PA6/PTFE和PA66/PTFE的力学性能和熔融行为的实验研究

研究了PA6/PTFE和PA66/PTFE共混物的熔融过程的热学性能、动态力学性能和吸水前后的静态力学性能.结果表明:吸收水和PTFE对共混物静态拉伸性能和弯曲性能的影响不同.共混物弯曲性能受PTFE含量的影响不显著,受吸收水的影响较大;而共混物的拉伸性能受吸收水的影响较小,但PTFE的加入使共混物的断裂伸长率比纯PA的断裂伸长率严重降低.PA6/PTFE共混物的熔融温度随PTFE含量的增加而升高,熔融热却随PTFE含量的增加而降低.     

Preparation and Luminescence Properties of Nylon 6 Composite Nanofibers

The luminescent fibers have a good application prospect. The feature of this paper is that efficient luminescent nylon 6(PA6) composite nanofibers are successfully prepared by electrospinning. The luminescent PA6 composite nanofibers composed of PA6, Eu(BA)_3Phen and Tb(BAO)_3Phen(BA= P-methylbenzoic acid, BAO=P-methoxybenzoic acid, and Phen=1,10-phenanthroline). The structure and properties were characterized by scanning electron microscopy(SEM), Fourier transform infrared spectroscopy(FT-IR), fluorescence spectroscopy, and thermogravimetriy(TG) analysis. The correspondence between polymer matrix and as-prepared composite nanofibers properties has also been studied in detail. Through using hexafluoroisopropanol(HFIP) as solvent, Eu(BA)_3Phen/PA6 and Tb(BAO)_3Phen/PA6 composite nanofibers exhibit good luminescence properties. It is noted that only 5% rare earth luminescent materials are added to Tb(BAO)_3Phen/PA6 composite nanofibers, and the luminescence intensity of the as-prepared nanofibers reaches half that of the pure rare earth luminescent materials. Furthermore, uniform dispersion of pure rare earth luminescent materials in the as-prepared nanofibers gives the composite nanofibers good mechanical properties and thermal stability. These results provide an important basis for the preparation and wide application of new PA6 luminescent fibers.     

Kevlar布层间及钢板单搭接黏结性能的试验研究

为了研究Kevlar纤维布层间以及纤维布与钢板单搭接的黏结性能,利用MTS微机控制电子万能试验机,分别对双层Kevlar 49纤维布和Kevlar 49纤维布/钢板单搭接剪切接头的力学性能进行测试.结果表明,双层Kevlar 49纤维布、Kevlar 49纤维布/钢板单搭接剪切接头试样的有效黏结长度分别为25mm和50mm.在有效黏结长度范围内,两种单搭接接头的黏结力均随着黏结长度的增加而增加,但增加幅度逐渐减小,当达到有效黏结长度时,黏结力达到最大值;黏结应力随着黏结长度的增加逐渐降低.本研究结果为土木工程结构补强所用Kevlar纤维布的合理黏结长度提供参考数据.     

加固用CFRTP模压成型工艺及片材力学性能研究

针对传统的混凝土结构加固用纤维增强热固性复合材料的一系列缺点，提出用热塑性树脂来制备加固用复合材料．并且研究了连续芳纶纤维Keylar49增强热塑性树脂基复合材料的模压成型工艺和片材力学性能．所研制的复合材料力学性能达到国外现有加固材料指标．纤维和片材的SEM照片表明该材料的破坏是韧性破坏，且纤维和树脂存在最佳配比，在该配比下树脂能良好地浸润纤维束．     

共混工艺对SMA增容ABS/PA6共混体系力学性能的影响

以苯乙烯-马来酸酐共聚物(SMA)为增容剂,研究了共混工艺对ABS/PA6共混物力学性能的影响。结果表明:力学性能最好的是通过ABS和SMA挤出,再与PA6挤出,注塑得到的ABS/PA6共混物;其次PA6/SMA挤出,再与ABS挤出,注塑得到的ABS/PA6共混物;力学性能最差的是PA6/SMA/ABS一起挤出,注塑得到的ABS/PA6共混物。     

热致性液晶共聚酯(60PHB/PET)和聚酰胺6(PA6)的原位复合增容的研究

在热致液晶性60PHB/PET共聚酯(LCP)与聚酰胺6(PA6)的共混体系中引入了增容剂;讨论了增容剂对PA6/LCP原位复合材料的微观结构和界面性能、结晶行为、流变行为,以及力学性能的影响。     

磁控溅射镀铜芳纶织物的制备及其性能研究

芳纶纤维具有优异的力学性能和加工性能,还具有极好的耐热和耐化学药品性能、尺寸稳定性、耐疲劳性及耐腐蚀性等。磁控溅射镀膜法是一种高效的薄膜沉积工艺,具有装置性能稳定、操作控制方便、无环境污染等优势。采用磁控溅射法在芳纶织物表面镀覆纳米铜薄膜,使纺织品表面金属化。镀铜芳纶织物采用XRD与扫描电镜进行表征,且评价镀铜织物的抗静电性、导电性及拒水性。结果表明,溅射镀膜50 min的镀铜纤维表面致密地沉积纳米铜;XRD图显示铜的结晶存在。溅射镀膜50 min的镀铜芳纶织物接触角高达132.5°,表面电阻为129Ω/sq,抗静电半衰期为0.4 s。表明其具有良好的拒水、导电及抗静电性。     

水分对尼龙1010/6力学性能的影响

通过研究饱和吸水的尼龙1010/6系列共聚物力学性能,并与干燥状态进行对比,发现水分对尼龙1010/6共聚物力学性能有明显影响.水分的存在可以明显降低尼龙1010/6共聚物的杨氏模量、弯曲模量、屈服应力、屈服应变,增大断裂应变,而对断裂强度、断裂能以及冲击强度的影响较为复杂.     

大变形条件下纤维增强复合材料的有效性能

纤维增强树脂基复合材料具有优异的力学性能,其应用领域十分广阔．在其中的许多应用中,复合材料会发生大变形．本文建立了大变形条件下纤维增强树脂基复合材料的细观力学模型和均匀化方法,计算了复合材料在不同应变情况下的有效切线模量,研究了纤维性能、体分比和组成方式对复合材料有效性能的影响．研究表明,在大变形条件下,复合材料的有效切线性能随着纤维性能和体分比的提高而显著提高,而纤维束增强复合材料的有效切线性能要优于单丝纤维增强复合材料的有效切线性能．     

纳米改性氢氧化铝(CG-ATH)表面处理工艺对纳米 CG-ATH/PA6复合材料力学性能的影响

用偶联剂对纳米改性氢氧化铝（CG-ATH）进行了表面处理,制备出纳米CG-ATH/PA6复合材料。研究了偶联剂用量、偶联剂种类及CG-ATH的改性温度对复合材料力学性能的影响。结果表明：填充表面处理后的CG-ATH,可以大幅提高复合材料的力学性能;填充用A₁偶联剂表面处理,偶联剂质量分数为1.0%,改性温度为75～80℃条件下处理的CG-ATH,得到的复合材料的力学性能最好;表面处理明显提高了CG-ATH在PA6中的分散性。     

芳纶短纤维/芳纶浆粕增强制备高性能氯丁橡胶复合材料

对芳纶短纤维和芳纶浆粕进行微观结构表征和热失重分析,系统地研究了芳纶短纤维和芳纶浆粕对橡胶复合材料基本物理性能、动态力学性能和动刚度的影响。结果表明,芳纶短纤维为巨原纤模型;芳纶浆粕为微纤模型,呈羽绒状。芳纶短纤维在500 ℃降解,650 ℃左右降解基本完全;芳纶浆粕在350 ℃左右开始降解,500 ℃左右迅速降解,直到650 ℃左右降解基本完全。芳纶短纤维/芳纶浆粕增强制备的氯丁橡胶复合材料的撕裂强度、拉断伸长率、屈挠性能随着芳纶短纤维/芳纶浆粕并用比值减小而提高,但其动刚度减小。动态力学性能表明芳纶短纤维与芳纶浆粕并用比为10:10时,有相对较高的储能模量,较低的损耗模量和损耗因子,动态疲劳性能较好。     

Mechanical properties of carbonfi ber/cellulose composite papers modified by hot-melting fibers

Carbon fiber(CF)/cellulose(CLS) composite papers were prepared by papermaking techniques and hot-melting fibers were used for modification. The mechanical properties of the obtained composite papers with different CF,CLS and hot-melting fiber ratios were studied and further discussed. It is observed that,for both CF/CLS composite papers and those modified by hot-melting fibers,the normal stress firstly increases and then declines with the addition of carbon fibers. The results also show that with the addition of hot-melting fibers,the modified papers exhibit enhanced mechanical performance compared to CF/CLS composite papers. Through SEM characterization,it is confirmed that the improvement of mechanical properties attributes to the reinforcement of adhesive binding at the fiber overlap nodes. Also,through four-probe method,the resistivity and the electrical performance of the modified and unmodified papers were characterized and the result shows that the hot-melting fiber modification brings no harm to the electrical properties.     

弹性聚四氟乙烯/聚氨酯共混薄膜的制备与性能研究

在分散型聚四氟乙烯树脂（PTFE）中混入热塑性弹性体聚氨酯（TPU）,采用二次双向拉伸制备了具有良好弹性的多微孔薄膜,并对薄膜进行弹性性能测试及透射电镜（TEM）和 表面扫描电镜（SEM）观察。结果表明：TPU在PTFE中能够均匀掺混,经二次双向拉伸后PTFE 形成了网状结构,TPU依附在PTFE纤维上也被拉伸成细小纤维,二者共同形成了多微孔薄膜,而且TPU的加入有效地改善了PTFE薄膜的弹性性能。     

几种纳米/PA6复合材料摩擦及加工性能研究

通过共混改性的方法制得纳米复合材料, 在MPX-销-盘式摩擦实验机上测试复合材料的摩擦性能,分析了各种不同的纳米粒子Al2O3, ZnO, SiO2对PA6复合材料摩擦性能的影响,同时研究了载荷对材料性能的影响以及在哈克流变仪(HAAKE)上的Al2O3/PA6复合材料加工性能的变化.结果表明:三种不同的纳米复合材料的摩擦性能得到了很大的提高,但当纳米粒子的质量含量大于6%时,材料的摩擦系数变化不大,比较而言,纳米SiO2粒子的PA6复合材料的摩擦性能最好.纳米粒子对复合材料的加工性能也有很大的影响,当复合材料中的纳米Al2O3质量含量为10%时,材料的转子扭矩力提高将近1倍.     

几种高性能芳纶纤维的耐光性评价

利用氙弧灯和碳弧灯分别照射3种高性能芳纶纤维（Kevlar 129,Zylon AS（PBO）和Kermel纤维）,分析它们力学性能的变化.Kevlar 129纤维耐光性最好,Kermel纤维耐光稳定性最差.实验发现,尽管Zylon AS（PBO）纤维初始强力最高,但其耐光性较差,在光照条件下下降剧烈.同时发现碳弧灯下纤维试样的损失比氙弧灯下辐照损失大.通过纤维表观和断裂端形貌观察可清楚看出,这3种高性能纤维都因光辐照损伤,且都有脆性断裂特征.     

短碳纤维增强尼龙6复合材料的制备与研究

碳纤维复合材料是通过双螺杆反应挤出机复合制备,研究了复合材料的微结构和力学性能,碳纤维的扫描电镜照片显示,处理后的碳纤维较未处理碳纤维有更好的表面粗糙度。复合材料断面照片显示处理后的碳纤维和基体尼龙6材料有着很好的界面结合。复合材料的力学性能得到提高,其拉伸强度和拉伸模量分别提高了33%和50%。     

聚酰亚胺复合材料的性能研究

以聚酰亚胺－聚四氟乙聚酰亚胺－聚四氟乙烯－石墨共混体系为基础,研究了体系的力学性能、摩擦性能,并进行了微观结构分析,试验结果表明,少量石墨的另入,并未使复合材料的摩擦性能有所提高,反而使冲击强度及布氏硬度下降,而聚四氟乙烯的加入,可使复 材料的摩擦性能有较大幅度的改善。     

三维编织碳/环氧复合材料的摩擦学特性

为研究三维编织复合材料的摩擦学行为，采用RTM工艺制备了三维编织碳纤维增强环氧树脂复合材料，讨论了纤维体积比、纤维表面处理和润滑条件等因素对复合材料摩擦磨损性能的影响。结果表明，随着纤维含量的增加，复合材料的摩擦系数先降后升，在35％时有最小值；磨损率则一直下降。纤维表面处理使复合材料的磨损率降低，耐磨性提高，水润滑条件下复合材料的摩擦磨损性能远优于干摩擦条件下的性能。干摩擦条件下复合材料的磨损机制主要为黏着磨损，水润滑条件下则以磨粒磨损为主。     

PP—g—MAH增容PP／PA6共混体系研究

研究(PP—g-MAH)相容剂对聚丙烯伲龙6(PP/PA6)体系的增容作用，并讨论了PP—g-MAH对PP/PA6共混物的力学性能的影响。结果表明：PP—g-MAH能有效地增强PP／PA6共混体系两相界面的相互作用，改善PP和PA6的相容性，是效果较好的相容剂。     

PES／PA共混合金的研究

通过力学性能、流变性能的测试，以及ＩＲ、ＳＥＭ研究了ＰＥＳ／ＰＡ合金在相容剂存在下的微观结构与宏观性能。结果表明，合成的环氧型相容剂与ＰＥＳ／ＰＡ合金体系中的ＰＡ发生了反应，并且相容剂的加入利于改善ＰＥＳ／ＰＡ合金的相容性，流变性和力学性能，尤其是抗冲性能。