聚酯型可降解水性聚氨酯的合成及表征

以聚己二酸乙二醇-1,4-丁二醇酯二醇（PBA ）为软段,以二羟基丙酸（DM PA ）为亲水扩链剂,合成水性聚氨酯（WPU ）预聚体,通过三元共聚硅油（S ）接枝改性制备了系列WPU 乳液。采用红外光谱（FT-IR）、水接触角、水降解性、耐水实验等对WPU 结构和性能进行表征。结果表明,聚氨酯胶膜的耐水性和水接触角随着S含量的增大而提高;胶膜水降解速率随着DM PA 含量的增加而提高。应用到羊绒织物上,使得羊绒织物的抗起毛起球性能得到改善。     

复合膜用PUA黏合剂的合成与性能

以丙烯酸酯单体为原料,水性聚氨酯为种子乳液和高分子乳化荆,合成了核-壳结构的聚氨酯-丙烯酸酯复合乳液.采用傅里叶红外光谱表征了反应产物的结构.研究丙烯酸酯与聚氨酯质量比、丙烯酸酯软硬单体质量比对复合乳液性能、胶膜耐水性、热稳定性及180°剥离强度的影响.结果表明:随丙烯酸酯与聚氨酯质量比和丙烯酸酯硬单体质量的增加,复合乳液黏度减小,粒径增大,胶膜耐水性和热稳定性提高.当丙烯酸酯与聚氨酯质量比为2.0,丙烯酸酯软单体与硬单体质量比为75/25时,聚氨酯-丙烯酸酯复合乳液黏合荆对双向拉伸聚丙烯/铝箔的粘接强度优于国外样品.     

扩链剂对水性聚氨酯乳液的影响

通过自乳化聚合引入低分子扩链剂制得具有嵌段结构的阴离子型水性聚氨酯乳液。研究了不同扩链剂及其用量对聚醚型和聚酯型聚氨酯乳液的影响。结果表明,以乙二醇为扩链剂制得的聚氨酯乳液稳定性较好,且所得的聚酯型聚氨酯涂膜的力学性能也较好,但耐水性较差。扩链剂的最佳用量为2.05%(质量分数)左右。     

环氧树脂用量对水性聚氨酯胶膜结晶性能的影响

以异佛尔酮二异氰酸酯、六亚甲基二异氰酸酯、聚己二酸1,4-丁二醇酯为主要原料,1,4-丁二醇为小分子扩链剂,乙二胺基乙磺酸钠为亲水性扩链剂,环氧树脂E-51为改性剂,合成了固含量为50%的环氧树脂改性磺酸盐型水性聚氨酯乳液,并采用FT-IR、XRD、SEM、AFM、DSC和DMA方法考察环氧树脂用量对乳胶膜结晶性能的影响.结果表明:随着环氧树脂用量的增多,XRD谱图中21.2°和24.3°处的两个尖锐的谱峰高度明显变小,SEM和AFM图中乳胶膜硬段和软段的相分离程度显著减弱,DSC曲线上可以观察到清晰的胶膜熔融峰和结晶峰,胶膜的结晶度减小,DMA曲线上改性树脂软段的玻璃化温度有朝低温方向移动的趋势,说明环氧树脂的加入降低了聚氨酯胶膜的结晶性能.     

脂肪族水性聚氨酯乳液的研究

采用内乳化法以聚酯多元醇、异佛尔酮二异氰酸酯（IPDI）和二羟甲基丙酸（DMPA）合成了水性聚氨酯乳液。研究了NCO／OH摩尔比对水性聚氨酯粒子尺寸、胶膜耐水性、乳液的电解质稳定性、胶膜的机械性能的影响。制备了稳定的水性聚氨酯乳液。     

聚酯型水性聚氨酯胶膜结晶性与耐热性的关系

以聚己二酸1,4-丁二醇酯、1,4-丁二醇、六亚甲基二异氰酸酯、异佛尔酮二异氰酸酯、N-(2-氨基乙基)-氨基乙烷磺酸钠、二羟甲基丙酸和乙二胺为主要原料,通过丙酮法合成了不同软段相对分子质量、硬段含量、硬段种类、亲水扩链剂及以液体石蜡共混改性5个系列的水性聚氨酯(WPU)乳液.采用FT-IR表征了WPU的结构和氢键化程度,采用DSC和TG表征了各系列WPU胶膜的结晶性和耐热性.结果表明,硬段含量较高、硬段较规整及添加了液体石蜡的WPU的氢键化程度较高;以较高相对分子质量的聚酯多元醇作为软段、分子结构规整的二异氰酸酯作为硬段、氨基磺酸盐作为亲水扩链剂及以液体石蜡改性所制备的WPU的结晶性较好;WPU胶膜结晶性的改善有助于提高其耐热性能.     

嵌段聚氨酯脲的形态与性能——软链段结构和分子量的影响

合成了不同软链段长度的聚醚型、聚酯型嵌段聚氨酯脲弹性体,以及聚醚-聚酯软链段聚氨酯脲弹性体(PUU)。借助SEM、DSC以及拉伸试验机分析其结构、形态对力学性能的影响。研究表明,相分离程度随软链段分子量的提高而提高。在软链段分子量相同时,聚醚为基础的PUU的相分离程度较聚酯为基础的PUU高。以聚醚-聚酯为软链段的PUU呈现了聚醚型和聚酯型PUU的各自形态,有较大的相区尺寸和较明显的相界面。力学性能数据证实了形态研究的结果。     

无皂种子乳液聚合法制备丙烯酸酯-聚氨酯共聚乳液

以水性聚氨酯为种子乳液,甲基丙烯酸丁酯和甲基丙烯甲酯为单体,采用乳液聚合法制备丙烯酸酯-聚氨酯乳液.研究了单体含量对共聚乳液性能的影响,结果表明:随着乙烯基单体含量的增加,乳液颜色加深,稳定性下降;胶膜的断裂伸长率降低,硬度和耐水性增加.当M/PU为25%,AIBN的含量为2.0%时,乳液的稳定性大于12个月,断裂伸长率为498%,硬度为0.64,吸水率可达到22.8%;红外光谱分析表明合成了丙烯酸酯聚氨酯乳液.     

聚对苯二甲酸乙二酯(PET)—聚ε-己内酯(PCL)嵌段共聚物链的化学结构

以芳族聚酯(PET)为硬链段,以脂族聚酯(PCL)为软链段的聚酯一聚酯嵌段共聚物,由于聚合反应过程中同时存在多种酯交换反应,链的化学结构变复杂了.应用核磁共振技术(氢谱和碳谱)和应用几种模型化合物的研究证明,PET—PCL嵌段共聚物软、硬链段间的联接有两种方式,软链段有两种结构形式,而硬链段的结构单元也有两种类型,从而确定了PET—PCL 嵌段共聚物链的化学结构.     

聚氨酯水分散体的性质和结构分析

研究了聚氨酯水分散体及其胶膜的性质和结构特征，测定了分散质的粒径大小及分布、涂膜材料红外光谱（ＩＲ）及热行为（ＤＳＣ）等特征．研究表明，合成体系为胶体分散状态，具有很好的稳定性，但胶膜耐水性、耐碱性有待提高；涂膜材料结构中存在着氢键行为和部分有序区域，并且聚氨酯的软、硬链段处于一定的微相分离状态．     

聚乳酸/海藻酸钠共混膜的制备及性能研究

本文以聚乳酸(PLA)和海藻酸钠(SA)为原料,采用流延成膜法制备了PLA/SA共混膜,并研究了PLA/SA共混膜的吸湿、力学性能及热学性能。结果表明:PLA与SA分子之间存在着较强的氢键作用力;SA的引入,提高了共混膜的结晶性能;共混膜的吸湿率随共混膜中SA含量的增加而增加;力学性能随SA含量的增加而减少。     

扩链剂含量对聚氨酯微孔材料性能的影响

采用聚酯多元醇、发泡剂、表面活性剂等混合而成的组合料与异氰酸酯－聚酯多元醇的预聚物,经反应注射成型,制备聚氨酯发泡材料,考察了扩链剂 EG 的添加量对聚氨酯微孔材料结构与性能的影响。研究结果表明,随着 EG的引入,经过水解,材料的力学性能影响最小;聚氨酯软硬段的最高热失重温度均呈现升高趋势,聚氨酯的耐热性有了提高。     

含氟聚氨酯的制备及性能研究

以二甲苯为溶剂,全氟聚醚二元醇和异佛尔酮二异氰酸酯（IPDI）为原料,1,4丁二醇（BDO）作为扩链剂合成了含氟聚氨酯（FPU）,通过改变软段全氟聚醚二元醇用量控制FPU的氟质量分数.并且以聚丙二醇（PPG）和异佛尔酮二异氰酸酯（IPDI）为原料,以1,4丁二醇（BDO）作为扩链剂合成了不含氟的聚氨酯（PU）作为对比.对PU与FPU的结构进行了表征,考察了氟质量分数对FPU热稳定性、力学性能以及疏水疏油性的影响.结果表明,制得的FPU具有更高的拉伸强度,同时在保持聚氨酯疏油性的同时,还获得了较好的疏水性.      

土体含盐量对长江口地区软黏土特性的影响

长江口地区广泛分布的软黏土是一种不良地质土,具有压缩性高、强度低、灵敏度高的特点.土体含盐量在不同的季节下会受河流、潮汐、降雨等因素的影响会发生波动.对长江口沿岸软黏土进行采样并测定其含盐量,然后通过对原状样进行直剪试验、侧限压缩试验、渗透试验,得到了土体含盐量对软黏土抗剪特性、压缩特性、渗透特性的影响规律.结果表明:原状软黏土含盐量在0.5％ ～1.1％时,土体含盐量越高,土体的抗剪强度越高、土体压缩性越低、渗透性越强.根据对渗滤过的原状土进行试验对比分析,黏土颗粒中的盐分、孔隙水中的盐分共同影响软黏土的特性;黏土颗粒中的盐分对软黏土特性的影响更大.最后通过压汞试验得到了含盐软黏土的孔隙分布特征.长江口沿岸地区土体冬季的力学性能较差,应该更加注重冬季工程地质灾害的防治.     

Effect of TiO<Subscript>2</Subscript> pigment gradation on the properties of thermal insulation coatings

This study was designed to evaluate the thermal performance and mechanical properties of coatings with different gradations of TiO₂ pigments. The solar reflectance, cooling performance, wash resistance, and film adhesion strength of the coatings were investigated. The influence of TiO₂ powder gradation on the final properties of the coatings was studed. The solar reflectance and the thermal insulation were observed to increase with increasing content of nanosized TiO₂. The mechanical properties of the coatings, such as their wash resistance and film adhesion strength, were observed to increase with increased incorporation of nanosized TiO₂. Such improvements in the properties of the coatings were attributed to the greater specific surface area and lower thermal conductivity of nanosized TiO₂ particles compared to normal TiO₂ particles.     

Investigation on Mechanical Properties of CMSLDS/Acrylate Copolymeric Blending Films for Warp Sizing

Carboxymethyl starch with lower degree of substitution was blended with acrylate copolymer for revealing the relation between mechanical properties and chemical structure of blending film.Effects of carboxymethylation of starch,acrylate constituent units of acrylate copolymers,and copolymer content of the film on the properties were investigated.The mechanical properties were evaluated in terms of tensile strength,breaking elongation,abrasion resistance,and flex-fatigue resistance.Film morphology was examined with X-ray diffraction (XRD),scanning electron microscopy (SEM),and atomic force microscope (AFM).It was found that the properties depended on the degree of substitution of carboxymethyl starch,chemical structure of acrylate units,and content of acrylate copolymer.Phase-separation of the two ingredients occurred within film matrix and the separation was decreased after starch carboxymethylation.Breaking elongation and flex-fatigue resistance of the film reached maximums when acrylate copolymer content was 50%.Excessively increasing the content of acrylate copolymer reduced the film properties.     

母料中弹性体含量对HDPE/E-TMB共混物力学性能及熔体流动速率的影响

用自制增韧母料(E-TMB)与高密度聚乙烯(HDPE)热机械共混制得增韧HDPE(2200J HDPE/E1-TMB和5000S HDPE/E2-TMB)共混物,研究了E-TMB中弹性体质量分数(E)对增韧HDPE力学性能及熔体流动速率(MFR)的影响.结果表明,两系列共混物熔体的MFR随母料中E的增加大体呈增大的趋势;当E为44%时,2200JHDPE/E1-TMB共混物的综合力学性能最好;当E为36%时,5000S HDPE/E2-TMB共混物的力学性能最好.     

BC/WPU功能涂膜制备及性能研究

以环保型水性聚氨酯（WPU）作成膜物,把环保、高附加值及功能化作为涂膜设计理念,以低成本竹炭（BC）作功能助剂,旨在合成宜居多功能涂膜,通过BC改性及优化配方制备了BC/WPU功能涂膜。研究了BC改性剂种类、用量和添加量、粒度及分散时间等因素对功能涂膜性能的影响。结果表明：γ-胺丙基三乙氧基硅烷（γ-APTES）改性BC/WPU功能涂膜具有优异的导电、力学性能;在γ-APTES为BC质量的2%、BC用量为20%、BC粒度为500目、分散40 min条件下,制备的涂膜体积电阻率为1.7×104Ω.cm,铅笔硬度为4H,冲击强度≥70kg.cm,耐洗刷性能≥11350次。     

丝胶蛋白膜的制备及其物理性能

以环氧树脂作为交联剂制备具有一定力学性能的丝胶蛋白膜。用X-射线衍射法研究丝胶蛋白膜的聚集态结构；对丝胶蛋白膜的热水溶失率和力学性能进行测定；并探讨了交联剂种类、比例对丝胶蛋白膜性能和结构的影响。结果表明，交联剂对丝胶蛋白膜的交联作用明显，引起了丝胶结晶形态的变化；并改善了丝胶蛋白膜的物理性能，交联剂PEGO10加入30％左右所制得的丝胶蛋白膜拉伸断裂强度和断裂伸长率较好。     

光聚合丝印胶的耐水性能

采用磨擦湿润网版的方法,研究了活性单体、成膜剂以及加热老化等因素对光聚合型丝印感光胶印版耐水性的影响,并采用坚膜剂对丝网印版进行坚膜处理。结果表明,合适的活性单体和成膜剂以及坚膜剂可以显著的提高印版的耐水性,加热老化对印版的耐水性影响不大。