杂多阴离子层柱双氢氧化物（LDH—HPOMs）的热性质研究

采用ＴＧ、ＤＳＣ和ＸＲＤ等手段研究了多酸层柱双氢氧化物Ｍｓ２Ａｌ－ＸＷ１１Ｚ（Ｍ＝Ｃｏ＾２＋,Ｎｉ＾２＋;Ｘ＝Ｓｉ＾４＋,Ｇｅ＾４＋,Ｂ＾３＋;Ｚ＝Ｃｕ＾２＋,Ｎｉ＾２＋,Ｃｏ＾２＋）在空气气氛中的热解过程,得到了Ｃｏ２Ａｌ－ＸＷ１１Ｚ系列化合物的三步热分解机理和热稳定性序列,而对于Ｎｉ２Ａｌ－ＸＷ１１Ｚ系列化合物,则表现出不同的热解过程。     

Al_2O_3/W层状复合材料性能及微观结构研究

本文利用离心注浆成型法成膜,热压烧结制备了Ａｌ２Ｏ３／Ｗ层状复合材料,研究了Ａｌ２Ｏ３层、金属Ｗ层厚度对材料性能的影响,利用ＸＲＤ、ＳＥＭ对金属Ｗ层的组成及材料微观结构进行了分析和观察,探讨了层状复合材料的微观结构和金属层的组成变化对材料性能的影响．     

负载型燃烧催化剂载体效应的研究

以二甲苯完全氧化作为“探针反应”,配合ＸＲＤ分析、ＢＥＴ表面积测定,用复合硝酸盐溶液浸渍αＡｌ２Ｏ３和γＡｌ２Ｏ３两种载体制取了负载型催化剂结果表明,在αＡｌ２Ｏ３上形成的钙钛矿型氧化物,晶型较为完整,活性相晶粒大小适合于催化燃烧反应;而在具有大比表面积的γＡｌ２Ｏ３上形成的Ｌａ０．８Ｓｒ０．２ＭｎＯ３颗粒细小,对二甲苯完全氧化具有低的催化活性,故认为αＡｌ２Ｏ３对Ｌａ０．８Ｓｒ０．２ＭｎＯ３是更为合适的载体．     

甲烷脱氢芳构化W／HZSM—5基催化剂EPR研究

利用ＥＰＲ等谱学方法,对Ｗ／ＨＺＳＭ－５基催化剂上Ｗ物种的价态及其在Ｈ２预还原过程中的动态行为进行了表征研究．结果表明,由碱性前驱液制备的Ｗ／ＨＺＳＭ５催化剂在１０７３Ｋ、Ｈ２预还原条件下只能还原产生一类主要Ｗ物种,Ｗ５＋;而由酸性前驱液制备的Ｗ－Ｈ２ＳＯ４／ＨＺＳＭ－５催化剂在相同反应条件下则可还原产生两类共存的Ｗ物种,Ｗ５＋和Ｗ４＋．关联到在相同的甲烷脱氢芳构化（ＤＨＡＭ）反应条件下Ｗ－Ｈ２ＳＯ４／ＨＺＳＭ－５对ＤＨＡＭ反应的催化活性比Ｗ／ＨＺＳＭ－５高得多的实验事实,可以推断,ＤＨＡＭ反应活性与催化剂上较高价态Ｗ物种（Ｗ５＋）的浓度并不存在顺变关系,而与Ｗ４＋物种的浓度则密切相关．     

高速钢马氏体回火特性的合金价电子结构分析

运用固体与分子经验电子理论（ＥＥＴ）对通用型高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２（Ｍ２）不同热处理状态的回火特性作了合金价电子结构的分析研究．通过马氏体内不同类型的价电子结构单元构成及其权重，用价电子结构信息ｎＡ及新参量Ｎ＿Ｄ￣Ｃ片分析了回火硬度曲线上显示的二次硬化强度及峰值温度的变化，从而对钢回火的认识深入到了材料价电子结构的层次．     

手性膦配位钯化合物的电化学性质

手性膦（Ｌ）配位的钯化合物ＰｄＣｌ２Ｌ２，Ｌ＝２－ＭＢＰＡ（１）；Ｌ＝３－ＭＢＰＡ（２），在ＤＭＦ中的循环伏安法电化学研究表明，二个化合物的氧还性质相近，与膦在Ｄ－醣上的碳取代位置无关．化合物的氧还反应有一个还原峰和两个氧化峰．比较化合物（２）在乙氰和ＤＭＦ中的ＣＶ图，显示两个氧化峰系由溶剂配位后的还原产物［ＰｄＬ２（Ｓｏｌｖｅｎｔ）２］１－氧化而得     

Al_2O_3／Al Lanxide材料的组成和显微结构的研究

通过Ｘ－射线衍射（ＸＲＤ）、透射电子显微镜（ＴＥＭ）和光学显微镜分析了ＡＩ－Ｍｇ－Ｓｉ合金直接氧化形成的Ａｌ２Ｏ３／ＡｌＬａｎｘｉｄｅ材料的组成和显微结构，并探讨了它们与母合金组成及氧化生长方式的关系。     

杂多阴离子柱撑水滑石类层柱状化合物的合成与表征

以硝酸根型水滑石做交换前驱体，采用离子交换法合成了过渡金属离子三元取代硅钨杂多阴离子柱撑水滑石Ｍ＿２Ａｌ（ＯＨ）＿６－ＳｉＷ＿９Ｚ＿３（Ｈ＿２Ｏ）＿３Ｏ＿（３７）（Ｍ＝Ｍｇ￣（２＋），Ｚｎ￣（２＋），Ｎｉ￣（２＋），Ｚ＝Ｃｕ￣（２＋），Ｃｏ￣（２＋））．用元素分析、ＸＲＤ、ＩＲ、ＵＶ－ＤＲＳ和ＤＴＡ等手段对产物的组成和结构进行了表征。结果表明，杂多阴离子引入水滑石层间后，水滑石的层间距从０．９２ｎｍ增大到１．４７ｎｍ；提高了柱撑材料的热稳定性，随层的组成不同热稳定性顺序为：Ｍｇ＿２Ａｌ≥Ｎｉ＿２Ａ１＞Ｚｎ＿２Ａｌ；随柱的组成不同热稳定性顺序为：ＳｉＷ＿９Ｃｏ＿３＞ＳｉＷ＿９Ｃｕ＿３．处于层中的杂多阴离子在层的脱羟基温度以下均能保持良好的Ｋｅｇｇｉｎ结构。     

高价钨砷杂多酸盐的合成及其氧化性质的研究

报道了高价钨砷杂多酸盐［（Ｃ＿４Ｈ＿９）＿４Ｎ］＿２１；［ＫＡｓ＿４Ｗ＿４０Ｏ＿１４０（ＣｒＯ）＿２］、［（Ｃ＿４Ｈ＿９）＿４Ｎ］＿２１［ＫＡｓ＿４Ｗ＿４０Ｏ＿１４０Ｃｏ＿２］和［（Ｃ＿４Ｈ＿９）＿４Ｎ］＿２１［ＫＡｓ＿４Ｗ＿４０Ｏ＿１４０Ｍｎ＿２］的合成，表征及其氧化性质．通过元素分析、磁化率、电子吸收光谱及ｅ．ｓ．ｒ谱证明，标题化合物中取代元素Ｃｒ、Ｍｎ、Ｃｏ的氧化态分别为５，３，３．合成化合物具有氧化性质，在甲苯中能将三苯基磷、苯乙烯及反－二苯乙烯氧化成氧化物．     

改性膨润土的制备(Ⅱ)

研究了在不同添加剂（ＭｇＣｌ２、ＡｌＣｌ３、ＭｇＣｌ２－ＣａＣｌ２）配比条件下,控制ＰＨ＝７￣９,通过静态吸附,筛选出对合格废水具有良好吸附性能的改性膨润土。结果说明,以ＡｌＣｌ３和Ｍｇ和Ｃｌ２－ＣａＣｌ２为加剂制香的改性膨润土,除铬效果良好。     

Phase transformation refinement of coarse primary carbides in M2 high speed steel

The decomposition of the coarse primary M_2C carbide in M2 high speed steel was investigated by using optical microscope,scanning electron microscope,energy dispersive spectrometer and X-ray diffraction analysis.It is indicated that the SEM observation using deeply etched samples can clearly reveal the details of the decomposition products of primary M_2C eutectic carbides.The MC is granular and M_6C is peanut-shaped in the decomposition products,and the decomposition products are found to be very small ...     

粉末包埋法渗铝对Q235钢恒温抗氧化性的影响

碳钢表面渗铝可以提高材料的耐蚀性和抗高温氧化性能,选择Q235钢作为基体材料,采用固体粉末包埋法对Q235钢进行650 ℃低温渗铝处理,利用SEM、XRD和EDS研究了渗Al层的微观组织结构,通过恒温氧化实验研究渗Al处理对Q235钢700 ℃恒温氧化行为的影响.结果表明：Q235钢渗Al层主要由Fe2Al5和FeAl金属间化合物组成.渗Al层表面有裂纹和空洞,界面不平整,致密性较差,氧化膜厚度200～300μm.渗Al能显著提高Q235钢700℃的恒温氧化性能,未渗Al时Q235钢的氧化动力学曲线遵循直线规律,氧化膜主要为Fe2O3,氧化过程中氧化膜脱落严重,对基体无保护作用;渗Al后动力学曲线呈抛物线规律,氧化膜较致密,缺陷较少,氧化膜主要由Al2O3和Fe2O3组成.渗铝能显著提高Q235钢的抗高温氧化性能.     

高温SiC/Al2O3复合抗氧化涂层性能的研究

本文通过SiC及SiC/Al2O3复合涂层抗氧化性能的研究，认为采用高温浸渗工艺，在石墨制品表面形成的SiC涂层与基体有合理的界面结构，该涂层能对石墨制品起到良好的抗氧化防护作用。而SiC/Al2O3复合涂层使石墨制品具有更佳的抗氧化能力。     

Isothermal oxidation behavior and mechanism of a nickel-based superalloy at 1000℃

The oxidation behavior of a nickel-based superalloy at 1000°C in air was investigated through X-ray diffraction, scanning electron microscopy, andenergy-dispersive spectroscopy analysis. A series of oxides, including external oxide scales (Cr2O3, (TiO2 + MnCr2O4)) and internal oxides (Al2O3,TiN), were formed on the surface or sub-surface of the substrate at 1000°C in experimental still air. The oxidation re-sistance of the alloy was dependent on the stability of the surface oxide layer. The continuity and density of the protective Cr2O3 scale were affected by minor alloying elements such as Ti and Mn. The outermost oxide scale was composed of TiO2 rutile and MnCr2O4 spinel, and the growth of TiO2particles was controlled by the outer diffusion of Ti ions through the pre-existing oxide layer. Severe internal oxidation oc-curred beneath the external oxide scale, consuming Al and Ti of the strength phaseγ′ (Ni3(Al,Ti)) and thereby severely deteriorating the sur-face mechanical properties. The depth of the internal oxidation region was approximately 35μm after exposure to experimental air at 1000°C for 80 h.     

W6 Mo5 Cr4 V_2钢真空离子渗碳的研究

本试验利用 X 射线物相分析、电解萃取、化学相分离和扫描电镜对 W6Mo5Cr4V2钢进行了真空离子渗碳的试验研究.结果指出,随着渗层碳浓度增加,碳化物数量明显增加:同时碳化物由低碳相(M_6C)向高硬度高碳相(M_2C,MC)转化.这两者均使渗碳层耐磨性提高;渗层淬火奥氏体量增加.在渗层含碳量为1.08～1.45%的范围内,耐磨性随含碳量的增加而提高。     

魔芋葡甘露聚糖的化学改性及其应用性能的研究

采用醚化氧化工艺,以魔芋粉为原料合成了系列印花糊料 Ｍ_１和 Ｍ_２并且就其应用性能分别与意大利的 Ｉｎｄａｌｃａ ＰＡ－４０及海藻酸钠进行比较,其中Ｍ_１各项达到了Ｉｎｄａｌｌａ ＰＡ－４０的水平,Ｍ_２各项指标接近海藻酸钠．     

钢塔对间冷散热器换热性能的影响

利用计算传热学软件Fluent,在自然通风状态下,对国内首个2×660 MW机组钢结构外覆铝板冷却塔间接空冷散热器的流动和换热性能进行数值模拟、分析和研究.考核工况下,水平加强环对散热器换热量和钢塔通风量的影响约占设计值的2.7%;铝板换热量约占机组排热量的0.6%;随着环境风速的增大,钢塔抽力逐渐降低;当环境风速高于10m/s时,出现塔内热空气流出冷却柱的现象;当环境风速高于20m/s时,塔内出现"穿堂风",间冷散热器的换热量和钢塔通风量明显增加;当环境风速低于12m/s时,随着环境风速的增大,间冷散热器的换热量和钢塔通风量逐渐降低;当环境风速高于12m/s时,随着环境风速增加,间冷换热量和钢塔通风量呈增大趋势.     

Effect of niobium alloying level on the oxidation behavior of titanium aluminides at 850°C

This work addresses the alloying of titanium aluminides used in aircraft engine applications and automobiles. The oxidation resistance behavior of two titanium aluminides of α₂ + γ(Ti₃Al + TiAl) and orthorhombic Ti₂NbAl, recognized as candidates for high-temperature applications, was investigated by exposure of the alloys for 100 h in air. Thus, oxidation resistance was expressed as the mass gain rate, whereas surface aspects were analyzed using scanning electron microscopy in conjunction with energy-dispersive X-ray spectroscopy, and the type of oxidation products was analyzed by X-ray diffraction and Raman spectroscopy. The orthorhombic Ti₂NbAl alloy was embrittled, and pores and microcracks were formed as a result of oxygen diffusion through the external oxide layer formed during thermal oxidation for 100 h.     

新型Al基复合脱氧剂脱氧效果研究

Al作为炼钢脱氧剂单独脱氧时易烧损,导致利用率较低;同时,其脱氧产物Al2 O3熔点高,形状不规则,不易在脱氧过程中上浮排出,造成水口堵塞,恶化钢材质量。为了提高铝的脱氧效率,同时使脱氧产物Al2 O3能快速从钢液中上浮排出,本文研究了一种以金属铝为有效脱氧组分,低熔点氧化物渣系为载体的新型复合脱氧剂。实验表明,使用该脱氧剂不仅可以保证钢液中溶解氧的质量分数在10×10-6以下,而且脱氧后钢中Al2 O3夹杂物与纯Al脱氧相比尺寸更小、数量更少,较显著地提高了钢材的纯净度,具有良好的脱氧效果。     

铈对Cr12铁素体不锈钢抗高温氧化性能的影响

参照标准HB 5258-2000中的增重法对不同铈含量的Cr12铁素体不锈钢的抗高温氧化性能进行测试,利用扫描电镜(SEM)、X射线衍射(XRD)技术等实验手段进行氧化形貌观察和氧化物物相分析,并对氧化物的生成热力学进行了计算. 实验结果表明:氧化物的分析结果与热力学计算结果相吻合. 在600℃、700℃及800℃较低温度时生成的氧化产物为具有尖晶石结构的M_3O_4型氧化物,具有良好的保护性,铈的添加可促进这种氧化膜的形成,降低氧化速率;在900℃时生成的氧化产物类型主要为M_2O_3型,保护性差,晶粒细的含铈钢初期氧化速率快,但是铈可改善氧化膜与基体的黏附性,在氧化后期阻止实验钢进一步的剧烈氧化. 利用反应元素效应和晶粒尺寸效应可以较好地解释该氧化动力学机制.