橡胶沙漠砂混凝土的力学性能及其本构模型

为研究橡胶和沙漠砂对混凝土力学性能的影响，试验采用沙漠砂(替代率为0%～60%)和改性橡胶集料(替代率为0%～15%)掺入混凝土中部分替代河砂，通过单因素试验，共设置16组配合比，分别通过混凝土立方体力学性能试验、混凝土棱柱体单轴压缩试验对橡胶沙漠砂混凝土的力学性能进行研究。试验结果表明：混凝土的立方体抗压强度及劈裂抗拉强度伴随沙漠砂替换率增加先增长后下降；当沙漠砂替换率一定时，橡胶集料替换率增加，混凝土的立方体抗压强度持续降低、峰值应变与极限应变小幅度增加、劈裂抗拉强度呈先降后增再降的规律；基于过镇海模型以及CEB-FIP拟合取得的橡胶沙漠砂混凝土应力-应变曲线与试验获得的曲线契合良好。就有效再利用废物资源来说，建议取用沙漠砂替代率为20%或40%,橡胶集料替代率为10%的橡胶沙漠砂混凝土。     

粉煤灰掺量和沙漠砂替代率对沙漠砂混凝土力学性能影响

为了研究粉煤灰掺量和沙漠砂替代率对沙漠砂混凝土力学性能影响,进行不同粉煤灰掺量和沙漠砂替代率的沙漠砂混凝土28 d抗压强度和28 d劈裂拉伸强度试验研究,分析粉煤灰掺量和沙漠砂替代率对沙漠砂混凝土28 d的抗压强度和劈裂拉伸强度的影响规律。实验结果表明:随着沙漠砂替代率增加,沙漠砂混凝土抗压强度和劈裂拉伸强度均呈现先增大后减小趋势,沙漠砂替代率为20%时,沙漠砂混凝土抗压强度和劈裂拉伸强度均达到最大值;随着粉煤灰掺量增加,沙漠砂混凝土抗压强度和劈裂拉伸强度先增大后减小,粉煤灰掺量为10%时,沙漠砂混凝土抗压强度和劈裂拉伸强度达到最大值。试验结果可为沙漠砂在工程中的应用提供指导和借鉴。     

高温后高强沙漠砂混凝土力学性能研究

为了研究高强沙漠砂混凝土高温后的力学性能,采用室温、200℃,400℃,600℃,800℃和900℃六个温度等级,利用自然冷却方式,通过正交试验,研究水胶比,粉煤灰掺量和沙漠砂替代率对高强沙漠砂混凝土高温后抗压强度的影响,对高强沙漠砂混凝土试件高温后的外观颜色变化进行了观察,分析了高温后高强沙漠砂混凝土试件的质量变化。试验研究表明:与室温下高强沙漠砂混凝土抗压强度相比,200℃高温后高强沙漠砂混凝土强度有所降低,在400℃至600℃高温后抗压强度有所升高,之后随着温度的升高抗压强度逐渐降低;随着温度升高,高强沙漠砂混凝土外观颜色由深变浅,质量损失率呈现逐渐增加趋势。通过方差分析和极差分析,给出了高强沙漠砂混凝土最佳配合比,为高强沙漠砂混凝土的工程应用提供借鉴和指导。     

沙漠砂混凝土轴心受压应力-应变曲线试验分析

为探究单一变量下沙漠砂混凝土应力-应变全曲线,分别设计4组不同沙漠砂取代率的棱柱体混凝土试块,进行单轴受压试验,分析沙漠砂混凝土破坏现象、破坏过程以及破坏特征,并研究不同沙漠砂取代率对沙漠砂混凝土峰值应变、极限应变、弹性模量的影响.研究结果显示:沙漠砂混凝土与普通混凝土相比,其破坏特征具有一定的差异性;取代率为20％时沙漠砂混凝土其轴心受压强度达到最高,且胶凝材料对沙漠砂包裹效果较为明显;沙漠砂混凝土脆性明显高于普通混凝土;沙漠砂混凝土无量纲应力-应变曲线上升段、下升段均采用过镇海模型较为贴合,且能准确描述沙漠砂混凝土在单轴受压作用下的变形特征.     

沙漠砂混凝土框架结构的抗震性能有限元分析

为了研究沙漠砂混凝土框架结构的抗震性能及破坏机理，基于ABAQUS有限元软件建立了9榀二层平面框架模型，研究了材料类型、混凝土楼板、配箍率和轴压比对沙漠砂混凝土框架抗震性能的作用规律。结果表明：沙漠砂混凝土框架的承载能力、初始刚度和屈服后承载能力余量均与普通砂混凝土框架相接近；与不带板的沙漠砂混凝土框架相比，带板的耗能提高近20%,承载力提高近6%;轴压比由0.2上升至0.6,试件的变形能力储备降低近15%;配箍率增加1.23%,结构的屈服载荷增长的幅度降低约1.5%,极限载荷增长的幅度降低约2%。     

粉煤灰掺量和沙漠砂替代率对高强沙漠砂混凝土力学性能影响

为了研究粉煤灰掺量和沙漠砂替代率对高强沙漠砂混凝土力学性能影响,进行不同粉煤灰掺量和沙漠砂替代率高强沙漠砂混凝土28 d抗压强度和劈裂拉伸强度实验,分析粉煤灰掺量和沙漠砂替代率对高强沙漠砂混凝土28 d抗压强度和劈裂拉伸强度影响规律.实验结果表明:随着沙漠砂替代率增加,高强沙漠砂混凝土抗压强度和劈裂拉伸强度呈现先增大后减小趋势,沙漠砂替代率为20％时,高强沙漠砂混凝土抗压强度和劈裂拉伸强度均达到最大值;随着粉煤灰掺量增加,高强沙漠砂混凝土抗压强度和劈裂拉伸强度先增大后减小,粉煤灰掺量为15％时,高强沙漠砂混凝土抗压强度和劈裂拉伸强度达到最大值,为沙漠砂在工程中的应用提供指导和借鉴.     

沙漠砂基础隔震垫层隔震性能试验研究

基于沙漠砂的有效利用,提出了一种沙漠砂基础隔震垫层,通过小型振动台试验,研究了沙漠砂基础隔震垫层的隔震性能,分析了沙漠砂基础隔震垫层的工作原理,探讨了不同地震波、垫层厚度、基底压力、垫层含水率等因素对沙漠砂基础隔震垫层减震效果的影响.结果表明,沙漠砂基础隔震层能有效降低上部结构的地震作用,尤其是应对高烈度地震时效果更加...     

C40沙漠砂混凝土抗碳化性能

通过设计水胶比、粉煤灰掺量、砂率和沙漠砂替代率四因素三水平正交试验,进行沙漠砂混凝土抗碳化性能试验,分析了各因素对C40沙漠砂混凝土抗碳化性能影响。研究表明:碳化3 d后各因素对沙漠砂混凝土碳化性能影响顺序为粉煤灰掺量水胶比砂率沙漠砂替代率;碳化7 d、14 d后各因素对沙漠砂混凝土碳化性能的影响顺序为粉煤灰掺量水胶比沙漠砂替代率砂率;碳化28 d、56 d后各因素对沙漠砂混凝土碳化性能的影响顺序为水胶比粉煤灰掺量沙漠砂替代率砂率。综合各因素对沙漠砂混凝土抗碳化性能影响,确定其最佳配合比为水胶比0.39,粉煤灰掺量10%,砂率30%,沙漠砂替代率30%。     

沙漠砂替代率对高强混凝土抗压强度影响研究

通过正交实验,分析了水胶比、粉煤灰掺量、砂率和沙漠砂替代率对不同龄期高强混凝土抗压强度影响。在正交试验基础上,保持水胶比、粉煤灰掺量和砂率不变,通过单因素实验,进一步研究不同沙漠砂替代率对高强混凝土抗压强度的影响规律。研究结果表明:用沙漠砂替代中砂配制高强混凝土是可行的;综合考虑正交试验和单因素试验中沙漠砂替代率对高强混凝土抗压强度的影响,沙漠砂高强混凝土中沙漠砂的最佳替代率20%。     

高温对沙漠砂混凝土抗压强度的影响

为了对沙漠砂混凝土高温后力学性能进行研究,通过不同沙漠砂替代率的沙漠砂混凝土高温试验,分析温度、沙漠砂替代率和冷却方式对沙漠砂混凝土高温后抗压强度的影响规律,建立沙漠砂混凝土高温后抗压强度的衰减模型。结果表明,与普通混凝土相似,随着温度升高,沙漠砂混凝土试件表面颜色逐渐变浅;随温度升高,沙漠砂混凝土抗压强度呈先增大后减小趋势;随着沙漠砂替代率增加,沙漠砂混凝土高温后抗压强度呈先增大后减小趋势,沙漠砂替代率40%时,沙漠砂混凝土高温后抗压强度达到最大。     

复合改性水玻璃的研究

介绍了水玻璃改性剂及改性水玻璃的合成工艺、性能及其在火车车辆零件的铸造生产中的应用情况。所合成的水玻璃改性剂可大幅度提高水玻璃的粘结性能和溃散性，有利于解决水玻璃砂的再生和回用问题。     

微波加热硬化水玻璃砂表面涂层的抗湿性研究

针对微波加热硬化水玻璃砂吸湿性强的特点,以PbO-ZnO系低温玻璃粉作为主要的涂层材料,研究测试了涂层的抗湿性．结果表明：表面涂层后的水玻璃砂样抗吸湿性明显高于普通水玻璃砂样,4h存放强度提高了2．33倍,4h吸水率降低了45．9％．通过SEM和XRD等测试方法,对表面涂层砂样和普通砂样的物相和成分进行了分析：SEM分析表明,表面涂层砂样的表层有涂层材料渗入形成防湿层,防湿层内砂粒表面的粘结桥有许多细小颗粒状物质分布．表面xRD扫描表明：涂层表面出现了3种新的物相,即Al2TiO3,NaAlO2和PbTiO3,它们是表面涂层提高砂样抗湿性的主要原因．     

Respondence and feedback of modern sand deserts to climate change

The research on the respondence and feedback of modern sand deserts to the climate change is an important component part in the studies on the global climate change. Deserts respond to the climate change, meanwhile, they affect the climate with their feedback of peculiar environment during the respondence. Many researches on desert climate have been carried out at home and abroad. However, there is little research on the respondence and feedback of modern fixed, semi-fixed and mobile deserts in arid areas to the climate change, in which the factor analysis as well as the parameter changing effects is especially the difficult problem all along. In this note, the parameters of the respondence and feedback of Gurbantunggut Desert to the climate change are measured and analyzed, some variable parameters of water-heat exchange are obtained, and a numerical model of desertification is developed according to a series of climate change of about 40 years and the variable relations of meteorological and physical features of the sand surface in Gurbantunggut Desert.     

Respondence and feedback of modern sand deserts to climate change--A case study in Gurbantunggut Desert

The research on the respondence and feedback of modern sand deserts to the climate change is an important component part in the studies on the global climate change. Deserts respond to the climate change, meanwhile, they affect the climate with their feedback of peculiar environment during the respondence. Many researches on desert climate have been carried out at home and abroad. However, there is little research on the respondence and feedback of modern fixed, semi-fixed and mobile deserts in arid areas to the climate change, in which the factor analysis as well as the parameter changing effects is especially the difficult problem all along. In this note, the parameters of the respondence and feedback of Gurbantunggut Desert to the climate change are measured and analyzed, some variable parameters of water-heat exchange are obtained, and a numerical model of desertification is developed according to a series of climate change of about 40 years and the variable relations of meteorological and physical features of the sand surface in Gurbantunggut Desert.     

环保型改性高分子材料固沙剂实用性能研究

针对沙漠公路沿线风积沙治理问题,通过对多种高分子材料共混物进行改性,得到了一种高性能环保固沙材料。该材料具有适宜喷洒施工、固化快、强度好等特点。取雅鲁藏布江河谷风积沙为实验对象,施以该种固沙剂,进行了渗透性、固化强度、耐久性等试验,得到了该材料在加固风积沙时的最短固化时间和最佳用量。同时将研制的固沙材料与现有固沙产品进行了对比。对比结果表明:该材料在加固风积沙时的抗压强度、抗冻融能力和耐久性均高于常规固沙材料;且环保性能较强,具有良好的应用前景。     

黄河砂与沙漠砂胶砂强度及微观机理

针对天然砂料日趋枯竭的问题,采用黄河砂和沙漠砂分别全部替代天然砂配置砂浆,通过扫描电镜(scanning electron microscope, SEM)、X-射线能量光谱(energy dispersive spectrometer, EDS)和背散射电子(back scatter electrons, BSE)及元素扫描微观表征手段并联合力学强度试验,从宏微观角度揭示两种砂浆强度发展机理。结果表明：沙漠砂体系中胶砂界面处的钙矾石(AFt)和水化硅酸钙(C-S-H)发育完善,养护前期大量层状Ca(OH)₂紧密堆积,强化了胶砂界面结构;沙漠砂砂浆中的Ca/Si随龄期增加1.64,黄河砂砂浆的钙硅比增加0.52,有效保证其强度稳定性;沙漠砂颗粒黏结性强,充分填充砂浆界面孔隙,优化了砂浆结构的密实性,从而提升了其力学强度。     

提高酯硬化水玻璃砂常温强度及溃散性研究

对酯硬化水玻璃砂的性能特征进行了分析，就提高酯硬化水玻璃砂常温强度及溃散性的措施与方法，进行了试验研究和探讨。结果表明，影响水玻璃砂常温强度及溃散性的因素包括水玻璃的种类及模数。原砂的品质、水玻璃的加入量、环境温度及湿度等。     

超细粉末材料改性水玻璃粘结剂

从几种可能的超细材料里面筛选出一种最合适的超细材料,就这种材料对水玻璃粘结剂的具体性能影响展开研究.结果表明:用经过特殊处理后的超细粉末材料改性水玻璃粘结剂,具有常温强度高、残留强度低等优点;超细粉末材料改性的水玻璃粘结剂采用酯硬化工艺,可使水玻璃粘结剂的加入量低于3.0%,在水玻璃砂常温强度有所提高的前提下,其溃散性显著改善.较佳的超细粉末材料改性水玻璃粘结剂的测试结果为(与不改性水玻璃相比):常温24h强度提高了30.7%,残留强度下降了40.1%.     

原砂对新型改性水玻璃型砂溃散性的作用机理

研究了原砂对水玻璃型砂溃散性的影响；通过扫描电镜观察了水玻璃型砂高温焙烧后的粘结桥形状和砂粒表面特征，用电子探针和X射线衍射分析了砂粒表面膜的主要生成物的成分和形态，揭示了不同品位的石英砂与水玻璃粘结剂发生高温反应后残留强度高低不同的原因．研究结果表明，都昌砂高温下与水玻璃反应生成了高熔点的蜂窝状钾长石，导致型砂的残留强度很低；而海城砂则生成了低熔点的物质，使得型砂的残留强度很高．因此，改变石英原砂的表面状态是提高水玻璃型砂溃散性的一个有效途径．     

硅酸盐钻井液室内评价与研究

着重对硅酸盐钻井液的性能进行研究。通过分析硅酸盐钻井液体系稳定井壁的机理,优选了基浆和与硅酸盐配伍性好的有机处理剂。结合硅酸盐钻井液在辽河油田的岩样中的应用进行室内评价研究,得出一套完整的硅酸盐钻井液体系配方,并对该配方进行综合性能的评价。