静高压在多层Al／Fe—Mo—Si—B纳米合金复合材料…

在３￣５．５ＧＰａ的压力范围内，经过８７３Ｋ，３０ｍｉｎｈ等温热处理由非（Ｆｅ０．９９Ｍｏ０．０１）７８Ｓｉ９Ｂ１３（ＦＭＳＢ）条带和纯金属Ａｌ片交替叠成的样品，制备出多层Ａｌ／Ｆｅ－Ｍｏ－Ｓｉ－Ｂ纳米合金复合材料。研究了静高压在复合材料制备中影响非晶ＦＭＳＢ合金晶化相，Ｆｅ－Ｍｏ－Ｓｉ－Ｂ纳米合金晶粒度和Ａｌ／Ｆｅ－Ｍｏ－Ｓｉ－Ｂ复合材料界面相的规律及机制。     

喷射沉积Al-20Si-5Fe-3Cu-Mg

利用喷射沉积技术制备了Ａｌ－２０Ｓｉ－５Ｆｅ－３Ｃｕ－１Ｍｇ合金,借助扫描电镜（ＳＥＭ）,Ｘ－射线衍射和拉伸试验等手段研究了喷射沉积合金的微观组织和力学性能,分析了Ｆｅ对合金挤压和热处理后的组织变化,拉伸试验结果表明,喷射沉积Ａｌ－２０Ｓｉ－５Ｆｅ－３Ｃｕ－１Ｍｇ合金具有比粉末冶金Ａｌ－２０Ｓｉ－３Ｃｕ－１Ｍｇ合金更高的高温（３００℃）强度。     

合金元素对铸造AlSi7Mg合金导电率的影响

研究了合金元素Ｓｉ、Ｍｇ及杂质元素Ｃｕ、Ｍｎ、Ｆｅ等对铸造ＡｌＳｉ７Ｍｇ合金导电率的影响。结果表明,Ｓｉ对合金的导电率有不利的影响,其含量应控制在下限;随着Ｍｇ含量的提高,合金的导电率降低,综合考虑强度和导电率,Ｍｇ含量应控制在０．２５％～０．４％;Ｆｅ是合金中的有害元素,但其对导电率影响不大,其含量应低于０．２％;Ｃｕ、Ｍｎ是合金中的杂质元素,对导电率有不利影响,应减小其含量。     

两种快凝AlFeX（V，W）Si合金的组织性能

采用喷射沉积坯轧制和ＲＳ／ＰＭ粉末挤压坯轧制的２种工艺制各了Ａｌ－８．５Ｆｅ－１．３Ｖ－１．７Ｓｉ和Ａｌ－８．５Ｆｅ－１．３Ｗ－１．７Ｓｉ合金的板材，并通过透射电镜，扫描电镜和力学拉伸实验研究了板材的组织性能．结果表明，综合性能ＡｌＦｅＷＳｉ合金优于ＡｌＦｅＶＳｉ合金的喷射沉积坯轧制板材．     

混合稀土对Al—Si—Cu系合金铸造组织与硬度的影响

该文借助金相，电镜和热分析等手段，研究微量混合稀土（０．０５％￣０．５０％，质量分数）对Ａｌ－Ｓｉ－Ｃｕ合金铸态组织与硬度的影响。结果表明，凝固速度显著影响稀土对代晶硅相的变质效果，稀土减小α（Ａｌ）二次枝晶间距，并使合金铸态硬度提高。试验证实，稀土使合金中化纹状三元共晶α（Ａｌ）＋Ｓｉ＋Ａｌ２Ｃｕ减少，块状Ａｌ２Ｃｕ相增加。     

Fe－Mn－Ni－Al系铸造合金的低温机械性能研究

本文研究了用于深冷条件下的Ｆｅ－Ｍｎ－Ｎｉ－Ａｌ系合金的化学成分、金相组织和低温机械性能．结果表明，Ｆｅ－２２Ｍｎ－３．５Ｎｉ－２．５Ａｌ－０．１Ｃ合金具有稳定的奥氏体组织和良好的机械性能，可用于－１９６℃下工作的低温铸件结构．试验中还发现，夹杂物的含量对降低低温冲击韧性具有显著的影响     

稀土和锶变质的Al—Si—Mg合金

选择理想的变质剂是制备高强韧铸造Ａｌ－Ｓｉ－Ｍｇ合金的重要手段。采用富镧混合稀土和锶对Ａ３５７合金进行了变质处理,研究了它们对合金铸态、力学性能及含量的影响。结果表明,在保证合金含铁量Ｆｅ≤０．１１％时,富镧混合稀土比锶有更理想的除氢和变质效果细化组织中共晶硅的能力和综合力学性能。     

ZL109激光表面改性处理--激光表面合金化

采用１０ｋＷ的连续横流ＣＯ２激光器在铸造Ａｌ－Ｓｉ合金基底上制备了厚度为２．０～２．５ｍｍ的镍合金化改性层．利用ＳＥＭ、ＸＲＤ、ＴＥＭ及ＥＤＸ等分析方法测试了其微观组织和结构．结果表明：合金化涂层是由α－Ａｌ、Ａｌ３Ｎｉ２、Ｎｉ３Ａｌ、ＡｌＮｉ等Ａｌ／Ｎｉ相以及少量Ｓｉ相组成,涂层与基底之间界面两侧存在明显的成分变化,合金化改性层的平均显微硬度为１７９～２３３ＨＶ０．１,比基底Ａｌ－Ｓｉ合金提高了８４ＨＶ０．１以上．耐磨性对比试验的结果表明,镍合金化涂层的表面磨损情况大大改善,相对耐磨性提高了４倍以上．     

FexMn1-x合金电子结构及其磁性的理论研究

采用第一性的线性缀加平面波（ＬＡＰＷ）的理论计算方法，对ＦｅｘＭｎ１－ｘ合金体系的电子结构与磁性进行了理论研究，并与实验进行了比较，结果表明，ｂｃｃ Ｆｃ０．７５Ｍｎ０．２５剑金为铁磁性，而ｆｃｃ结构的Ｆｅ０．５Ｍｎ０．５和Ｆｅ０．２５Ｍｎ０．７５合金为反铁磁性，而且在铁磁性区域，理论计算磁矩的大小与实验值符合得很好。     

山东平阴地区中元古代层状硅质岩热水沉积地球化学特征及沉积环境意义

在山东平阴地区中元古界地层中存在与地层整合产出的层状硅质岩。硅质岩富Ｆｅ、Ｍｎ，相对贫Ａｌ；富集Ａｓ、Ｓｂ、Ｂｉ、Ｇａ；ＲＥＥ总量低，Ｃｅ负异常，ＨＲＥＥ相对富集；δ３０Ｓｉ变化范围为－０．１‰～０．４‰，δ１８Ｏ变化范围为＋１３．６‰～＋２０．１‰，具有热水沉积硅质岩的地球化学特征。在Ａｌ－Ｆｅ－Ｍｎ和Ｆｅ－Ｍｎ－（Ｎｉ＋Ｃｏ＋Ｃｕ）三角图上均属热水沉积硅质岩。硅质岩ＭｎＯ／ＴｉＯ２比值、δＣｅ值和δ３０Ｓｉ值分析表明本区层状硅质岩主要是在深海环境下沉积的。     

Nb 对氢在 Fe-13Cr-6Al-2Mo 合金中扩散行为的作用

采用电化学氢渗透方法研究氢原子在 Fe-13Cr-6Al-2Mo 和 Fe-13Cr-6Al-2Mo-0.5Nb 合金中的扩散行为, 分析了 0.5%Nb(质量分数, 下同)对氢原子在 Fe-13Cr-6Al-2Mo 合金中扩散行为的作用. 研究结果表明: 当在 Fe-13Cr-6Al-2Mo 合金中添加 0.5%Nb 后, 合金的晶粒得到细化, 同时合金中析出大量弥散分布的细小 Fe$_{2}$Nb 相. 0.5%Nb 的添加大幅度降低了氢原子在 Fe-13Cr-6Al-2Mo 合金中的表观扩散系数, 使氢原子在合金中的扩散激活能提高了 50.3%. Nb 原子通过提高合金中的氢陷阱浓度, 有效降低了氢原子在 FeCrAlMo 基合金中的扩散速率.     

喷射沉积Al-20Si-5Fe-3Cu-1Mg合金的微观组织与力学性能

利用喷射沉积技术制备了Al－20Si－5Fe－3Cu-1Mg合金,借助扫描电镜（SEM）,X-射线衍射和拉伸试验等手段研究了喷射沉积合金的微观组织和力学性能,分析了Fe对合金挤压和热处理后的组织变化．拉伸试验结果表明,喷射沉积Al－20Si-5Fe-3Cu-1Mg合金具有比粉末冶金Al-20Si-3Cu-1Mg合金更高的高温（300℃）强度．     

热海水中热浸镀用锌及锌铝合金的电化学性能

为了定量比较不同热浸镀层用金属(或合金)在热海水中对钢铁基体的阴极保护作用,参照国标GB/T 17848-1999的要求对几种典型的热浸镀用锌及锌铝合金测试了50℃条件下的恒电流性能,计算了电流效率,观察了腐蚀产物脱落情况及腐蚀均匀性,并据此评价了它们的电化学保护性能.结果表明:Zn的电化学性能最好,Zn-55Al-1.6Si合金的电化学性能最差,Zn-5Al-0.1RE,Zn-5Al-0.5Mg,Zn-6Al-3Mg,Zn-11Al-0.2Si-3Mg,Zn-25Al-0.2Si-0.2Mg和Zn-25Al-0.2Si-0.2RE合金介于二者之间.     

High Temperature Corrosion of Fe-25Cr and Fe-17Cr-1.5Si-0.5Al Alloys in Oxidizing and Sulfidizing Enviornments

The simultaneous oxidation and sulfidation of Fe 25Cr and Fe-17Cr-l.5Si-0.5Al alloys was studied at 1023K and 1223K in H2-H2O-H2S gas mixtures. The kinetic boundary which indicates the transition from oxide to sulfide has heen found in these two alloys. The critical oxygen partial pressures of Fel7Crl.5SiO.5Al alloys were systematically lower than those of Fe-25Cr alloy. The reaction kinetics were measured by the stainless steel spring balance, and the reaction products were characterized by X-ray diffraction and scanning electron microscopy. The reaction rate usually decreased with the increase of the oxygen partial pressure at the constant sulfur partial pressure. The exista-nce of silicon plays an important role to suppress the sulfidation of Fel7Cr alloy.     

Macrosegregation and the underlying mechanism in Ti-6.5Al-1.0Cr-0.5Fe-6.0Mo-3.0Sn-4.0Zr alloy

A novel method for the analysis of composition distribution of titanium alloys over a large area(64 mm × 72 mm) was investigated by exploring the original position statistic distribution based on spark spectrum(OPA-SS) in Ti-6.5 Al-1.0 Cr-0.5 Fe-6.0 Mo-3.0-Sn-4.0 Zr titanium alloy. The results showed that OPA-SS could characterize the distribution of elements in different positions on the titanium alloy. The macrosegregation of Sn was the most pronounced, with a statistic segregation degree higher than 18%; the macrosegregation of Mo followed with a statistic segregation degree of 10%; the macrosegregation of Al and Fe was relatively milder,lower than 8%. The main reason for the macrosegregation state of the as-cast Ti-6.5 Al-1.0 Cr-0.5 Fe-6.0 Mo-3.0 Sn-4.0 Zr alloy can be the solute redistribution during liquid solidification and the diffusion rate of each element in the solid phase.     

Mn元素对过流冷却过共晶Al-22Si-2Fe-xMn合金显微组织及耐磨性的影响

采用常规铸造和分段式倾斜板过流冷却铸造工艺制备Al-22Si-2Fe-xMn合金,研究表明:过流冷却制备工艺能够改善初生Si形貌及尺寸,但对针状富Fe相作用有限.利用扫描电镜、X射线衍射及透射电镜等手段分析过流冷却条件下Mn元素添加对富Fe相晶体结构的影响,通过摩擦磨损实验研究不同Mn/Fe质量比的过共晶Al-Si合金的硬度及耐磨损性能.结果表明:随着过流冷却铸造过共晶Al-Si合金中Mn/Fe质量比增加,合金中四方结构的长针状富Fe相逐渐减少直至基本消失,当Mn/Fe质量比为0.7时,富Fe相主要为六方结构的块状或鱼骨状α-Al15(Fe,Mn)3Si2相,此时,合金耐磨性较未添加Mn元素时有所提升,磨损机制以磨料磨损方式为主.     

多组元铁基非晶复合材料的力学性能研究

采用真空感应水冷铜坩埚磁悬浮熔炼以及负压铜模吸铸法制备了Fe-15Mn-5Si-10Cr-xC(x=0.6~1.0)铁基非晶合金复合材料,由C元素含量变化调控合金的热力学参数,分析其组织和室温力学行为变化.结果表明:随着C含量的增加,合金的原子尺寸差δ增大,混合熵ΔS_mix提高,混合焓ΔH_mix降低.合金铸态组织由非晶相和过冷γ-Fe奥氏体相组成,在压应力加载过程中发生马氏体相变并表现出显著的加工硬化.Fe-15Mn-5Si-10Cr-0.9C合金的ΔS_mix和ΔH_mix分别为1.13 RJ·mol^－1·K^－1和－19.6 kJ·mol^－1,其综合力学性能优异,屈服强度、断裂强度和塑性应变分别为1 300、2 378 MPa和17.2%.     

原位反应TiC颗粒对喷射沉积Al-20Si-5Fe合金微观组织的影响

利用熔铸－原位反应喷射沉积成形技术制备了TiC颗粒增强Al-20Si-5Fe复合材料,分析了内生TiC颗粒对喷射沉积Al-20Si-5Fe合金微观组织的影响。结果表明：喷射沉积Al-20Si-5Fe合金微观组织中常出现脆性、针状的Al-Si-Fe三元金属间化合物相,在Al-20Si-5Fe合金中内生一定量的TiC颗粒,有助于减小粗晶Si颗粒的尺寸、消除针状的Al-Si-Fe三元金属间化合物相。