂直接反浮选技术可以获得合格铁精矿;有用铁矿物和脉石矿物细颗粒无选择性粘附在有用铁矿物和脉石粗颗粒表面,是造成铁矿石分离困难的主要原因;分散剂的加入有利于颗粒分散,从而实现了有用铁矿物与脉石矿物的选择性分离.     

尖晶石及含钛尖晶石的添加对MgO质材料性能的影响

以电熔氧化镁、电熔镁铝尖晶石和电熔含钛尖晶石为原料,分别在镁质材料中添加15％电熔镁铝尖晶石和电熔含钛尖晶石,研究了两种不同类型的尖晶石的加入对镁质材料性能的影响。结果表明：在MgO质材料中分别加入15％的镁铝尖晶石和含钛尖晶石后,试样的烧结性能和抗渣渗透性提高,而试样的冷态抗折强度和抗渣侵蚀性能变差。且在镁质材料中加入含钛尖晶石后材料的各项性能高于加入镬铝尖晶石后的各项性能。     

从蛇纹石制备轻质碳酸镁和轻质氧化镁的新方法

在富含氧化镁的蛇纹石中添加一种可分解的含氧无机盐,无机盐中金属氧化物与蛇纹石中二氧化硅按1:1摩尔比配方,在600—950℃下煅烧5—8小时.经分离、碳化、热分解,氧化镁提取率达90%以上.     

Comprehensive recovery of gold and base-metal sulfide minerals from a low-grade refractory ore

The comprehensive recovery of small amounts of valuable minerals such as gold and base-metal sulfide minerals from a low-grade refractory ore was investigated. The following treatment strategy was applied to a sample of this ore: gold flotation–gold concentrate leaching–lead and zinc flotation from the gold concentrate leaching residue. Closed-circuit trials of gold flotation yielded a gold concentrate that assayed at 40.23 g·t-1 Au with a recovery of 86.25%. The gold concentrate leaching rate was 98.76%. Two variants of lead-zinc flotation from the residue—preferential flotation of lead and zinc and bulk flotation of lead and zinc—were tested using the middling processing method. Foam from the reflotation was returned to the lead rougher flotation or lead–zinc bulk flotation, whereas middlings from reflotation were discarded. Sulfur concentrate was a byproduct. The combined strategy of flotation, leaching, and flotation is recommended for the treatment of this kind of ore.     

从竖罐炼锌蒸馏残渣旋涡炉处理烟化渣中浮选回收银

由于竖罐蒸馏炼锌工艺中锌精矿所含的银几乎全部进入蒸馏残渣,因此以蒸馏残渣经旋涡炉烟化处理后得到的烟化渣为原料,开展了浮选回收银的研究.浮选实验考查了浮选过程pH值、温度、捕收剂用量、起泡剂用量对粗选过程的影响.在优化的粗选工艺参数条件下进行了多级开路浮选和闭路浮选实验,最终确定采用一粗四精三扫工艺,捕收剂用量800g·t-1,起泡剂用量350g·t-1,获得银精矿品位6100g·t-1,银回收率8610%.     

再结合镁锆砖的研制及性能

由于水泥回转窑用镁铬质耐火材料在使用中生成有害的六价铬盐对环境和人体有危害,所以替代镁铬质耐火材料的研究已成为迫在眉睫的问题。以电熔二钙砂、方镁石一氧化锆共晶材料为原料,制备出了再结合镁锆砖,并对制品的烧结性能进行了研究。     

镁-铝水滑石及其衍生复合氧化物的合成

用共沉淀法制备Mg Al水滑石。利用XRD、BET等手段 ,考察了共沉淀剂、pH值、原料的滴加速度、搅拌速度、晶化温度、晶化时间、焙烧温度等合成条件对合成物相、结晶度及其衍生复合氧化物的比表面、孔径的影响。实验结果表明 ,共沉淀剂种类不影响水滑石的晶体形成 ;单一晶相水滑石形成的pH值范围为 8.5～ 9.0 ;镁与铝摩尔比 (nMg∶nAl)、晶化温度及晶化时间对水滑石的结晶度有影响 ,水热晶化法晶化时间短 ,且所得晶型好、晶粒大 ;原料的滴加速度、搅拌速度、焙烧温度对所得Mg Al O复合氧化物的比表面及孔径也有影响。由其衍生复合氧化物为载体制备的加氢脱硫催化剂的氢脱硫 (HDS)与氢氧化物 (HYD) ,随nMg∶nAl值及水滑石在载体中的质量分数的提高而降低 ,但HDS/HYD值降低 ,即对HDS的影响大于对HYD的影响。     

铝、硅添加对方镁石-铝镁尖晶石质免烧耐火材料性能的影响

采用电熔镁砂和电熔尖晶石为主要原料,以葡萄糖和水合硫酸铝为复合结合剂,以金属铝粉和单质硅为添加剂,制备方镁石-铝镁尖晶石质免烧耐火材料,研究了不同热处理温度下铝加入量及硅铝复合添加对耐火材料显微结构、烧结性能及力学性能的影响。结果表明,随着铝粉加入量的增加,方镁石-铝镁尖晶石免烧耐火材料经不同温度处理后的线膨胀率、常温抗折强度和常温耐压强度增加,并且高温抗折强度也不断提高;另外,金属铝和单质硅的添加会引起耐火材料在升温过程中的增重并减少材料的体积膨胀,从而进一步提高材料的常温力学性能。     

成分对MgO-Al_2O_3-C耐火材料抗侵蚀性能的影响

除工作环境外,原料配比对MgO-Al2O3-C材料抗侵蚀性能具有重要影响.采用不同杂质含量的电熔镁砂原料,按照不同C含量和Al2O3含量制备MgO-Al2O3-C试样.通过转动试样浸渣方法测得不同试样在富CaO熔渣中的侵蚀速率,从而研究了成分对抗侵蚀性能的影响.结果表明抗侵蚀性能随着镁砂杂质含量的增加而迅速降低,随着碳含量以及Al2O3含量的增加而先增加后降低.过多的Al2O3导致了熔渣黏度下降,而过多的碳导致了空隙率增大.根据上述结果,在富CaO熔渣中MgO-Al2O3-C材料理想的Al2O3质量分数为10%~30%,理想的C质量分数为10%~20%.     

低品位难选钼中矿的选别试验

在研究福建省某钼矿厂难选低品位钼中矿性质基础之上,通过高效捕收剂、组合抑制剂的优化配伍,结合浮选与重选技术,实现了该钼矿物的高效综合利用,得出合理的浮选流程结构与药剂制度和最佳的重选工艺参数.浮选钼精矿产品品位为45.14%,回收率达到64.7%,钼浮选尾矿由重选可分别获得硫精矿和重选钼精矿,其中重选钼精矿产品品位为3.17%,回收率达到17.2%,整个流程中钼总回收率达到81.9%.     

An alternative magnesium-based root canal disinfectant: Preliminary study of its effi cacy against Enterococcus faecalis and Candida albicans in vitro

Organisms invading root canal systems result in serious pulpal and periapical disease. To eliminate microorganisms and restrain secondary infections, dental materials with antibacterial properties are urgently needed in endodontics. Magnesium is considered as a promising biodegradable and biocompatible implant material. However, there are barely researches about its application in endodontic therapy. This work investigated the in vitro efficacy of magnesium powder against Enterococcus faecalis and Candida albicans compared with a common disinfectant, calcium hydroxide. With Calcium hydroxide served as a comparison it demonstrated the qualified antibacterial and anti-fungus properties of Mg as root canal disinfectant due to its high alkalinity of degradation, and the antimicrobial efficacy enhanced with the decreasing powder size.     

钢渣对磷酸盐水泥基材料性能的影响机制

研究了利用钢渣制备磷酸镁水泥基材料的可行性,分析了钢渣对磷酸盐水泥基材料的凝结时间、水化特性、力学性能及微结构的影响机制.结果表明:钢渣对磷酸盐水泥性能的作用规律与粉煤灰相似.掺10%钢渣时,因钢渣引入的CaO及水化生成的氢氧化钙,使得磷酸盐水泥凝结硬化加快,且钢渣自身硬度在一定程度改善了硬化水泥浆体抗压强度;随钢渣掺量增加,起胶结作用的水化产物减少,整个体系孔隙增加、结构疏松,游离氧化钙还会使磷酸盐水泥基材料性能出现劣化.钢渣掺入在浆体中并未观察到新的水化产物,但较高掺量下体系微裂纹增多.     

共沉淀法制备镁锰双金属氢氧化物及表征

以氯化镁、氯化锰、氢氧化钠及碳酸钠为原料,采用共沉淀法合成镁锰双金属氢氧化物(Mg-Mn-LDH).探讨镁锰摩尔比、反应温度、反应时间等条件对镁锰双金属氢氧化物(Mg-Mn-LDH)结晶性的影响.通过XRD和SEM对产物结晶性、组成结构等进行表征.实验结果表明,在镁锰摩尔比3∶1、反应温度40℃、反应3h、长陈化时间和反应体系pH 13下,制备出的产物的结晶性最好,层状结构也最清晰.     

高纯微细氢氧化镁的水热法制备

以国内丰富的镁资源为应用背景，借助SEM、X荧光光谱仪等现代测试手段，研究水热技术在制备高纯微细氢氧化镁中的应用，测试结果表明水热技术使氢氧化镁平均粒径明显增大，晶型发育完善，纯度提高，有助于改善氢氧化镁作为高效阻燃剂在合成材料中的分散和阻燃性能，为海水镁资源的有效利用提供了适宜的处理途径．     

八水磷酸镁的制备

以六水氯化镁、氢氧化钠和磷酸为基本原料制备八水磷酸镁(Mg_3(PO_4)_2·8H_2O)。其主要条件:温度323K,pH值6.8。八水磷酸镁在435K脱去八个结晶水,得到无水磷酸镁。