采用液固相轧制法可以稳定、连续生产AlSn8Si2.5Pb2Cu0.8Cr0.2覆钢双层轴瓦带·通过金相和EPMA照片显示其组织与铸造组织相似,但含有大量致密细小、发达的柱状枝晶,组织内Si、Sn等元素分布均匀·由于复合界面结合强度较高,撕开后钢表面有大量的铝块,其复合机理主要是由于钢、铝充分润湿,高温和较大的轧制力使钢表面污染层、氧化层变薄,形成牢固的冶金结合所致·     

有助复剂温轧不锈钢复铝板实验研究

实验研究了浸涂助复剂和中温轧制工艺对不锈钢和铝固相复合界面结合强度及复合板深加工性能的影响·结果表明,原料表面浸涂助复剂不仅可以有效清除不锈钢和铝表面的氧化层,同时反应生成的覆盖膜在加热时又可防止和减少材料表面的再氧化和二次污染,有利于提高界面的结合强度;采用中温轧制工艺不仅在小变形的条件下即可实现不锈钢和铝复合界面的良好结合,而且能明显降低复合过程中不锈钢的变形率分配,有利于改善复合板的深加工性能     

表面处理方式对钛/钢复合板界面结合性能的影响

采用真空制坯轧制复合法,在相同的加热温度、轧制道次和压下量等工艺条件下,分别对钢丝刷打磨、酸洗和带水砂带机打磨的表面处理方式,研究了3组钛/钢复合板的界面组织和力学性能.分析了表面处理方式对界面结合性能的影响.结果表明:带水砂带机表面处理方式下的钛/钢复合界面生成连续均匀的TiC层,剪切断口呈韧窝状,界面剪切强度稳定,平均强度达到242.6MPa.其他两种表面处理方式下的钛/钢复合板界面生成断续的TiC层,其剪切强度均未满足国家标准.     

反向凝固复合不锈钢带及其轧制的实验研究

介绍了用反向凝固的方法生产薄带的工艺过程及目前的实验研究方法,借助金相显微镜分析了轧制温度、轧制速度及变形率对母带与凝固层结合质量的影响,为以后的工业化生产提供依据·并运用拉剪方法测定了界面结合强度·结果表明:热轧温度为１２５０℃,变形率为４０％,轧制速度为０－２～０－４ｍ／ｓ时,界面结合较好,结合强度达２４８ＭＰａ·进一步的热轧、冷轧证明用反向凝固的方法生产薄带是可行的·     

复合轧制工艺对Al/Mg复合板冶金结合层组织和性能的影响

采用AZ31镁合金和纯铝进行高温复合轧制制备镁-铝复合板,使其兼具铝的表面耐蚀性和镁合金的高比强度特性.采用金相显微镜、扫描电子显微镜和电子万能拉伸机等设备,研究了不同热轧温度及退火工艺参数对铝-镁复合界面的显微组织和结合强度的影响.结果表明：300 ℃轧制,镁-铝复合板出现严重边裂;450 ℃轧制,边裂消失;在轧制温度为400 ℃、压下率为50%、300 ℃退火2 h的条件下得到的复合板界面结合强度最大,为7.5 MPa.     

轧制温度对TA1/Q345复合板性能的影响

相对于爆炸复合法和爆炸-轧制复合法而言,采用真空-轧制生产钛钢复合板的方法更加适应大规模生产需要.本实验将TA1钛材置于两块Q345钢材中间组成组合坯,组合坯经抽真空至0.1 Pa后密封,在840～930℃下进行加热轧制,对轧制复合样进行力学性能检测,并利用扫描电镜、X射线衍射分析及显微硬度仪对组织与界面结合度进行分析.在该实验条件下,钛钢复合板剪切强度在159 MPa以上,达到了1类复合板标准要求,870℃轧制复合板性能较优.900和930℃轧制时,钛发生相变,同时在界面处生成了较多的金属间化合物,钛和钢的变形抗力相差过大和变形不协调导致界面附近的内应力变大,这些因素都降低了界面的剪切强度.840℃轧制后剪切强度低的原因是由于温度过低影响了界面附近元素的扩散.     

铜/钢反向凝固及加工变形的结合机理

介绍了铜/钢反向凝固及加工变形复合的工艺过程,利用光学显微镜和扫描电镜等手段分析了铜和钢界面形态、组织结构·在Instron拉伸机上测定了铜/钢界面的结合强度·结果表明,经预处理的钢丝表面呈现细微的凸凹不平状态,特别有利于液态铜在钢丝表面异质形核、凝固、结晶,使铜和钢的晶粒在界面上相互镶嵌,达到良好结合·此外,CS线再经加工变形后,伴随着晶粒的拉长和界面的扩展,导致晶粒间相互插入,机械咬合能力加强,使铜/钢界面结合强度进一步提高·     

7475/LY12金属多层复合材料的研制

采用“热压合＋轧制复合”的方法研制出了７４７５／ＬＹ１２多层金属复合材料,其复合层数高达１９层·复合材料的剪切强度达到了１３０ＭＰａ,撕裂强度为１３－６Ｎ／ｍｍ,界面两侧元素扩散平缓,扩散层宽度约在５０～９０μｍ之间,说明复合材料具有良好的冶金结合状态·     

铜-钢反向凝固复合带的实验研究

以12mm厚的08Al钢作为母带,纯铜作为复合层材料,系统地研究了浸渍复合时间、铜液温度及钢带预热温度等工艺参数对铜复合层厚度变化的影响规律·研究结果表明:随浸渍复合时间的增加,复合层的厚度变化经历了凝固生长和回熔两个阶段,钢带的预热温度越低,铜复合层厚度越厚,在通常的铜液过热度(<100℃)范围内,铜液温度的变化对复合层的厚度影响不大·     

反向凝固过程铜/钢复合界面的研究

界面是复合材料特有的而且是及其重要的组成部分·采用光学显微镜、扫描电镜等手段,分析了反向凝固复合铜/钢界面形态,组织结构和过渡区成分变化,探索反向凝固复合的初结合机制·研究表明,铜/钢反向凝固复合经历液态铜在固态钢表面初始润湿;液态铜的凝固、结晶;Fe,Cu原子互扩散等物理冶金变化过程,从而实现复合界面良好的冶金结合     

Mathematical modeling and simulation of the interface region of a tri-layer composite material, brass-steel-brass, produced by cold rolling

The object of this study was to find the optimum conditions for the production of a sandwich composite from the sheets of brass-steel-brass. The experimental data obtained during the production process were used to validate the simulation program, which was written to establish the relation between the interface morphology and the thickness reduction amount of the composite. For this purpose, two surfaces of a steel sheet were first prepared by scratching brushing before inserting it between two brass sheets with smooth surfaces. Three sheets were then subjected to a cold rolling process for producing a tri-layer composite with various thick- nesses. The sheet interface after rolling was studied by different techniques, and the bonding strength for each rolling condition was determined by peeling test. Moreover, a relation between interfacial bonding strength and thickness reduction was found. The simulation results were compared with the experimental data and the available theoretical models to modify the original simulation program with high application efficiency used for predicting the behavior of the interface under different pressures.     

爆炸焊接轧制复合板的结合界面研究

通过实验测试不同爆炸焊接工艺 轧制获得的1Cr18Ni9Ti/20G复合板结合界面的组织、强度和性能进行了比较研究。实验表明：用下限获得的微小波状界面的爆炸焊接复合板，才能实现成功轧制，而大波状复合板本身存在一定的微观缺陷，在轧制时由于分层会使轧制失效。     

感应重熔对高速轧机轴承热喷涂层微观组织性能的影响

为了改善高速轧机轴承热喷涂层的微观组织性能,采用感应重熔技术对GCr15轴承钢表面预制备的高能火焰喷涂Ni60A涂层进行感应重熔处理,并利用金相显微镜、扫描电镜、X射线衍射仪、显微硬度计对感应重熔前后涂层的孔隙率、微观组织、显微硬度等进行对比研究,探讨感应重熔对涂层以及界面微观组织、显微硬度的影响.结果表明,高能火焰喷...     

金属表面预处理对环氧树脂粘结剂粘结强度的影响

利用拉伸剪切实验系统地研究了砂纸打磨、喷砂、酸洗和磷化四种表面处理方法对粘结剂粘结强度的影响,并结合扫描电镜（SEM）、表面粗糙度测试仪对金属表面形貌的研究,结合能谱测定拉剪试样破坏面的成分数据,详细分析了不同表面处理方法影响界面粘结强度的作用机理。结果表明,各种表面处理方法均可改变金属表面形态,从而有效提高界面粘结强度,为进一步提高粘结剂／金属界面结合强度打下一定的基础。     

碳扩散对非真空热轧不锈钢复合板结合性能的影响

采用非真空热轧方法制备304不锈钢/Q235碳钢复合板材,利用OM、SEM、EDS等研究了不同压下率和轧后冷却方式下复合界面夹杂物、界面组织及力学行为的演变,并分析了C扩散对复合板界面组织形成及结合强度的影响。结果表明,随着轧制压下率的增加,界面夹杂物由块状向线型、连续点状乃至弥散点状分布变化。当压下率较低(28%)时,复合板剪切断裂位于结合界面处,随着压下率增加至47%及以上,复合板断裂位置为脱碳铁素体区。另外,热轧复合板经水冷工艺处理后,由于冷却速率较快,要抑制碳钢侧C元素的扩散,避免复合界面处脱碳区域的形成,从而提高了复合界面的结合强度。     

不锈钢和铝固相轧制复合的结合机理

通过实验研究了不锈钢和铝双金属的固相轧制复合，研究表明，增加变形程度和选择合适的轧制温度能提高复合板的界面初结合强度，通过电子显微镜观察分析复合界面形貌，提出了不同于钢和铝或其他金属轧制复合时形成最初结合的结合机制。     

工艺参数对楔横轧42CrMo/Q235复合材料层合轴界面剪切强度的影响

对楔横轧42CrMo/Q235层合轴进行轧制实验和界面剪切强度试验,研究成形角α、展宽角β、断面收缩率Ψ、轧制温度T、基材直径d等工艺参数对界面剪切强度的影响规律.结果表明:对楔横轧层合轴界面剪切强度的影响主次为:断面收缩率Ψ、轧制温度T、基材直径d、展宽角β、成形角α.层合轴界面剪切强度随着断面收缩率Ψ、轧制温度T和基材直径d的增大而增大,但过高的轧制温度与过大的基材直径将减小界面剪切强度;随着展宽角β和成形角α的增大而减小.研究结果对楔横轧层合轴模具优化设计和增强界面结合性能提供了依据.      

AlTiCrN涂层结合界面组织特征与结合性能

以Ti、Al和Cr为靶材,采用阴极离子镀在YT14硬质合金刀具表面制备一层AlTiCrN涂层,通过扫描电镜、能谱仪和X射线衍射仪分析了其表面和界面形貌、化学元素组成和物相,并用线扫描和面扫描研究了涂层中化学元素在结合界面处扩散机理. 用划痕法表征其界面层结合强度,对界面结合机理进行了讨论. AlTiCrN涂层的物相主要以AlN、CrN和TiN为主,涂层在(111)晶面具有很强的择优取向. 涂层中Al、Ti、Cr和N原子数分数高于基体,在结合界面处呈阶梯状过渡分布,基体中C原子扩散进入TiN、AlN和CrN晶格点阵中,形成明显的扩散层. 涂层结合界面为机械﹢扩散形式,其结合方式主要是由吸附结合、扩散结合和化合结合方式组成. 划痕过程中涂层经历弹性变形、塑性变形和涂层剥离三个阶段,界面结合强度为59. 2 N.