Mechanical properties and wear resistance of ultrafine bainitic steel under low austempering temperature

The mechanical properties and wear resistance of the ultrafine bainitic steel austempered at various temperatures were investigated.Scanning electron microscopy(SEM) and X-ray diffraction were used to analyze the microstructure. The worn surfaces were observed via laser scanning confocal microscopy and SEM. Results indicated that, under low austempering temperatures, the mechanical properties differed, and the wear resistance remained basically unchanged. The tensile strength of the samples was above 1800 MPa, but only one sample austempered at 230°C had an elongation of more than 10%. The weight loss of samples was approximately linear with the cycles of wear and nonlinear with the loads. The samples showed little difference in wear resistance at different isothermal temperatures, whereas the thickness of their deformed layers varied greatly. The results are related to the initial hardness of the sample and the stability of the retained austenite. Meanwhile, the experimental results showed that the effect of austempering temperature on the wear resistance of ultrafine bainitic steel can be neglected under low applied loads and low austempering temperature.     

Production of 316L stainless steel implant materials by powder metallurgy and investigation of their wear properties

In this study,the mechanical and wear properties of AISI 316L stainless steel implant materials,produced by powder metallurgy(P/M),were investigated.AISI 316L stainless steel powder was cold-pressed with 800 MPa of pressure and then sintered at 1200,1250 and 1300°C for 30 min as three sample groups.The microstructure,and mechanical and wear properties of the resulting steels were investigated.Light optical and scanning electron microscopiese were used to characterize the microstructure of the steels.Room temperature mechanical properties of the steels were determined by hardness measurements and impact tests.Wear was determined using the pin-on-disc wear test,and the results were evaluated according to weight loss.The results indicate that the sintering temperature,time and atmosphere are important parameters that affect the porous ratio of materials produced by P/M.Sintering at high temperature can eliminate small pores and make the residual pores spherical.The wear tests showed that the wear of the AISI 316L stainless steel implants changed depending on the sintering temperature and load.Spherical pores in the samples increase the wear resistance.Moreover,decreasing the porosity ratio of these materials improves all of their mechanical properties.     

Development of a new coated electrode with low nickel content for welding ductile iron and its response to austempering

Coated Electrodes with small amounts of nickel were developed for welding ductile iron (DI) and conversion of the same into austempered ductile iron (ADI) after austempering. Among six electrodes, Trials 3 and 4 were selected for establishing crack-free weld deposits via preheating and post-weld heat treatment. Austenitization was performed at 900℃ for 2 h and austempering at 300 or 350℃ for three different holding times to observe the results of austempering with respect to the microstructure, hardness, and austempering kinetics of the samples. The microstructures of the weld deposits showed needle-like bainitic ferrite with small amounts of retained austenite when treated at 300℃ and feathery bainitic ferrite with large amounts of retainedaustenite when treated at 350℃. The electrode labeled with Trial 3 revealed greater austenite contents than that labeled with Trial 4 when treated with a 2 h holding time regardless of the austempering temperature applied. The transformation rate of the bainitic ferrite of Trial 3 was relatively higher than that of Trial 4 and showed a lower rate constant, leading to a higher diffusion rate of carbon in austenite.     

Effect of tempering temperature on the mechanical properties and microstructure of an copper-bearing low carbon bainitic steel

The effect of tempering temperature on the microstructure and mechanical properties of ultra-high strength, copperbearing, low-carbon bainitic steel has been investigated in the experiment. The results showed that the microstructure was mainly the laths of bainite in the as-quenched steel. The bainitic laths were restored and combined after the steel tempered at various temperatures. There were rnartensite/austenite (M/A) islands and numerous dislocations within and between the bainitic laths, while very t-me precipitates of ε-Cu were also observed within the laths. With increasing the tempered temperature from 400 to 600℃, the yield strength (YS) increased from 877 to 957 MPa, whereas the ultimate tensile strength (UTS) decreased from 1020 to 985 MPa. The Charpy V-notch (CVN) varied from 68.5 to 42 J, and the value was minimal for the steel tempered at 500℃.     

Effects of annealing temperature on the microstructure and properties of the 25Mn-3Si-3Al TWIP steel

Microstructures and mechanical properties of the 25Mn twinning induced plasticity (TWIP) steel at different annealing temperatures were investigated. The results indicated that when the annealing temperature was 1000℃, the 25Mn steel showed excellent comprehensive mechanical properties, the tensile strength was about 640 MPa, the yield strength was higher than 255 MPa, and the elongation was above 82%. The microstructure was analyzed by optical microscopy (OM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). Before deformation the microstructure was composed of austenitic matrix and annealing twins at room temperature; at the same time, a significant amount of annealing twins and stacking faults were observed by TEM. Mechanical twins played a dominant role in deformation and as a result the mechanical properties were found to be excellent.     

淬火分配处理对高碳钢组织、力学性能和磨损性能的影响

The present work employed the X-ray diffraction, scanning electron microscopy, electron backscattered diffraction, and electron probe microanalysis techniques to identify the microstructural evolution and mechanical and abrasive behavior of high carbon steel during quenching-partitioning treatment with an aim to enhance the toughness and wear resistance of high carbon steel. Results showed that, with the increase in partitioning temperature from 250 to 400°C, the amount of retained austenite (RA) decreased resulting from the carbide precipitation effect after longer partitioning times. Moreover, the stability of RA generally increased because of the enhanced degree of carbon enrichment in RA. Given the factors affecting the toughness of high carbon steel, the stability of RA associated with size, carbon content, and morphology plays a significant role in determining the toughness of high carbon steel. The analysis of the wear resistance of samples with different mechanical properties shows that hardness is the primary factor affecting the wear resistance of high carbon steel, and the toughness is the secondary one.     

Wear behavior of bainite ductile cast iron under impact load

The dry impact wear behavior of bainite ductile cast iron was evaluated under three different impact loads for 30000 cycles. The strain-hardening effects beneath the contact surfaces were analyzed according to the surfaces’ micro-hardness profiles. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to observe the worn surfaces. The results indicated that the material with the highest hardness was the one continuously cooled at 20°C, which exhibited the lowest wear rate under each set of test conditions. The hardness of the worn surface and the thickness of the hardened layer increased with the increases in impact load and in the number of test cycles. The better wear performance of the sample cooled at 20°C is attributed to its finer microstructure and superior mechanical properties. All the samples underwent the transformation induced plasticity (TRIP) phenomenon after impact wear, as revealed by the fact that small amounts of retained austenite were detected by XRD.     

Effect of deep cryogenic treatment on the properties of 80CrMo12 5 tool steel

The effect of deep cryogenic treatment on the mechanical properties of 80CrMo12 5 tool steel was investigated. Moreover, the effects of stabilization (holding at room temperature for some periods before deep cryogenic treatment) and tempering before deep cryogenic treatment were studied. The results show that deep cryogenic treatment can eliminate the retained austenite, making a better carbide distribution and a higher carbide amount. As a result, a remarkable improvement in wear resistance of cryogenically treated specimens is observed. Moreover, the ultimate tensile strength increases, and the toughness of the sample decreases. It is also found that both stabilization and tempering before deep cryogenic treatment decrease the wear resistance, hardness, and carbides homogeneity compared to the deep cryogenically treated samples. It is concluded that deep cryogenic treatment should be performed without any delay on samples after quenching to reach the highest wear resistance and hardness.     

Reverse-transformation austenite structure control with micro/nanometer size

To control the reverse-transformation austenite structure through manipulation of the micro/nanometer grain structure, the influences of cold deformation and annealing parameters on the microstructure evolution and mechanical properties of 316L austenitic stainless steel were investigated. The samples were first cold-rolled, and then samples deformed to different extents were annealed at different temperatures. The microstructure evolutions were analyzed by optical microscopy, scanning electron microscopy (SEM), magnetic measurements, and X-ray diffraction (XRD); the mechanical properties are also determined by tensile tests. The results showed that the fraction of stain-induced martensite was approximately 72% in the 90% cold-rolled steel. The micro/nanometric microstructure was obtained after reversion annealing at 820-870℃ for 60 s. Nearly 100% reversed austenite was obtained in samples annealed at 850℃, where grains with a diameter ≤ 500 nm accounted for 30% and those with a diameter >0.5 μm accounted for 70%. The micro/nanometer-grain steel exhibited not only a high strength level (approximately 959 MPa) but also a desirable elongation of approximately 45%.     

Influence of carbon-partitioning treatment on the microstructure,mechanical properties and wear resistance of in situ VCp-reinforced Fe-matrix composite

The wear resistance of iron(Fe)-matrix materials could be improved through the in situ formation of vanadium carbide particles(VCp)with high hardness. However, brittleness and low impact toughness limit their application in several industries due to addition of higher carbon content. Carbon-partitioning treatment plays an important role in tuning the microstructure and mechanical properties of in situ VCp-reinforced Fe-matrix composite. In this study, the influences of carbon-partitioning temperatures and times on the microstructure, mechanical properties, and wear resistance of in situ VCp-reinforced Fe-matrix composite were investigated. The experimental results indicated that a certain amount of retained austenite could be stabilized at room temperature through the carbon-partitioning treatment. Microhardness of in situ VCp-reinforced Fematrix composite under carbon-partitioning treatment could be decreased, but impact toughness was improved accordingly when wear resistance was enhanced. In addition, the enhancement of wear resistance could be attributed to transformation-induced plasticity(TRIP) effect, and phase transformation was caused from γ-Fe(face-centered cubic structure, fcc) to α-Fe(body-centered cubic structure, bcc) under a certain load.     

碳分配处理对原位VCp增强铁基复合材料组织、力学性能和耐磨性的影响

The wear resistance of iron (Fe)-matrix materials could be improved through the in situ formation of vanadium carbide particles (VCp) with high hardness. However, brittleness and low impact toughness limit their application in several industries due to addition of higher carbon content. Carbon-partitioning treatment plays an important role in tuning the microstructure and mechanical properties of in situ VCp-reinforced Fe-matrix composite. In this study, the influences of carbon-partitioning temperatures and times on the microstructure, mechanical properties, and wear resistance of in situ VCp-reinforced Fe-matrix composite were investigated. The experimental results indicated that a certain amount of retained austenite could be stabilized at room temperature through the carbon-partitioning treatment. Microhardness of in situ VCp-reinforced Fe-matrix composite under carbon-partitioning treatment could be decreased, but impact toughness was improved accordingly when wear resistance was enhanced. In addition, the enhancement of wear resistance could be attributed to transformation-induced plasticity (TRIP) effect, and phase transformation was caused from γ-Fe (face-centered cubic structure, fcc) to α-Fe (body-centered cubic structure, bcc) under a certain load.     

Production and characterization of ZnO nanoparticles and porous particles by ultrasonic spray pyrolysis using a zinc nitrate precursor

ZnO nanoparticles and porous particles were produced by an ultrasonic spray pyrolysis method using a zinc nitrate precursor at various temperatures under air atmosphere. The effects of reaction temperature on the size and morphology of ZnO particles were investigated. The samples were characterized by energy dispersive spectroscopy, X-ray diffraction, transmission electron microscopy, and scanning electron microscopy. ZnO particles were obtained in a hexagonal crystal structure and the crystallite shapes changed from spherical to hexagonal by elevating the reaction temperature. The crystallite size grew by increasing the temperature, in spite of reducing the residence time in the heated zone. ZnO nanoparticles were obtained at the lowest reaction temperature and ZnO porous particles, formed by aggregation of ZnO nanoparticles due to effective sintering, were prepared at higher temperatures. The results showed that the properties of ZnO particles can be controlled by changing the reaction temperature in the ultrasonic spray pyrolysis method.     

Preparation of high-strength Al-Mg-Si-Cu-Fe alloy via heat treatment and rolling

An Al-Mg-Si-Cu-Fe alloy was solid-solution treated at 560°C for 3 h and then cooled by water quenching or furnace cooling. The alloy samples which underwent cooling by these two methods were rolled at different temperatures. The microstructure and mechanical properties of the rolled alloys were investigated by optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, and tensile testing. For the water-quenched alloys, the peak tensile strength and elongation occurred at a rolling temperature of 180°C. For the furnace-cooled alloys, the tensile strength decreased initially, until the rolling temperature of 420°C, and then increased; the elongation increased consistently with increasing rolling temperature. The effects of grain boundary hardening and dislocation hardening on the mechanical properties of these rolled alloys decreased with increases in rolling temperature. The mechanical properties of the 180°C rolling water-quenched alloy were also improved by the presence of β″ phase. Above 420°C, the effect of solid-solution hardening on the mechanical properties of the rolled alloys increased with increases in rolling temperature.     

Influence of Re-Ti modification on the high impact wear resistance of high Si bainitic cast steel

The effect of rare earth (Re) and titanium (Ti) multi-modification on the impact wear behavior of Mn-B high-Si bainitic cast steel was investigated systematically. The experiments show that the impact wear resistance can be improved greatly with the addition of Re and Ti. Its wear loss is only about 1/3-1/2 as large as that of the unmodified bainitic cast steel. By the Re/Ti modification, coarse dendrite grains and bainitic/martensite duplex structure have been refined effectively, and the impact toughness of the bainitic cast steel is nearly tripled (10 mm×10 mm×55 mm, with unnotched sample). Consequently, the modified bainitic cast steel possesses good wear resistance under high impact. For both modified and unmodified bainitic cast steels, high hardness white layer and deformed zone are developed beneath the worn surface under the high impact wear, but the formation and propagation of cracks are different for these bainitic casting steels. Different models for the formation and propagation of cracks for both modified and unmodified bainitic cast steels under high impact wear are proposed.     

Experimental and numerical study on plasma nitriding of AISI P20 mold steel

In this study, plasma nitriding was used to fabricate a hard protective layer on AISI P20 steel, at three process temperatures (450°C, 500°C, and 550°C) and over a range of time periods (2.5, 5, 7.5, and 10 h), and at a fixed gas N₂:H₂ ratio of 75vol%:25vol%. The morphology of samples was studied using optical microscopy and scanning electron microscopy, and the formed phase of each sample was determined by X-ray diffraction. The elemental depth profile was measured by energy dispersive X-ray spectroscopy, wavelength dispersive spectroscopy, and glow dispersive spectroscopy. The hardness profile of the samples was identified, and the microhardness profile from the surface to the sample center was recorded. The results show that ε-nitride is the dominant species after carrying out plasma nitriding in all strategies and that the plasma nitriding process improves the hardness up to more than three times. It is found that as the time and temperature of the process increase, the hardness and hardness depth of the diffusion zone considerably increase. Furthermore, artificial neural networks were used to predict the effects of operational parameters on the mechanical properties of plastic mold steel. The plasma temperature, running time of imposition, and target distance to the sample surface were all used as network inputs; Vickers hardness measurements were given as the output of the model. The model accurately reproduced the experimental outcomes under different operational conditions; therefore, it can be used in the effective simulation of the plasma nitriding process in AISI P20 steel.     

Effect of sintering temperature on phase evolution of Al_(86)Ni_6Y_(4.5)Co_2La_(1.5) bulk amorphous composites synthesized via mechanical alloying and spark plasma sintering

Al_(86)Ni_6Y_(4.5)Co_2La_(1.5) amorphous powders were synthesized by mechanical alloying for 200 h. Subsequent consolidation was performed via spark plasma sintering in the temperature range of 250 ℃ to 500 ℃ at the pressure of 500 MPa. The role of viscous flow on densification was investigated by studying the viscosity change of the amorphous phase at different consolidation temperatures. The decrease in viscosity at higher sintering temperatures resulted in better particle bonding and densification of consolidated samples. The formation of only FCC Al was observed in the consolidated samples at sintering temperatures ≤ 300 ℃ and the intermetallic phases formed at temperatures ≥ 400 ℃. The mechanical properties of the bulk samples were measured by Vickers microhardness and nanoindentation tests. The testing results showed that the average values of microhardness, nanohardness and elastic modulus of the sample consolidated at 500 ℃ were 3.06 ± 0.14 GPa,4.85 ± 1.14 GPa and 89.53 ± 9.25 GPa, respectively. The increase in hardness and elastic modulus of the higher temperature consolidated samples is attributed to the improvement in particle bonding, densification and distribution of various hard intermetallic phases in the amorphous matrix.     

Mechanical properties and microstructure of 3D-printed high Co-Ni secondary hardening steel fabricated by laser melting deposition

The mechanical properties and microstructure of the 3D-printed high Co-Ni secondary hardening steel fabricated by the laser melting deposition technique was investigated using a material testing machine and electron microscopy. A microstructure investigation revealed that the samples consist of martensite laths, fine dispersed precipitates, and reverted austenite films at the martensite lath boundaries. The precipitates are enriched with Co and Mo. Because the sample tempered at 486℃ has smaller precipitates and a higher number of precipitates per unit area, it exhibits better mechanical properties than the sample tempered at 498℃. Although the 3D-printed samples have the same phase constituents as AerMet 100 steel, the mechanical properties are slightly worse than those of the commercial wrought AerMet 100 steel because of the presence of voids.     

Mo含量对Ti–Mo系铁素体钢热稳定性影响

The effects of tempering holding time at 700°C on the morphology, mechanical properties, and behavior of nanoparticles in Ti–Mo ferritic steel with different Mo contents were analyzed using scanning electron microscopy and transmission electron microscopy. The equilibrium solid solution amounts of Mo, Ti, and C in ferritic steel at various temperatures were calculated, and changes in the sizes of nanoparticles over time at different Mo contents were analyzed. The experimental results and theoretical calculations were in good agreement with each other and showed that the size of nanoparticles in middle Mo content nano-ferrite (MNF) steel changed the least during aging. High Mo contents inhibited the maturation and growth of nanoparticles, but no obvious inhibitory effect was observed when the Mo content exceeded 0.37wt%. The tensile strength and yield strength continuously decreased with the tempering time. Analysis of the strengthening and toughening mechanisms showed that the different mechanical properties among the three different Mo content experiment steels were mainly determined by grain refinement strengthening (the difference range was 30–40 MPa) and precipitation strengthening (the difference range was 78–127 MPa). MNF steel displayed an ideal chemical ratio and the highest thermodynamic stability, whereas low Mo content nano-ferrite (LNF) steel and high Mo content nano-ferrite (HNF) steel displayed relatively similar thermodynamic stabilities.     

粉末冶金制备的AISI 8620钢渗碳后的磨损和力学性能

The effect of carburization on the tensile strength and wear resistance of AISI 8620 steel produced via powder metallurgy was investigated. Alloys 1 and 2 (with 0.2wt% C and 0.25wt% C, respectively) were first pressed at 700 MPa and then sintered at 1300, 1400, or 1500°C for 1 h. The ideal sintering temperature of 1400°C was determined. Afterward, Alloys 1 and 2 sintered at 1400°C were carburized at 925°C for 4 h. The microstructure characterization of alloys was performed via optical microscopy and scanning electron microscopy. The mechanical and wear behavior of carburized and noncarburized alloys were investigated via hardness, tensile, and wear tests. After carburization, the ultimate tensile strength of Alloys 1 and 2 increased to 134.4% and 138.1%, respectively. However, the elongation rate of Alloys 1 and 2 decreased to 62.6% and 64.7%, respectively. The wear depth values of Alloy 2 under noncarburized and carburized conditions and a load of 30 N were 231.2 and 100.1 μm, respectively. Oxidative wear changed to abrasive wear when the load transitioned from 15 to 30 N.     

Effect of Mo content on the thermal stability of Ti–Mo-bearing ferritic steel

The effects of tempering holding time at 700°C on the morphology, mechanical properties, and behavior of nanoparticles in Ti–Mo ferritic steel with different Mo contents were analyzed using scanning electron microscopy and transmission electron microscopy. The equilibrium solid solution amounts of Mo, Ti, and C in ferritic steel at various temperatures were calculated, and changes in the sizes of nanoparticles over time at different Mo contents were analyzed. The experimental results and theoretical calculations were in good agreement with each other and showed that the size of nanoparticles in middle Mo content nano-ferrite(MNF) steel changed the least during aging. High Mo contents inhibited the maturation and growth of nanoparticles, but no obvious inhibitory effect was observed when the Mo content exceeded 0.37 wt%.The tensile strength and yield strength continuously decreased with the tempering time. Analysis of the strengthening and toughening mechanisms showed that the different mechanical properties among the three different Mo content experiment steels were mainly determined by grain refinement strengthening(the difference range was 30–40 MPa) and precipitation strengthening(the difference range was 78–127 MPa). MNF steel displayed an ideal chemical ratio and the highest thermodynamic stability, whereas low Mo content nano-ferrite(LNF) steel and high Mo content nano-ferrite(HNF) steel displayed relatively similar thermodynamic stabilities.