以聚合物／硅藻土为控释材料的阿维菌素颗粒剂的制备及其性能研究

以聚合物/硅藻土复合材料为缓释剂,阿维菌素(Avermectin)为模型药物,采用转动包衣法制备了阿维菌素控释颗粒剂,应用红外光谱及扫描电镜分别对颗粒剂及复合控释材料的表面结构进行了表征,同时,利用体外释放实验测定了控释颗粒剂的释药特性,并用其进行了防治胡椒根结线虫的田间药效试验.结果表明:复合控释材料较单一硅藻土的表面结构致密,粒间堆积紧凑,孔隙量少,且与有效成分阿维菌素之间无化学键合,为物理包膜吸附作用.控释颗粒剂释药机理不属化学反应型释放,初步确定为Super Case Ⅱ型传递机理.该颗粒剂对胡椒根结线虫具有较好的防治效果,用量为75 kg·hm -2时,药后60 d,防效能保持在95%以上.     

不同药剂处理对地黄胞囊线虫病的防效研究

在室内盆栽实验和田间实验条件下研究了10％噻唑磷颗粒剂、5亿孢子/g淡紫拟青霉粉剂、5％特丁磷颗粒剂、1．8％阿维菌素乳油、3％氯唑磷颗粒剂5种杀线虫剂及其不同施用剂量对地黄胞囊线虫病的防治效果．结果表明,室内盆栽条件下5种药剂的不同施药剂量对地黄胞囊线虫病防治效果存在显著差异;田间实验条件下,10％噻唑磷颗粒剂40kg／hm2,5亿孢子／g淡紫拟青霉粉剂50kg／hm2和3％氯唑磷颗粒剂50kg／hm。施用30d后,土壤中胞囊线虫虫口减退率达65％以上;施用药剂150d后,5亿孢子版淡紫拟青霉粉剂50kg／hm^2时防效最好,达67．95％;其次为施用10％噻唑磷颗粒剂40kg／hm^2,防效达61．00％,满足地黄的GAP栽培要求,显示出较好的应用前景．     

共和县绵羊肺线虫病的调查

对20副共和县屠宰绵羊的肺脏进行了肺线虫检查，结果：共检出肺线虫79条，其中丝状网尾线虫64条，舒氏歧线虫15条，总体感染率为20％。     

新疆甘薯茎线虫生物学特性的初步研究

对新疆甘薯茎线虫的生物学特性进行了初步研究，结果表明：甘薯茎线虫在30℃存活率为98％，完全致死温度为45℃。对盐、酸碱的适应性较广，0．2％-3．5％NaCl溶液中其均有存活，1．6％浓度时其存活率迅速下降，浓度高于3．5％时基本不能存活；低盐、酸性环境较有利于甘薯茎线虫的生活，最适pH为7．2。     

克线丹颗粒剂对甘薯茎线虫病的防治效果

试验研究了室内、室外不同剂量的克线丹颗粒剂对甘薯茎线虫病的防治效果。室内试验结果表明:各处理中以药土比1∶1200处理防治效果最佳,对甘薯茎线虫的致死率最高,校正死亡率达100%;田间试验结果表明:各处理中以45.0 kg/hm2和37.5 kg/hm2克线丹颗粒剂对甘薯茎线虫病的防治效果最佳,防治效果分别达到了97.68%和91.64%。     

蜡样芽胞杆菌BCJB01粉剂防治番茄根结线虫的研究

为提高蜡样芽胞杆菌BCJB01粉剂对蔬菜根结线虫病的田间防治效果,采用添加营养基质、有机肥等方式,进行了蜡样芽胞杆菌BCJB01防治番茄根结线虫病的田间技术研究。结果表明,在整地时同时添加有机肥和营养基质的处理对番茄根结线虫的防治效果最好,防效为77.45%,优于对照药剂10%噻唑膦颗粒剂对番茄根结线虫的防治效果。     

植物颗粒剂对蜗牛和蛞蝓诱杀作用初报

利用药用植物的粉碎物配合对蜗牛和蛞蝓有引诱作用的食物引诱素及成型剂等原料制成的植物颗粒剂在室内和菜地进行诱杀实验，结果表明：植物颗粒剂对蜗牛和蛞蝓都有较强的诱杀效果，防效分别达到83．4％和67．8％，显示了一定的实用性。植物颗粒杀虫剂对环境无污染，对人畜及害虫天敌无毒害，是一种新型的低毒植物源农药。     

保护地蔬菜根结线虫的综合防治

近年来根结线虫在保护地蔬菜栽培中发生较为严重，主要为害黄瓜、丝瓜、苦瓜、葫芦、甜瓜、番茄、茄子、菜豆、芹菜、白菜等20多种蔬菜。随着保护地蔬菜栽培面积迅速扩大，特别是随着连作栽培时间的延长．根系自毒产物增多，抵抗力下降，为根结线虫侵染提供了更为适宜的条件，使根结线虫的为害成为生产上的突出问题。产量损失一般达30％～50％，严重的达50％以上。     

长沙多索线虫生物学特性的研究

１９９３～１９９４年对寄生于稻飞虱的长沙多索线虫在湖北省的分布进行了调查，结果表明所调查到稻田均有分布，其宿主有褐飞虱等４种，寄生率为６３％～９２．５％，线虫在田间呈聚群分布，土壤含水量低于１５％的时致死。     

丙烯酸树脂在药物制剂中的研究进展

药用丙烯酸树脂是一种新型药用辅料，具有安全、稳定、无刺激、高效等特点，主要用于片剂、丸剂、颗粒剂的薄膜包衣及载体，能够达到防潮、避光、掩盖气味及延缓药物释放的效果，能够提高患者依从性和药物稳定性而广泛应用于药物制剂中.现针对丙烯酸树脂在药物制剂方面的应用研究进展进行总结，以期为今后丙烯酸树脂在药物制剂领域的发展提供一定的参考.     

可食性壳聚糖复合涂膜包装对鲜切莲藕保鲜效果的影响

采用不同质量浓度壳聚糖（0.5％、1.0％、2.0％）分别添加0.5％淀粉、1.0％氯化钙（CaC12）和1.0％抗坏血酸（AsA）作为涂膜剂,在（4±0.5）℃保存条件下对鲜切莲藕进行涂膜处理,测定鲜切莲藕贮藏过程中失重率和腐烂率、总糖含量、维生素C、褐变强度（BD）、多酚氧化酶（PPO）活性等的变化.结果表明：壳聚糖涂膜处理可有效降低鲜切莲藕的水分、维生素C等成分的损失,延缓鲜切莲藕褐变的发生,从而延长鲜切莲藕的货架期,且2.0％壳聚耱涂膜处理对鲜切莲藕具有良好的保鲜效果.     

Microstructure and wear behavior of Mo–60Si–5B coating doped with 0.5 ​at% La by spark plasma sintering

Mo–60Si–5B coating doped with 0.5 ?at% La was prepared on niobium silicon based alloy by spark plasma sintering. The microstructure and wear behavior of the 0.5La–Mo–60Si–5B (0.5La-MSB) coating were investigated. The results show that the mean grain sizes of the Mo–60Si–5B (0La-MSB) and 0.5La-MSB coatings are calculated to be 3.27 ?μm and 2.85 ?μm, respectively. The addition of La plays a role of refining the grains of 0.5La-MSB coating. The specific wear rate of 0.5La-MSB coating is decreased by up to 26.8% at the oscillation frequency of 20 ?Hz and the sliding load of 11 ?N compared to 0La-MSB coating. The anti-friction performance of Mo–60Si–5B coating is modified by the addition of 0.5 ?at.% La. The improvement of anti-friction performance of the Mo–60Si–5B coating is due to the increased hardness and the provided lubrication function by La₂O₃.     

农药对美洲斑潜蝇Liriomyza sativae的毒力和美洲斑潜蝇抗药性测定

有机磷类农药乐斯本,沙蚕毒素类农药杀虫双和阿维菌素类农药阿巴丁、害极灭、杀虫素对美洲斑潜蝇Liriomyza sativae实验种群成虫和1—2龄幼虫的LC_(50)分别为:成虫48.68,20.97,4.27,1.40和0.63ppm;幼虫70.94,30.42,2.21,2.91和2.08ppm。阿维菌素类农药对美洲斑潜蝇成虫和幼虫均具有较强的毒性.通过比较测定美洲斑潜蝇敏感种群和自然种群幼虫对农药敏感性的差异,得出美洲斑潜蝇对乐斯本的抗性已达到低抗性水平,抗性倍数为9.6倍;而对阿维菌素类农药处于敏感水平.     

Diffusion mechanism in molten salt baths during the production of carbide coatings via thermal reactive diffusion

The diffusion mechanism of carbide-forming elements from a molten salt bath to a substrate surface was studied in this research, with particular focus on the processes occurring in the molten bath at the time of coating. Metal, oxide, and metal-oxide baths were investigated, and the coating process was performed on H13 steel substrates. Scanning electron microscopy and electron-probe microanalysis were used to study the coated samples and the quenched salt bath. The thickness of the carbide coating layer was 6.5 ±0.5, 5.2 ±0.5, or 5.7 ±0.5 μm depending on whether it was deposited in a metal, oxide, or metal-oxide bath, respectively. The phase distribution of vanadium-rich regions was 63%, 57%, and 74% of the total coating deposited in metal, oxide, and metal-oxide baths, respectively. The results obtained using the metal bath indicated that undissolved suspended metal particles deposited onto the substrate surface. Then, carbon subsequently diffused to the substrate surface and reacted with the metal particles to form the carbides. In the oxide bath, oxide powders dissolved in the bath with or without binding to the oxidative structure (Na₂O) of borax; they were then reduced by aluminum and converted into metal particles. We concluded that, in the metal and oxide baths, the deposition of metal particles onto the sample surface is an important step in the formation of the coating.     

可光热除冰的纳米碳管/环氧树脂复合涂层的制备及防腐性能研究

针对民航飞机在高空、寒冷区域飞行时存在的结冰问题,以环氧树脂中掺杂一定含量的碳纳米管制备复合材料涂层,优化提升民航飞机的除冰性能,同时对改善民航飞机机翼蒙皮的防腐性能展开研究。测试表明碳纳米管含量为0.5%时复合材料光热性能更好,温度上升明显。光热循环稳定性测试表明,碳纳米管含量为0.5%时,在150mW/cm2的光照下该复合涂层具有光热稳定性能;自愈性能分析测试得知,在表面受到一定程度的破坏后,该复合涂层能通过加温的方式实现自愈合;电化学工作站测试极化曲线分析中,碳纳米管含量为0.5%的复合涂层腐蚀电位最大为-1.510V,表明其腐蚀速率最低;在静态全浸测试中,碳纳米管含量为0.5%的复合涂层质量减少最小,表明其防腐蚀性能更好。     

消失模铸造水基涂料的研制

涂料是消失模铸造最关键的辅助材料之一。为降低消失模铸造涂料的成本，研制了水基消失模涂料。文中采用石英粉为耐火骨料，石英粉共有3种粒度分布。所有涂料用碾轮式混砂机制成膏状涂料，在搅拌机中加入适量水搅拌成液体涂料，然后测其性能。研制出的涂料，配方为：石英粉100％，膨润土4％，白乳胶2．5％，羧甲基纤维素钠（CMC）0．5％，以及其它附加物，其中石英粉要求粒度分布相对集中。该涂料成本低且具有优良的工艺性能，特别适用于球墨铸铁件的消失模铸造生产。     

医用可降解Mg-3Zn-0.5Sr合金耐蚀性及细胞毒性

采用仿生法在Mg-3Zn-0.5Sr合金表面制备涂层,通过SEM,EDS和XRD分析表征涂层形貌和结构;采用电化学实验和浸泡腐蚀实验来研究涂层对合金降解速率的影响;采用生物毒性实验验证有无涂层Mg-3Zn-0.5Sr合金的毒性等级.实验结果表明:在Mg-3Zn-0.5Sr合金表面可以沉积致密的羟基磷灰石(HA)涂层,厚度约为30~40μm,HA涂层可以有效地降低Mg合金的降解速率;在体积分数为25%的有无涂层合金浸提液中培养细胞4d,细胞相对增值率均超过100%,有无涂层合金的细胞毒性均为0级.     

地热水管道防腐涂层的研究

地热水防腐涂层的耐温性和耐水性,利用高硅含量成膜物并配合颜填料,制备了一种常温固化涂料。通过对涂层的综合性能测试,确定涂料的优化配方为（质量分数）：环氧改性有机硅树脂SMH-30 50%～60%、云母氧化铁灰 22%～30%、绢云母 9%～14%、固化剂 4.5%～6%、分散剂0.2%～0.5%、消泡剂0.1%～0.4%;热重-差示扫描分析涂层的分解温度为216.4℃;全反射红外光谱分析结果显示,涂层在120℃ 的腐蚀模拟液中性能稳定;在质量分数为35%的氯化钠溶液中浸泡30d后,涂层的交流阻抗值在10⁸Ω/cm²以上,表明涂层具有良好耐腐蚀性能。     

Microstructure and Corrosion Resistance of Cr7C3/γ-Fe Ceramal Composite Coating Fabricated by Plasma Cladding

A new type in situ Cr7C3/γ-Fe ceramal composite coating was fabricated on substrate of hardened and tempered grade C steel by plasma cladding with Fe-Cr-C alloy powders. The ceramal composite coating has a rapidly solidified microstructure consisting of primary Cr7C3/γ- and the Cr7C3/γ-Fe eutectics, and is metallurgically bonded to the degree C steel substrate. The corrosion resistances of the coating in water solutions of 0.5 mol/L H2SO4 and 3.5% NaCl were evaluated utilizing the electrochemical polarization corrosion-test method. Because of the inherent excellent corrosion-resisting properties of the constituting phase and the rapidly solidified homogeneous microstructure, the plasma clad ceramal composite coating exhibits excellent corrosion resistance in the water solutions of 0.5 mol/L H2SO4 and 3.5% NaCl.     

交联壳聚糖膜制备及对酸性大红染料吸附作用

以采用流延法制备得到的交联壳聚糖膜作为吸附剂,对酸性大红染料废水进行吸附脱色处理,考察了吸附时间、pH值、吸附剂投加量和酸性大红起始浓度等对吸附脱色效果的影响。在吸附时间为60min,pH值为4．5,1L废水中壳聚糖投加量为1．25g时,交联壳聚糖膜对酸性大红的脱色效果良好,吸附率可达95．46％。对实验数据运用相关数学模型拟合,结果表明,该等温吸附平衡同时符合Freundlich或Langmuir模型,线性相关回归系数较好（R^2均高于0．98）;吸附过程动力学符合二级反应,线性相关系数良好（R^2〉0．99）。