Effect of Ag addition on the thermal stability and glass-forming ability of Zr<Subscript>35</Subscript>Ti<Subscript>30</Subscript>Cu<Subscript>7.5</Subscript>Be<Subscript>27.5</Subscript> bulk metallic glass

The thermal stability and glass forming ability (GFA) of Zr35-xTi30Cu7.5Be27.5Agx (x = 0-10) alloys were studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and ultrasonic techniques. We found that the addition of 1 at.% Ag can considerably enhance the GFA as indicated by an increase in the critical glass dimension from 15 mm in the Zr35Ti30Cu7.5Be27.5 alloy to 20 mm in the Zr34Ti30Cu7.5Be27.5Ag1 alloy. However, with the addition of more Ag the supercooled liquid region (△Tx) and y parameter (defined as Tx/(Tg+Tl)) drastically decreased from 155 K and 0.436 to 76 K and 0.363, respectively, resulting in a decrease in the GFA. Additionally, the elastic constant (the ratio of shear modulus to bulk modulus or Poisson’s ratio) was also used as a gauge to evaluate the GFA in Zr35-xTi30Cu7.5Be27.5Agx alloys.     

Work toughening effect in Zr_（41）Ti_（14）Cu_（12.5）Ni_（10）Be_（22.5） bulk metallic glass

Work hardening is a well-known phenomenon occurring in crystalline metals during deformation,which has been widely used to increase the strength of metals although their ductility is usually reduced simultaneously. Here we report that the plastic strain of Zr41Ti14Cu12.5Ni10Be22.5 (at.%) bulk metallic glasses has been increased from 0.3% for the as-cast sample to 2.5%-8.0% for samples that have experienced pre-deformation under constrained conditions. The pre-deformed glassy alloys possess more free volume and abundant introduced shear bands,which are believed to promote the activation of shear bands in post-deformation and result in an increase in plasticity. The orientation of the pre-introduced shear bands relative to the loading direction will affect the deformation behavior of pre-deformed samples. The present results show that pre-deformation of this glassy alloy will result in work toughening. This work toughening effect can be removed by isothermal annealing at a sub-Tg (glass transition) temperature,which causes annihilation of free volume and healing of shear bands.     

<Emphasis Type="Italic">In situ</Emphasis> synthesis of TiC reinforced Cu<Subscript>47</Subscript>Ti<Subscript>34</Subscript>Zr<Subscript>11</Subscript>Ni<Subscript>8</Subscript> bulk metallic glass composites

In situ synthesized TiC particles and β-Ti dendrites reinforced Cu47Ti34Zr11Ni8 bulk metallic glass (BMG) composite ingots were prepared by the suction casting method.The ingots with diameters from 1 up to 4mm were successfully obtained. It was shown that introducing TiC micro-sized particles into the amorphous matrix did not disturb the glass forming ability (GFA) of the matrix,while the yield strength and ductility could be well improved.The phase constitution, microstructure and elements distribution in the composites were studied by OM, XRD, SEM and EDS.It was shown that the in situ synthesized TiC particles acting as heterogeneous nucleation sites promoted the precipitation of β-Ti dendrites, resulting in the formation of the TiC particles and β-Ti dendrites co-reinforced BMG composites. The compressive tests were employed to probe the yield strength and ductility of BMG composites.     

Super-plasticity of Zr<Subscript>64.80</Subscript>Cu<Subscript>14.85</Subscript>Ni<Subscript>10.35</Subscript>Al<Subscript>10</Subscript> bulk metallic glass at room temperature

Generally, bulk metallic glasses （BMGs） exhibit a very limited plastic deformation under a compression load at room temperature, often less than 2% before fracturing. In this letter, through an appropriate choice of BMGs＇ composition, an amorphous rod of Zr64.80Cu14.85Ni10.35Al10 with a diameter of 2 mm was prepared by using copper mold suction casting. X-ray diffraction and differential scanning calorimetry were utilized to determine its structure and thermal stability, and the uniaxial compression test was adopted to study its plastic deformation behavior at room temperature simultaneously. The results showed that the glass transition temperature and onset temperature of the exothermic reaction of the amorphous rod were 646 and 750 K, respectively, and its micro-hardness was 594.7 Hv. During compression, when the engineering strain and engineering stress arrived at 9.05% and 1732 MPa, respectively, i.e., the true strain and true stress reached 9.42% and 1560 MPa, respectively, the amorphous rod started to yield. After yielding, with the increase of load, the strain increased and the glass rod ulti- mately were compressed into flake-like form. Although the maximum engineering strain was larger than 70%, i.e., the maximum true strain exceeded by 120%, the amorphous specimen was not fractured, indicating that it has super-plasticity at room temperature. Through the appropriate choice of composition and optimization of the technological process, flexible BMG with super-plasticity at room temperature could be produced.     

Rolling-induced microstructure change in Zr_（65）Al_（7.5）Ni_（10）Cu_（12.5）Ag_5 bulk metallic glass

The microstructures and free-volume evolutions of as-cast and pre-annealed Zr65Al7.5Ni10Cu12.5Ag5 bulk metallic glasses during rolling deformation have been investigated. No phase transformation is detected in the as-cast/rolled specimen. However,the structural stability of the glass against plastic deformation is worse after pre-annealing,indicated by nanocrystallization in preannealed/rolled specimens with large deformation degrees. Moreover,with increasing deformation degree,the free-volume content in a pre-annealed/rolled specimen increases at a lower average rate than that in an as-cast/rolled specimen.     

Preparation of Al<Subscript>72</Subscript>Ni<Subscript>8</Subscript>Ti<Subscript>8</Subscript>Zr<Subscript>6</Subscript>Nb<Subscript>3</Subscript>Y<Subscript>3</Subscript> amorphous powders and bulk materials

Amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were successfully fabricated by mechanical alloying. The microstructure, glass-forming ability, and crystallization behavior of amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), and differential scanning calorimetry (DSC). The isothermal crystallization kinetics was analyzed by the Johnson–Mehl–Avrami equation. In the results, the supercooled liquid region of the amorphous alloy is as high as 81 K, as determined by non-isothermal DSC curves. The activation energy for crystallization is as high as 312.6 kJ·mol?1 obtained by Kissinger and Ozawa analyses. The values of Avrami exponent (n) imply that the crystallization is dominated by interface-controlled three-dimensional growth in the early stage and the end stage and by diffusion-controlled two- or three-dimensional growth in the middle stage. In addition, the amorphous Al₇₂Ni₈Ti₈Zr₆Nb₃Y₃ powders were sintered under 2 GPa at temperatures of 673 K and 723 K. The results show that the Vickers hardness of the compacted powders is as high as Hv 1215.     

Correlation of mechanical properties in bulk metallic glasses with ~（27）Al NMR characteristics

We report 27Al NMR and magnetic susceptibility measurements of Zr and ZrHf-based bulk metallic glasses (BMGs). 27Al NMR Knight shift shows that there exists a clear correlation between the local electronic properties at Al sites and mechanical properties. In addition,magnetic susceptibility measurements also provide clues on the influence of the electronic states,especially the strong influence of d-orbital characteristics on the mechanical properties of toughness and hardness.     

Effect of TRT process on GFA, mechanical properties and microstructure of Zr-based bulk metallic glass

The effect of yttrium addition on the glass-forming ability(GFA) and mechanical properties of the Zr-based (Zr_(0.525)Al_(0.1)Ti_(0.05)Cu_(0.179)Ni_(0.146))_(100-x)Y_x and(Zr_(0.55)Al_(0.15)Ni_(0.1)Cu_(0.2))_(100-x)Y_x(x=0,0.2,0.4 0.6,1,2) alloys was studied.Micro-alloying of 0.6%yttrium enhances the room temperature ductility as well as the GFA of the Zr-based alloys.The mechanism of enhancing the GFA and room temperature ductility was analyzed.It is indicated that proper yttrium addition stabilizes the...     

Zr_(55)Al_(10)Ni_5Cu_(30)大块金属玻璃的晶化行为研究

分别在603 K、653 K、683 K、723 K、753 K、793 K和0.5 h、1 h、2 h、3 h、5 h的保温时间下对Zr55Al10Ni5Cu30大块金属玻璃进行了退火热处理.采用x射线衍射(XRD)法分析了退火后Zr55Al10Ni5Cu30大块金属玻璃的弛豫和晶化相析出的过程,计算了不同温度下结晶度和纳米晶粒尺寸的大小.通过差示扫描量热(DSC)法分析了Zr55Al10Ni5Cu30大块金属玻璃的热稳定性.Kjssinger曲线分析表明,Zr55Al10Ni5Cu30大块金属玻璃弛豫后晶化激活能高于其淬态的晶化激活能,退火温度对大块金属玻璃热稳定性有显著影响.     

Effect of different deformation and annealing procedures on non-magnetic textured Cu<Subscript>60</Subscript>Ni<Subscript>40</Subscript> alloy substrates

In this work, a series of specimens was prepared by the casting method. Sharp cube-textured substrates were processed by heavy cold rolling and recrystallization annealing (i.e., the rolling-assisted biaxially textured substrates (RABiTS) method). Both the rolling and the recrystallization texture in the alloy tapes were investigated by X-ray diffraction and electron back-scatter diffraction, respectively. The results showed that a strong copper-type deformation texture was obtained in the heavy cold-rolled substrate. In addition, the recrystallization annealing process was found to be very important for the texture transition in the Cu–Ni alloy substrates. The cube texture content in the Cu₆₀Ni₄₀ alloy substrates reached 99.7% (≤10°) after optimization of the cold-rolling procedure and the recrystallizing heat-treatment process, whereas the content of low-angle grain boundaries (from 2° to 10° misorientation) in the substrate reached 95.1%.     

深冷处理对Cu40Zr44Ag8Al8非晶复合材料组织和力学性能的影响

研究了深冷处理对Cu40Zr44Ag8Al8非晶复合材料组织演变和力学性能的影响.运用光学金相、X射线衍射分析（XRD）、差示扫描量热分析（DSC）和显微硬度等实验手段,对Cu40Zr44Ag8Al8非晶复合材料深冷处理前后的非晶结构和晶化相进行测试分析.结果表明：深冷处理2h,Cu40Zr44Ag8Al8非晶复合材料的第二相体积份数增多.随着深冷处理时间增加到24h,第二相的体积份数和尺寸进一步增多,同时非晶复合材料的显微硬度也有一定的提高.XRD分析表明Cu40Zr44Ag8Al8非晶复合材料中形成了Cu10Zr7相和AgZr相.非晶复合材料非晶基体的玻璃转变温度Tg随着深冷处理时间的增加而提高,晶化潜热则随着深冷时间的增加而降低.Cu40Zr44Ag8Al8非晶复合材料组织结构的演变与深冷处理过程产生的内应力有关.     

Nb元素对Cu48Zr48Al4合金组织与性能的影响

以高纯铜锆金属母材为原料,采用铜模滴注的方法制备Cu Zr基非晶合金及其复合材料,并进行拉伸实验。利用扫描电镜、X射线衍射仪和扫描量热分析仪对Cu48Zr48Al4和Cu44.8Zr48Al4Nb3.2合金进行结构表征和拉伸性能分析。结果表明:Nb元素微量添加能够改变Cu48Zr48Al4合金的组织形貌。Cu48Zr48Al4合金为非晶复合材料,抗拉强度较小、塑性微弱,断口呈现树枝脉络;Cu44.8Zr48Al4Nb3.2为非晶合金,具有较大的抗拉强度,没有塑性,断口为单一的塑坑形貌;两种合金断口表面均存在熔化现象,样品侧表面形成较少的剪切带。该研究为实际生产Cu Zr Al Nb非晶复合材料提供了基础数据。     

Effect of Co on the martensitic transformation,crystal structure and magnetization of Ni<Subscript>52.5</Subscript>Mn<Subscript>23.5</Subscript>Ga<Subscript>24</Subscript> based ferromagnetic shape memory alloys

Five(Ni52.5Mn23.5Ga24)100-xCox(x = 0,2,4,6,8) alloys were prepared by arc melting,and the effects of Co addition on the martensitic phase transformation,crystal structure and magnetization were investigated.The phase transformation temperatures Ms,Mf,As and Af are proportional to the content of Co in the(Ni52.5Mn23.5Ga24)100-xCox alloys,which appears to be due to the variation in the valance electron concentration.The Curie temperature is sensitive to the composition of the alloy.As the amount of Co changes,both the Co-Mn exchange interaction and the distance between Mn atoms change.These,in turn,affect the Curie temperature and magnetization behavior of the alloy.The martensite phases in all the alloys are domained in three different orientations,the domain boundary was determined to belong to the family of {112} lattice planes.