熔焊工艺对自熔合金涂层组织的影响

利用显微镜和X射线衍射仪对感应熔焊、火焰喷焊、等离子堆焊Ni基自熔合金涂层的金相组织、结合面形态、涂层微区成分及焊层合金化学成分进行了分析。研究结果表明，感应熔焊涂层与基体界面出现了白亮带，焊层底部形成了明显的针条状组织，并且涂层中部w（Fe）整体高于粉末本身；火焰喷焊层得到均匀一致的奥氏体和碳化物共晶析出物，涂层与基体也属于冶金结合，扩散熔合区w（Cr）和w（Ni）较感应熔焊涂层的有所降低；等离子堆焊层在快速冷凝过程中生成了树枝状结晶组织，焊层中的C、B、Si、Cr等元素烧损率以等离子堆焊最大，火焰喷焊重熔次之，感应熔焊最小；感应熔焊对基体与涂层界面处Fe原子的激活度最大。     

钢液内气泡尾涡去除夹杂物的物理模拟

采用物理模拟方法,基于莫顿数相等及夹杂物运动行为相似准则,采用聚乙烯粒子模拟钢液中夹杂物,并采用高速摄像技术记录气泡及夹杂物颗粒的运动行为,分析了气泡尾涡对夹杂物去除的影响机理.实验结果表明:在气泡尾涡作用下,夹杂物运动轨迹表现为两种方式:一是夹杂物从气泡下端两侧向气泡尾涡靠近,随气泡上浮一段距离后上升速度变快,然后脱离气泡尾涡区;二是位于气泡上方的夹杂物,在不与气泡发生碰撞黏附的条件下,以回旋方式运动至气泡下方,然后在尾涡区内随气泡上浮,从而沿竖直方向以回旋方式上升.在相同上浮距离条件下,与小气泡相比,大气泡的尾涡去除夹杂物颗粒的效果更好.     

等离子喷焊耐磨涂层制备及性能分析

针对石油化工行业中关键零部件的磨损问题,采用等离子喷焊技术喷焊Fe基和Ni基自熔性合金粉末,获得超厚涂层,从而达到表面改性的目的.结果表明,采用该工艺制备的涂层与基体呈冶金结合,耐磨性能相较于基体金属分别提高约6倍和4倍,大大延长了零部件的使用寿命.进而对涂层的微观组织和耐磨机理进行了分析和研究,并且与氧乙炔火焰喷焊技术所制备的涂层进行了对比测试分析,结果表明,利用等离子喷焊技术所制备的超厚涂层耐磨性能更为出色.     

新型高铝铜合金喷焊层的组织与形成过程

利用等离子喷焊技术在45#钢表面制备新型高铝铜合金(Cu-14Al-X)喷焊层.采用光学显微镜、场发射扫描电镜(SEM)、电子探针显微分析仪(EPMA)、X射线衍射仪(XRD)研究喷焊层金相组织特征、宏观硬度和显微硬度、喷焊层与基体的结合特点以及喷焊层形成过程.结果表明,该合金粉末喷焊层的重熔过程具有快速凝固的特征.在重结晶过程中,富含Fe、Co等元素的高熔点、高硬度相首先析出,在喷焊层中形成硬质相,使得合金喷焊层的宏观硬度和显微硬度均较普通铜合金涂层高,宏观硬度高达261 HV,显微硬度高达424.2 HV.     

轧辊工作面的 WC 颗粒等离子弧喷焊

通过试验，确定了３５ＣｒＮｉ３Ｍ０Ｖ钢轧辊进行粉末等离子弧喷焊时，ＷＣ颗粒向喷焊层过渡的方式和粘接合金材料。提出了喷焊层内ＷＣ颗粒与作为粘接剂的镍基合金的合理比例，防止产生裂纹的工艺措施和最佳喷焊工艺参数。     

铝青铜合金粉末涂层制备中Fe元素的扩散特性

利用等离子喷焊和激光熔敷技术,将铝青铜合金粉末涂敷在45#钢表面,通过对涂层金相组织观察、界面金相观察、X-ray分析、表面EDS分析、对Fe元素的EPMA分析,研究Fe元素在铜合金涂层中的扩散特性.结果表明,采用等离子喷焊技术制备的涂层中,Fe元素从基材到合金涂层有较强烈持续的扩散过程;采用激光熔敷技术制备的涂层中,Fe元素在基体与合金涂层之间无明显的扩散现象.可见,Fe元素在等离子喷焊层中扩散率较高,在激光熔敷层中扩散率较低.     

细WC添加量对Ni基WC喷焊涂层性能的影响

采用金相显微镜和X射线衍射仪分析了氧乙炔火焰喷焊WC含量不同的Ni基WC涂层的显微组织和相结构,采用湿砂橡胶轮式磨粒磨损实验机对各涂层的抗磨粒磨损性能进行了比较研究,并采用扫描电镜观察了喷焊粉末的形貌和喷焊层的磨损形貌.结果表明,喷焊层的组织为在γ-Ni固溶体基体上弥散分布着细小的碳(硼)化物硬质相,这些细小的硬质相主...     

Al2O3-MxOy硬面陶瓷涂层的喷焊制备及性能研究

在碳钢母材上，用氧乙炔焰喷焊镍包铝合金粉末制取预涂层，喷焊50%Al2O3+50%Ni的复合粉末制取过渡层，用等离子喷焊Al2O3-MxOy复合粉末制取最终涂层。在质量分数为60%的硫酸与磷矿粉组成的混合介质（质量比为6∶4）中运转，所获得涂层的抗腐抗磨能力为18-8不锈钢的7.46倍，为德产316L不锈钢的4.06倍。     

超细碳化钨体积分数对喷焊层耐磨性的影响

为了获得质量较好的喷焊层,提高喷焊层的耐磨性,在镍基自熔性合金粉末F102中加入不同体积分数的亚微米碳化钨（WC）进行氧一乙炔火焰喷焊．通过磨粒磨损试验、显微硬度测试和显微组织分析,研究了不同WC体积分数对喷焊层质量及其耐磨性的影响．试验结果表明WC的体积分数为1％时,喷焊层的质量最优,耐磨性最好,硬度也最高．但随着WC体积分数的进一步增加,喷焊层的耐磨性和硬度反而有所下降．涂层的耐磨性主要与涂层硬度．WC硬相的含量,空洞的数量及大小等有关．硬度越高,WC硬相越多,空洞越少、越小,涂层的耐磨性越好,反之越差．     

金属材料内部非金属夹杂超声检测的数值模拟

在金属材料内部夹杂物的超声检测中,如何通过检测获得的回波信号辨识夹杂物的属性和位置,一直是其重点和难点问题.通过建立包含夹杂物缺陷的二维金属板模型,采用有限元数值模拟的方法,对材料内部超声波场进行计算,获得了两种最典型的夹杂物Al2O3和TiN,以及二者在材料内部不同深度时的超声回波信号.研究了夹杂物类型和夹杂物深度对超声回波时域波形以及对界面波、夹杂物缺陷回波和底面回波频谱分布的影响规律.     

TiC/Fe cermet coating by plasma cladding using asphalt as a carbonaceous precursor

A new Ti-Fe-C compound powder for plasma cladding was prepared by heating a mixture powder of ferrotitanium and asphalt pyro-lyzed as a carbonaceous precursor. The carbon by the pyrolysis of the asphalt acts as a reactive constituent as well as a binder in the compound powder. The TiC/Fe cermet coatings were prepared by plasma cladding with the compound powder. Results show that the Ti-Fe-C compound powder has a very tight structure, which can avoid the problem of the reactive constituent particles being separated during cladding. The TiC/Fe cermet coating presents a typical morphology of plasma cladding coatings with two different laminated layers: one is the composite layer in which the round fine TiC particles (<500 nm) are dispersed within a Fe matrix, the other is the paragentic layer of TiC and Ti2O3. The coating shows high hardness and excellent wear resistance. The surface hardness of the coating is 68 ± 5(HR30N). In the same fretting conditions, the wear area of Ni60 coating is about 11 times as much as the TiC/Fe cermet coating.     

室外涂料对山毛榉木材气体渗透性的影响

通过比较山毛榉木材在4种室外用涂料涂饰前和涂饰后的气体渗透能力,研究木材弦向和径向的气体渗透能力的变化.结果表明:漆膜可较好地保护木材免受空气和水的侵害,经4种涂料涂饰后,山毛榉木材的气体渗透值均有所下降;溶剂型涂料的气体渗透性能比水溶性涂料差,色漆比清漆更难渗透;山毛榉基材弦向的气体渗透能力在涂饰前和涂饰后均比径向略大.     

TiC/Fe cermet coating by plasma cladding using asphalt as carbonaceous precursor

A new Ti-Fe-C compound powder for plasma cladding was prepared by heating a mixture powder of ferrotitanium and asphalt pyrolyzed as carbonaceous precursor. The carbon by the pyrolysis of the asphalt acts as a reactive constituent as well as a binder in the compound powder. TiC/Fe cermet coatings were prepared by plasma cladding with the compound powder. Results show that the Ti-Fe-C compound powder has a very tight structure, which can avoid the problem that reactive constituent particles are separated during cladding. The TiC/Fe cermet coating presents a typical morphology of plasma cladding coatings with two different laminated layers: one is the composite layers in which the round fine TiC particles (<500nm) are dispersed within a Fe matrix, the other is the paragentic layers of TiC and Ti₂O₃. The coating shows high hardness and excellent wear resistance. The surface hardness of the coating is 68±5(HR30N). In the same fretting conditions, the wear area of Ni60 coating is about 11 times as much as the TiC/Fe cermet coating.     

TiC/Fe cermet coating by plasma cladding using asphalt as carbonaceous precursor

A new Ti-Fe-C compound powder for plasma cladding was prepared by heating a mixture powder of ferrotitaniurn and asphalt pyro- lyzed as a carbonaceous precursor. The carbon by the pyrolysis of the asphalt acts as a reactive constituent as well as a binder in the compound powder. The TiC/Fe cermet coatings were prepared by plasma cladding with the compound powder. Results show that the Ti-Fe-C compound powder has a very tight structure, which can avoid the problem of the reactive constituent particles being separated during cladding. The TiC/Fe cermet coating presents a typical morphology of plasma cladding coatings with two different laminated layers： one is the composite layer in which the round fine TiC particles （〈500 nm） are dispersed within a Fe matrix, the other is the paragentic layer of TiC and Ti2O3. The coating shows high hardness and excellent wear resistance. The surface hardness of the coating is 68 ± 5（HR30N）. In the same fretting conditions, the wear area of Ni60 coating is about Ⅱ times as much as the TiC/Fe cermet coating.     

金属颜料对保温涂料发射性和反射性的影响

论文基于高原、严寒及寒冷地区对外墙涂料光学性能的要求,研究涂料组分中各类金属颜料对其红外发射率及太阳能反射比的影响。研究结果表明：金属颜料能显著降低油性涂料的红外发射率;颜料种类、掺量及形貌对涂料的发射率有较大影响;铜粉对油性涂料发射率的降低效果最好;发射率随颜料掺量的增加而降低,在40%~50%范围内达到最低;同掺量下片状铜粉在油性涂层中的效果优于球状的;漂浮型铝颜料对油性涂料发射率的降低效果优于非漂浮型铝颜料。水溶性金属铝粉能显著降低水性涂料的红外发射率,红外发射率和太阳能反射比均随铝粉的粒径增大而下降。上述各类涂料涂层的红外发射率均可达到0.35~0.45、太阳能反射比0.39~0.56,基本符合采暖地区外墙涂料光学性能的要求。     

Ti-Ni-C系反应超音速火焰喷涂合成研究

以Ti粉、Ni粉和石墨为原料,制备了3种喷涂粉末,研究了制粒方式和粉末组成对超音速火焰合成金属陶瓷涂层组织的影响。结果表明,制粒方式在喷涂过程中对反应程度和涂层相组成起到关键的影响作用,聚乙烯醇(PVA)制粒比混合制粒更有利于喷涂过程中反应的进行,PVA制粒粉末喷涂涂层的相组成为TiC,Ni和少量Ti与Ni的氧化物,混合制粒粉末喷涂涂层中含有大量的氧化物相;超音速火焰喷涂合成过程中,粉末组分中一定量的Ti和Ni被氧化,增加Ni与C的含量对喷涂粉末的氧化有一定的抑制作用。     

化学沉积法制备Ni-P-SiC(C)复合镀层的研究

选择廉价的SiC和石C颗粒作为复合镀层添加物，用化学沉积法在碳钢表面制度Ni-P-SiC(C)复合镀层，研究了复合镀层的制备工艺，镀液配方以及复合镀层的性能等，结果显示：风表面开成的复合镀层厚薄均一，SiC和石墨C颗粒在镀层中分布均匀，镀层开成速度理想，表明本文采用的工艺技术合理可行，与单一的Ni-P镀层相比，Ni-P-SiC和Ni-P-C复镀层耐磨性能均有不同程度的提高，而将2种不同性能的SiC和C颗粒同时加入槽液，形成的Ni-P-SiC－C复合镀层具有最优异的耐磨性能。     

热喷涂用Ni60-B4C复合粉制备及涂层耐磨性的研究

采用高能球磨及化学镀镍技术来改善B4C颗粒的粒度、分布及其表面状态，制备了热喷涂用Ni60／（Ni／B4C）团聚粉和Ni60-B4C（包覆Ni）复合粉，采用亚音速热喷涂技术制备了其耐磨涂层，在自制的销盘式磨损试验机上进行涂层的磨粒磨损实验，结果表明：Ni60-B4C（包覆Ni）涂层与Ni60／（Ni／B4C）涂层相比更耐磨。     

氧化铈对NiCoCrAlY涂层抗热腐蚀性能的影响

为了研究纳米氧化铈对NiCoCrAlY涂层抗热腐蚀性能的影响,考察了添加3种不同含量纳米氧化铈的NiCoCrAlY熔覆涂层在1 050℃混合硫酸盐(质量分数为75％ Na2SO4-+25％ K2SO4)作用下的热腐蚀行为,并与未加纳米颗粒的涂层进行了比较.结果表明:添加纳米氧化铈后,涂层的抗热腐蚀性能得到了较大提高,其...     

铝合金表面ZSM-5型分子筛涂层耐蚀性研究

【目的】探究分子筛作为填料添加到水性涂料中对涂层防腐性能的影响。【方法】利用光学显微镜、XRD及SEM对涂层的中分子筛填料分散效果和涂层微观形貌进行表征,利用极化曲线分析分子筛水性涂层的电化学性能。【结果】分子筛粉末在水性漆中的最大添加比例为15%,超过此比例会出现大块团聚现象。其中10%的分子筛粉末对涂料耐蚀性提升最大。【结论】分子筛良好的高温水热稳定性有助于提高涂料的耐蚀性,但由于水性树脂不能够将分子筛颗粒紧密粘结,其添加量过大时会导致涂层耐蚀性能下降。