通过力学性能、流变性能的测试，以及ＩＲ、ＳＥＭ研究了ＰＥＳ／ＰＡ合金在相容剂存在下的微观结构与宏观性能。结果表明，合成的环氧型相容剂与ＰＥＳ／ＰＡ合金体系中的ＰＡ发生了反应，并且相容剂的加入利于改善ＰＥＳ／ＰＡ合金的相容性，流变性和力学性能，尤其是抗冲性能。     

PA／PP塑料合金的研制

研究了ＰＡ／ＰＰ合金体系的制备和力学性能，结果表明，加入马来酸酐对ＰＰ进行接枝改性后，与ＰＡ共混可以提高合金体系的力学性能。当引入第三组分ＥＰＤＭ或ＮＢＲ组成三元体系ＰＡ／ＰＰ／ＥＰＤＭ或ＰＡ／ＰＰ／ＮＢＲ，可以大幅度提高合金体系冲击强度，且三元组分ＰＡ／ＰＰ／ＥＰＤＭ与ＰＡ／ＰＰ／ＮＢＲ的力学性能接近，可以用ＮＢＲ替代ＥＰＤＭ混入ＰＡ／ＰＰ合金体系中，降低产品成本。     

PE—g—MAA在PA1010／PE合金中的增容作用研究

研究ＰＥ－ｇ－ＭＡＡ（聚乙烯接枝甲基丙烯酸）或ＧＰＥ在ＰＡ１０１０／ＰＥ（尼龙１０１０／聚乙烯）合金中的增容作用。结果表明：合金中ＧＰＥ与ＰＡ１０１０反应形成了ＰＥ－ｇ－ＭＡＡ－ｇ－ＰＡ１０１０增容剂，它影响了ＰＡ１０１０－ＰＥ合金的结构，改善了其力学性能。     

SiC_P／ZA22复合材料组织及性能

对采用半固态搅拌法制备的ＳｉＣＰ／ＺＡ２２复合材料的组织和常温、高温力学性能进行了研究，并和ＺＡ２２基体合金作了对比．研究发现：ＳｉＣ颗粒大多分布于晶界，部分ＳｉＣ颗粒和基体界面上有反应物生成，ＳｉＣ可以充当合金初生相形核衬底，分布于晶内并细化枝晶。力学性能与颗粒分布均匀性、界面结合强度密切相关。和ＺＡ２２合金相比，该复合材料弹性模量上升，冲击韧性下降，高温条件下表现出较好的力学稳定性     

PE－g－MAA在PA1010／PE合金中的增容作用研究

研究ＰＥ－ｇ－ＭＡＡ（聚乙烯接枝甲基丙烯酸）或ＧＰＥ在ＰＡ１０１０／ＰＥ（尼龙１０１０／聚乙烯）合金中的增容作用．结果表明：合金中ＧＰＥ与ＰＡ１０１０反应形成了ＰＥ－ｇ－ＭＡＡ－ｇ－ＰＡ１０１０增容剂，它影响了ＰＡ１０１０－ＰＥ合金的结构，改善了其力学性能．     

Fe3Al基合金力学性能和显微组织的关系研究

显微组织对Ｆｅ３Ａｌ基合金的室温和高温力学性能以及抗蠕变性能有较大影响。研究表明，减少横向晶并不是提高Ｆｅ３Ａｌ合金室温塑性的最有效途径。通过加大形变量，细化显微组织可以明显改善合金的室温力学性能，但会使其高温性能下降。     

添加钇对TiAl合金组织和性能的影响

设计并熔炼了成分为（Ｔｉ５０Ａｌ５０）１００－ｘＹｘ（ａｔｏｍ）＝０－２．０％）的合金，用金相显微镜、扫描电镜、三点弯曲试验等手段，研究了添加钇（Ｙ）对ＴｉＡｌ合金显微组织和力学性能的影响。结果表明：２的添加能改变ＴｉＡｌ合金中Ｏ、Ｎ等间隙原子含量并增加ＴｉＡｌ合金显微组织，使γＴｉＡｌ使合金晶粒细化，促进γ＋α２片层状组织的形成，适量钇的添加能降低ＴｉＡｌ合金中Ｏ、Ｎ等间隙原子含量并增加ＴｉＡｌ     

稀土和锶变质的Al—Si—Mg合金

选择理想的变质剂是制备高强韧铸造Ａｌ－Ｓｉ－Ｍｇ合金的重要手段。采用富镧混合稀土和锶对Ａ３５７合金进行了变质处理,研究了它们对合金铸态、力学性能及含量的影响。结果表明,在保证合金含铁量Ｆｅ≤０．１１％时,富镧混合稀土比锶有更理想的除氢和变质效果细化组织中共晶硅的能力和综合力学性能。     

ZA27合金锻造及挤压成形实验分析

ＺＡ２７合金可以锻造和挤压成形，但挤压成形态塑性偏低，通过热处理可有效地提高挤压合金的综合力学性能。     

喷射沉积成形合金及金属基复合材料力学性能

介绍了近年来北京科技大学在该领域的部分研究结果，重点介绍典型喷射沉积材料（Ｎｉ３Ａｌ金属间化合物为基的合金儿２６１８Ａｌ＋ＳｉＣ颗粒增强金属基复合材料）的显微组织和力学性能。     

锌基颗粒复合材料的磨损特性与力学性能

利用电磁搅拌凝固技术制备了锌基-WC、SiC颗粒复合材料,并研究了其磨损特性与力学性能。WC、SiC颗粒的加入均使材料的耐磨性明显提高,其抗压强度变化不大。     

Study on PTFE/Kevlar49/PA6 Composites

The mechanical properties and material volume fractions of PTFE/Kevlar49/PA6 composite are studied. The focus of this paper is to get the relationship between the volume fraction of three constituents and the mechanical properties of the composite by doing tensile, hardness and wear test. The effect of the constituent volume fractions was evaluated. Short Kevlar49 fibers reinforced PA6 （Polyamide 6） with PTFE filler were studied in five different combinations. The results of the experiments show that the mechanical properties increase with Keviar fibers increase, then they decrease after the Kevlar fiber volume reaches one number.     

锌基石墨复合材料的研究

本课题对铸造锌合金—石墨复合材料的制造工艺、力学性能和摩擦特性、金属—石墨界面状态等进行了研究。在高铝锌基合金ZA—27中,加入5%(wt)以下的石墨时,仍保持比较高的力学性能。而摩擦系数和磨损率则得到成倍的降低。展示了很好的使用前景。     

Study on Surface Optimization by Ion Beams

Preliminary tribo-mechanical properties of IBED filmsof GCr15 bearing steels have been studied in this paperalong with the comparison between IBED films and PVDfilms as well as non-implanted surface in wear resis-tance,micro-hardness,friction and surface morpholo-gy.Experiments gave a consistent picture and statedclearly that TIN films can really improve the tribo-me-chanical properties of materials and have practical usesin a certain sense.However,further theoretical and ex-perimental studies must be performed in respect thatthere are some defects on IBED films.     

Production of 316L stainless steel implant materials by powder metallurgy and investigation of their wear properties

In this study,the mechanical and wear properties of AISI 316L stainless steel implant materials,produced by powder metallurgy(P/M),were investigated.AISI 316L stainless steel powder was cold-pressed with 800 MPa of pressure and then sintered at 1200,1250 and 1300°C for 30 min as three sample groups.The microstructure,and mechanical and wear properties of the resulting steels were investigated.Light optical and scanning electron microscopiese were used to characterize the microstructure of the steels.Room temperature mechanical properties of the steels were determined by hardness measurements and impact tests.Wear was determined using the pin-on-disc wear test,and the results were evaluated according to weight loss.The results indicate that the sintering temperature,time and atmosphere are important parameters that affect the porous ratio of materials produced by P/M.Sintering at high temperature can eliminate small pores and make the residual pores spherical.The wear tests showed that the wear of the AISI 316L stainless steel implants changed depending on the sintering temperature and load.Spherical pores in the samples increase the wear resistance.Moreover,decreasing the porosity ratio of these materials improves all of their mechanical properties.     

SiC颗粒增强铁基粉末冶金复合材料的研究

采用粉末冶金方法制备了ＳｉＣ颗粒增强铁基复合材料,考察了ＳｉＣ颗粒含量与铁基粉末冶金复合材料的显微组织、相对密度、力学性能及磨损性能之间的关系,并探讨了其摩擦磨损机理。结果表明,合适的ＳｉＣ含量能在基本不降低材料强度的基础上大幅度提高耐磨性能。     

反式聚环戊烯橡胶在轮胎胎肩胶中的应用研究

对合成的3种不同相对分子质量的反式聚环戊烯橡胶（TPR）用于轮胎胎肩胶进行了研究,结果表明：与使用天然橡胶（NR）及顺丁橡胶（BR）/NR并用胶相比,TPR硫化胶的回弹性、老化性能、耐磨性和低温性能优异,耐疲劳性能好,动态生热低,滚动阻力小,抗湿滑性稍差,拉伸强度和撕裂性能较差;TPR/NR并用硫化胶与NR相比物理性能有所改善,耐老化性、耐磨性和低温性能优异,回弹性、耐疲劳性及动态生热相当,滚动阻力小,有较好的动态力学性能。相对分子质量较低的TPR2具有较佳的综合性能,TPR不适合单独应用于轮胎胎肩胶,其与NR并用具有较好效果。     

医用不锈钢表面TiN薄膜的组织结构和力学性能研究

为改善医用不锈钢的耐磨性,采用反应磁控溅射在304不锈钢表面沉积了TiN薄膜,研究了Ti过渡层沉积时间对TiN薄膜微观结构和力学性能的影响。通过Ｘ射线衍射仪、扫描电子显微镜、纳米压痕仪、FST1000型薄膜应力测试仪、HSR-2M摩擦磨损试验机和WS-2005型涂层附着力自动划痕仪对样品进行微观组织表征和力学性能测试。结果表明,当Ti过渡层沉积时间为20 min,Ti过渡层厚度为340 nm时,TiN薄膜结晶性最强,硬度和弹性模量达到最大值,分别为21.6 GPa和327.5 GPa,平均摩擦因数达到最小值0.45,临界载荷达到最大值24.7 N,TiN薄膜的力学性能、摩擦性能以及与基体的结合力达到最优。进一步延长Ti过渡层的沉积时间,TiN薄膜的柱状晶组织粗化、力学性能、摩擦性能以及与基体的结合力均降低。     

TiB_2弥散强化Al_2O_3陶瓷刀具的切削性能

研究了Al2O3－TiB2复合陶瓷的力学性能．结果表明，当TiB2含量为20wt％时，能获得较高的综合性能．用此配方制成的陶瓷刀具具有较高的耐磨性能．后刀面磨损量VBmax比YW1低1倍左右．陶瓷刀具的磨损以微区剥离为主要机制．此外，还对比了陶瓷刀具和硬质合金刀具的切削力变化情况．