喷丸对渗碳件接触疲劳及裂纹萌生扩展的影响

通过一系列试验表明,渗碳后喷丸可使接触疲劳强度提高,在低接触应力下接触疲劳寿命明显增加。对接触疲劳裂纹萌生。扩展至失效全过程所进行的连续追踪观测发现,裂纹萌生于渗碳过渡区;渗碳喷丸后比未喷丸的裂纹萌生寿命增加,扩展速率减小;由钢丸坑连接而成的浅小裂纹为非扩展裂纹;在喷丸影响区,裂纹扩展不同于未喷丸试件,即主裂纹平行于表面扩展;分叉裂纹发生再次分叉向下扩展,从而使裂纹扩展后期速率减小。     

残余应力对表面纳米化316L不锈钢疲劳性能影响

超声喷丸处理工艺在316L不锈钢表面制备出了纳米表面晶层,对表面纳米化后和未表面纳米化的316L不锈钢试样进行拉拉低周疲劳试验,然后对试件进行表面残余应力进行测试,并对表面纳米化后材料疲劳性能的影响机理进行了初步分析探讨.研究结果表明,超声喷丸表面纳米化处理可以有效使材料在表面产生残余压应力,并使得表面晶粒细化,从而有效抑制疲劳裂缝萌生,提高材料疲劳寿命.     

激光冲击、喷丸及其复合强化对TB6钛合金表面完整性及轴向疲劳性能的影响

 为了提升TB6钛合金旋翼的疲劳性能,研究了喷丸、激光冲击及两者的复合工艺等3种表面强化方法对钛合金表面完整性及高周疲劳性能的影响规律。采用白光干涉仪、X射线残余应力测试仪和扫描电子显微镜分别对加工前后试样的表面形貌、表面残余应力分布和微观组织等表面完整性特征参数进行了表征,并采用疲劳试验机分别测试了轴向应力疲劳寿命和疲劳极限。结果表明,在相同加载条件下,相比磨削试样,采用单一的激光冲击试样的轴向应力疲劳寿命提高了32.2倍,而单一的喷丸和激光冲击+喷丸复合强化的试样疲劳寿命均提高了至少126.4倍。激光冲击+喷丸复合强化表现出比单一的喷丸强化更优的疲劳极限增益效果。     

车轮钢形变断裂过程的原位研究及氢影响

在扫描电镜下对CL60车轮钢单边缺口薄试样(厚度≤0.5mm)进行了原位拉伸实验,并研究了氢的影响.在金相显微镜下观察了带预裂纹的厚度为30mm的楔形张开加载试样开裂过程.结果表明,对薄试样拉伸变形时,不论是否有氢,先共析铁素体优先发生塑性变形,微裂纹沿先共析铁素体与珠光体团的边界形核、扩展;在有氢的情况下,微裂纹更容易通过夹杂物的剥落或夹杂物与基体界面的分离而萌生;薄试样拉伸主要是韧窝断口;对厚试样,裂纹主要通过珠光体中渗碳体片层开裂而扩展,断口也因此主要呈解理特征.     

热处理对TiAl基合金喷丸试样组织与性能的影响

TiAl合金在高温下服役时,表面因受循环载荷而容易产生疲劳裂纹,因此有必要进行表面处理以改善其力学性能。使用直径0.2 mm钢丸在0.7 MPa气压下对TiAl合金进行室温喷丸实验,使用ABAQUS有限元分析软件进行喷丸仿真模拟研究。随后,对喷丸试样进行不同温度和保温时间的热处理。通过SEM观察TiAl合金纵截面的显微组织,使用X射线残余应力仪测量TiAl合金表面的残余压应力,使用显微硬度仪测量热处理后TiAl合金表面的显微硬度。结果发现,喷丸后TiAl合金表面出现许多凹坑和层片状突起,次表面处发生明显塑性变形并出现许多变形孪晶。热处理后TiAl合金表面残余压应力会随着保温时间的增加和热处理温度的升高而变小。硬度几乎表现出与残余应力相同的趋势,但当热处理温度为1 200℃时,因金相组织发生变化,α₂相含量明显增多,导致硬度增加。     

氢对铜电化学行为和NaNO2溶液应力腐蚀的影响

纯铜充氢后并不改变组织结构和晶粒大，而且抗拉强度、延伸率和面缩率也不变化，这表明铜没有氢脆，在ＮａＮＯ２溶液中，氢使纯铜的腐蚀电位、反应电阻降低，使应力腐蚀开裂敏感性升高，断口形貌不发生变化。     

喷丸强化对40#车轴钢静态拉伸及疲劳寿命的影响

通过对喷丸工艺处理后的４０＃ 车轴钢静态拉伸和疲劳寿命的测定,对试验结果进行了分析,找出了因喷丸产生的压应力距表面深度的变化曲线,通过成组的对比性试验后发现喷丸强化作用在初期效果显著,当裂纹穿过了喷丸强化层后,其强化作用就逐渐减弱直至消失。     

渗碳齿轮钢接触疲劳性能的研究

就五种国外渗碳齿轮钢和目前国内普遍使用的20CrMnTi渗碳齿轮钢,经渗碳热处理和强化喷九处理后,进行了接触疲劳快速法强度试验,以及显微硬度分布、残余应力、断口分析等较系统的试验研究。结果表明,除了SAE8620钢比20CrMnTi钢的接触疲劳强度极限低外,其它四种钢ZF_7、20MnCr5、SCM420H(脱气)、SCM420H与20CrMnTi钢相当;接触疲劳强度与其表面有效硬化层深度关系密切;喷丸处理后的试件,和冶炼时采用特殊脱气工艺(简称脱气)的钢材,其试验数据离散性小,接触疲劳强度高。     

弹簧钢60Si2Mn脱碳表面的应力分析

弹簧钢60Si2Mn在热处理过程中会发生脱碳.由于脱碳会严重影响零件的使用性能,因此可采用喷丸的方法来提高零件的使用性能,喷丸在材料表面产生的残余应力是二维的.基于此,讨论了喷丸强化对脱碳表层的影响,利用X射线应力分析技术及Mises等效应力法,可测得弹簧钢60Si2Mn脱碳表层在喷丸前后的屈服强度.实验结果表明,喷丸试样的表面屈服强度比未喷丸试样的表面屈服强度有了很大的提高,这说明了喷丸可以改善脱碳零件的性能.     

压裂泵阀箱钢43CrNi2MoV疲劳断裂的试验研究

本文介绍了1050型压裂泵阀箱钢—43CrNi2MoV的疲劳断裂试验研究。一系列的实验表明,回火温度影响着钢的疲劳断裂强度,在约620℃回火时,可以获得高的疲劳断裂抗力;表面淬火后再喷丸硬化和表面爆炸强化可以明显提高钢的疲劳寿命;25%的盐酸溶液使钢的裂纹形成和扩展加快。     

经喷丸处理后40~#车轴钢裂纹的萌生及其沿表面扩展规律

以４０＃车轴钢为试验材料，选择了两种不同的喷丸强度对试件施喷。经试验后找到了裂纹萌生与应力的关系曲线，同时给出了经喷丸处理后基体沿表面方向的裂纹扩展速率表达式。认为喷丸能提高金属材料疲劳寿命的原因主要体现在因喷丸产生的残余压应力和结构强化两方面，在低应力区前者起主要作用，而在高应力区后者起主要作用。     

Q&P1180高强钢激光焊接头的抗氢脆性能研究

采用激光焊技术对汽车用Q&P1180高强钢进行焊接试验,分析焊接工艺参数对激光焊接头组织演变和性能的影响。选择综合力学性能较好的试样进行低应变速率拉伸试验,研究激光焊接头不同区域的微观组织对Q&P1180高强钢氢脆敏感性的影响。结果表明,当激光功率为2.5～3.5 kW、焊接速度为4.0 m/min(或激光功率为3.0 kW,焊接速度为3.6～4.2 m/min)时,Q&P1180高强钢激光焊获得了全焊透及表面成形良好的接头。不同激光功率和不同焊接速度下,焊缝区和热影响区的硬度均高于母材区的,且在焊缝的两边都存在一个软化区。在激光功率为3.0 kW、焊接速度为4.0 m/min时,激光焊接头的综合性能最佳。在预充氢的慢应变速率拉伸试验中,随着充氢电流密度的增大或充氢时间的延长,其抗拉强度和塑性逐渐下降。其中,当充氢电流密度为2 mA/cm²、充氢时间为5 min时,氢脆敏感性因子为78.0%,具有较高的氢脆敏感性。     

水附着状态下奥贝球铁断裂韧性的脆化行为

研究了水附着状态下奥贝球铁(ADI)断裂韧性的脆化行为．研究结果表明，干燥状态下ADI具有较高的断裂韧性，但水附着状态下ADI的弹塑性断裂韧性JIc降至干燥状态下的20％以下，发生显著的脆化行为；断裂韧性的脆化与试样水浸泡履历无关，长时间(480h)水浸泡试样经再干燥后，其断裂韧性恢复到原有水平．裂纹尖端附着的水在ADI基体塑性变形时分解放出氢，氢扩散至试样的内部使ADI基体中的应力诱变马氏体发生氢脆，导致了ADI断裂韧性的脆化．     

涉氢环境中连续/间断腐蚀对X80钢力学性能的影响

This study investigated the susceptibility of X80 pipeline steel to hydrogen embrittlement given different hydrogen pre-charging times and hydrogen charging–releasing–recharging cycles in H₂S environment. The fracture strain of the steel samples decreased with increasing hydrogen pre-charging time; this steel degradation could almost be recovered after diffusible hydrogen was removed when the hydrogen pre-charging time was<8 d. However, unrecoverable degeneration occurred when the hydrogen pre-charging time extended to 16–30 d. Moreover, nanovoid formation meant that the hydrogen damage to the steel under intermittent hydrogen pre-charging–releasing–recharging conditions was more serious than that under continuous hydrogen pre-charging conditions. This study illustrated that the mechanical degradation of steel is inevitable in an H₂S environment even if diffusible hydrogen is removed or visible hydrogen-induced cracking is neglected. Furthermore, the steel samples showed premature fractures and exhibited a hydrogen fatigue effect because the repeated entry and release of diffusible hydrogen promoted the formation of vacancies that aggregated into nanovoids. Our results provide valuable information on the mechanical degradation of steel in an H₂S environment, regarding the change rules of steel mechanical properties under different hydrogen pre-charging times and hydrogen charging–releasing–recharging cycles.     

Hydrogen-induced cracking behaviors of Incoloy alloy 825

The effect of hydrogen on the fracture behaviors of Incoloy alloy 825 was investigated by means of slow strain rate testing (SSRT). Hydrogen was introduced into the sample by electrochemical charging. The results show that surface microcracks form gradually during aging at room temperature when desorption of hydrogen takes place after hydrogen charging at a current density of 5 mA/cm2 for 24 h. SSRT shows that the increase of ductility loss is significantly obvious as the hydrogen charging current density increases. Scanning electron microscopy (SEM) images reveal ductile fracture in the pre-charged sample with low current densities, while the fracture includes small quasi-cleavage regions and tends to be brittle fracture as the hydrogen charging current density increases to 5 mA/cm2.     

缺口对转向架用SMA490BW钢的疲劳性能的影响

基于高速列车转向架在运行进程中常因承受各种交变载荷而导致疲劳断裂问题,针对CRH2高速列车转向架用SMA490BW钢试样进行拉伸试验,确保SMA490BW钢的力学性能符合标准要求下,对此种钢进行疲劳性能研究并通过扫描电镜进行断口分析。结果表明：与光滑试件(kt = 1)相比缺口试件(kt = 3),疲劳极限应力减小了61％,S-N曲线左侧的斜率更大;其缺口敏感系数为0.786;光滑试样的裂纹源为角部裂纹,缺口试样的裂纹源为表面裂纹。     

EHL下矿场用重载齿轮的喷丸及疲劳性能分析

弹流润滑（ＥＨＬ）条件下,石油矿场用大模数重载齿轮的承载能力得到提高,齿面接触疲劳失效与齿根弯曲疲劳断裂则成为其主要的失效形式．喷丸强化是改善齿轮表层种种缺陷的有效而简便的方法,喷丸产生的硬化层残余压应力场和显微组织相变是提高齿轮接触疲劳强度的重要因素．从单齿弯曲疲劳,齿面接触疲劳,接触疲劳裂纹萌生与扩展,表层显微硬度,残余奥氏体情况,表层残余应力及亚组织结构等方面讨论了喷丸对齿轮接触疲劳性能的影响．     

ZCE36Z35钢腐蚀疲劳的研究

本文对ZCE36Z35钢在3.5%Nacl 和10%NH_4NO_3水溶液中的疲劳裂纹扩展速率(FCGR)及外加极化电位的影响进行了实验研究,结合应力腐蚀(SCC)实验,作者认为,除非在阴极极化条件下出现强烈充氢情况,该钢在中性水溶液中的麦劳裂纹扩展主要受氧去极化作用(ODR)控制而不是氢脆(HE)机制.     

电火花加工表面喷丸残余应力场的有限元分析

喷丸强化作为表面改性技术,对增强工件实际应用,提高使用寿命具有重要意义.采用ABAQUS有限元软件,对电火花单脉冲放电和喷丸强化,在GH3039高温合金材料表层产生的残余应力场进行有限元分析,获得残余应力场的分布规律及残余应力沿层深方向上的变化规律,对电火花单脉冲放电一个脉冲周期后和喷丸强化后工件表面应力分布进行仿真分析.结果表明：电火花加工表面喷丸强化后的残余应力分布规律与理想表面喷丸相同,经喷丸强化后,工件表面残余拉应力明显降低,表层残余压应力有大幅提升,强化效果显著,表面对称轴处径向残余应力比喷丸前降低79.406％,最大径向残余压应力比喷丸前提高了339.143％.     

氢对镍基合金Inconel Alloy600力学性能的影响

通过建立一套电化学充氢和可扩散氢含量测量装置,对镍基合金Inconel Alloy 600(600合金)板试样充氢后进行常温拉伸试验,研究了600合金在充氢前后力学性能的变化及其与氢含量的关系.结果表明:材料在充氢后塑性有一定的减损,且减损的程度随着平均氢浓度的增加而增加,当充入试样中的平均氢质量分数大于10×10-6时,相对断面收缩率达到10％以上,达到氢损伤范畴.此外氢进入600合金还使材料的屈服强度、抗拉强度和弹性模量也降低.扫描电镜(SEM)测试表明:充氢前后试样断口的表层由韧性断裂变为由氢导致的沿晶脆性断裂.