Fabrication and morphology of NbCx-C composite three-dimensinal netted fibers

The raw materials were commercial powders of Nb₂O₅ (99.95%), reactive carbon (99.99%), NaCI (99.95%) and sucrose (99.94%). By the carbothermal method, the NbC_x (x= 0.98)-C composite three-dimensional netted fibers were prepared in graphite resistance furnace in 0.1 MPa/N₂ ambient atmosphere at temperature from 970 to 1 120°C. The diameters of composite three-dimensional netted fibers are 12–38 μm, the hole circumferences of netted fibers are 0.22–2.2 mm and the hole diameters are 70–701 μm. The process conditions for fabricating NbC_x-C composite three-dimensional netted fibers and related morphology, composition and crystal structure of NbC_x-C composite netted fibers were investigated in detail.     

Fabrication and formation mechanism of NbCx-C three-dimensional netted fibers

Micrometer NbCx-C three-dimensional netted fibers were synthesized by the carbothermal method under 0.1 MPa of N2 ambient atmosphere at a relatively low temperature. Raw materials were commercial powders of Nb2O5 (99.95%), reactive carbon (99.99%), NaCl (99.95%) and sucrose (99.94%). The relationship of the fabrication processing with the composition, crystal structure and morphology of fibers was investigated. The formation mechanism was also proposed and discussed.     

橡胶基复合材料中的短纤维长径比及其分布

对3种不同直径，相同表观长径比的涤纶短纤维增强4172氯丁橡胶基复合材料中的短纤维长度进行了研究，用全统计法测量了短纤维的实际长度，讨论了短纤维直径，用量及混炼工艺等因素对短纤维长度及其分布的影响，结果表明：在相同条件下，短纤维直径越小的纤维断裂速度越慢，短纤维长径比越大，随着纤维含量的增加，纤维的平均长度增加，并且没有发生断裂的纤维的含量越来越多，在相同的辊距下进行多次薄通时，不同直径的纤维最后趋向于具有相同的长径比，研究结果可为短纤维橡胶基复合材料性能的研究提供参考。     

红外AgCl单晶光纤的研制

利用直接成型法技术研制AgCl等单晶光纤, 光纤直径分别为10 μm, 150 μm和300 μm, 长度为40~105 cm. 探讨单晶光纤生长条件, 并讨论产生光纤缺陷的原因.     

地理信息系统与地形特征值的提取

以地理信息系统中栅格数据结构为基础，建立数字地形模型（DEM），然后以从地形图上读取的各栅格点的高程值为准，求算出格栅格点的地形特征值坡度、坡向，以便对所研究地区的地形概况有全面的了解，可在计算机上显示三维立体图。     

原位合成TiB_2颗粒增韧SiC的显微组织与断裂韧性

在前期对原位生成TiB2增韧SiC制备工艺研究的基础上,研究了TiB2/SiC复合陶瓷的显微组织与力学性能.研究发现:在φ(TiB2)介于5%~20%时,原位生成的TiB2相在SiC基体中的分布都比较均匀;当φ(TiB2)为5%和20%时,TiB2颗粒等面积圆直径平均值分别为2.6和3.9μm;另外,TiB2颗粒能起到明显细化SiC晶粒的作用.随着φ(TiB2)的增加,TiB2/SiC复合材料的相对密度、维氏硬度和断裂韧性均增大.当φ(TiB2)为20%时,复合材料相对密度、维氏硬度和断裂韧性分别为94.8%,29.1 GPa和5.9 MPa.m1/2.经优化工艺制备的TiB2/SiC复合陶瓷...     

碳纤维增强树脂开孔层合板轴向拉伸失效模拟分析

基于ABAQUS平台,建立了开孔复合材料层合板轴向拉伸渐进失效模型.以二维Hashin作为损伤准则,考虑了基体拉伸、压缩失效和纤维拉伸、压缩失效模式.讨论了层合板的受力与失效形式,分析了铺层角度、中心孔尺寸对极限载荷的影响.研究结果表明:失效模式主要表现为纤维拉伸失效和基体拉伸失效,纤维作为复合材料板的主要强度来源,在力与纤维方向发生偏差时,层合板力学性能急速下降;中心孔越大,层合板力学性能越差,并且层合板力学性能与中心孔尺寸成线性关系.     

组网雷达中旋转目标微多普勒效应分析及三维微动特征提取

目标微动特征提取是当前研究的一个热点,在组网雷达技术中研究了旋转目标的微多普勒效应,分别分析了组网雷达中不同信号形式下的目标微多普勒效应,并给出了其参数化表达。利用组网雷达的多视角特性,将不同信号形式下分布在不同位置的雷达获得的回波信号进行参数提取,通过构造多元非线性方程组,以提取的参数作为变量,进行目标3维微动参数解算,实现了目标3维微动特征的提取。仿真实验验证了所提算法的有效性。     

Three-dimensional interconnected cobalt oxide-carbon hollow spheres arrays as cathode materials for hybrid batteries

Hierarchical porous metal oxides arrays is critical for development of advanced energy storage devices. Herein, we report a facile template-assisted electro-deposition plus glucose decomposition method for synthesis of multilayer CoO/C hollow spheres arrays. The CoO/C arrays consist of multilayer interconnected hollow composite spheres with diameters of ～350 nm as well as thin walls of ～20 nm. Hierarchical hollow spheres architecture with 3D porous networks are achieved. As cathode of high-rate hybrid batteries, the multilayer CoO/C hollow sphere arrays exhibit impressive enhanced performances with a high capacity (73.5 mAh g?1 at 2 A g?1), and stable high-rate cycling life (70 mAh g?1 after 12,500 cycles at 2 A g?1). The improved electrochemical performance is owing to the composite hollow-sphere architecture with high contact area between the active materials and electrolyte as well as fast ion/electron transportation path.     

一维纳米SnO2/TiO2复合薄膜电极的制备及光电性能

采用静电纺丝的方法,通过调节前驱体液中SnCl₂·2H₂O的质量分数,制备了直径为90~180nm的SnO₂纳米线,经TiCl₄溶液水解处理制备得到了SnO₂/TiO₂薄膜电极。使用SEM和EDS对薄膜电极进行表征,通过线性扫描伏安法和光电催化测试,分析研究了SnO₂/TiO₂ 纳米复合薄膜电极的光电化学性质。结果表明,当SnCl₂·2H₂O质量分数为3%时,SnO₂/TiO₂ 复合薄膜电极的光电流密度达到最大;随后将其与TiO₂、SnO₂薄膜电极相比,SnO₂/TiO₂ 复合薄膜电极产生的光电流明显增大;复合薄膜电极对罗丹明B（RhB）的光电催化降解率在90min后可达到95%,而TiO₂仅为56%、SnO₂为58%。     

含预成型孔复合材料单层板的一种设计方法

基于有限元应力分析和强度准则以及纤维连续绕过孔边的约束条件,对含孔纤维增强复合材料单层板的纤维取向和密度分布进行迭代设计,结果表明：在平均纤维含量不变的条件下其拉伸强度取得较大幅度的提高。此研究结果可进一步用于含孔复合材料层合板的设计。     

泡沫浸渍法制备小梁金属及性能

采用有机泡沫浸渍法,选用预处理过的聚氨酯泡沫为模板制备具有较高强度和与人体弹性模量相匹配的小梁金属(多孔钽生物材料).通过流体静力学法、SEM、EDS等方法研究表征多孔钽材料的密度、微观结构、孔隙形貌、杂质含量等.研究结果表明:材料密度为6.06～7.02g/cm3,孔隙率为57.7％～63.5％,孔径为313～622um,制备的多孔钽具有与人体骨相似的三维、连通开孔隙形貌,材料基体上无杂质残留.力学性能结果表明:抗压强度为50～73MPa,弹性模量为1.73～2.72GPa,与人体松质骨相似.     

Superelasticity of Cu-Ni-Al shape-memory fibers prepared by melt extraction technique

In the paper, a melt extraction method was used to fabricate Cu–4Ni–14Al (wt%) fiber materials with diameters between 50 and 200 μm. The fibers exhibited superelasticity and temperature-induced martensitic transformation. The microstructures and superelasticity behavior of the fibers were studied via scanning electron microscopy (SEM) and a dynamic mechanical analyzer (DMA), respectively. Appropriate heat treatment further improves the plasticity of Cu-based alloys. The serration behavior observed during the loading process is due to the multiple martensite phase transformation.     

含填充孔复合材料层压板极限压缩强度分析与预测

基于复合材料层压板与填充螺栓之间的载荷分配情况,提出一种估算含填充孔复合材料层压板压缩极限强度的方法。利用MSC.Patran/Nastran有限元分析软件,建立考虑界面接触的有限元模型。分析了层压板刚度和螺栓刚度对载荷分配系数的影响规律,界面单元应力表明层压板与螺栓之间接触力分布为余弦函数形式。同时,开展了三种铺层T700/LT—03A碳纤维复合材料层压板开孔和填充孔极限压缩强度试验。试验结果表明,含填充孔层压板压缩强度较开孔压缩极限强度提高约30%左右。与试验结果相比,方法的预测值较为保守,且预测误差小于5%。此外,对文献中的T800/3900—2层压板试验数据进行分析,预测误差小于5%,说明该方法能较好地预测含填充孔复合材料层压板压缩极限强度,具有一定的工程应用意义。     

Cu-Fe-Cr原位复合材料和Fe-Cr纤维的磁学特性研究

采用拉拔变形法制备了Cu-Fe-Cr原位复合材料,并从线材中提取出Fe-Cr纤维。用扫描电镜观察了复合线材和纤维的微观形貌,并用VSM对复合线材和Fe-Cr纤维进行了磁性测试,绘制了磁滞回线。结果表明:复合线材具有磁各向异性,其易磁化方向平行于线材轴向;随着变形量的增大,复合线材的剩磁和矫顽力逐渐增大;Fe-Cr纤维的比饱和磁化强度Ms达到了150 emu.g-1,是一种有潜在应用价值的吸波材料。     

利用蚕丝制作的微米光器件的研究

利用Na2CO3水溶液将蚕茧去除丝胶得到直径为5～15μm的生物纤维,采用扫描电镜(SEM)和透射电镜(TEM)观察了其形貌特征。通过倏逝波耦合的方法,利用SiO2微纳光锥将波长为671 nm的红光、532 nm的绿光、473 nm的蓝光分别耦合进入微米蚕丝生物光纤,分析了其导光特性,测量了光在蚕丝纤维中的传输损耗。制作了2×2、3×1、1×4、环形等光子结构。实验证明蚕丝微米生物光纤具有良好的柔韧性和表面光滑度,其中波长为532 nm的绿光在直径为9.0μm的蚕丝纤维中传输时的损耗为0.78 dB.mm-1。     

活性碳纳米纤维对VOC的吸附性能

通过对比不同直径的活性碳纳米纤维及活性碳纤维对苯、甲苯和乙醇蒸汽的吸附等温线,研究不同直径的活性碳纳米纤维及活性碳纤维吸附挥发性有机物(VOC)气体性能的差异。经扫描电子显微镜(SEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)等测试分析,结果表明:活性碳纤维直径在10μm数量级,随直径减小,纤维晶体性变差,结构无序性增大;微孔达0.4～0.8 nm时VOC气体分子更易进入与吸附位结合;活性碳纳米纤维及活性碳纤维氮吸附-脱附曲线均为Ⅰ型。故分压比低于0.01时活性碳纳米纤维对苯、甲苯和乙醇的吸附量要高于活性碳纤维的吸附量。     

非概率可靠性的拉伸载荷下飞机含孔复合材料安全性分析

针对拉伸载荷作用下飞机含孔复合材料易发生损伤失效的问题,为研究穿透型圆孔对复合材料安全性的影响,根据某型飞机实际使用的碳纤维复合材料,设计了无孔和含孔试样进行拉伸试验,获得宏观拉伸性能参数,对比分析穿透型圆孔对拉伸性能的影响;基于非概率可靠性分析方法,采用最小无穷范数指标,分别对训练强度提高前后的拉伸强度可靠性进行计算与分析,并总结了复合材料安全性分析方法。结果表明：穿透型圆孔会导致该复合材料拉伸强度的大幅下降,而对拉伸刚度影响不大,且拉伸强度下降率与孔径成正比;穿透型圆孔会引起该复合材料拉伸强度可靠性的大幅下降,下降程度随孔径的增大而增大;训练强度提高后,可靠性进一步下降,三种孔径的复合材料拉伸强度可靠性均降至1以下,严重影响复合材料安全性。     

预处理对PAA膜制备的影响

利用两步阳极氧化法制备多孔氧化铝膜,以膜的孔直径、孔密度和膜厚等作为膜质量指标,探讨预处理膜制备的影响;利用扫描电镜,X—射线衍射观察不同条件下氧化膜的微观结构。结果表明:经过高温退火和电化学抛光等预处理,能够得到质量较高的膜,孔直径为55~60 nm,孔间距为90~95 nm,膜厚度为8.5~9μm,孔密度高达1.28×1010个/cm2。     

聚氨酯/ 羧甲基壳聚糖/壳聚糖) n 复合涂层血液相容性

在心血管支架表面构建仿生细胞外基质结构的涂层是提高支架生物相容性的有效方法.结合静电纺丝及静电自组装技术,在316L医用不锈钢基底上制备出网状聚氨酯/(羧甲基壳聚糖/壳聚糖)n复合涂层.血小板黏附实验表明,对于网状聚氨酯涂层,血小板较易黏附在直径小于1μm的纤维上,在直径大于1μm的纤维上几乎无血小板黏附;而聚氨酯/(羧甲基壳聚糖/壳聚糖)n复合涂层的血小板黏附数量明显下降,血液相容性得到改善.