BaMoO_4微晶的微乳液可控合成及形成机理探讨

采用聚乙二醇对异辛基苯基醚(Triton X-100)/正戊醇/环己烷/水溶液所形成的微乳液体系,控制合成出了四方晶系BaMoO4微晶,考察了微乳液中水与表面活性剂物质的量之比和反应物浓度对产物形貌的影响。采用扫描电子显微镜(SEM)、X-射线衍射(XRD)分别对产物的结构、粒度和形貌进行了表征。结果表明,在微乳液体系中,控制不同的实验条件,可以成功地合成蝴蝶结状以及不同长度树枝状的BaMoO4微晶,并且粒径分布集中,无团聚现象。论文还对不同形貌BaMoO4微晶的形成机理进行了初步探索。     

熔盐法合成片状NaNbO3晶体

片状NaNbO3晶体可作为反应模板晶粒生长技术(RTGG)制备高取向铌酸钾钠无铅压电陶瓷的模板晶体,通常采用两步熔盐法合成.首先合成片状Bi2.5Na3.5Nb5O18(BNN5)晶体,然后以BNN5晶体作为前驱体合成NaNbO3晶体.借助X射线衍射(XRD)仪、扫描电镜(SEM)及高分辨透射电镜(HRTEM),考察合成温度以及保温时间对晶体物相、形貌和尺寸的影响并揭示片状NaNbO3晶体的形成机理.结果表明:以NaCl为熔盐,1 150 ℃保温4 h,得到物相单一、形貌规则、尺寸均一的片状NaNbO3晶体,晶体尺寸约为15 μm×10 μm×1 μm.片状NaNbO3晶体的形成机理是高温条件下由于熔盐中Na2CO3作用,BNN5晶体中[Bi2O2]层被破坏,Bi3+、O2-不断从结构中析出,[Bi2O2]层脱离.同时一部分Na+进入晶格中取代[NbO6]八面体空隙中的Bi3+,另一部分Na+进入[Bi2O2]层脱离后形成的空位中与NaNbO3基元进行结构重排,最终形成NaNbO3晶体.     

熔盐法合成ZnTiO_3粉体的相结构研究

采用熔盐法合成了ZnTiO3粉体,研究了熔盐体系、氧化物掺杂、及煅烧制度对产物相结构的影响.结果表明:以NaCl/KCl复合熔盐可合成近于纯相的六方ZnTiO3.MgO、V2O5和W2O3掺杂获得的粉体主晶相均为ZnTiO3;MgO掺杂量为0.3时相稳定效果最好;而V2O5和W2O3掺杂量的变化对相结构影响不明显.在800～850℃获得了稳定的六方ZnTiO3相,保温时间的延长会促进ZnTiO3的分解.     

熔盐法合成钽酸锌粉体

以Ta2O5和Zn(NO3)2·6H2O为原料,KCl-ZnCl2为熔盐,采用熔盐法在700°C保温3 h合成了钽酸锌陶瓷粉体.粉体的晶相组成、形貌分析和化学组成通过XRD, SEM和EDS来表征.研究了不同反应条件,包括温度和熔盐体系中KCl/ZnCl2的摩尔比对产物粉体的晶相和形貌影响.结论显示当KCl/ZnCl2的摩尔比低于0.1:1时,在700°C保温3 h为制备钽酸锌的最优工艺条件.     

新型熔盐法合成多省并醌

以蒽醌(AQ)和均苯四甲酸酐(PMA)为原料在三氯化铝的催化作用下,对比采用溶液(硝基苯)法和熔盐(NaCl-AlCl3)法合成了具有一定介电常数的多省并醌聚合物(PAQR)。通过红外对产物进行结构表征,然后对产物进行热失重(TG)分析测试,最后测量两种方法PAQR的介电常数。结果显示两种方法合成的PAQR热稳定性均良好。采用熔盐法得到了在20Hz频率下,介电常数为4350的PAQR,而溶液法的介电常数仅为48.5。     

熔盐法制备钛酸锶的光解水研究

以熔盐法和固相法分别制备了5个钛酸锶光催化剂,并采用XRD、BET、SEM等表征了制备样品的性质.熔盐法制备的样品呈现立方体小颗粒状.采用浸渍法,在钛酸锶的表面担载氧化镍助催化剂,评价了该光催化剂光解水的催化活性.结果表明光解水催化剂钛酸锶的制备过程明显影响催化剂的反应活性.NaCl为熔盐时制备的SrTiO3晶体光催化...     

NiFe2O4晶微粉的共沉淀法和熔盐法制备

用化学共沉淀法和熔盐法制备了一系列NiFe2O4纳米粉体,在室温下测定了它们的磁性能,利用X衍射确定了粉体的相结构、比表面积和晶格常数,利用扫描电子显微镜观察了颗粒的形貌.结果显示,由于制备方法的差异使得粉体的各项指标都有比较明显的差异.     

熔盐法合成多孔碳材料及其电催化产氢性能

能源危机问题一直在困扰着人们,能源短缺已经成为人类亟待解决的首要问题.目前,人们正在避免不必要地使用化石能源等不可再生能源.氢能是二次能源,其储量丰富、没有污染、并且可以再生.因此,人们将目光放在寻找既节能又能够大量生产氢气的方法,并且在不断地探究更好的产氢催化剂.熔盐法是一种新型的制备无机粉体的方法,在能源、材料、化...     

LD泵浦Nd:GdVO4水热法与熔盐法KTP腔内倍频绿光的对比研究

报道了分别使用水热法和熔盐法的KTP对Nd:GdVO4晶体倍频绿光的对比研究.通过理论分析和计算两种方法的KTP倍频效率与温度的关系,在实验中,当抽运功率为6.11 W时,水热法与熔盐法KTP倍频的Nd:GdVO4激光器输出绿光功率分别为0.7 W、0.63 W,光-光转换效率为11.5%、10.3%,并分析了转换效率不同以及偏低的原因.     

Molten salt synthesis of mullite nanowhiskers using different silica sources

Mullite nanowhiskers with Al-rich structure were prepared by molten salt synthesis at 1000℃ for 3 h in air using silica, amorphous silica, and ultrafine silica as the silica sources. The phase and morphology of the synthesized products were investigated by X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy, and transmission electron microscopy. A thermogravimetric and differential thermal analysis was carried out to determine the reaction mechanism. The results reveal that the silica sources play an important role in determining the morphology of the obtained mullite nanowhiskers. Clusters and disordered arrangements are obtained using common silica and amorphous silica, respectively, whereas the use of ultrafine silica leads to highly ordered mullite nanowhiskers that are 80-120 nm in diameter and 20-30 μm in length. Considering the growth mechanisms, mullite nanowhiskers in the forms of clusters and highly ordered arrangements can be attributed to heterogeneous nucleation, whereas disordered mullite nanowhiskers are obtained by homogenous nucleation.     

异型纳米AlOOH微观晶体结构

利用RTO金属包埋切片微米--纳米表征法,通过高分辨透射电镜观察了γ--AlOOH薄膜切片中的晶格点阵条纹像,分析了添加复合添加剂后异型纳米AlOOH的微观晶体结构,从原子层面揭示了由于铁离子的同晶替代以及硫酸根离子的插层而导致的晶格畸变.阐述了极性添加剂在晶须生长过程中首先形成复合的高聚体、进而定向生长的诱导机理,并指出了非极性表面活性剂对异型纳米AlOOH晶体形貌表面的修复和美容作用.用能谱及红外光谱佐证了复合多聚体的存在.     

Structure of heterotypic nano AIOOH microcrystals

利用RTO金属包埋切片微米--纳米表征法,通过高分辨透射电镜观察了γ--AlOOH薄膜切片中的晶格点阵条纹像,分析了添加复合添加剂后异型纳米AlOOH的微观晶体结构,从原子层面揭示了由于铁离子的同晶替代以及硫酸根离子的插层而导致的晶格畸变.阐述了极性添加剂在晶须生长过程中首先形成复合的高聚体、进而定向生长的诱导机理,并指出了非极性表面活性剂对异型纳米AlOOH晶体形貌表面的修复和＂美容＂作用.用能谱及红外光谱佐证了复合多聚体的存在.     

二次熔盐锂电池用二硫化铁的合成及性能测试

利用加压水溶液法合成了黄铁矿型二硫化铁，研究了反应压力和溶液ｐＨ对产物中二硫化铁含量的影响，给出了合成反应的可能机理，测定了二硫化铁活性材料的利用率。     

Mo-Al_2O_3金属陶瓷在NaCl熔盐中的腐蚀行为

为提高 Mo-Al_2O_3金属陶瓷热电偶保护管在熔盐中的使用寿命,在实验室采用坩埚法,模拟现场实际使用情况,探讨了Mo-Al_2O_3在NaCl熔盐中的腐蚀行为,结果表明,Mo-Al_2O_3金属陶瓷在纯NaCl熔盐中,主要是电化学蚀损,并随Mo含量的增加而加快,Al_2O_3则与此相反;在添加硼砂的熔盐中,除金属相蚀损外,陶瓷相也严重蚀损。如在Mo-Al_2O_3中添加Cr_2O_3则可提高金属陶瓷在含硼砂的NaCl介质中的抗蚀能力,本工作为保护管的研制及其在现场的合理使用提供了依据。     

氯化物熔体中钐离子在铁电极上的电还原

利用线性扫描伏安法研究了Ｓｍ（Ⅲ）在等摩尔ＭａＣｌ－ＫＣｌ熔体中铁电极上还原的电化学行为．结果表明，Ｓｍ（Ⅲ）第一步可逆还原为Ｓｍ（Ⅱ），Ｓｉｎ（Ⅱ）进一步还原并与铁形成合金．测定了Ｓｍ（Ⅲ）在氧化物熔体中的扩散系数及扩散活化能．     

用CIS理论估算三元熔盐相图

用共形离子理论(CIS)计算了若干三元熔盐相图,其中一个体系在一定范围内改变了原始参数的数值(m.p.-5K,Teut-5K,△H°-10%)以考察原始参数中测量误差对相图计算精度的影响。结果表明,所用的方法具有一定的自适应能力,可以利用少量的原始参数较好地预报三元共晶型熔盐相图。