酯侧链结构对丙烯酸酯聚合物与天然乳胶共混相容性的影响

制备了5种具有不同烷基数目与链段长度的丙烯酸酯聚合物,将它们按照不同添加量(w=5%,10%,15%)分别添加到天然乳胶中,研究酯侧链结构对丙烯酸酯聚合物与天然乳胶共混相容性的影响。结果表明,当丙烯酸聚合物质量分数为10%时,酯侧链烷基数目最多、链段最长的聚合物所改性的乳胶薄膜的拉伸强度、撕裂强度、硬度和断裂伸长率最大,并具有最小的拉伸永久变形。表征测试进一步证实聚合物酯侧链上烷基数目越多、链段越长,改性薄膜表面越趋于平整和光滑,其薄膜断面变得致密而无析出物,共混薄膜的玻璃化转变温度也逐渐升高,说明共混物两相间相互扩散程度不断增强。实验获得一种具有优良性能的改性薄膜材料。     

硅-丙乳液/天然乳胶共混膜的制备与性能

在丙烯酸丁酯(BA)/苯乙烯(ST)体系中引入硅氧烷3-甲基丙烯酰氧基丙基三异丙氧基硅烷(C1757),通过乳液聚合法合成了可交联型共聚硅-丙乳液(PBSC),并采用傅里叶红外光谱仪(FT-IR)对其结构进行表征。利用共混法制备了天然乳胶(NR)/PBSC复合膜,并通过扫描电子显微镜(SEM)、热重分析仪(TG)及差示扫描量热仪(DSC)等仪器对其性能进行测试。结果表明:随着PBSC的加入,改性NR膜表面及内部孔洞数量减少。当w(C1757)=12%和PBSC添加量(质量分数)为12%时,NR/PBSC拉伸强度由14.4 MPa提高到23.3 MPa,热降解特征温度T0、Tp、Tf分别提升了12.9、3.7、11.5℃。同时改性乳胶膜耐溶剂性能及耐水性能均得到改善,蛋白质溢出量明显降低(低于110μg/g)。     

苯丙-硅溶胶纳米复合乳液的制备及其性能

采用原位乳液聚合法制备了苯丙-硅溶胶纳米复合乳液,系统研究了乳化剂种类和用量对乳液稳定性、乳胶膜吸水率以及乳胶粒子粒径的影响.结果表明:相比单独使用,十二烷基硫酸钠(SDS)与壬基酚聚氧化乙烯基醚(OP-10)按质量比为2∶1复配时制备的乳液稳定性最好;当乳化剂用量为0.75%～1.5%时,所制复合乳液稳定性好,乳胶膜的吸水率为3.64%～5.72%.与共混乳液(硅溶胶和苯丙乳液的共混物)和苯丙乳液的乳胶膜相比,复合乳胶膜的吸水率显著降低;透射电子显微镜(TEM)检测结果表明:与共混乳液相比,复合乳液中游离的纳米SiO2粒子数大大减少.     

碳酸钙晶须/天然胶乳复合胶膜的研究

研究经钛酸酯偶联剂NDZ101表面改性的碳酸钙晶须对于天然胶乳胶膜的补强作用。结果表明:经改性后,碳酸钙晶须与天然橡胶界面结合作用增强;与纯胶胶膜相比,改性碳酸钙晶须/天然胶乳复合胶膜的力学性能显著提高,热稳定性也有所提高。改性碳酸钙晶须用量为3%时,复合胶膜综合力学性能最佳:300%定伸应力、500%定伸应力、拉伸强度、撕裂强度和断裂伸长率分别提高了133.6%、121.1%、35.8%、34.1%和15.93%。     

封闭聚氨酯的制备及其对聚丙烯酸酯的改性

通过合成聚氨酯的预聚体,并成功的用三种苯酚类封闭剂对其封闭,随后用封闭聚氨酯预聚体对聚丙烯酸酯进行改性,得到了水性的环境友好型聚氨酯/聚丙烯酸酯的复合乳液,并对封闭异氰酸预聚体与复合乳胶膜进行了一系列测试：傅里叶红外光谱分析(FTIR)、差示扫描量热法测试(DSC)、热重分析测试(TGA)以及万能力学仪测试.还研究了三种不同苯酚类封闭剂对异氰酸酯的封闭,并通过加入少量的封闭型聚氨酯,对聚丙烯酸酯进行化学交联改性.相对于单一的聚丙烯酸酯膜,得到改性后的复合膜,复合膜的热稳定性、力学性能均得到提高,而且随着聚氨酯含量的增加,膜的抗拉伸强度上升,同时,断裂伸长率有所下降;但增加到一定程度时,过多的聚氨酯会破坏成膜过程,导致膜的性能下降.     

含氟丙烯酸酯共聚物乳液的结构与性能

采用可反应乳化剂,合成稳定的甲基丙烯酸十二氟庚酯、甲基丙烯酸甲酯和丙烯酸丁酯的共聚物乳液.红外光谱和核磁共振表征成膜后的共聚物组成和结构,结果显示随着混合单体中含氟丙烯酸酯质量分数的提高,共聚产物中氟含量也提高.X射线光电子能谱表征结果表明,在一定范围内,乳胶膜表面含氟量随含氟丙烯酸酯单体量的增加而增加,当甲基丙烯酸十二氟庚酯在单体中的质量分数超过20%,其量的继续增加不能引起乳胶膜表面氟含量的明显增大.乳胶膜表面水接触角的测定结果也具有同样的变化规律.含氟侧链在乳胶膜表面的富集,使得含少量氟丙烯酸酯共聚物就可提供织物良好的抗水抗油性能.     

壳聚糖-大豆分离蛋白共价复合物改性天然乳胶的研究

通过可控干热法制备壳聚糖和大豆分离蛋白共价复合物,并将其与天然乳胶共混制成共混膜。壳聚糖和大豆分离蛋白共混液与共价复合物的粒径分布对比可以验证共价复合物的形成。通过对复合物改性天然乳胶膜的表面形貌、力学性能及蛋白质溢出量等性能进行测试,结果发现膜表面光滑度、平整度、致密性和力学性能均有所改善,蛋白质溢出量降低,作为医用薄膜材料具有广泛的应用前景。     

聚苯酯对Ekonol/POM复合材料力学性能的影响

用转矩流变仪共混-模压成型方法制备了Ekonol / POM复合材料,在对复合材料的力学性能(含拉伸强度、弯曲强度、冲击强度、压缩强度和断裂强度)以及显微硬度进行测试的基础上,考察了聚苯酯的含量对于复合材料力学性能的影响.结果表明, Ekonol的最佳含量为20%(质量分数),此时,复合材料的压缩强度比POM提高42.4%,显微硬度提高24.7%.而其拉伸强度、弯曲强度、冲击强度和断裂强度有所降低,但并不妨碍其作为结构零件使用.     

超细羽绒粉体/天然橡胶共混膜的制备及力学性能研究

采用γ-巯基丙基三甲氧基硅烷(KH590)、苯基异氰酸酯(PI)和十八烷基异氰酸酯(ODI)对超细羽绒粉体进行表面疏水化改性,制备了不同羽绒粉体含量的超细羽绒粉体/天然橡胶弹性体共混膜.分析了粉体含量及不同改性剂对天然橡胶共混膜吸水性能和拉伸力学性能的影响.结果表明:粉体的添加提高了共混膜的吸水率,与未改性粉体相比,PI和0DI对粉体改性可降低共混膜的吸水率,并提高了共混膜的断裂强度和断裂伸长率.共混膜的弹性模量随粉体含量的影响较大.     

P(3,HB-co-4,HB)/PLA共混物的扩链改性研究

以异佛尔酮二异氰酸酯(IPDI)和亚磷酸三苯酯(TPP)为扩链剂,对聚(3–羟基丁酸酯–co–4–羟基丁酸酯)/聚乳酸[P(3,HB-co-4,HB)/(PLA)]共混物进行扩链改性.采用毛细管流变仪、电子万能试验机、差示扫描量热仪和扫描电子显微镜等研究两种扩链剂及用量对扩链前后共混物的流变性能、力学性能、结晶性能及断面形态的影响.结果表明:两种扩链剂均显著提高了共混物的熔体剪切黏度和两组分间的相容性,IPDI和TPP添加量分别为1.5份和1.0份时,改性效果最明显,共混物断裂伸长率及缺口冲击强度分别提高了34.5%、69.6%和89.6%、81.0%;IPDI扩链体系的拉伸强度提高8.3%,而TPP扩链体系的拉伸强度略有下降,表明IPDI扩链效果优于TPP.     

改性石墨烯/聚氨酯复合乳液的合成及性能表征

通过逐步聚合反应将改性氧化石墨烯(DIGN)接枝到水性聚氨酯(WPU)链段中,制备得到DIGN/WPU纳米复合乳液。通过IR、AFM、SEM对氧化石墨烯(GO)、DIGN、WPU及DIGN/WPU纳米复合材料的结构进行表征;并研究了DIGN用量对乳液粒径,流变性能及其胶膜的热稳定性和力学性能的影响。结果表明:DIGN的引入使得乳液具有了假塑性流体特性,并随DIGN含量的增加,乳液黏度,粒径及分布指数增大,纳米复合材料的热稳定性明显改善;当w(DIGN)=1wt%时,拉伸强度增加80.33%,杨氏模量提高192.11%,断裂伸长率下降了42.74%。     

甲基丙烯酸甲酯改性聚醚聚氨酯的结构形态与力学性能

采用同步法合成了聚氨酯(PU)/聚甲基丙烯酸甲酯(PMMA)的线型共混物、嵌段共聚物和互穿高聚物(IPN)。凭藉力学性能测试、电镜观察和动态力学谱分析,研究了光固化、热固化、化学组成、物理结构等因素对体系力学性能、结构形态和粘弹行为的影响。结果表明:PU/PMMA是呈两相结构的部分相容体系,其中线型共混物伸长率最大,IPN强度最高,而嵌段共聚物的力学性能较差。此外,嵌段共聚物和IPN光固化体系形成的相畴结构均一,其抗张强度和伸长率明显高于热固化体系。聚合物的力学性能除了受化学结构影响以外,还与化学组成有关,随体系中PMMA含量和PU中硬链段含量增加,聚合物抗张强度升高,伸长率下降。     

Preparation and Investigation on Novel Biodegradable Films Based on Konajac Glucomannan and Palmitoylated Konjac Glucomannan

Konjac glucomannan(KGM) has been generally used in food,film-former and biomedical applications,especially in the edible packing films due to its excellent film-forming ability,good biocompatibility and biodegrade-ability.It has the common flaws of natural polymers,such as low mechanical properties and poor antimicrobial activity,which severely limit their applications.In this paper,novel biodegradable films(NBF) of KGM with palmitoylated KGM(PKGM) were prepared by using the solventcasting technique.The structure,thermal and mechanical properties of the NBF were investigated.The results suggested that a strong hydrogen bonding was formed in NBF,which resulted in good miscibility between KGM and PKGM.The tensile strength and elongation at break of the NBF were enhanced significantly with the increase of PKGM in a certain range.With the addition of 0.75%PKGM by weight,tensile strength and elongation at break of NBF were improved largely to 117.12 MPa and 14.39%.From this work,we hope to provide one of the promising ways to design new edible food films and coatings materials with good mechanical properties.     

丝胶蛋白膜的制备及其物理性能

以环氧树脂作为交联剂制备具有一定力学性能的丝胶蛋白膜。用X-射线衍射法研究丝胶蛋白膜的聚集态结构；对丝胶蛋白膜的热水溶失率和力学性能进行测定；并探讨了交联剂种类、比例对丝胶蛋白膜性能和结构的影响。结果表明，交联剂对丝胶蛋白膜的交联作用明显，引起了丝胶结晶形态的变化；并改善了丝胶蛋白膜的物理性能，交联剂PEGO10加入30％左右所制得的丝胶蛋白膜拉伸断裂强度和断裂伸长率较好。     

碱浸处理对壳聚糖膜性质的影响

分别通过浇铸-蒸发法和浇铸-蒸发-碱浸法制备了壳聚糖膜,采用扫描电镜(SEM)、Fourier红外光谱(FT-IR)、X射线衍射(XRD)对膜的微观结构进行了表征,并分析了碱浸处理对膜的外观形貌、厚度、拉伸强度、断裂伸长率、可挥发物含量、接触角、水蒸气透过系数、总溶解物含量和溶胀指数等性质的影响.结果表明:碱浸处理将膜中的壳聚糖乙酸盐还原为壳聚糖,降低了膜中共价键的振动强度,但对膜的表面形貌没有影响.壳聚糖膜经过碱浸处理后,其厚度、可挥发物含量、总溶解物含量、溶胀性都减小,其接触角、拉伸强度、断裂伸长率都增大.碱浸法处理提高了壳聚糖膜的机械性能和防水性能.研究结果为经过碱浸处理的壳聚糖膜的实际应用提供了技术依据.     

大豆分离蛋白/二氧化硅改性水性聚氨酯膜性能的研究

采用溶胶-凝胶法制备了大豆分离蛋白/二氧化硅杂化溶胶,并应用于水性聚氨酯的改性.采用流延法制备大豆分离蛋白/二氧化硅/水性聚氨酯共混膜,红外光谱研究表明大豆分离蛋白、二氧化硅和水性聚氨酯间发生了多层次的氢键作用,以膜的拉伸强度、断裂伸长率和溶失率为指标,研究了各组分混配比例对共混膜力学性能及耐溶剂性能的影响.通过接触角、热重分析、扫描电镜和原子力显微镜分析讨论了共混膜的亲水亲油性、耐热性能,以及膜表面的形态形貌.结果表明,大豆分离蛋白/二氧化硅添加量为6％（质量分数）、两者之间质量比为1∶1时,改性膜的力学性能最优,耐溶剂性随添加量增加而改善.     

Preparation of high-strength Al-Mg-Si-Cu-Fe alloy via heat treatment and rolling

An Al-Mg-Si-Cu-Fe alloy was solid-solution treated at 560°C for 3 h and then cooled by water quenching or furnace cooling. The alloy samples which underwent cooling by these two methods were rolled at different temperatures. The microstructure and mechanical properties of the rolled alloys were investigated by optical microscopy, scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, and tensile testing. For the water-quenched alloys, the peak tensile strength and elongation occurred at a rolling temperature of 180°C. For the furnace-cooled alloys, the tensile strength decreased initially, until the rolling temperature of 420°C, and then increased; the elongation increased consistently with increasing rolling temperature. The effects of grain boundary hardening and dislocation hardening on the mechanical properties of these rolled alloys decreased with increases in rolling temperature. The mechanical properties of the 180°C rolling water-quenched alloy were also improved by the presence of β″ phase. Above 420°C, the effect of solid-solution hardening on the mechanical properties of the rolled alloys increased with increases in rolling temperature.     

柠檬酸基聚酯/聚乳酸共混物的力学性能

通过缩聚反应制备一种可生物降解的柠檬酸基聚酯（PEGCA）,采用转矩流变仪将不同反应程度的PEGCA与聚乳酸（PLA）共混,制备出一种可完全生物降解的柠檬酸基聚酯/聚乳酸共混物,考察了共混物的拉伸、冲击和弯曲性能,并采用扫描电子显微镜观察其形貌.结果表明：PEGCA对PLA的增韧效果明显,使得共混物的断裂伸长率可达316%,冲击强度提高了近7倍;在不同的应变速率下,PEGCA/PLA共混物的力学性能不同,增大应变速率,将使共混物的拉伸强度提高,断裂伸长率降低;不同反应程度的PEGCA在PLA基体中的分散性不同,低反应程度的PEGCA的分散性较差,其共混物在较高变形速率下表现出更优异的韧性和延展性.     

Influence of Dispersion of Nano-ZnO Particles in Polymer Matrices on Properties of Relevant Nano Composite Fibers

IntroductionIt is well knownthat nanoparticles have rich propertiesand are useful for functional composites . The nanometricsize ,leading to huge specific surface area up to or morethan1 000m2/g ,andtheir unique properties have attractedintensive interests . Thus many articles have elucidated thepreparation of polymer matrix nanocomposites( PMNC)[1 6]. Polymers are very i mportant matricesbecause of their flexibility and easy processing .Nanoparticles i mpart larger-size congeries because of…