坡口宽度对超窄间隙焊接电弧特性的影响

坡口宽度小于5mm的超窄间隙焊接中,当坡口宽度进一步减小时,电弧特性变得很敏感,对焊接工艺参数的适应性要求提高.采用焊剂带约束电弧超窄间隙焊接技术,通过调节坡口宽度和焊接工艺参数研究其对超窄间隙电弧特性的影响规律.结果表明:在超窄间隙坡口中,保持工艺参数不变,坡口宽度减小,会使焊接电流增大,侧壁熔深变宽.当坡口宽度和送丝速度一定时,其焊接电流随电弧电压的增大呈上升趋势,且坡口宽度越窄,焊接电流对电弧电压的变化越敏感.利用不同坡口宽度下的电弧特性可对超窄间隙焊接时所匹配的工艺参数进行有效调控,坡口宽度变窄,所适用的焊接参数减小.     

焊剂带约束电弧超窄间隙焊接的气保护方法

利用焊剂带约束的电弧进行超窄间隙焊接时,采用合适的气体保护工艺十分重要.为了获得成形良好的超窄间隙焊缝,通过分析和试验确定粗扁管单侧倾斜送气的气保护方法,设计用于研究气保护效果的试验装置,并利用该装置研究气流量、喷嘴截面尺寸以及喷嘴与保护区距离对气保护效果的影响.结果表明,在气体喷嘴截面尺寸为2.5 mm×12 mm,气体喷嘴与电弧距离为20～25 mm的情况下,保证焊缝成形良好的最佳气流量为10 L/min.     

热输入对430铁素体不锈钢热影响区组织和韧性的影响

430铁素体不锈钢在焊接时,热影响区晶粒粗化会使接头韧性下降.利用热模拟技术和焊剂带约束电弧超窄间隙焊接方法对430铁素体不锈钢进行试验,得到不同热输入下粗晶区的组织,并测试其韧性性能.结果表明:当热输入低于3kJ/cm时,粗晶区组织主要为板条贝氏体和少量针状铁素体,铁素体晶粒尺寸小于48μm,室温冲击功与母材相当.铁素体晶粒不断长大是造成冲击韧性下降的主要原因.采用超窄间隙焊接方法,可以有效缩短高温停留时间,将铁素体晶粒尺寸限制在50μm以内,从而使韧脆转变温度降低至约-30℃,避免粗晶区韧性下降.     

窄间隙约束下熔化极气体保护焊的电弧形态和熔滴过渡分析

为研究采用平特性焊接电源和窄间隙约束下的电弧行为,建立了窄间隙熔化极气体保护焊(GMAW)试验系统,利用高速摄像系统观察电弧的爬升现象、电弧的形态和熔滴过渡过程,分析了窄间隙约束条件下产生电弧爬升现象的原因,并利用静力平衡理论分析不同电弧形态下熔滴过渡中的受力情况.结果表明:窄间隙GMAW焊接过程中的电弧爬升现象是由最小电压原理与电弧自调节共同作用的结果;电弧形态可按不同的导电路径分为3类,并均归结于最小电压原理的作用;窄间隙GMAW的熔滴过渡形式与不同电弧形态下的电磁力的大小和方向有关.     

窄间隙P-GMAW电弧行为分析

在窄间隙P-GMAW焊接中,电弧行为将直接影响焊缝成型效果,而侧壁和电流会影响电弧的形态。通过高速摄影技术分析窄间隙P-GMAW焊接中同一电流脉冲周期内不同时刻,以及同一摆动周期内不同电流脉冲周期的电弧形态变化情况,得出结论如下:(1)窄间隙摆动焊接中,电弧形态变化因素主要是脉冲电流的大小和焊枪与侧壁的距离;(2)由于电弧形态和熔滴过度相互影响,它们共同决定焊缝成型效果,因此电弧形态是决定焊接效果的重要因素。     

铬钼钢窄间隙埋弧焊用烧结焊剂的研制

本文叙述了铬钼钢窄间隙埋弧焊用烧结焊剂的研制,结合生产使用中对该焊剂的特殊要求,提出了使用该焊剂时对脱渣性、氧化性、电弧稳定性及表面压坑的解决办法。通过各项性能的试验,结果表明:GZ-3,GZ-4焊剂生产制造过程简单,具有较高颗粒强度,较低吸潮性,焊接工艺过程稳定,达到了国内外同类型焊剂水平。     

电弧作用位置对厚板侧壁连续熔合的影响

对焊接过程中电弧作用位置产生波动进行误差分析，提出了相应的实验方法，研究了低热输入条件下电弧作用位置对厚板窄间隙焊接侧壁熔合质量的影响，得到连续焊缝的有效电弧作用位置的范围，为低热输入条件下实现全自动焊打下了基础。     

浅水湿法和常压空气中焊接的电弧稳定性

由于水和压力对焊接过程的影响,浅水湿法焊接的电弧稳定性较差.为此,文中提出以焊接电弧电压差异系数的倒数作为衡量电弧稳定性的指标,利用高压舱水下焊接平台进行湿法焊接试验,通过采集不同焊接参数下湿法和空气中焊接的电压波形并计算焊接电压差异系数的倒数,定量研究了浅水湿法和常压空气中药芯焊丝焊接电弧的稳定性.结果表明,在所试验的焊接参数范围内,浅水湿法焊接的电弧稳定性与电流呈负相关,与电压呈正相关,故应选择最优的导电嘴至工件距离以使电弧稳定性最高;浅水湿法焊接的电弧稳定性随焊接速度的增大而减小,而常压空气中焊接基本不变;湿法焊接可采用的焊接电压和电流的工艺参数窗口更窄;焊接电流一定时,湿法焊接应比空气中焊接选用更高的电压,以提高焊接电弧的稳定性.     

厚板窄间隙磁控电弧TIG焊接自动控制系统设计

设计了一套厚板窄间隙磁控电弧惰性气体保护(TIG)焊接自动控制系统,介绍了通过交变磁场控制电弧周期性左右偏转以消除侧壁未熔合缺陷的原理.以可编程控制器(PLC)作为控制核心,根据该工艺的特点对控制系统进行了总体设计.设置两套独立的电弧长度控制系统,分别用于控制钨极处于间隙的居中位置和处于相对稳定的高度;设计并建立了一套运动控制系统;利用高精度气体传感器检测和控制各路保护气的实际流量,同时对保护气拖罩与工件表面之间的距离进行实时检测和控制,实现对厚板焊接过程的有效保护;对焊接电源进行选型及改造以实现数字化控制;搭建适用于工业化生产的视频监控系统.针对大厚板钛合金的焊接试验表明,该系统运行稳定可靠,具备在工业领域进行推广的潜力.     

窄坡口MAG焊摆动参数对焊缝成形的影响

为了解决窄坡口侧壁熔合问题,改善焊缝成形,采用窄坡口高速摆动MAG焊枪,进行了不同摆动宽度和摆动频率的焊接试验。通过测量焊缝宏观金相获得焊缝截面尺寸,对焊缝截面尺寸随摆动宽度、摆动频率的变化趋势进行曲线拟合,研究了高速摆动电弧窄坡口MAG焊摆动参数对焊缝成形的影响规律。结果表明,增加摆动宽度和频率都能减小焊缝熔深,增加侧壁熔深,当焊枪摆动宽度使侧间距大于-0.5mm、小于1mm时会获得好的焊缝成形,摆动频率增加到5Hz以上时,能消除焊缝指状熔深,但是当摆动频率高于9Hz时,增加摆动频率,焊缝截面尺寸的变化不明显。获得的这些摆动参数对焊缝成形的影响规律能够为焊接工艺参数的选择提供指导。     

低碳钢A-TIG焊活性剂的焊接性研究

利用自行研制的低碳钢A TIG焊活性剂进行了各种焊接工艺试验 .试验结果表明 ,使用本活性剂可使焊缝熔深比常规的TIG焊增加 3倍 ,对 12mm以下的低碳钢板对接无须开坡口 ,可一次焊接完成并能单面焊双面成型 .焊缝表面成型良好 ,接头微观组织、焊缝的化学成分和接头力学性能均不受影响 .焊接电流、弧长、焊接速度、涂层厚度和气体种类等均对焊接熔深的增加产生影响     

Effects of different friction stir welding conditions on the microstructure and mechanical properties of copper plates

Friction stir welding is a new and innovative welding method used to fuse materials. In this welding method, the heat generated by friction and plastic flow causes significant changes in the microstructure of the material, which leads to local changes in the mechanical properties of the weld. In this study, the effects of various welding parameters such as the rotational and traverse speeds of the tool on the microstructural and mechanical properties of copper plates were investigated; additionally, Charpy tests were performed on copper plates for the first time. Also, the effect of the number of welding passes on the aforementioned properties has not been investigated in previous studies. The results indicated that better welds with superior properties are produced when less heat is transferred to the workpiece during the welding process. It was also found that although the properties of the stir zone improved with an increasing number of weld passes, the properties of its weakest zone, the heat-affected zone, deteriorated.     

视觉系统在窄间隙焊缝自动跟踪的研究

本文论述了一种经济有效的视觉系统的研究及其在窄间隙 TIG 焊接中焊缝自动跟踪的应用。该系统以 IBM-PC AT 为主机带有图像存取扩充板,用 CCD 摄像机摄取电弧区域及焊接坡口的图像,然后把它数字化,化为具有7位(即128级)灰暗度的256×256个像点(成像素),并存入图像存取板。IBM PC 对获得的数字图像进行实时图像处理,应用了寻边及模板耦合两种方法所得到的视觉信息被反馈到焊接控制器进而对焊接过程进行有效的焊缝自动跟踪。     

手工电弧焊与CO2气体保护焊焊缝成形特征研究

采用手工电弧焊与CO2气体保护焊对Q235钢板进行表面堆焊,研究了两种焊接方法的焊缝成形特征．结果表明,虽然手工电弧焊是气渣联合保护,有利于焊缝成形,但手工操作使得焊接速度难以保证匀速,导致焊缝表面粗糙,焊缝弯曲不平直;并且由于药皮焊条直径粗,导致手工电弧焊热影响区宽．而细丝CO2气保焊由于形成稳定的熔滴过渡,使得焊缝表面波纹细致、美观,焊缝平直,热影响区窄．CO2气保焊能精确控制焊接规范,可通过调节焊接规范来获得良好的焊缝成形,手工电弧焊不能精确控制焊接规范,不利于得到成形良好的焊缝．     

起重机车架用Q345B/HG785D钢板焊接实验研究

以异种钢板Q345B与HG785D端头对焊为研究对象,通过在不同焊接热输入工艺条件下的MAG焊(熔化极活性气体保护电弧焊),对其端头焊接缺陷、力学性能及组织进行实验研究.实验发现:异种钢板端头对焊中,减小焊接电流可有效提高焊接接头强度;焊前预热、焊后缓冷可减少焊接接头的淬硬组织,提高焊接热影响区韧性.在焊接电流为140~200A、电压为22~24V、焊接速度为28cm/min的热输入条件下,采用预热+后热焊接工艺,焊接接头力学性能和弯曲特性可得到最佳效果.合理的焊接工艺可有效抑制汽车起重机车架焊缝开裂.     

AZ31镁合金板材自动氩弧焊接工艺研究

利用六轴焊接机器人夹持氩弧焊枪进行AZ31镁合金自动氩弧焊接工艺研究,焊后利用金相显微镜、扫描电子显微镜、X射线衍射仪和万能试验机等对焊接接头进行微观组织表征及力学性能测试。结果表明,在焊接电流160 A、焊接速度0.45 m/min、填丝速度0.6 m/min、钨极针与板材距离0.5 mm（前半段）和2.0 mm（后半段）以及保护气体流量16 L/min（正面）和21 L/min（背面）的条件下,能得到外观形貌良好、质量可靠的AZ31镁合金焊接接头。焊接接头的金相组织显示,焊缝区微观组织可清晰地分为母材区,热影响区和熔化区。焊接过程在热影响区和熔化区出现了大量的沉淀相,X射线衍射结果表明,该沉淀相为β Mg17Al12沉淀相。拉伸结果显示,焊接接头的抗拉强度达到了母材的81.02%,在断口观察到了大量的解离面和韧窝的存在,呈现出脆性断裂与韧性断裂相结合的混合断裂特征。     

CO2药芯焊丝的焊接工艺研究

对 CO2 药芯焊丝的焊接工艺进行了研究 .分析了电弧电压、电弧电流、焊接速度对药芯焊丝焊接工艺的影响 ,并对 CO2 药芯焊丝和实芯焊丝的性能作了部分对比试验 .研究表明 :CO2 药芯焊丝的焊缝成形、焊缝的熔合、焊接质量明显好于 CO2 实芯焊丝 .     

用于TIG焊缝跟踪的表面活性剂对电弧电压的影响

提出一种基于表面活性剂示踪的电弧传感焊缝跟踪方法,该方法能实现I型对接坡口TIG焊缝的焊接.建立电弧信号采集和分析的试验系统,实验研究表面活性剂不同涂覆方式对电弧电压的影响.结果表明,涂覆方式和摆动频率对电压信号影响较大,而焊接电流和涂覆厚度的影响较小.通过电弧摆动和焊缝表面涂覆活性剂的方式,可以得到明显的周期性电压信号,此信号可以用于焊缝跟踪传感.     

高速埋弧焊烧结焊剂的研制

探讨了高速埋弧焊焊缝咬边的机理、影响因素和解决途径。研制了一种新型的焊速可大于80m/h的高速埋弧焊烧结焊剂,并介绍了这种焊剂的性能。阐述了焊接工艺参数的焊剂成份对高速焊焊接工艺性的影响。利用这种焊剂对16Mn和20g材料进行了焊接工艺实验评定,结果表明:利用这种焊剂可以解决高速焊咬边和焊接工艺性的问题,并能满足压力容器和锅炉钢焊接要求,是一种较为理想,可推广使用的焊剂。     

低碳钢A-TIG焊接法的试验研究

研究了一种高效的 TIG焊接方法 A- TIG,进行了系列 TIG焊堆焊试验 .结果表明 :在相同焊接规范下 ,涂敷表面活性剂后焊接电弧有明显收缩 ,熔池深度有显著增加 ,而熔宽稍有减小 .同时还介绍了活性剂成分的调配及活性剂成分对熔深变化的影响 ,并对熔深增加机理进行了分析