Dielectric properties, electrical modulus and current transport mechanisms of Au/ZnO/n-Si structures

Au/Zn O/n-Si(MIS)structures were fabricated by using the RF sputtering method and their complex dielectric constant(ε~*=ε’-jε’’),electric modulus(M~*=M′+j M’’)and electrical conductivity(σ=σ_(dc)+σ_(ac))values were investigated as a function of frequency(0.7 k Hz-1 MHz)and voltage(-6–(+6 V))by capacitance-voltage(C-V)and conductance-voltage(G/ω-V)measurements to get more information on the conduction mechanisms and formation of barrier height between Au and n-Si.The lnσ-Lnf plots have two different regions corresponding to low-intermediate and high frequencies.Such behavior of lnσ-lnf plots shows that the existence of two different conduction mechanisms(CMs)at low-intermediate and high frequencies.Moreover,the reverse bias saturation current(I_o),ideality factor(n),barrier height(Φ_(Bo))were determined from the forward bias I-V data and they were found as a strong function of temperature.The value of n especially at low temperature is considerably higher than unity.The values ofΦ_(B0)and standard deviation(σ_s)were found from the intercept and slope ofΦ_(Bo)-q/2k T plots as 0.551 e V and 0.075 V for the region I(80–220 K)and 1.126 e V and 0.053 V for the region II(220–400 K),respectively.The values ofΦ_(Bo)and effective Richardson constant(A~*)were found from slope and intercept of activation energy plots as 0.564 e V and 101.084 Acm~(-2)K~(-2)for the region I and 1.136 e V and41.87 Acm~(-2)K~(-2)for the region II,respectively.These results confirm that the current-voltage-temperature(I-V-T)characteristics of the fabricated Au/Zn O/n-Si SBDs can satisfactorily be explained on the basis of TE theory with double GD of the BHs.     

Size-manipulat ion, compacti on and electrical properties of barium manganite nanorods synthesized via the CHM method

A composite-hydroxide mediated method was employed to synthesize barium manganite nanorods.Diameter,surface smoothness and uniformity of these nanorods were optimized by varying reaction temperature and reaction time.The rods with an average diameter of 200 nm and length of1–1.5 μm were obtained at optimum conditions of 200 1C/48 h.The dielectric study of these rods reveals that they have higher value of dielectric constant at lower frequencies which was attributed to the interfacial and rotational type polarizations.Similarly,the increase in dielectric constant with temperature was attributed to the thermal activation of such polarizations.Furthermore,the analysis of ln(J) vs.E1/2characteristics in the temperature range of 300–400 K shows that possible operative conduction mechanism was of Poole–Frenkel type.The value of βexp was found to be 4.85 times greater than the expected theoretical value of feld lowering coeffcient with an internal feld enhancement factor ofα2 23.5.This high value of βexp may be due to some localized electric felds existing inside the sample.     

光竞争条件下邻域效应对植物高生长可塑性的影响

构建了以个体为基础,空间明晰的"影响域"模型来研究植物高生长对局域光竞争的可塑性反应.结果表明:植物个体会将其高度维持在一最优值以使其适合度最大,这一最优高度值会随着植物个体所经受的局域光竞争强度的增加而增大.种群中小个体相对于大个体能更早地将其高度维持在最优值,但小个体由于邻域光竞争强度过大而导致的不能继续维持在最优高度及随后的死亡过程也比大个体要早.这种植物个体间高生长可塑反应的不同步性是由于个体的局域光竞争环境存在差异而导致的.研究表明空间分布与邻域效应对植物种群中多样性的高度和高生长策略的产生具有重要意义.在植物高生长的可塑性研究中,忽略邻域效应的"平均作用"博弈理论模型往往会导致片面的,甚至是错误的结论.     

Effect of La and Co-doping on microstructure and electrical properties of Bi FeO_3 thin films

Adding both La3＋and Co3＋was used to tune the microstructure and electrical properties of Bi Fe O3（BFO） thin films, and Bi1-xLaxFe0.90Co0.10O3 thin films were grown on the Sr Ru O3-buffered Pt-coated silicon substrates by a radio frequency sputtering. A polycrystalline structure with（110） orientation was shown in thin films, and their resistivity dramatically increases as the La3＋content increases. Their dielectric constant increases,and dielectric loss decreases with increasing La3＋content.In addition, their ferroelectric and fatigue properties were enhanced with rising La3＋content. The thin films with x = 0.03 have optimum electrical properties（e.g., remanent polarization 2Pr＊ 175.6 l C/cm2, coercive field2Ec＊ 699.5 k V/mm, dielectric constant er＊ 257 and tan d ＊ 0.038）, together with a good fatigue behavior. The impendence analysis of the films was conducted to identify the defects type during conductivity, and both hopping electrons and single-charged oxygen vacancies are mainly responsible for the conduction of grain and grain boundaries regardless of La3＋content. As a result, the doping with both La3＋and Co3＋benefits the improvement in the electrical properties of BFO thin films.     

电工实验测量误差的分析

分析在电工实验测量时产生测量误差的原因及减小测量误差的方法，正确估计测量误差和有效数字的正确表示。     

含氟单体对聚氨酯-氟化丙烯酸酯复合乳液性能的影响

以甲基丙烯酸十二氟庚酯(DFMA)和丙烯酸酯为单体,以水性聚氨酯作种子乳液,通过单体滴加法和单体预乳化法两种不同的聚合工艺制备聚氨酯-氟化丙烯酸酯(FPUA)复合乳液.对FPUA胶膜的结构和性能进行了检测与表征,探讨了含氟单体、不同聚合工艺对FPUA复合乳液聚合稳定性及胶膜性能的影响.     

早龄期持续拉力对混凝土性能的影响

为研究早龄期持续拉力对混凝土后期力学性能的影响,设计了7个系列共77个混凝土试件,探讨早龄期持荷轴拉比、持荷时间、混凝土强度等3个因素对混凝土后期轴心抗压性能的影响规律。为此,制作了对6个混凝土试件同时施加持续拉力的试验装置,龄期1.5d时开始施加轴向拉力,持荷一定时间后卸载,龄期28d时进行轴心抗压试验。持荷轴拉比和持荷时间对混凝土后期轴心抗压性能有一定的影响:持荷时间为7d时,轴拉比为0.15和0.3试件后期轴心抗压性能基本没有劣化,而轴拉比为0.5时试件产生了不可自愈的损伤,初始弹性模量、轴压峰值应力下降、峰值应变增大;轴拉比为0.3的试件持荷时间增加到14d,混凝土后期性能产生了劣化。混凝土强度等级越低,早龄期持续拉力对其弹性模量的影响较大,但峰值应力和峰值应变的影响相对较小。在试验结果的基础上,采用最小二乘法回归得到了持荷时间和持荷轴拉比对混凝土初始弹性模量、峰值应力与峰值应变的早龄期持荷影响系数。最后,在普通混凝土的应力应变关系的基础上考虑早龄期持荷影响因数,得到了受早龄期持荷影响的混凝土应力应变关系。     

温度作用下复合道面力学性能试验研究

为治理寒区机场跑道入口等待区复合道面轮辙病害,提出了复合道面原位加铺刚性层的处置方法。依据弹性地基梁理论制作了两种8组试块并对其分组进行了常温、高温、低温环境以及冻融循环作用后的力学试验,记录了试块破坏过程的实效模态和应变时程曲线,利用应力变化率法研究了试块的力学性能和破坏特征,对比于传统复合道面结构,分析了夹心型道面结构的优缺点。结果表明：常温环境下两种道面结构承载力接近;在高温和冻融循环作用下,夹心型道面结构上下部刚性层对中部沥青层具有保护作用,结构整体表现出较好延性;低温条件下两种道面结构中的沥青层抗裂性能变差,试块易发生整体脆性破坏;通过试件应力变化率分析可知,夹心型道面结构的承载力和延性在不同温度状况及冻融循环作用下较传统复合道面结构有所改善。特别地,相较于传统型道面结构,夹心型道面结构沥青混合料不易脱落到道面表面形成FOD,符合机场严格的FOD管理标准,表明该新型复合道面结构具有一定工程适用性。     

Effects of SrTiO3 buffer layer on structural and electrical properties of Bi3.15Nd0.85Ti3O12 thin films prepared by a chemical method

Ferroelectric Bi3.15Nd0.85Ti3O12 (BNT) thin films have been grown on Pt/Ti/SiO2/Si substrates at 750 ℃ by a chemical solution deposition method using SrTiO3 (STO) as a buffer layer.The influence of STO...     

微创经皮椎弓根内固定术对胸腰椎骨折患者功能障碍指数、伤椎高度及疼痛程度的影响

目的 探讨经皮椎弓根内固定术(MIPPSO)对胸腰椎骨折患者功能障碍指数、伤椎高度以及疼痛程度的影响。方法 回顾性分析2018年10月-2020年10月期间我院进行微创经皮椎弓根内固定术治疗的45例胸腰椎骨折患者临床资料。观察记录所有手术患者创面愈合时间、手术时间、术中出血量。同时比较患者术前、术后的功能障碍指数(ODI)、疼痛程度(VAS)以及伤椎高度与Cobb角。结果 本次研究的45例患者胸腰椎手术均已完成。其中创面愈合时间为(7.34±1.23)d,手术时间为(83.98±6.22)min,术中出血量为(66.45±5.11)ml。术后6d与术后10个月,ODI、VAS评分均明显低于术前(P<0.05)。术后6d与术后10个月,患者伤椎前缘高度均明显高于术前(P<0.05),但Cobb角度明显均低于术前(P<0.05)。结论 胸腰椎骨折患者进行经皮椎弓根内固定术治疗,能够改善患者腰椎功能障碍,同时减少术中出血量,缩短手术时间,促进创面快速愈合,并有效减轻术后机体疼痛,值得临床应该与推广。     

基于信息熵的网络数据演化涌现性度量方法研究

为了衡量网络数据演化过程中产生的"涌现现象",从涌现性特征的宏观分析出发,建立信息熵与网络数据演化涌现性之间的关联关系,基于概率估计提出1种可行的信息熵值计算方法,用信息熵对网络数据演化涌现性进行度量,并对演化行为和系统层次可能引入的误差进行校正,使度量方法更贴近实际情况.用实验分析说明该方法的合理性和有效性.     

相似关系下的粗糙映射的一些性质

目的 研究模糊粗糙映射的性质.方法 通过研究相似关系下粗糙集的性质,进一步研究相似关系下粗糙映射的性质.结果与结论 得出相似关系下模糊粗糙映射的部分性质.     

薄膜表面粗糙度对内应力测量的影响初析

薄膜表面粗糙度对内应力的测量产生复杂的影响。文章通过理论分析和计算 ,得到如下结论 :表面粗糙度使得内应力的测量值小于其真实值 ;当表面粗糙颗粒可以用球体描述时 ,粗糙度对内应力测量值的影响仅取决于球状颗粒与表平面之间的接触角 ,而与颗粒的半径大小无关 ,若颗粒恰为半球体 ,内应力测量值与实际值之比为 0 .785 4;当粗糙表面轮廓线可以用正弦曲线表示时 ,上述影响则取决于正弦波的波幅和波距之比。     

Al^3＋代换Fe^3＋对钴铁氧体结构与磁性能的影响

采用化学共沉法制备了CoFe2-xAlxO4（x=0．1～0．5）铁氧体纳米粉料,并在不同温度下进行退火处理,利用X射线衍射仪（XRD）、振动样品磁强计（VSM）对样品的结构和磁性进行了测量和分析．结果表明：所有样品均形成了单一的尖晶石相,晶粒尺寸为35～45nm;经1280℃退火后的样品能同时获得较高的比饱和磁化强度如和矫顽力Hc;随铝代换量x的增大,比饱和磁化强度起初变化平缓然后迅速降低,而矫顽力却呈现出了先增后减的趋势,在x=0．3附近出现峰值。     

矿物掺合料的颗粒级配对水泥砂浆性能的影响

在水泥中掺入适当细度的矿物掺合料,使胶凝材料的颗粒级配接近紧密堆积状态时,砂浆的强度会有所提高,水泥凝胶体的微观结构也会得到改善。     

膨胀运算的代数性质及其在提高膨胀运算效率方面的应用

该文主要研究和分析了数学形态学中膨胀运算的代数性质,对膨胀运算的两种定义,即基于集合论的定义和基于二维欧氏空间的定义,给出了等价性证明,说明了两种定义各自的侧重点,并在此基础上进一步阐明了膨胀运算满足交换律和结合律,并以结合律为基础讨论了结构元素分解在提高膨胀运算效率上的应用,给出了分解后各子结构元素中非零象素点的个数的乘积上限为eNe.     

合金凝固组织对氢扩散和MH电极性能的影响

用电位阶跃法和恒电流充放电法研究了贮氢合金凝固组织中的氢扩散行为和合金氢化物（ＭＨ）电极放电的速度特性．研究表明：合金ＭＬＮｉ３．４５（ＣｏＭｎＴｉ）１．５５的各凝固组织中氢扩散系数及合金的电极性能均明显不同，随合金凝固时冷却速度增大，氢扩散系数和晶胞体积减小；合金电极的高倍率放电率主要取决于氢在合金中的扩散速度和电极表面的电催化活性．定向凝固组织具有良好的放电速度特性与其凝固组织中存在Ｎｉ的析出相关系密切．