Effect of Added Poly （vinyl pyrrolidone） during Condensation on Properties of Poly（p-phenylene terephthalamide）Pulp

Poly (p-phenylene terephthalamide) (PPTA) pulp was prepared by polycondensation of the p-phenylene diamine (PPDA) with terephthaloyl chloride (TPC) in the completely anhydrous solvent system of N-methyl pyrrolidone (NMP) having calcium chloride, in the presence of poly (vinyl pyrrolidone) (PVP) having a viscosity average molecular weight lower than 40 000. It was confirmed that the polycondensation could be accelerated, the inherent viscosity of the polymer could be increased, and the polymers could be fibrillated more easily by the addition of the PVP. FTIR and X-ray spectra proved that PVP had not combined into molecular chains of the resultant PPTA pulps. The morphology of the resultant pulps, the effect of viscosity average molecular weight, amount and adding mode of PVP on inherent viscosity, specific surface area,and mean length of the resultant pulps were discussed in detail. And the friction and wear properties of the compound reinforced by the resultant pulps were simply investigated.     

溶解对PPTA结构性能的影响

采用性能相同的聚对苯二甲酰对苯二胺(PPTA)原料在双螺杆中进行溶解实验,通过红外和热失重测试分析测定溶解过程对PPTA结构以及热性能的影响.分析溶解时间、温度、溶液质量分数、硫酸质量分数、双螺杆转速等溶解条件对PPTA的比浓对数黏度ηinh、相对分子质量的影响.实验结果表明,整个溶解过程中的各种影响因素对PPTA的比浓对数黏度均有负面影响,PPTA会发生部分的降解.     

热处理对Lyocell纤维结构和性能的影响

研究了热处理时不同的温度、时间及张力对Lyocell纤维结构和性能的影响。结果表明热处理能提高Lyocell纤维的强度和模量，但是断裂伸长率有所下降。热处理温度为160℃，时间为12～25s时效果较好。热处理中施加张力可以进一步提高Lyocell纤维的强度和模量，但纤维的断裂伸长率迅速下降。热处理后的Lyocell纤维结晶度略有提高，但随着张力的增加，结晶度基本不变。热处理后纤维的总取向增大，而晶区取向基本不变，故无定形区取向大幅度提高。研究结果还表明Lyocell纤维通过热处理而提高的力学性能并不能长久地维持，随着放置时间的延长，其力学性能会逐渐下降并回复到热处理以前的状态。     

剪切速率对直接法制备芳纶浆粕缩聚反应影响的研究

研究了剪切速率对低温溶液直接缩聚法制备聚对苯二甲酰对苯二胺浆粕(芳纶浆粕，PPTAPulp)缩聚反应过程的影响。利用PPTA刚性分子发生逐步缩聚反应的缩聚模型，解释了在缩聚反应过程中，分子链的取向是提高PPTA相对分子质量的必要条件。实验结果表明，提高剪切速率有利于PPTA分子沿流动方向取向，从而提高缩聚反应速率以及芳纶浆粕的相对分子质量，同时还有利于提高浆粕的长径比(L／D)。     

聚对苯二甲酰对苯二胺三元共聚物溶液的流变性

将对苯二胺、对苯二甲酰氯及4,4'-二氨基二苯醚(ODA)在极性有机溶剂体系中进行低温缩聚,得到了聚对苯二甲酰对苯二胺(PPTA)三元共聚物溶液.研究了溶液中共聚物质量分数、温度、CaCl<,2>质量分数、共聚物的比浓对数黏度和ODA的摩尔分数对PPTA三元共聚物溶液的非牛顿指数、黏流活化能、结构黏度指数等重要参数的影响,为纺丝工艺的制定提供重要依据.     

聚苯撑苯并二噁唑(PBO)的合成

分别由对苯二甲酸（TPA）、对苯二甲酰氯（TPC）和4，6－二氨基间苯二酚盐酸盐（DAR）聚合得到了[η]＝15.2、10.4dL/g的PBO聚合物，对聚合物进行了红外光谱及元素分析，用透射电镜观察了聚合物膜的形态，同时比较了两种聚合体系对聚合反应的影响。     

聚氯乙烯/蒙脱土纳米复合材料的结构与力学性能

选用钠基蒙脱土和2种烷基季铵盐(十八烷基季铵盐和双十八烷基季铵盐)改性的蒙脱土，采用熔融共混的方法制备聚氯乙烯／蒙脱土纳米复合材料，并通过广角X射线衍射和透射电镜对复合材料的结构进行了表征．研究了蒙脱土种类和用量对复合材料力学性能的影响．结果表明，3种复合材料均具有插层型结构，钠基蒙脱土用量在ω＝0．5％-7．0％，有机蒙脱土用量在20＝0．5％-3．0％时，复合材料的综合力学性能均有明显提高；有机蒙脱土用量ω＞5．0％以后，材料的力学性能降低，热稳定性变差．     

涂层扩散热处理工艺对DD6单晶高温合金组织和力学性能的影响

研究了870℃/6 h涂层扩散热处理工艺对第二代镍基DD6单晶高温合金(简称DD6合金)组织和性能的影响。研究结果表明,采用870℃/6 h涂层扩散热处理工艺处理后,DD6合金的显微组织、760℃拉伸性能、980℃/250 MPa持久性能、700℃高周疲劳性能无明显变化。DD6合金760℃拉伸断裂类型为准解理断裂,980℃/250 MPa持久断裂类型为韧窝断裂,700℃高周疲劳断裂类型为准解理断裂。涂层扩散处理没有改变DD6合金的断裂机制。     

感光性可溶共轭聚合物聚对苯的合成

利用反应性高分子的取代反应,合成了含肉桂酸酯侧基的新型感光性共轭聚合物．首先用无水三氯化铁作氧化剂,利用氧化聚合法合成可溶性聚对苯——聚(1,4-二(4-氯丁氧基))苯,然后与肉桂酸钾进行高分子反应,合成了所设计的感光性共轭聚合物．采用FT-IR,UV-VIS,NMR,TGA和荧光光谱对聚合物的化学结构和性能进行了测试．聚合物在氯仿、THF、DMSO等溶剂中溶解性较好,在紫外光辐照下聚合物薄膜可进行交联反应。     

各种烷氧基取代聚对苯乙炔的合成和表征

利用脱氯化氢的方法合成了聚(2-甲氧基-5-己氧基)对苯乙炔(PMOHOPV)、聚(2-甲氧基-5-辛氧基)对苯乙炔(PMOCOPV)、聚(2,5-二丁氧基)对苯乙炔(PDBOPV)、聚(2,5-二己氧基)对苯乙炔(PDHOPV)、聚(2,5-二辛氧基)对苯乙炔(PDCOPV)等5种聚合物发光材料.通过核磁和红外表征了它们的结构.通过热失重曲线考察了它们的热稳定性.并从温度、催化剂、反应时间、烷氧基取代等方面考察了对聚合物溶解性、分子量、发光性能等的影响.发现可以通过催化剂的用量来改变聚合物分子量,聚合物的分子量与聚合物的溶解性成正比.     

热处理对桑蚕丝纤维结构与性能的影响

文章以普通桑蚕丝纤维和经壳聚糖处理的桑蚕丝纤维为研究对象,对其进行热处理,研究热作用对其结构与性能的影响.研究结果表明,两种真丝纤维经热处理后均产生失重与泛黄现象,且壳聚糖处理真丝纤维较普通桑蚕丝更明显.热处理后,普通桑蚕丝纤维结晶度提高,壳聚糖处理真丝纤维结晶度下降,同时其纤维表面出现皱缩条纹.经壳聚糖处理的真丝纤维更易老化.     

热处理工艺对38CrMoAlA钢组织与性能的影响

 通过热处理工艺试验研究了38CrMoAlA钢不同淬火温度、冷却方式和回火温度对38CrMoAlA钢微观组织及力学性能的影响。结果表明,在900—1000℃淬火温度范围内,淬火温度对该钢的力学性能影响不大。不同的冷却方式因淬火介质的冷却强度不同,导致淬火后的组织不同,从而影响该钢的力学性能。回火温度对该钢的力学性能的影响较为显著,100—400℃范围内回火表现出回火脆性,在620℃回火能得到较好的强韧配合。该钢采用940℃,1h,油冷620℃,5h,油冷的热处理工艺时,可获得适宜的力学性能。     

Fe-Mn-Al(Cr)-C系合金热处理组织的研究

利用金相显微分析，X衍射分析，测量显微硬度和电子探针分析研究了在固溶处理和时效处理时Fe-Mn-Al(Cr)-C系合金的组织形态，结果表明在1120℃以上温度固溶处理时，合金组织中仍有少量的碳化物(Cr，Mn，Fe)7C3。合金元素在组织中分别起着不同的作用，Cr元素主要参与碳化物的形成，而AL、Mn元素的作用是固溶强化和稳定奥氏体组织和碳化物。     

PU／PGMA同步互穿网络的力学性能

研究影响高增塑聚氨酯／聚甲基丙烯酸缩水甘油酯同步互穿网络力学性能的因素,寻求最佳力学性能配方。方法,制备了不同配方的样品,对其进行拉伸试验以及动态力学分析。结果与结论改变ＰＵ与ＰＧＭＡ的组成比,ＳＩＮ的拉伸强度和延伸率呈非单调变化,在ＰＵ含为６０％附近时出现极大值,在体系中引入ＰＧＭＡ组分的交联剂及引入网间接枝剂均使体系的交联密度上升,导致抗张强度升高,断裂伸长率下降。     

Changes in Structure and Properties of Soybean Protein/Poly （vinyl alcohol） Blended Fibers Subjected to Wet Heat Treatment

The properties of soybean protein/poly（vinyl alcohol） （SP/ PVA） blended fibers subjected to wet heat treatment in hot water were measured. The structure of fibers was investigated by scanning electron microscope （SEM）, Fourier transform infrared （FTIR） spectroscopy, wide-angle X-ray diffraction （WXD） and differential scanning calorimetry （DSC）. The results show that the wet heat treatment above 100℃ has a great influence on the properties and structure of SP/PVA blended fibers. After the wet heat treatment at high temperature, the fibers exhibit the severe shrinking and yellowing, the great decrease in breaking strength and adhesive aggregation. The fibers show a broader main X-ray diffraction peak with the disappearance of minor diffraction peaks, a double DSC melting behavior with the peak temperatures of 215 and 233℃, and a weaker intensity of crystallization-sensitive absorbance peak of PVA component at 1 142 cm^-1. Therefore it is concluded that the wet heat treatment above 100℃ leads to a change in the crystalline structure of fibers and the scission and degradation of PVA macromolecular chains.     

聚酰亚胺薄膜层叠体热处理过程中的结构演变

将双向拉伸PI薄膜,层叠后经800℃炭化所得样品在热压机中进行从2 500℃到2 800℃的高温石墨化处理制得了高定向石墨材料。借助SEM、XRD、四探针法等测试手段分析了PI薄膜层叠成型体在热处理过程中尺寸、传导性能、微观结构等的变化。结果表明石墨化处理后,样品径向增大,厚度减小;2 800℃处理后材料层间距接近单晶石墨的理论层间距,表现出了较高的石墨化程度,且具有高的取向性和传导性能,根据电阻率与热导率的相关公式推得其热导率为1 000 W/(m.K)～1600 W/(m.K).在整个热处理过程中,所生成的物质继承了原料分子的取向性。     

[Ni(dien)2](NO3)2的合成与晶体结构

合成出硝酸镍与二乙烯三胺(dien)的新的配位化合物，并分析讨论该配合物的晶体结构。     

N-(4-硝基苯)-(L)-脯氨醇的晶体结构

Ｎ－（４－硝基苯）－（Ｌ）－脯氨醇晶体属单斜晶系，空间群为Ｐ２１，单胞参数为：ａ＝０．５２４３（１）ｎｍ，ｂ＝１．４８６０（６）ｎｍ，ｃ＝０．７１６６（１）ｎｍ，β＝１０５．１６（１）°ｖ＝０．５３８８４（ｎｍ）～３，Ｚ＝２，Ｄｃ＝１．３７０ｇ·ｃｍ～（－３），Ｆ（０００）＝２３６，μ＝０．９ｃｍ～（－１）在ＡＦＣ—５Ｒ四圆衍射仪上用ＭｏＫα射线，收集了０＜２θ＜５５．ｌ°的独立衍射点１４５７个．晶体结构 利用Ｍｕｌｔａｎ程序找出大多数非氢原子的初始坐标．后由差值Ｆｏｕｒｉｅｒ合成找出其它非氢原子坐 标．经全矩阵最小二乘精修，最终偏离因子为Ｒ＝０．０６０，Ｒｗ＝０．０５６．     

一种三元配合物的合成和晶体结构

邻香草醛、乙醇胺、8-羟基喹啉与硫酸氧钒反应,得到氧钒西夫碱三元配合物,(C39H42C12N4O12V2)中心原子钒(Ⅳ)与六个原子配位,形成了畸变的八面体结构.所得晶体属于三斜晶系,P-1空间群.晶体学参数为: a=12.724 (13) 10-10m,b=13.297(13) 10-10m,c=13.458(13) 10-10m, (=85.079(19)°, (=70.696(19)°,(=72.788(17)°, Z=2, Dc=1.507mg·m-3, F(000)=960, R1=0.0742, wR2=0.2108.     

蒙脱土改性PET纤维性能

采用熔融插层法制备聚对苯二甲酸乙二酯（PET）/蒙脱土（MMT）纳米复合材料,对其纤维的结晶性能、力学性能及染色性能进行详细研究.结果表明,与纯PET纤维相比,蒙脱土改性PET纤维具有较高的模量和较低的收缩率,改性纤维的上染率亦有明显提高.含磺酸基团改性的聚对苯二甲酸乙二酯（CDP）/MMT纤维的上染率和上染速率大于PET/MMT纤维,表明蒙脱土和聚合物中的离子基团对促进PET纤维的染色性能有协同作用.