Martensitic transformation and magnetic properties of aged Ni-Fe-Ga-Ti shape memory alloy

This article reports the effect of ageing on the microstructure, martensitic transformation, magnetic properties, and mechanical properties of Ni₅₁Fe₁₈Ga₂₇Ti₄ shape memory alloy. There are five specimens of this alloy aged at 573 up to 973 K for 3 h per each. This range of ageing temperature greatly affects the microstructure of the alloy. As the ageing temperature increased from 573 up to 973 K, the microstructure of Ni₅₁Fe₁₈Ga₂₇Ti₄ alloy gradually changed from the entirely martensitic matrix at 573 K to the fully austenitic microstructure at 973 K. The volume fraction of precipitated Ni₃Ti particles increased with the ageing temperature increasing from 573 to 773 K. Further increasing the ageing temperature to 973 K decreased the content of Ni₃Ti in the microstructure. The martensitic transformation temperature was decreased steadily by increasing the ageing temperature. The magnetization saturation, remnant magnetization, and coercivity increased with the ageing temperature increasing up to 773 K. A further increase in ageing temperature decreased these magnetic properties. Moreover, the hardness values were gradually increased at first by increasing the ageing temperature to 773 K, and then dramatically decreased to the lowest value at 973 K.     

Dependence of nitrogen concentration in type Ib diamonds on synthesis temperature

Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500－1560 K in a china-type cubic anvil high pressure apparatus using Ni₇₀Mn₂₅Co₅ alloy as solvent/catalyst. The concentration of nitrogen (C_N) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of C_N in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni₇₀Mn₂₅Co₅ as catalyst, its C_N decreases along with the increase of synthesis temperature.     

Strain glass transition in high damping Mn-22Cu-5Ni-2Fe alloy

It has been recognized that the high damping capacity of MnCu based alloys is closely related to the formation of elastic twins as a result of antiferromagnetic transition and martensitic transformation. However, the mechanism for these transitions in this kind of alloy has not been fully understood. For example, previous investigations ascribed the elastic modulus softening prior to martensitic transformation to antiferromagnetic or pre-martensitic transitions, although no convincing evidence was reported. In this paper, an intensive experimental study was made of the modulus softening and microstructural evolution in a typical high damping Mn-22Cu-5Ni-2Fe alloy, and the evidence of strain glass transition was reported. Such a transition, characterized by a continuous formation of nano-martensite domains, is accompanied by a gradual frequency-dependent modulus softening over a broad temperature range prior to martensitic transformation.     

Effect of Ni addition on the glass-forming ability and soft-magnetic properties of FeNiBPNb metallic glasses

The effect of Ni addition on the glass-forming ability (GFA) and soft-magnetic properties of an (Fe1-xNix)75.5B14.5P7Nb3 (x=0-0.6) alloy system were investigated. We found that the addition of Ni was effective in allowing the alloy to approach a eutectic point as well as increasing the thermal stability of the supercooled liquid. By increasing the amount of Ni,the supercooled liquid region (ΔTx),the reduced glass transition temperature Trg (Tg/Tl) and the Y parameter [Tx/(Tg+Tl)] increased from 49 to 75 K,0...     

Effects of aging treatment on the microstructure and superelasticity of columnar-grained Cu<Subscript>71</Subscript>Al<Subscript>18</Subscript>Mn<Subscript>11</Subscript> shape memory alloy

The effect of aging treatment on the superelasticity and martensitic transformation critical stress in columnar-grained Cu₇₁Al₁₈Mn₁₁ shape memory alloy (SMA) at the temperature ranging from 250°C to 400°C was investigated. The microstructure evolution during the aging treatment was characterized by optical microscopy, scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The results show that the plate-like bainite precipitates distribute homogeneously within austenitic grains and at grain boundaries. The volume fraction of bainite increases with the increase in aging temperature and aging time, which substantially improves the martensitic transformation critical stress of the alloy, whereas the bainite only slightly affects the superelasticity. This behavior is attributed to a coherent relationship between the bainite and the austenite, as well as to the bainite and the martensite exhibiting the same crystal structure. The variations of the martensitic transformation critical stress and the superelasticity of columnar-grained Cu₇₁Al₁₈Mn₁₁ SMA with aging temperature and aging time are described by the Austin–Rickett equation, where the activation energy of bainite precipitation is 77.2 kJ·mol?1. Finally, a columnar-grained Cu₇₁Al₁₈Mn₁₁ SMA with both excellent superelasticity (5%–9%) and high martensitic transformation critical stress (443–677 MPa) is obtained through the application of the appropriate aging treatments.     

Preparation and thermal stability of Pd<Subscript>40.5</Subscript>Ni<Subscript>40.5</Subscript>Si<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>P<Subscript>19−<Emphasis Type="Italic">x</Emphasis></Subscript> bulk metallic glasses

With the addition of Si to replace some P, Pd_40.5Ni_40.5Si _x P_19−x (x=0, 2.5, 5, 9.5, 14, and 19 in atomic number fraction) bulk glassy samples with the diameter of about 5 mm were successfully prepared by use of flux treatment and water quenching technology. With the increase of Si content, the glass forming ability of Pd_40.5Ni_40.5Si _x P_19−x increases first for low Si content and then decreases for high Si content (Si≥9.5at%). The Pd_40.5Ni_40.5Si ₅ P₁₄ glassy alloy possesses the largest supercooled liquid region ΔT of 119 K, the largest reduced glass transition temperature of 0.621, and the largest γ parameter of 0.460, indicating that this glassy alloy possesses very large glass forming ability and very high thermal stability.     

Primary dendrite growth of Ni<Subscript>3</Subscript>Sn intermetallic compound during rapid solidification of undercooled Ni-Sn-Ge alloy

Liquid Ni-31.7%Sn-2.5%Ge alloy was highly undercooled by up to 238 K(0.17TL) with glass fluxing and drop tube techniques.The dendritic growth velocity of primary Ni3Sn compound shows a power-law relation to undercooling and achieves a maximum velocity of 380 mm/s.The addition of Ge reduces its growth velocity as compared with the binary Ni75Sn25 alloy.A structural transition from coarse dendrites into equiaxed grains occurs once undercooling exceeds a critical value of about 125 K,which is accompanied by both grain refinement and solute trapping.The Ni3Sn intermetallic compound behaves like a normal solid solution phase showing nonfaceted growth during rapid solidification.     

Effect of Co on the martensitic transformation,crystal structure and magnetization of Ni<Subscript>52.5</Subscript>Mn<Subscript>23.5</Subscript>Ga<Subscript>24</Subscript> based ferromagnetic shape memory alloys

Five(Ni52.5Mn23.5Ga24)100-xCox(x = 0,2,4,6,8) alloys were prepared by arc melting,and the effects of Co addition on the martensitic phase transformation,crystal structure and magnetization were investigated.The phase transformation temperatures Ms,Mf,As and Af are proportional to the content of Co in the(Ni52.5Mn23.5Ga24)100-xCox alloys,which appears to be due to the variation in the valance electron concentration.The Curie temperature is sensitive to the composition of the alloy.As the amount of Co changes,both the Co-Mn exchange interaction and the distance between Mn atoms change.These,in turn,affect the Curie temperature and magnetization behavior of the alloy.The martensite phases in all the alloys are domained in three different orientations,the domain boundary was determined to belong to the family of {112} lattice planes.     

Fabrication of bulk glassy Zr41Ti14Ni8Cu12.5Be22.5Fe2 alloy by water quenching

A glassy Zr₄₁Ti₁₄Ni₈Cu_12.5Be_22.5Fe₂ rod with a diameter of 9 mm was successfully produced by water quenching. The effects of iron addition on thermal stability and hardness of Zr₄₁Ti₁₄Ni₈Cu_12.5Be_22.5Fe₂ bulk amorphous alloy were investigated by XR D, DSC and microhardness test. It is found that the full annealing would enhance the strength of the alloy significantly. The cause of the increase in hardness was analyzed and the formation mechanisms of the bulk amorphous alloy are discussed.     

Influence of pulsing current on the glass transition and crystallizing kinetics of a Zr base bulk amorphous alloy

Based on the thermal analysis, the influence of pulsing current on the glass transition and crystallizing kinetics of Zr41.3Ti14.2CU12.8Ni10.3Be21.4 bulk amorphous alloy has been studied. The obtained results show that after the Zr41.3Ti14.2CU12.8Ni10.3Be21.4 bulk amorphous alloy was pretreated by high-density pulsing current at low temperature, its glass transition temperature Tg, the initial crystallizing temperature Tx and the corresponding exothermic peak of crystallization Tpi were reduced. But the temperature range of supercooled liquid △T=Tx-Tg is almost the same. The calculated results with Kissinger equation show that the activation energy of glass transition of the alloy pretreated is reduced significantly, while the activation energy of crystallization is basically unchanged. The influence of pulsing current on the glass transition and crystallization of theZr41.3Ti14.2CU12.8Ni10.3Be21.4 bulk amorphous alloy is believed to be related with the structure relaxation of the glass caused by the current.     

Dendrite growth and micromechanical properties of rapidly solidified ternary Ni-Fe-Ti alloy

The rapid solidification of undercooled liquid Ni_(45)Fe_(40)Ti_(15)alloy was realized by glass fluxing technique.The microstructure of this alloy consists of primaryγ-(Fe,Ni)phase and a small amount of interdendritic pseudobinary eutectic.The primaryγ-(Fe,Ni)phase transferred from coarse dendrite to fragmented dendrite and the lamellar eutectic became fractured with the increase of undercooling.The growth velocity ofγ-(Fe,Ni)dendrite increased following a power relation with the rise of undercooling.The addition of solute Ti suppressed the rapid growth ofγ-(Fe,Ni)dendrite,as compared with the calculation results of Fe-Ni alloy based on LKT model.The microhardness values of the alloy and the primaryγ-(Fe,Ni)phase increased by 1.5 times owing to the microstructural refinement caused by the rapid dendrite growth.The difference was enlarged as undercooling increases,resulting from the enhanced hardening effects on the alloy from the increased grain boundaries and the second phase.     

Study on the hydrogen storage property of (TiZr0.1)xCr1.7-yFeyMn0.3 (1.05

Jigang Li  Li Xu  Xiaojing Jiang  Xingguo Li 《自然科学进展(英文版)》2018,28(4):470-477

Effects of gravity field on glass forming ability in ZrTiCuNiBe alloy

The solidification and glass forming ability of Zr₄₁Ti₁₄Cu_12.5Ni₁₀Be_22.5 bulk glassy forming alloy is investigated by Bridgman unidirectional solidification at different growth velocities under different gravity field orientations. Large differences in glass formation, undercooling and crystallization morphology on different solidification conditions have been found and discussed from the point of view of gravity induced convection. The results are useful for understanding the nucleation and growth in the melt and glass formation mechanism in the alloy.     

Influence of heat exchanger structure on hydrogen absorption-desorption performance of hydrogen storage vessel

The influence of heat exchanger structure on hydrogen absorption-desorption performance of hydrogen storage vessel was studied, in which the AB₅ (La_0.25Ce_0.75Ni_4.4Al_0.1Mn_0.1Co_0.4) hydrogen storage alloy was used as a typical representative. In order to obtain the data on reaction enthalpy, the PCT curve of the alloy was measured with three different temperatures, and the linear fitting was carried out according to the Van't Hoff relation curve. The SMCR (Spiral-mini-channel Reactor) reactor structure was adopted. The heat transfer method and its simplified model were studied by finite element method to explore the effect of size of heat transfer structure, particularly for heat pipe diameter, on the hydrogen absorption-desorption performance of hydrogen storage alloy in the vessel.     

Mechanical, deformation and fracture behaviors of bulk metallic glass composites reinforced by spherical B2 particles

Ti_(45)Cu_(40)Ni_7Zr_5Sn_(2.5)Si_(0.5) alloys were prepared under various cooling rate conditions during solidification.The alloys exhibited different volume fractions of B2 particles with 0～40 vol%in an amorphous matrix.Monolithic bulk metallic glass of 1 mm diameter showed no macroscopic plasticity and exhibited the typical vein patterns in a maximum shear stress plane on the fracture surface.However,a bulk metallic glass composite containing the B2 particles revealed obvious plasticity(～5.6%)with a remarkable work-hardening behavior that resulted from a stress-induced martensitic transformation of the B2 particles.Moreover,the composite displayed the complicated fracture morphologies containing of three types of fracture features.Through detailed investigations on the microstructural evolution,mechanical,deformation and fracture characteristics,the influence of B2 particle on overall behavior of the TiCu-based bulk metallic glass composites was elucidated.     

Multi-index analysis of the melting process of laterite metallized pellet

Herein, a multi-index analysis of the nickel content of an alloy, output rate of the alloy, nickel recovery rate, and iron recovery rate during the melting of laterite metallized pellets was performed. The thermodynamic reduction behavior of oxides such as NiO, FeO, Fe₃O₄, and Cr₂O₃ was studied using the FactSage software, which revealed that SiO₂ is not conducive to the reduction of iron oxides, whereas the addition of basic oxides such as CaO and MgO is beneficial for the reduction of iron oxides. On the basis of a comprehensive analysis to achieve greater nickel recovery and lower iron recovery rates, the optimum experimental parameters in the orthogonal experiment were A3B1C3 (t=30 min, C/O=0.4, R=1.2); the indicators w_Ni, φ_alloy, η_Ni, and η_Fe had values of 15.0wt%, 12.1%, 44.9%, and 96.4%, respectively. In single-factor experiments, increasing basicity (R) substantially improved the separation effect in the low-basicity range 0.5 ≤ R ≤ 0.8 but not in the high-basicity range 0.8 ≤ R ≤ 1.2. Similar results were obtained for the effect of the C/O ratio. Moreover, the recovery rate of nickel increased with increasing recovery rate of iron.     

Cu-Ni-Al系合金铸态组织研究

对Cu-Ni-Al系合金的铸态组织进行研究,使企业更好地认识和了解Cu-Ni-Al系列合金,进而更好地开发利用该合金.采用金相显微镜、扫描电子显微镜和能谱仪,对Cu-Ni-Al和Cu-Ni-Al-Ti合金进行观察和分析.结果表明：Cu-9.0Ni-1.4Al合金铸态组织中枝晶组织与偏析区（Ni₃Al）界限十分明显,且枝晶组织比较粗大.而Ti的加入促使Ni和Cu的分布变得均匀,并且Ti的加入使合金中有魏氏体产生,致使合金的力学性能降低,减小了合金的变形能力,导致Cu-9.0Ni-1.4Al-0.5Ti合金在热轧时有开裂的现象发生.并且能谱分析显示Ni₃Al存在于枝晶中和枝晶间,说明Ni₃Ti的稳定性较好,在高温时就有Al₃Ti形成,在固溶扩散过程中,Ni₃Ti被排挤到枝晶之间,形成第二相.     

Microstructure characteristics of Ni/WC composite cladding coatings

A multilayer tungsten carbide particle (WCp)-reinforced Ni-based alloy coating was fabricated on a steel substrate using vacuum cladding technology. The morphology, microstructure, and formation mechanism of the coating were studied and discussed in different zones. The microstructure morphology and phase composition were investigated by scanning electron microscopy, optical microscopy, X-ray diffraction, and energy-dispersive X-ray spectroscopy. In the results, the coating presents a dense and homogeneous microstructure with few pores and is free from cracks. The whole coating shows a multilayer structure, including composite, transition, fusion, and diffusion-affected layers. Metallurgical bonding was achieved between the coating and substrate because of the formation of the fusion and diffusion-affected layers. The Ni-based alloy is mainly composed of γ-Ni solid solution with finely dispersed Cr₇C₃/Cr₂₃C₆, CrB, and Ni+Ni₃Si. WC particles in the composite layer distribute evenly in areas among initial Ni-based alloying particles, forming a special three-dimensional reticular microstructure. The macrohardness of the coating is HRC 55, which is remarkably improved compared to that of the substrate. The microhardness increases gradually from the substrate to the composite zone, whereas the microhardness remains almost unchanged in the transition and composite zones.     

Nonstoichiometric Li1±x Ni0.5Mn1.5O4 with different structures and electrochemical properties

Li1±xNi0.5Mn1.5O4(x=0.05,0) spinel powders were synthesized using a solid-state reaction.Their structures were characterized by X-ray diffraction,scanning electron microscopy and Raman spectroscopy.Their electrochemical properties for use as active cathode materials in lithium-ion batteries were measured.The LiNi0.5Mn1.5O4,Li1.05Ni0.5Mn1.5O4 and Li0.95Ni0.5Mn1.5O4 samples crystallized in Fd 3m,Fd 3m and P4332,respectively.The LiNi0.5Mn1.5O4 and Li0.95Ni0.5Mn1.5O4 samples exhibited better cycle performance than the Li1.05Ni0.5Mn1.5O4 sample,while Li0.95Ni0.5Mn1.5O4 had the worst rate performance.Thus,it appears unnecessary to introduce nominal lithium nonstoichiometry in LiNi0.5Mn1.5O4 electrode materials.     

Tailoring of microstructure and martensitic transformation of nanocrystalline Ti–Ni-Hf shape memory thin film

The amorphous Ti-Ni-Hf thin films with the specific compositions were prepared from single Ti-Ni-Hf alloy target by adjusting processing parameters of direct current magnetron sputtering deposition. Prior to the crystallization,a glass transition occurred in the present Ti-Ni-Hf thin films. The annealed Ti-Ni-Hf thin films were characterized by the nano-crystalline. With the annealing temperature increasing, the grain size firstly increased and then decreased owing to the presence of(Ti,Hf)_2Ni precipitate. Two endothermic and exothermic peaks corresponding to B19'■B2 martensitic transformation in heating and cooling curves were observed for the Ti-Ni-Hf thin films with the lower annealing temperature and shorter annealing time, which was closely related to the inhomogeneous composition. However, the Ti-Ni-Hf thin films annealed at higher annealing temperature and longer annealing time showed the single stage B19'■B2 martensitic transformation. In addition, the martensitic transformation temperatures firstly increased and then decreased with the annealing temperatures rising.