常温下AlCl_3／SbCl_3引发α－蒎烯阳离子聚合

研究了常温下（２５℃）ＡｌＣｌ３／ＳｂＣｌ３复合引发体系的α－蒎烯聚合反应．结果表明，控制一定的引发剂浓度、［Ｓｂ］／［Ａｌ］比等条件，即使温度高达室温仍可获得较高摩尔质量的固态树脂．［ＡｌＣｌ３］＝２１．３ｍｍｏｌ／Ｌ，［Ｓｂ］／［Ａｌ］＝１时，聚合产物Ｍｎ可达到８１０，二聚体含量仅为７％．复合引发体系的聚合动力学研究表明该复合引发剂两组分相互作用产生了本质不同于Ｌｅｗｉｓ阳离子引发剂活性种的新活性种．     

Co—Cu—Sn三元系合金相图的室温截面

用Ｘ射线粉末衍射法对Ｃｏ－Ｃｕ－Ｓｎ三元系合金相图的室温截面进行了测定，得出了３１个相区，它们分别是９个单相区，１５个两相区，７个三相区。     

W－Ni－Co三元系1100℃等温截面的测定

借助三元扩散偶／电子探针分析技术测定了Ｗ－Ｎｉ－Ｃｏ三元系在１１００℃时的等混截面．它包含了：３个单相区，即ｂｃｃ（Ｗ），μ－Ｃｏ７Ｗ６和ｆｃｃ；３个两相区，即ｂｃｃ（Ｗ）＋μ－Ｃｏ７Ｗ６，ｂｃｃ（Ｗ）＋ｆｃｃ和ｆｃｃ十μ－Ｃｏ７Ｗ６；１个三相区，即ｂｃｃ（ｗ）＋ｆｃｃ＋μ－Ｃｏ７Ｗ６．     

α－（AlMnSi）空间构型与价电子结构分析

分析了金属间化合物α－（ＡｌＭｎＳｉ）的空间结构，并运用余瑞璜的固体与分子经验电子论中的键距差分析法计算了α－（ＡｌＭｎＳｉ）的理论键距及其各种原子所选取的杂阶．在此基础上计算出α－（ＡｌＭｎＳｉ）中Ｍｎ原子键络的共价键键能．     

掺杂元素物态对PTC材料性能的影响

研究了Ｙ－Ｓｂ，Ｌｉ－Ｍｎ，Ｓｉ－Ａｌ等元素以固相或液相掺杂对正温度系数热敏电阻（ＰＴＣ）材料性能的影响。实验结果表明，Ｌｉ－Ｍｎ液相掺杂可以提高材料ＰＴＣ效应及耐压值；Ｓｉ－Ａｌ液相掺杂可降低材料室温电阻率，提高材料耐压值，Ｙ－Ｓｂ液相掺杂可以降低材料室温电阻率，但ＰＴＣ效应有所降低     

4－（8－氨基喹啉－5－偶氮）－苯磺酸钠的极谱行为研究

研究了４－（８－氨基喹啉－５－偶氮）－苯横酸钠（ＳＡＯＡＢＳ）的极谱行为。在０．０２ｍｌ／ＬＮＨ＿３·Ｈ＿２Ｏ－０．３６ｍｏｌ／ＬＮＨ＿４Ｃｌ的缓冲溶液中，ＳＡＱＡＢＳ产生两个明晰的阴极化极谱波，其二次导数波的峰电位分别为－０．５２Ｖ和－１．３０Ｖ（Ｖｓ．ＳＣＥ）。用ＳＡＱＡＢＳ的第一个波作为定量分析的基础，其线性范围为１．０×１０￣（－６）～８．０×１０￣（－５）ｍｏｌ／Ｌ。氧不干扰ＳＡＱＡＢＳ的测定。还研究了ＳＡＱＡＢＳ的电极过程及反应机理。     

Ti—Al—Y三元系相图1000℃部分等温截面重新确定

利用扩散偶局部平衡原理，通过金相观察和电子探针微区成分分析，重新测定了１０００℃下Ｔｉ－Ａｌ－Ｙ三元部分等温截面相图。首次发现该系在１０００℃存在两个三元化合物均相区Ｙ（ＡｌｘＴｉ１－ｘ）２（ｘ＝８０％￣１００％）和Ｙ３（ＡｌｘＴｉ１－ｘ）２（ｘ＝８０％￣１００％）改变了以前发表的关于Ｔｉ－Ａｌ－Ｙ三元相图１０００℃等温截面的研究结果。此外在所测部分等温截面相图中存在６个单相区，９个两相平衡区，４     

流态化化学气相淀积制备Al_2O_3－SnO_2复合粒子的研究

利用流态化化学气相淀积（ＣＶＤ）制备Ａｌ＿２Ｏ＿３－ＳｎＯ＿２复合粒子。探讨了ＳｎＯ＿２在Ａｌ＿２Ｏ＿３超细颗粒上的包敷状态，考察了反应温度、反应物进料浓度比、反应时间等对反应结果的影响。结果表明，ＳｎＯ＿２在复合粒子团聚体体相中呈均匀分布，形成Ａｌ＿２Ｏ＿３－ＳｎＯ＿２复合粒子，ＳｎＯ＿２均匀淀积在Ａｌ＿２Ｏ＿３超细颗粒原生粒子表面，流态化ＣＶＤ包敷效果优于非流化过程；随反应时间的延长，产物中ＳｎＯ＿２含量线性递增；而当反应温度高于３００℃，反应物Ｈ＿２Ｏ和ＳｎＣｌ＿４配比大于４：１时，ＳｎＯ＿２含量基本保持不变。     

快速凝固Al－Fe－V－Si合金薄带微观结构的热稳定性

通过示差热分析、Ｘ射线衍射、能谱分析和透射电镜观察，研究了快速凝固Ａｌ－Ｆｅ－Ｖ－Ｓｉ合金薄带微观结构的热稳定性．结果表明，室温时已存在立方结构的α－Ａｌ（１３）（Ｆｅ，Ｖ）３Ｓｉ相，呈近球形弥散分布；加热时α粒子长大，但直到５１０℃／１００ｈ粒子粗化仍不明显．升温到６５０℃发生相转变．出现多边形θ－Ａｌ２（Ｆｅ，Ｖ，Ｓｉ）六方结构相；而经６５０℃／２５ｈ处理后观察到长条形析出相，其成分近似为（Ａｌ，Ｓｉ）（１３）Ｆｅ４，并与原来立方相、六方相粒子共存．     

Cu—Mn—Pt／γ—Al2O3系列催化剂中组分间的活性增强效应

通过ＣＯ氧化活性测试，采用ＸＲＤ、ＸＰＳ、ＴＰＲ等方法表征，研究了Ｃｕ－Ｍｎ－Ｐｔ／γ－Ａｌ２Ｏ３系列催化剂中组分间的活性增强效应，并对其固相结构和表面组成进行表征．结果表明：（１）氧化型ＣｕＭｎ／γ－Ａｌ２Ｏ３催化剂中Ｃｕ和Ｍｎ之间存在一定的活性增强效应，两种活性组分发生协同作用；（２）还原型Ｐｔ－Ｃｕ／γ－Ａｌ２Ｏ３和Ｐｔ－Ｍｎ／γ－Ａｌ２Ｏ３催化剂的氧化活性在系列中最高，Ｐｔ－Ｍｎ／γ－Ａｌ２Ｏ３的ＣＯ氧化活性增强效应最为显著．这与加人Ｐｔ后，Ｃｕ２＋易被还原，Ｃｕ＋明显增多有关；（３）同时含有Ｃｕ、Ｍｎ组分的几种催化剂中，催化剂表面上Ｃｕ均有一定富集，加人Ｐｔ后，表相以Ｃｕ＋为主．由于Ｃｕ－Ｍｎ－Ｐｔ三元催化剂的制备方法不同，以致氧化活性相差很大，共浸制备较分浸制备的催化剂活性要好的多．     

Phase relationships in 500℃ isothermal section of Ho-Ni-Ti 牋爐ernary system and the fundamental characteristics of the related compounds

By means of X-ray powder diffraction (powder XRD), differential thermal analysis (DTA), scanning electron microscopy (SEM) and X-ray electron dispersed spectrum microanalysis (EDS), the isothermal section at 500℃ in Ho-Ni-Ti ternary system is determined. Intermetallic phases in this section and the relationships among them are studied. In addition, the characteristics of some of these compounds are analyzed. This section consists of 13 singlephase regions, 23 two-phase regions and 11 three-phase regions. The existence of 10 binary compounds is confirmed.No ternary. compound is found.     

Isothermal section of ternary Sn ? Zn?Ni phase equilibria at 250 °C

Ternary Sn ?Zn? Ni alloys were prepared and equilibrated at 250 °C for 4? 15 weeks. The phases formed in these equilibrated alloys were determined experimentally. The isothermal section of Sn ?Zn? Ni system was constructed, based on the phase diagrams of the three constituent binary sy stems and the ternary phase equilibria data, determined in this study and referenced in literatures. 12 single-phase regions were identified in the Sn? Zn?Ni ternary system at 250 °C, including the three ternary compounds, δ , τ1 and τ2. There were 13 ternary phase regions and 23 binary phase regions in the 250 °C Sn ? Zn? Ni isothermal section. The solubility of Zn in the binary Sn ?Ni compounds is significant, and is 15.1% (mole fraction) in the Ni3Sn phase.     

Sn-Sb-Te三元合金相图200℃等温截面

【目的】获得在SnTe基热电材料中掺杂Sb后的相关系。【方法】采用X-ray Diffraction Analysis(XRD)、Scanning Electron Microscope(SEM)及Energy-Dispersive X-ray Spectroscopy(EDS)对合金样品进行测试,绘制Sn-Sb-Te三元系图200℃等温截面并进行相关系分析。【结果】Sn-Sb-Te三元体系200℃等温截面由3个单相区、5个两相区和5个三相区组成。其中,5个三相区分别是Sb_2Te_3+Te+SnSb_2Te_4、SbTe+SnSb_2Te_4+Sb_2Te_3、SnTe+δ-Sb_2Te+Sb、SnTe+SnSb+Sb和SnTe+SnSb+Sn。200℃时,Sb元素在SnTe相中的固溶度为3.57at.%;此外,在200℃下Sn-Sb-Te三元系中出现文献报道的SnSb_2Te_4三元相。【结论】通过合金法测定了Sn-Sb-Te三元合金相图在200℃的相平衡关系,为进一步开发SbTe基热电材料提供有益参考。     

Al2O3-CaO-SiO2系截面图的计算与验证

以实测相图为依据选择溶液的基本相,采用FACT软件计算了复杂的Al2O3-CaO-SiO2三元氧化物体系的两个等温截面和两个多温截面,并根据实测相图绘制了同等条件下的截面图,对其进行验证分析.结果表明,由于Al2O3-CaO-SiO2三元系化合物数量多,结构复杂,计算相图与实测相图相差较大.在用FACT软件计算组元间相互作用较强的氧化物体系相图时,尚需进一步改进计算模型,完善热力学数据库.存在强相互作用的三元氧化物体系的等温截面和多温截面应以实验数据为基础,同时参考计算相图.     

45 ℃ Na2SO4-MgSO4-H2O三元水盐体系相平衡研究

利用湿固相法研究了Na2SO4-MgSO4-H2O三元水盐体系在45℃时的固液相平衡关系。采用等温法测定了该体系的溶解度数据,并绘制了相图。结果表明,该体系在45℃时的相图存在5个区域,即纯Na2SO4的结晶区、Na2SO4和复盐Na2SO4.MgSO4.4H2O的结晶区、复盐Na2SO4.MgSO4.4H2O的结晶区、复盐Na2SO4.MgSO4.4H2O和MgSO4.7H2O的结晶区、MgSO4.7H2O的结晶区。     

Fe-Pt-Au三元系950℃富角等温截面的研究

为了控制细小的L10-FePt纳米相均匀分布在非磁性基体中,有必要对Fe-Pt-X系的相图进行系统研究.通过合金法和扩散偶法,利用X射线衍射(XRD)、扫描电镜及能谱成分(SEM-EDS)分析确定了Fe-Pt-Au三元系950℃富Fe角处相平衡关系及各相平衡成分,从而建立了富Fe角的等温截面相图.结果表明,该等温截面存在成分范围很宽的(γFe+αAu)两相区和成分范围很窄的(γFe+L10-FePt)两相区.Pt的加入使Au在γFe中的固溶度从约4%提高到约15%(原子数分数),而大大降低了Fe在αAu中的固溶度;Au的加入使Pt在γFe中的固溶度降低,并且没有扩大(γFe+L10-FePt)...     

Fe—C基三元合金相图计算

本工作设计了Fe-C基三元合金热力学计算软件，它可计算Fe-C与Cr,Mn,Si,Cu,Mo,W,Ni,V,Ti,Nb组成的三元系在不同温度下的等温载面图，并可提供有关的热力学数据。     

镧系离子(Nd~(3 ),Ho~(3 ),Er~(3 ))同PMDCP和DPG三元配合物的超灵敏跃迁及其在分析上的应用研究

本文用光度法研究了Nd~(3 ),Ho~( 3),Er~(3 )离子同PMDCP和DPG所形成的三元配合物的超灵敏跃迁现象;测定出三元配合物的组成比为Ln~(3 ):PMDCP:DPG=1:4:1;实验了该体系在尤吸收最大时遵守比耳定律的浓度间隔,同时对一些干扰离子进行了实验.     

1000℃MgO—B2O3—SiO2三元相关系研究

ＭｇＯ－Ｂ２Ｏ３－ＳｉＯ２三元系１０００℃时，３５％≤ＭｇＯ％〈６０％组成范围内平衡相均为固相，其相关系可由Ｍｇ３Ｂ２Ｏ６－Ｍｇ２ＳｉＯ４－Ｍｇ２Ｂ２Ｏ５，Ｍｇ２Ｂ２Ｏ５－Ｍｇ２ＳｉＯ４－ＭｇＳｉＯ３，Ｍｇ２Ｂ２Ｏ５－ＭｇＳｉＯ３－ＳｉＯ２三个结线三角形表示。各平衡相量之间关系可应用ＸＲＤ定量相分析或重心规则计算。