蔗渣浆的全无氯漂白工艺

对蔗渣浆采用过氧化氢强化的氧脱木素(OP)-螯合预处理(Q)-压力过氧化氢漂白(PO)的短序漂白,探讨了将蔗渣浆漂至82%ISO和用非硅过氧化氢漂白稳定剂代替硅酸钠用于过氧化氢漂白的可行性.研究表明,非硅过氧化氢稳定剂PP-1与PP-2耐高温、耐高压,可用于压力过氧化氢漂白.OP段氢氧化钠用量为2.0%(相对于绝干浆质量,下同)、过氧化氢用量为0.5%,PO段过氧化氢用量为3.0%、PP-1用量为0.1%、PP-2用量为0.5%时,蔗渣浆采用OPQPO流程漂白后,浆的白度可达到85%ISO.而且OPQPO从根本上消除了可吸附有机卤化物的产生;经测定,漂白废水属于可生物降解废水.     

蔗渣浆ECF短序漂白流程的对比

对典型的蔗渣浆无元素氯(ECF)短序漂白流程D0EpD、OpDEp及OpD进行了对比,探讨了二氧化氯脱木素(D0)与过氧化氢强化氧脱木素(Op)的脱木素效率差异及对后续漂白的影响,并分析了漂白过程中可吸附有机卤化物(AOX)的产生量和各漂白流程的直接化学品成本.结果表明:D0段脱木素选择性好,ClO2用量为0.8%时脱木素率即达40%以上,且用量越高脱木素作用越强;Op段在脱出纸浆中残余木素的同时能大幅提升纸浆白度,纸浆白度明显高于D0浆;相同后续漂白化学品用量下,OpDEp漂后浆白度高于D0EpD漂后浆白度,且比OpD漂后浆白度约高12个百分点;相同纸浆白度下,OpDEp漂白过程中产生的可吸附有机卤化物总量约为D0EpD的50%,其直接化学品成本比后者低约40.00元/t,具有更好的环境、经济效益.     

蔗渣浆的压力过氧化氢漂白

对烧碱-蒽醌(Soda-AQ)法蔗渣浆分别进行了螯合预处理(Q)和常压过氧化氢(P)、压力过氧化氢(PO)漂白的研究,探讨了单段PO漂白蔗渣浆的可行性.正交试验结果表明,PO漂白蔗渣浆优化的漂白条件为漂白温度100℃、时间80min、压力0.6MPa、NaOH用量0.4%.PO漂白浆的白度较高,达84.0%ISO,特性黏度为825.3mL/g,比QP漂白浆的白度高9.9%ISO;PO漂白浆的物理强度性能也较好,浆料的抗张指数为66.67N.m/g,撕裂指数为9.34mN.m2/g,耐破指数为4.31 kPa.m2/g,耐折度为39次.PO漂白废水的化学耗氧量、生化耗氧量及色度较低,漂白废水可全部逆流回用,大大减少了污染排放.     

碱抽提强化的麦草浆ClO_2漂白及ECF漂白流程

采用常规碱抽提(E)、氧加强的碱抽提(EO)、H2O2强化的碱抽提(EP)、氧和H2O2强化的碱抽提(EOP)对ClO2脱木素(D0)麦草浆进行改性,考查不同碱抽提方式的改性效果在后续漂段(D1)的体现,并就不同无元素氯(ECF)漂白流程(D0ED1、D0P、D0A/QP、D0EP、D0EPD1、D0EPP)进行对比.结果表明:不同碱抽提方式对D0浆木素的改性效果不同,就对后续漂段D1的影响而言,4种不同碱抽提方式下纸浆的可漂性顺序为D0EOPD0EPD0EOD0E;在4种碱抽提方式所对应的D0ED1漂白流程中,D1段ClO2用量的增加对白度的提升是有限的,以0.8%~1.0%为佳;D0EPD1和D0EPP流程漂白效果优于其它流程,采用D0EPD1和D0EPP流程漂后白度可分别达到82.3%ISO和83.8%ISO,均适用于麦草浆短序ECF漂白.     

H2O2 的分解过程影响因素及其稳定剂

对 H2 O2 的分解过程影响因素进行了研究 ,对 H2 O2 的稳定剂进行了比较 ,SH— 2 2非硅型氧漂稳定剂效果最好 ,使 H2 O2 8小时分解率为 1 .89% ,漂白白度为 83%左右     

碱抽提强化的麦草浆二氧化氯漂白及ECF漂白流程研究

摘要：采用四种不同的碱抽提方式对麦草浆二氧化氯漂白(D0)进行强化,考查了不同碱抽提方式的强化效果,并对不同ECF漂白流程进行了对比研究。结果表明：在D0ED1漂白流程中,不同碱抽提方式对D0木素的修饰效果不同,就后续D1漂段而言,四种不同碱抽提模式下纸浆的可漂性顺序为：D0EOP>D0EP>D0EO>D0E。在D0ED1漂白流程中,D1段ClO2对白度的提升是有限的,达到白度极限后再增加ClO2用量对白度提高不明显。本实验条件下D1段ClO2用量以1.0%~1.2%为佳。从D0ED1与D0EP各漂白流程的对比来看,在终段漂白中以P取代D1效果要好,表明H2O2用于终段漂白其效果要好于ClO2。从其它ECF漂白流程的对比来看,D0EPP和D0EOPP流程漂白效果优于其它流程。本实验条件下采用D0EPP和D0EOPP漂白流程,麦草浆漂后白度可分别达到83.8%和85.7%。     

马尾松SGW高白度全无氯漂白研究

对马尾松磨石磨木浆(SGW)进行了单段H2O2漂白和2段H2O2漂白试验，研究了不同预处理方法和条件对H2O2漂白效果的影响，提出了最佳的预处理工艺；同时还研究了以EDTA和MgSO4作为金属螯合剂改善H2O2漂白效果，进而确定了H2O2漂白的最佳工艺参数．结果表明，应用EDTA和MgSO4作为金属螯合剂，SGW经预处理后，采用两段H2O2漂白，漂后纸浆白度可由原浆的47．8％提高到74．5％，从而使制得的漂白浆能满足低定量高白度胶印新闻纸和其他高级纸种的生产要求．结果还表明，与传统CEH3段漂白相比，漂白废水中的CODCr减少78．5％，BOD5减少97％，且不再含有可吸附的有机卤化物(AOX)．     

碱性H_2O_2处理蔗渣化学浆的漂白效应

目前采用次氯骏盐漂白纸浆纤维的损伤大,废水严重污染.研究采用无污染漂白剂H_2O_2探索了总碱、碱比、预处理和漂温等对漂白过程的影响和作用机理,指出H_2SO_4预处理后的蔗渣化学浆,在NaOH用量1.5%、Na_2SiO_3用量3.5%、MgSO_4用量0.05%、70℃的漂温下漂白2小时H_2O_2消耗2.367%,经草酸适当的中和还原后,漂浆的白度从39.5%(SBD)提高到7l%,白度增值高,白度的稳定性好,得率也高,因之H_2O_2漂白剂是发展我国草浆漂白有前途的力法.     

白腐菌改性桉木CTMP浆的漂白研究

利用白腐菌改性处理可以显著提高机械浆的强度性能,有利于拓宽机械浆的应用范围.本文采用白腐菌Trametes hirsute 196对桉木CTMP浆进行改性处理,并探讨了白腐菌处理后纸浆的漂白工艺.研究结果表明:白腐菌处理使桉木CTMP浆白度值从49.6%下降到37.8%,且这种改性后纸浆的可漂性较差,H2O2和Na2S2O4单段漂后纸浆白度均在60%以下,但采用Na2S2O4—H2O2两段组合漂白工艺可以使漂后Bio-CTMP浆白度达到71.3%.     

日本落叶松硫酸盐浆漂白特性

为了解日本落叶松的纸浆物理性能,以日本落叶松KP浆为原料,对纸浆的漂白特性进行了系统研究.结果表明:在常规CEH三段漂白中,最佳有效氯质量分数为8%,NaOH质量分数为2.5%,漂白纸浆白度可达到71%(ISO);在CDEHD漂白中,最佳有效氯质量分数为9%,EH段合理NaOH质量分数为2%,纸浆白度能够达到81%(ISO);在D/CE1D1E2D2和DE1D1E2D2漂白中,当总有效氯质量分数为7.9%时,两种漂白流程都能将纸浆漂到82%(ISO)的高白度.采用过氧化氢加强氧漂再加两段过氧化氢漂白的漂白流程(即OpQP1P2)可以将白度为27.3%(ISO)的纸浆漂到76.6%(ISO).     

STUDY ON THE ELEMENTAL CHLORINE FREE BLEACHING OF BAMBOO KRAFT PULP

1INTRODUCTIONChina is a country using the most variety of non-wood fiber raw material and is the largest country producing non-wood fiber pulp and paper in the world[1]. Bamboo is one kind of the main non-wood species for papermaking in China. Although the structure of raw materials for papermaking has being adjusted through increasing the proportion of wood pulp and by effectively utilizing waste paper source, non-wood species will still remain an important fiber resource[1,2].At present…     

MODIFIED OPAL:A NOVEL STABILIZER FOR HYDROGEN PEROXIDE BLEACHING OF PULPS

The possibility of modified opal as the stabilizer of hydrogen peroxide bleaching was investigated. The results showed that the modified opal in place of sodium silicate as the stabilizer of hydrogen peroxide bleaching is feasible. At the same dosage, above 3% ISO can be increased for both wheat straw pulp and deinked pulp. The stabilizing ability of the modified opal to hydrogen peroxide bleaching of pulp is improved markedly. It is favorable for bleaching to increase temperature and time within a permissive extent. The suitable process conditions are 10% of pulp consistency, 3% of hydrogen peroxide, 1.5% of sodium hydroxide, 3% of the modified opal, 70℃ and 60 min when the modified opal is used as the stabilizer of hydrogen peroxide bleaching. At these conditions, the brightness gain can reach about 16% ISO for wheat straw pulp. In addition, it is favorable for bleaching to add a little magnesium sulfate when the modified opal is used as the stabilizer of hydrogen peroxide bleaching, the brightness of pulp can increase I%ISO if0.05% of magnesium sulfate is added. The cost analysis indicated that the modified opal is superior to sodium silicate as the stabilizer of hydrogen peroxide bleaching in economical aspect and has further the potential of market development.     

过渡金属离子对废纸浆H2O2漂白的影响

研究了过渡金属离子对废纸浆H2O2漂白的影响.研究结果表明,经较强的螯合处理之后重新加Cu2 ,Fe2 和Mn2 ,漂后纸浆的白度降低,残余H2O2减少,漂白效率降低.     

桉木硫酸盐浆TCF漂白的研究

研究桉木硫酸盐浆H2O2强化的氧脱木素效果;研究KMnO4和螯合物对桉木硫酸盐氧漂浆H2O2漂白的改善效果,并对其最佳工艺条件及各种因素对漂白效果的影响进行探讨。结果表明：在氧脱木素过程中加入少量的H2O2,就能起到很好的强化效果;氧漂浆在KMnO4的预处理、DTPA处理后再经过H2O2漂白,可使KP法桉木浆白度达80％以上。     

竹子化机浆漂白工艺及其机理

 竹子作为一种重要的非木材制浆造纸资源,具有生长周期短、储量大及成本低等优点,但是其成浆存在白度低、白度稳定性差、易返黄、废液硅含量高难处理等问题。本研究利用H₂O₂、NaBH₄、Na₂S₂O₄和CH₃COOOH等漂白剂对粉单竹碱性过氧化氢化学机械浆（APMP）进行单段或者两段组合补充漂白,以提高竹子APMP浆的可漂性、白度及其稳定性、强度等。研究结果表明,常规H₂O₂漂白是竹子化机浆最佳单段补充漂白方法。两段补充漂白实验表明,白度提高最大的是H₂O₂→Na₂S₂O₄组合,为73.85% ISO;黏度下降最大的是H₂O₂→NaBH₄组合,漂后浆黏度从960下降到601 mL·g^-1。虽然两段补充漂白漂后浆的黏度有所下降,但其物理强度得到提高。补充漂白的示差红外分析发现：H₂O₂、H₂O₂→Na₂S₂O₄、H₂O₂→NaBH₄ 3种漂白方法的纸浆中共轭羰基含量降低了,而H₂O₂→CH₃COOOH漂白浆中的共轭羰基含量反而增加。甲氧基、紫丁香型木素和缩合的愈创木基环在H₂O₂→Na₂S₂O₄两段补充漂白过程脱除效果最显著。X射线衍射分析表明,补充漂白过程单段H₂O₂和H₂O₂→Na₂S₂O₄两段漂白对碳水化合物的降解作用最小。     

环多胺型仿酶金属配合物的制备与应用

合成了1,4,7-三甲基三氮杂环壬烷(Me3tacn),以Me3tacn为原料与CoⅡCl2·6H2O反应,制备[Co2ⅡCl3(Me3tacn)2]·[CoⅡCl3(H2O)3]环多胺型仿酶金属配合物催化剂,采用傅里叶变换红外光谱和元素分析的方法对合成的金属配合物进行表征.将这种仿酶金属配合物应用于棉织物的温堆漂白工艺试验,探讨了温度、配合物浓度及稳定剂质量浓度3种因素对双氧水漂白棉织物效果的影响.研究结果表明,在80℃条件下,环多胺金属配合物浓度为12μmol/L,稳定剂XT-A质量浓度为1g/L时,漂白棉织物的白度为78.1%,且强力损失小.与传统漂白工艺相比较,应用环多胺金属配合物催化双氧水漂白棉织物工艺在一定程度上实现了低温低碱漂白.     

马尾松化学预热机械浆镁碱过氧化氢漂白

研究了用镁碱代替钠碱的马尾松化学预热机械浆（CTMP）浆过氧化氢漂白工艺及其对纸浆性能的影响,分析了镁碱和钠碱过氧化氢漂白废液对环境的影响.试验结果表明,马尾松CTMP浆镁碱漂白过氧化氢的最佳漂白工艺条件为：H2O2体积浓度为4%,Mg（OH）2质量浓度为1.2%,Na2SiO3质量浓度为1.5%、漂白温度为80℃、漂白时间为120 min,其白度可至63.5%（ISO）,而经钠碱漂白后纸浆的白度值为61.4%（ISO）.镁碱过氧化氢漂白废液化学耗氧量（CODcr）为193.6 g/L,比钠碱过氧化氢漂白废液化学耗氧量（CODcr=312.86 g/L）降低了38.12%.