Bilirubin sensor based on CuO-CdO composites deposited in a nafion/glassy carbon electrode matrixes

Copper oxide-cadmium oxide nanocomposites(CuO-CdO NCs) were synthesized by solvothermal technique in a basic medium. CuO-CdO NCs were characterized using conventional techniques, such as Fourier Transform Infrared Spectroscopy(FTIR), UV–Visible Spectroscopy(UV/Vis), Field-Emission Scanning Electron Microscopy(FESEM), X-ray electron dispersive spectroscopy(XEDS), X-ray photoelectron spectroscopy(XPS), and powder X-ray diffraction(XRD). A selective and enzyme-less Bilirubin(BLR) sensor was developed with a thin-layer of NCs onto a glassy carbon electrode(GCE, surface area = 0.0316 cm~2) using 5% nafion binders at room conditions. Improved electrochemical performances of higher sensitivity, lower detection limit,linear dynamic range(LDR), and long-term stability of preferred BLR were achieved by a reliable currentvoltage(I-V) approach. The calibration curve was found linear(R~2= 0.9347) in a wide range of BLR concentration(10.0 pM ~ 10.0 mM). Based on the signal to noise ratio value of 3, the sensitivity and limit of detection(LOD) of the sensor were calculated as 95.0 pA μM~(-1) cm~(-2) and 1.0 ± 0.1 pM respectively.Solvothermally synthesized CuO-CdO NCs/GCE is an excellent advancement of developing a selective and sensitive BLR sensor by electrochemical approach and practically implemented in real sample applications.     

Corrosion study of resorbable Ca60Mg15Zn25 bulk metallic glasses in physiological fluids

The corrosion activity of amorphous plates of Ca_(60)Mg_(15)Zn_(25)alloy was investigated.The biocompatible elements were selected for the alloy composition.The electrochemical corrosion and immersion tests were carried out in a multi-electrolyte fluid and Ringer's solution.Better corrosion behavior was observed for the samples tested in a multi-electrolyte fluid despite the active dissolution of Ca and Mg in Ringer's solution.The experimental results indicated that reducing concentration of NaCl from 8.6 g/dm~3for Ringer's solution to 5.75 g/dm~3caused the decrease of the corrosion rate.The volume of the hydrogen evolved after 480 min in Ringer's solution(40.1 ml/cm~2)was higher in comparison with that obtained in a multi-electrolyte fluid(24.4 ml/cm~2).The values of opencircuit potential(E_(OCP))for the Ca_(60)Mg_(15)Zn_(25)glass after 1 h incubation in Ringer's solution and a multielectrolyte fluid were determined to be-1553 and-1536 m V vs.a saturated calomel electrode(SCE).The electrochemical measurements indicated a shift of the corrosion current density(j_(corr))from 1062μA/cm~2for the sample tested in Ringer's solution to 788μA/cm~2for the specimen immersed in a multi-electrolyte fluid.The corrosion products analysis was conducted by using the X-ray photoelectron spectroscopy(XPS).The corrosion products were identified to be CaCO_3,Mg(OH)_2,CaO,MgO and Zn O.The mechanism of corrosion process was proposed and described based on the microscopic observations.The X-ray diffraction and Fourier transform infrared spectroscopy(FTIR)also indicated that Ca(OH)_2,CaCO_3,Zn(OH)_2and Ca(Zn(OH)_3)_2·2H_2O mainly formed on the surface of the studied alloy.     

Sonochemical synthesis of nanostructured nickel hydroxide as an electrode material for improved electrochemical energy storage application

A facile and fast approach for the synthesis of a nanostructured nickel hydroxide(Ni(OH)_2) via sonochemical technique is reported in the present study. The X-ray diffraction results confirmed that the synthesized Ni(OH)_2 was oriented in β-phase of hexagonal brucite structure. The nanostructured Ni(OH)_2 electrode exhibited the maximum specific capacitance of 1256 F/g at a current density of 200 mA/g in 1 M KOH_((aq)). Ni(OH)_2 electrodes exhibited the pseudocapacitive behavior due to the presence of redox reaction. It also exhibited long-term cyclic stability of 85% after 2000 cycles, suggesting that the nanostructured Ni(OH)_2 electrode will play a promising role for high performance supercapacitor application.     

Activated carbon derived from rice husk by NaOH activation and its application in supercapacitor

Four activated carbon(AC) samples prepared from rice husk under different activation temperatures have been characterized by N2adsorption–desorption isotherms, thermogravimetric analysis(TGA–DTA), Fourier transform infrared spectroscopy(FTIR) and scanning electron microscopy(SEM). The specific surface area of AC sample reached 2681 m2 g 1under activation temperature of 800 1C. The AC samples were then tested as electrode material; the specific capacitance of the as-prepared activated carbon electrode was found to be 172.3 F g 1using cyclic voltammetry at a scan rate of 5 mV s 1and 198.4 F g 1at current density 1000 mA g 1in the charge/discharge mode.& 2014 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.     

Microstructure and growth kinetics of Ce and Y jointly modified silicide coatings for Nb–Ti–Si based ultrahigh temperature alloy

In order to protect Nb-Ti-Si based ultrahigh temperature alloy from oxidation, pack cementation processes were utilized to prepare Ce and Y jointly modified silicide coatings. The Ce and Y jointly modified silicide coating has a double-layer structure: a relatively thick (Nb, X)Si2 (X represents Ti, Cr and Hf elements) outer layer and a thin (Ti, Nb)5Si4 transitional layer. The pack cementation experiments at 1150 ℃ for 8 h proved that the addition of certain amounts of CeO2 and Y2O3 powders in the packs distinctly influenced the coating thickness, the contents of Si, Ce and Y in the (Nb, X)Si2 outer layers, and the density of cavities in the coatings. In order to study the effects of Ce and Y joint modification in the silicide coatings, both only Ce and only Y modified silicide coatings were also prepared for comparison. The mechanisms of the beneficial effects of Ce and Y are discussed. A pack mixture containing 1.5CeO2-0.75Y2O3 (wt%) powders was employed to investigate the growth kinetics of the Ce and Y jointly modified silicide coating at 1050, 1150 and 1250 ℃. It has been found that the growth kinetics obeyed parabolic laws and the parabolic rate constants were 109.20 mm2/h at 1050 ℃, 366.75 mm2/h at 1150 ℃ and 569.78 mm2/h at 1250 ℃, and the activation energy for the growth of the Ce and Y jointly modified silicide coating was 197.53 kJ/mol.     

Structure and properties of solid-state synthesiz ed poly (3,4-propylenedi oxythiophene) /nano-ZnO composite

Poly（3,4-propylenedioxythiophene）/nano-Zinic Oxide（PProDOT/ZnO） composites with the content of 3-7 wt%nano-ZnO were synthesized by the solid-state method with FeCl₃ as oxidant.The structure and morphology of the composites were characterized by Fourier transform infrared（FTIR）spectroscopy,ultraviolet-visible（UV-vis） absorption spectroscopy,X-ray diffraction（XRD） and transmission electron microscopy（TEM）.The electrochemical performances of the composites were investigated by galvanostatic charge-discharge,cyclic voltammetry and electrochemical impedance spectroscopy（EIS）.The photocatalytic activities of the composites were investigated by the degradation of methylene blue（MB） dyes in aqueous medium under UV light irradiation.The results from FTIR and UV-vis spectra showed that the PProDOT/ZnO composites were successfully synthesized by solid-state method,and nano-ZnO had great influences on the conjugation length and oxidation degree of the polymers.Furthermore,the PProDOT/5 wt%ZnO had the highest conjugation and oxidation degree among the composites.The results of XRD analysis indicated that there were some FeCl₄^- ions as doping agent in the PProDOT matrix,and the content of ZnO had no effect on diffraction pattern of PProDOT.Morphological studies revealed that the pure PProDOT and composites had similar morphological structure,and all the composites displayed an irregular sponge like morphology.The results of electrochemical tests showed that the PProDOT/5 wt%ZnO had a higher electrochemical activity with a specific capacitance value of 220 F g^-1 than others.The results from photocatalytic activities of the composites indicated that the PProDOT/5 wt%ZnO had better photocatalytic activity than other composites.     

Electroch emical properties and interfacial reactions of LiNi0.5Mn1.5O4-δ nanorods

LiNi0.5Mn1.5O4-δ which possesses a high voltage of 4.7 V vs.Li+/Li and stable structure has been considered as a promising cathode material for high energy Li-ion batteries.In this study,well-crystalli...     

Microstructure, mechanical and thermo-physical properties of hot-pressed Al2O3-GdAlO3-ZrO2 ceramics with eutectic composition

A low cost chemical co-precipitation method was employed to fabricate nanoscale Al_2O_3-GdAlO_3-ZrO_2 powder with eutectic composition. A careful control of reaction conditions was required during the preparation. The synthesized nanopowders exhibited a particle size of 20-200 nm, and were highly dispersive and uniform. The results showed that calcination temperature had an important influence on the phase constituents of the nanopowders. With increasing the calcination temperature, a phase transformation from θ-Al_2O_3 to α-Al_2O_3 and a thermal decomposition from Gd_3 Al_5O_(12)(GdAG) to GdAlO_3 and α-Al_2O_3 occurred in sequence. A calcination temperature of 1300 ℃ was needed for the crystallization of α-Al_2 O_3. These nanosized powders were consolidated via hot pressing to produce a fully densified ceramic composite with eutectic composition. The Al_2O_3-GdAlO_3-ZrO_2 ceramic hot-pressed at 1500 ℃ exhibited a relative density of 99.4%, a flexural strength of 485 MPa and a fracture toughness of 6.5 MPa m~(1/2). The ceramic had a thermal conductivity of 1.9 W m K~(-1) at 1200 ℃ and a thermal expansion coefficient of 9.49 ×10~(-6) K~(-1) at 1100 ℃.     

In-situ secondary growth of nanocube-based Prussian-blue film as an ultrasensitive biosensor

A regular nanostructure has been widely confirmed to result ina marked improvement in material performance in biosensing applications.In the present study,a regular nanostructured Prussian blue(PB) film with two heterogeneous crystal layers was synthesized in-situ using a secondary growth method.A PB seed layer was first controlled to form uniform cube-like crystal nuclei through an ultrasonic reaction with a single reactant.Then,well-defined 100 nm PB nanocubes were further crystallized on this seed layer using a self-assembly approach.In order to accelerate the electron transfer rate during the enzyme reaction for glucose detection,the graphene was used as the main cross-linker to immobilize glucose oxidase on the PB film.The as-prepared biosensor exhibited high electrocatalysis and electron conductivity for the detection of trace glucose with a sensitivity of141.5 μA mM~(-1) cm~(-2),as well as excellent anti-interference ability in the presence of ascorbic acid and uric acid under a low operation potential of-0.05 V.     

Synthesis of dental resins using diatomite and nano-sized SiO2 and TiO2

The mechanical properties of dental composites were improved by porous diatomite and nano-sized silica (OX-50) used as co-fillers.The resin composites,filled with silanized OX-50 and silanized diatomit...     

A facile and green preparation of durian shell-derived carbon electrodes for electrochemical double-layer capacitors

A facile and green preparation of high surface area activated carbons with mixed microporosity and mesoporosity from durian shell waste is reported in this work. The pore structure and surface chemistry of the parent carbon were modified by the combination of ultrasonication and microwave irradiation techniques. The effects of temperature and time in the ultrasonication treatment and power output and time in the microwave irradiation were studied. The electrochemical performance of carbon electrodes for supercapacitors was tested by cyclic voltammeter (CV) and galvanostatic charge–discharge. The results show that the capacitive energy storage of electrodes is critically dependent on the microporosity and surface chemistry of activated carbons. The highest electrode capacitance in this work was 103.6 F/g that prepared from activated carbon modified at an ultrasonication temperature of 323.15 K for 10 min and microwave power output of 900 W for 10 min.     

Phase stability and thermal conductivity of ytterbia and yttria co-doped zirconia

Rare earth oxides doping has been extensively investigated as one of the effective methods to lower thermal conductivity of 4.55 mol% Y2O3stabilized ZrO2(YSZ) thermal barrier coatings(TBCs).In the present work,5–6 mol% Yb2O3and Y2O3co-doped ZrO2ceramics were synthesized by solid reaction sintering at 1600 1C.The phase stability of the samples after heat treatment at 1500 1C was investigated.Yb2O3and Y2O3co-doped zirconia,especially when Yb2O3/Y2O3≥1,contained less monoclinic phase than single Yb2O3or Y2O3phase doped zirconia,indicating that co-doped zirconia was more stable at high temperature than YSZ.The thermal conductivity of the 3 mol% Yb2O3+3 mol% Y2O3co-doped ZrO2was 1.8 W m 1K 1at 1000 1C,which was more than 20% lower than that of YSZ.     

La2O3–Al2O3 –SiO2 glass-infiltrated 3Y-TZP all-ceramic composite for the dental restora tive application

The 3 mol% yttria stabilized tetragonal zirconia polycrystals (3Y-TZP) powder had three particle size distributions, while the fine one was lower than 100 nm. The 3Y-TZP compact was prepared by dry-pressing under pressures ranged from 10 to 30 MPa and then presintered at 1250°C for 2 h. The matrix dry-pressed under the pressure of 20 MPa had a porosity of 16.7% and could be easily processed by computer aided design and computer aided manufacturing (CAD/CAM), and which had been infiltrated by the La2O3–Al2O3–SiO2 glass at 1200°C for 4 h. The flexural strength and fracture toughness of the composite were 710.7 MPa and 6.51 MPa m^1/2, respectively. The low shrinkage (0.3%) of the composite can satisfy the net-shape fabrication standard. XRD results illustrated that zirconia in the La2O3–Al2O3–SiO2 glass-infiltrated 3Y-TZP all-ceramic composite was mainly in the tetragonal phase. SEM and EDS results indicated that the pores of the matrix were almost filled by the La2O3–Al2O3 –SiO2 glass     

The enhanced corrosion resistance of UMAO coatings on Mg by silane treatment

The surface silanization was carried out on ultrasonic micro-arc oxidation(UMAO) coatings on pure magnesium using KH550 as silane coupling agent(SCA). The surface morphology, chemical bonds and corrosion resistance of the silane films were investigated by scanning electron microscope(SEM), Fourier transform infrared spectroscopy(FTIR) and electrochemical workstation, respectively. The results showed that hybrid coatings were successfully prepared on pure magnesium by UMAO-Na OH(1 mol/L, 2 mol/L, 3 mol/L)-SCA processing. The organic films with Si–O–Mg bonds are helpful for the reduction of the pores in UMAO coatings. The pores decreased with increasing Na OH concentration. Compared with single UMAO treatment, the corrosion potentials(Ecorr) of magnesium plates with UMAO-Na OH(1 mol/L,2 mol/L, 3 mol/L)-SCA treatment increased by 29 m V, 53 m V and 75 m V, respectively, meanwhile the corrosion current density(Icorr) reduced one to two orders of magnitude. It indicated that the corrosion resistance of the coatings was improved by silane treatment.     

Addition of IrO2 to RuO2+TiO2 coated anodes and its effect on electrochemical performance of anodes in acid media

Ternary mixed metal oxide coatings with the nominal composition IrxRu(0.6-x)Ti0.4O2(x=0, 0.1, 0.2, 0.3) on the titanium substrate were prepared by thermal decomposition of a chloride precursor mixture. Surface morphology and microstructure of the coatings were investigated by Scanning electron microscopy(SEM), Field emission scanning electron microscopy(FE-SEM) and X-ray diffraction(XRD) analysis. Systematic study of electrochemical properties of these coatings was performed by cyclic voltammetry(CV) and polarization measurements. The corrosion behavior of the coatings was evaluated under accelerated conditions(j=2 A cm-2) in acidic electrolyte. The role of iridium oxide admixture in the change of electrocatalytic activity and stability of Ru0.6Ti0.4O2coating was discussed. Small addition of IrO2can improve the stability of the RuO2+TiO2mixed oxide, while the electrocatalytic activity for oxygen evolution reaction(OER) is decreased. The shift of redox potentials for Ru0.6Ti0.4O2electrode that is slightly activated with IrO2and improvement in the stability can be attributed to the synergetic effect of mixed oxide formation.     

Oxygen-rich carbon-nitrogen quantum dots as cocatalysts for enhanced photocatalytic H2 production activity of TiO2 nanofibers

We developed an one-step hydrothermal method to synthesize carbon-nitrogen quantum dots(CNQDs) with oxygen-rich functional groups.The sample was characterized by TEM,AFM,FT-IR,XPS,UV-vis absorption and PL spectra.The 0/C and N/C atomic ratio of typical CNQDs with diameters of 3-6 nm are ca.0.4 and 0.2,respectively.Without noble metal cocatalyst,the photocatalytic H_2 production rate of CNQDs/TiO_2 nanofibers(NFs)(112.4 μmol h~(-1) g~(-1)) is 1.8 times higher than that of TiO_2 NFs.The good absorption of light contributes to the enhanced photocatalytic H_2 performance.The CNQDs could be promising in biomedical imaging,optical data recording storage and photo/electrocatalysis,etc.     

Fabrication of fine spongy nanoporous Ag-Au alloys with improved catalysis properties

Fine NP-AgAu(nanoporous AgAu) alloys with spongy structure was fabricated by chemical dealloying from rapidly solidified amorphous precursors Ag_(38.75-x)Cu_(38.75)Si_(22.5)Au_x(x=0, 0.5, 1 and 5). The results indicate that the addition of small content Au in precursor can refine both the ligaments and pores obviously. Among the present components of the precursors, NP-AgAu alloys dealloying from Ag_(37.75)Cu_(38.75)Si_(22.5)Au_1 had the finest spongy structure. The size of pores was 5–10 nm and the grain size of ligaments was 10–20 nm. It also had the highest surface area of 106.83 m~2g~(-1) and the best catalytic activity towards electro-oxidation of formaldehyde with the peak current of 665 mA mg~(-1).     

Properties of garnet-type Li6La3ZrTaO12 solid electrolyte films fabricated by aerosol deposition method

The garnet-type Li_6La_3ZrTaO_(12)(LLZT) solid electrolyte films were fabricated by aerosol deposition(AD)method.Ball-milled LLZT powder with a cubic garnet structure and a particle size of 1-2 urn was used as raw material and deposited directly on a SUS316L or a glass substrate via impact consolidation.As-deposited LLZT film has a cubic garnet structure but contains Li_2CO_3 and La_2Zr_2O_7 phases.SEM observation revealed that the film consists of LLZT particles fractured into submicron size.The impurity phase formation during AD process was caused by the local heating by the collision between LLZT particles and deposition surface and reaction with CO_2.The Li~+ ion conductivity of LLZT film was estimated to be 0.24 × 10~(-5)S cm~(-1) at room temperature.Electronic conductivity of LLZT film was confirmed to be around 10~(-12) S cm~(-1),indicating the dominant Li~+ ion conduction of LLZT film.     

Effect of La0.8Sr0.2Co0.2Fe0.8O3-δ morphology on the performance of composite cathodes

In the present work,one dimensional La0.8Sr0.2Co0.2Fe0.8O3 δ(LSCF) nanofibers with the mean diameter of about 100 nm prepared by electrospinning were deposited on Gd0.2Ce0.8O1.9(GDC) electrolyte followed by sintering to form one dimensional LSCF nanofiber cathode. And LSCF/GDC composite cathodes were formed by introducing GDC phases into LSCF nanofiber scaffold using infiltration method. The polarization resistances for the composite cathode with an optimal LSCF/GDC mass ratio of 1/0.56 are 0.27,0.14 and 0.07 Ω cm2at 650,700 and750 1C,respectively,which are obviously smaller than 2.26,0.78 and 0.29 Ω cm2of pure LSCF nanofiber cathode. And the activation energy is1.194 eV,which is much lower than that of pure LSCF nanofiber cathode(1.684 eV). These results demonstrate that the infiltration of GDC into LSCF nanofiber scaffold is an effective approach to achieve high performance cathode for solid oxide fuel cells(SOFCs). In addition,the performance of composite cathode in this work was also compared with that of our previous nanorod structured LSCF/GDC composite cathode.     

Preparation of Cu（In,Ga）Se2 thin film by sputtering from Cu（In,Ga）Se2 quaternary target

Cu(In,Ga)Se2 (CIGS) thin films were prepared by directly sputtering Cu(In,Ga)Se2 quaternary target consisting of Cu:In:Ga:Se 25:17.5:7.5:50 at%. The composition and structure of CIGS layers have been investigated after annealing at 550 ℃ under vacuum and a Se-containing atmosphere. The results show that recrystallization of the CIGS thin film occurs and a chalcopyrite structure with a preferred orientation in the (112) direction was obtained. The CIGS thin film annealed under vacuum exhibits a loss of a portion of Se, while the film annealed under Se-containing atmosphere reveals compensation of Se. Several solar cells with three different absorber thicknesses were fabricated using a soda lime glass/Mo/CIGS/CdS/i-ZnO/ZnO:Al/Al grid stack structure. The highest conversion efficiency of 9.65% with an open circuit voltage of 452.42 mV, short circuit current density of 32.16 mA cm2 and fill factor of 66.32% was obtained on a 0.755 cm2 cell area.