Comparison between the Direct Dyeing Kinetics of Bamboo and Conventional Viscose Fibers

Two direct dyes were applied to conventional viscose(CV)and bamboo viscose(BV)fibers,which were prepared from bamboo cellulose pulps,and the dyeing kinetics of two fibers were compared.Three kinetic equations,namely Chrastil,Cegarra-Puente,and Vickerstaff,were used to fit the experimental dyeing rate points,showing that the best result was obtained by the Chrastil equation.BV fibers displayed slightly higher dyeing rates and dye adsorption values at initial stages,but a bit lower dye adsorption values at eq...     

Preparation and the Pore Structure of Viscose - based Activated Carbon Fibers Treated with Pretreatment Reagents

The viscose rayon was pretreated with four different pre-treatment reagents respectively, and the preparation ofactivated carbon fibers (ACF) was performed undersame carbonizing and activating conditions. The poresize distribution, the specific surface area, and the porestructure parameter of these viscose - based ACF werestudied by using quartz spring balance BET- weightmethod. The experiment result indicates that the poresize distribution and the pore structure parameter ofACF is varied by using different pretreatment reagents.     

用辐射处理浆粕制造粘胶纤维的研究

主要研究用高能辐射处理浆粕前后材料性能的变化：纤维素聚合度（ＤＰ）随着辐射剂量的增加而减小；辐射对浆粕的主要成份α－纤维素和半纤维素含量影响很小；在氢氧化钠溶液中，处理后浆粕材料吸收碱量增加且膨胀度变大，并从辐射引起纤维素结晶度降低角度解释了导致这种变化的原因，也讨论了经辐射处理的浆粕为原材料给粘胶纤维工业和环境带来的好处。     

中空粘胶纤维的发展与前景

综述了中空粘胶纤维的发展、制造、工艺、性能、应用和经济效益关键词：中空纤维；粘胶纤维；纤维性能     

聚乙烯醇纤维和维尼纶纤维增强水泥石的研究

以聚乙烯醇纤维和维尼纶纤维为增强纤维，研究了水化时间、养护方式和纤维对水泥石力学性能的影响。发现：随着水化时间的延长，水泥石力学性能提高；养护方式影响素水泥石的力学性能，但较小影响纤维增强水泥石的力学性能；少量纤维加入到水泥基体中，能有效提高水泥石的力学性能；较高强度模量的聚乙烯醇纤维的增强增韧效果优于较低强度模量的维尼纶纤维。     

丙烯酸改性黏胶纤维及其吸水性研究

为提高黏胶纤维的吸水性,以硝酸铈铵(CAN)硝酸溶液为引发剂、丙烯酸(AA)为亲水单体、去离子水为溶剂,采用自由基聚合法进行黏胶纤维的接枝共聚反应。利用红外光谱仪(FT-IR)、X射线光电子能谱仪(XPS)、扫描电子显微镜(SEM)和X射线衍射仪(XRD)等对接枝黏胶纤维的结构进行研究,同时探讨了接枝共聚反应条件对改性黏胶纤维接枝率和吸水性能的影响。结果表明,黏胶纤维表面成功接枝上聚丙烯酸,且当硝酸铈铵、硝酸、丙烯酸的质量分数分别为10%、1.0%、2.0%,反应温度为60℃时,改性黏胶纤维的接枝率和吸水倍率达到最大值。     

档案修裱胶粘剂的研究

通过对档案修裱胶粘剂－－淀粉浆糊的性能、制作技术及胶粘剂与纸张结合机理的研究,探讨了小麦淀粉浆糊作为档案修裱胶粘剂的合理性和科学性。文中还分析了使用市售胶粘剂修初档案的危害性。     

新型高科技纤维研究进展

借助高技术、新工艺研制生产的各种纤维统称为高科技纤维,包括具有高强、高模、耐高温的高性能纤维,具有良好服用性能的超真纤维、高感性纤维,以及具有特殊功能的高功能纤维.通过讨论高科技纤维的研究现状和进展,明确了纺织工业发展的方向,指出提高纤维产品的附加值是纺织企业增强竞争力的核心所在.只有依靠高科技才能推动传统纤维的更新换代和产业升级,才能使我国的纤维产业在激烈的国际竞争中占据一席之地,为我国创造出更大的社会、经济效益.     

高梁叶中的多核纤维和分隔纤维

高粱(Sorghum vulgares Pers.)叶中的纤维在发育过程中出现多个细胞核现象,细胞核的数目1～7个,一般为1～3个。这种多核纤维的细胞核形状也不同,有圆球形、纺锤形和伸长的线形。纤维中出现的多核现象是由于纤维在早期发育过程中连续进行核分裂形成的,或者是发育的分隔纤维在形成横隔前出现短暂的多核时期。除这种多核纤维外,高粱叶中还青许多具有生活原生质体的分隔纤维。     

粘胶长丝连续式纺丝机的设计分析

论述了粘胶长丝连续式纺丝机必须满足的设计要求，介绍了纺丝、后处理和卷绕等部件的基本型式，并对它们的结构特点进行了对比分析，为我国自行研制拥有自主知识产权的连续式纺丝机提供了理论基础。     

醋酸纤维的改性研究

醋酸长丝是优良的纺织原料，既有纤维素纤维的服用舒适性，也有合成纤维的尺寸稳定性。在美国、日本等发达国家，目前醋酸纤维在纺织领域的应用和发展已比较成熟。综述了醋酸纤维的改性研究现状，重点讨论了差别化醋酸纤维的开发和改善醋酸纤维强力的研究。认为国内有必要对醋酸纤维的结构、特性进行研究，加深对该纤维的认识和理解，并在此基础上开发、推广醋酸纤维在我国纺织领域的应用，从而解决该纤维长期进口的问题。     

羊毛纤维和黏胶长丝玻璃化转变的测试和应用

利用动态力学分析的温度扫描和湿度扫描试验测试了羊毛纤维和黏胶长丝的玻璃化转变,两种纤维在温度扫描试验中并没有表现出玻璃化转变行为,而在湿度扫描试验中存在玻璃化转变特有的特征.通过比较不同温度下的转变行为,初步探索了湿度及染色对黏胶长丝玻璃化转变的影响.     

不同活化工艺制得粘胶基ACF的吸附性研究

将粘胶丝用前处理剂进行预处理后,在相同的碳化条件下,通过不同的活化时间及活化温度来制备活性碳纤维(Activated Carbon Fibers).采用石英弹簧秤BET法测出不同预处理条件下制备粘胶基ACF各自相应的甲醇吸附等温线和比表面积,并通过不同样品对苯酚、亚甲基兰和碘的吸附量的测定,对不同活化条件下所制备的粘胶基ACF吸附性能进行了初步的探讨.     

Researches on Mechanism of Treatment Technology of Wastewater from Viscose Fibre Production

This paper centres on the mechanism of wastewater treatment technology for viscose fibre production, in-volving the removal of sulphide (S2-), zinc(Zn2+), and organic substances( CODer), and meanwhile, de-termines the optimal strategy for wastewater treatment of Shanghai No. 1 Chemical Fibre Factory. Hydrosul-phuric acid is a weak acid, and in a certain range of pH value(pH < 8 .18) the concentration of free S2- is below 1 mg/1. The H2S gas can be removed by intro-ducing compressed air. Actually, when pH < 3, the concentration of sulphide in wastewater can meet the discharge standard. As to zinc (Zn2+), owing to its amphiprotic nature, it can be precipitated completely while pH value is within 8.24-10.5 . With the com-bined method of oxidation and coagulation, the average removal of CODer reaches 81.37% , and the concentra-tion of CODer In the effluent is about 50mg/1 under the best conditions: both the concentrations of oxidant and coagulant are about 60 ppm and the pH is 7 .     

沥青基石墨纤维中的夹杂物

用透射电子显微镜观察各向同性沥青基石墨纤维中的夹杂物,大多数夹杂物呈鞋形、椭圆形、圆形或纺锤形。所观察到的夹杂物部具有明显的层状结构。而这种结构是由夹杂物内部的片状石墨晶体平行堆叠形成的。这些片状石墨在取向上都与纤维轴相垂直。在夹杂物内部还发现了垂直于纤维轴的裂纹。     

圆柱形纤维的色散

以产生虹现象小水珠的色散原理为基础，分析了透明圆形截面纤维在平行光照条件下，一次内表面反射光中笛卡尔线的色散机理与特征；证明了透明圆形截面纤维与水珠在产生虹现象时的色散机理与特征是相似的；揭示了透明圆形纤维内部反射光的特征．研究结果对纤维光泽感的研究和特殊光泽纤维的开发，有一定的借鉴与指导意义．     

粘胶纤维生产中回收芒硝的综合利用

对某黏胶纤维生产企业的废水进行分析及综合处理,从而开发出各种废气处理技术,以期以较低的设备投资,较少的原辅材料投入和运行成本,清除废水中的有害物质,使之变成可以重复利用的原料己经提到了黏胶纤维工厂的紧迫日程.通过工艺比较,最后得到最佳方案为从废水中回收芒硝,再用芒硝制备烧碱.国内外已有这个方向的研究,理论上和实验所改进的工艺设施都是可行的,操作简单、运行可靠、自动化程度高,且等于企业大范围治理、生产.实验在芒硝制烧碱过程中的关键是加入了碳酸氢钠,大大提高了烧碱的转化率.     

光纤的极化色散

由于应力的各向异性和纤芯的非理想圆将会引起极化色散。本文从介电常数微扰理论得到极化色散与波长的关系。     

活性炭纤维的性能及应用

介绍了近年来引起广泛关注的新型高性能吸附材料一活性炭纤维的性能及其在气体净化、污水处理等领域的应用现状和发展前景．     

聚苯胺涂层导电纤维的研制

采用化学氧化聚合方法,在气相中将nylon6纤维表面合成一层导电高分子-聚笨胺。盐酸作质子酸掺杂剂,得到纤维的电导率高达10～-1S/cm数量级。用傅立叶红外光谱仪测试方法分析了不同反应条件得到的聚苯胺结构的不同,显微摄影法确认了导电纤维是皮芯层结构。