矽卡岩型含锌铁矿回收锌试验

根据矽卡岩含锌铁矿的矿物组成，对其进行了回收锌的试验，提出先浮后磁流程，并对磨矿细度、石灰用量、硫酸铜用量和丁黄药用量进行了条件试验，得到了合格的锌精矿，为矿山回收锌提供了可行性依据。     

镁质矽卡岩型铁矿尾矿免烧砖

对镁质矽卡岩型铁矿尾矿成分、组成、性质等做了分析,并对尾矿免烧砖工艺中几个影响因素进行了探讨,出了适宜的比例,使免烧砖的性能指标满足国家要求,为类似矿山利用尾矿提供了理论依据和实践经验.     

镁质矽卡岩型铁矿尾矿免烧砖

对镁质矽卡岩型铁矿尾矿成分、组成、性质等做了分析，并对尾矿免烧砖工艺中几个影响因素进行了探讨，出了适宜的比例，使免烧砖的性能指标满足国家要求，为类似矿山利用尾矿提供了理论依据和实践经验。     

中关铁矿钴回收试验研究

通过试验研究,确定对磁选尾矿中Co金属作为副产物回收的可能性,并确定合适的浮选工艺,在不影响原有磁选工艺的前提下,加入适当的调节剂CaO、起泡剂2#油、捕收剂丁基黄药,浮选钴精矿品味即达到0.341%,回收率71.06%,经济效果显著。     

山东潘店地区矽卡岩型铁矿地质特征及找矿意义

山东省潘店地区矽卡岩型铁矿是在综合研究该区航磁异常基础上勘查发现的,该区矿产勘查和科研方面取得了较大进展。在对区内成果资料进行系统收集的基础上,对其铁矿成矿地质条件和矿床特征进行了系统分析梳理,并对铁矿成矿过程及勘查技术方法进行了探讨。根据潘店地区航磁特征,该航磁异常可以分为李屯、潘店、大张和薛官屯共4个次级磁异常,其中李屯和大张次级磁异常的铁矿勘查工作取得了重要进展。勘查工作表明区内隐伏铁矿体形态较为复杂,可分为接触带赋存式、断裂充填式、层间充填式、裂隙贯入式、捕虏体构造式等。区内成矿地质体为中基性侵入体,与济南、淄博、莱芜地区的中基性岩体近于一致,同属中生代燕山晚期;该区铁矿成矿过程为中基性岩浆侵入到奥陶纪马家沟群碳酸盐岩地层中,在岩体与地层接触带附近发生接触交代作用并形成矽卡岩带,富矿热液在有利部位富集沉淀进而形成矽卡岩型铁矿床。在今后工作中要注重在潘店和薛官屯次级磁异常的勘查工作。区内铁矿勘查流程为系统收集资料→面积性物探测量→综合物探剖面测量→重点异常区查证→找矿预测评价及综合研究工作;找矿工作可采用"地质-磁法-重力-电法-钻探-测井"等综合找矿方法,该勘查流程和找矿方法组合为深覆盖区矽卡岩型铁矿勘查提供了勘查经验。     

山西交城矽卡岩铁矿的形成条件

以山西省交城县水峪贯一带的矽卡岩铁矿为主要勘查对象,通过对其进行地质勘查,研究了水峪贯地区的矽卡岩铁矿形成的地质环境、成矿地质条件、地质特征及二长岩体与矽卡岩铁矿成矿作用的关系等。矽卡岩铁矿以西冶岩体为中心,断续环绕岩体分布。岩浆岩主要为以狐偃山为中心的燕山期偏碱性杂岩体,岩性主要为二长岩。二长岩体为矽卡岩铁矿提供了成矿需要的热能、物质来源及容矿空间。     

尾矿库回水对齐大山铁矿浮选影响的实验室模拟

在实验室条件下研究了调军台选厂尾矿库回水中可能含有的淀粉、石灰、氢氧化钠和ＲＡ－３１５对齐大山铁矿浮选的影响。结果表明，影响齐大山铁矿浮选过程的主要因素是回水的ｐＨ值，其他药剂的存在也有一定的影响；但经过调整捕收剂石油磺酸钠的用量可以消除其影响，耐不需对该选厂尾矿库回水进行特殊处理即可作为选厂浮选用水。     

狐堰山矽卡岩型铁矿化学脱硫工艺的探讨

采用化学净化法，对狐堰山矽卡岩型铁矿的脱硫工艺进行了初步研究，应用正交设计者统计分析法得到一组优化组合条件，并做了验证实验，同时考查了粒工对反应的影响，其结果可为进一步理论研究提供了重要依据。     

辽宁某磷铁矿中回收磷灰石浮选试验研究

辽宁某磷铁矿石中P2 O5品位2.57％,主要以磷灰石形式存在.脉石矿物以石英为主.为了回收磷灰石,降低尾矿中P2 O5含量,设计了浮选试验.试验以捕收剂种类、药剂之间相互作用、精选次数为研究对象,探索了磷灰石的浮选指标.研究表明,采用一粗二扫四精浮选流程,在磨矿细度为-0.074 mm占55％条件下,以碳酸钠为调整剂...     

对矽卡岩型铁矿成矿过程的认识和一种新的铁释放、富集机制

铁矿的成矿过程包括:铁的释放、富集和沉淀。矽卡岩反应对铁矿成因的重要性在于阻止铁进入人类尚不能利用铁的硅酸岩矿物中,或者是从已结晶的这些硅酸岩矿物中置换出来。矽卡岩系统中,已有岩石学实验证明,可以释放铁的地质过程有3个,即岩浆矽卡岩形成过程、Na交代过程和绿帘石交代钙铁榴石、钙铁辉石的过程。释放出的铁多与Cl、F组成络合物溶解在流体从而富集。自然界存在碳酸岩浆,但不存在矽卡岩浆。     

含铁低品位氧化锌矿石浸出研究

针对含铁低品位氧化锌矿石,进行了碱性浸出与硫酸浸出研究.其中碱性浸出主要考察了采用不同浸出剂时浸出时间以及采用氨水——氯化铵作浸出剂时浸出温度对锌、铁浸出率的影响;硫酸浸出主要考察了硫酸初始浓度、矿浆液固比以及不同硫酸初始浓度时浸出温度和不同浸出温度时浸出时间对锌、铁浸出率的影响.研究结果表明,碱性浸出时锌浸出率不到5...     

红土镍矿镍和铁的综合回收试验

多米尼加某红土镍矿属强烈氧化的含镍酸性铁矿石,矿石中主要含有褐铁矿、石英、氧化铝和氧化镁等矿物.采用硫酸常压浸出-黄钠铁矾沉铁工艺对该红土镍矿进行湿法回收工艺研究.研究结果表明:镍、铁的浸出率分别为91.95％和67.96％;经黄钠铁矾法沉淀分离和焙烧工艺能够获得Fe品位为55.56％的氧化铁产品,且镍和铁的总回收率分别达到89.39％和67.46％.     

磁法勘探在铁矿勘查中的应用

磁法勘探是利用地下各种岩（矿）石间的磁性差异所引起的磁性变化（磁异常）来寻找地下有用矿产或查明地下地质构造的一种地球物理勘探方法,是应用最早的地球物理勘探方法,在铁矿勘探中更是使用广泛,成效显著,随着磁测仪器的逐步更新和磁学理论的日臻完善,磁法勘探必将在地质科学中发挥更大的作用。     

Development of carbon composite iron ore micropellets by using the microfines of iron ore and carbon-bearing materials in iron making

Iron ore microfines and concentrate have very limited uses in sintering processes. They are used in pelletization; however, this process is cost intensive. Furthermore, the microfines of non-coking coal and other carbon-bearing materials, e.g., blast-furnace flue dust (BFD) and coke fines, are not used extensively in the metallurgical industry because of operational difficulties and handling problems. In the present work, to utilize these microfines, coal composite iron oxide micropellets (2-6 mm in size) were produced through an innovative technique in which lime and molasses were used as binding materials in the micropellets. The micropellets were subsequently treated with CO₂ or the industrial waste gas to induce the chemical bond formation. The results show that, at a very high carbon level of 22wt% (38wt% coal), the cold crushing strength and abrasion index of the micropellets are 2.5-3 kg/cm2 and 5wt%-9wt%, respectively; these values indicate that the pellets are suitable for cold handling. The developed micropellets have strong potential as a heat source in smelting reduction in iron making and sintering to reduce coke breeze. The micropellets produced with BFD and coke fines (8wt%-12wt%) were used in iron ore sintering and were observed to reduce the coke breeze consumption by 3%-4%. The quality of the produced sinter was at par with that of the conventional blast-furnace sinter.     

铁矿石中全铁的分析方法改进

该文介绍了无汞测铁技术应用于铁矿石中全铁的测定新方法。用甲基橙作SnCl2还原Fe3＋的指示剂,再用K2Cr2O7标准溶液滴定亚铁。     

滴定分析法测定铁矿石中铁含量

SnCl2-TiCl3-K2Cr2O7滴定分析法是试样用盐酸加氟化钠加热分解,让有铁的氧化物及硅酸盐都变成氧化铁进入溶液中。先用氯化亚锡将大部分三价铁离子还原成二价铁,以钨酸钠为指示剂,用三氯化钛将剩余的三价铁还原成二价铁至生成"钨蓝",再用重铬酸钾标准溶液氧化至蓝色消失,加入硫磷混合酸以二苯胺磺酸钠为指示剂,用重铬酸钾标准液滴定。通过调节不同的还原酸度,还原温度,试剂用量和溶样时间,对其最佳实验条件进行了优化。用SnCl2-TiCl3-K2Cr2O7滴定分析法测定铁矿石中铁含量,相对标准偏差在0.68%~2.6%之间,回收率在91.9%~97.9%之间,方法准确可靠。     

氧化锌矿的碱浸出

将处理氧化铝矿物的拜耳法移植于氧化锌矿的湿法处理形成"锌拜耳法",用浓碱浸出氧化锌矿,然后降低温度或浓度使锌以氢氧化锌的形式析出,析出母液经浓缩处理后返回浸出矿,研究氧化锌矿的碱浸出过程。研究结果表明:当氢氧化钠浓度为5mol/L,浸出温度为85℃,液固比为10:1,浸出时间为2h时,氧化锌矿中锌的浸出率为77%,铅的浸出率为9%,镉的浸出率为5%。     

铁精粉氧化过程的动力学研究

通过恒温和均匀升温实验,采用大载荷热重分析仪研究了铁精粉氧化过程动力学.结果表明:均匀升温过程中,铁精粉氧化的主要控制环节变化是外扩散型→内扩散型→外扩散型,氧化结束后,部分Fe2O3发生分解反应生成Fe2O4和O2,使得TG曲线质量变化率减小;等温实验也证明了氧化主体部分的控制环节是内扩散,其表观活化能为26.193 kJ·mol-1;铁精粉氧化过程促进了钛元素富集,改变了产物的微观结构.     

Study on the pre-treatment of oxidized zinc ore prior to flotation

The pre-treatment of zinc oxide bearing ores with high slime content is important to ensure that resources are utilized optimally. This paper reports an improved process using hydrocyclone de-sliming, dispersion reagents, and magnetic removal of iron minerals for the pre-treatment of zinc oxide ore with a high slime and iron content, and the benefits compared to traditional technologies are shown. In addition, this paper investigates the damage related to fine slime and iron during zinc oxide flotation, the necessity of using hydrocyclone de-sliming together with dispersion reagents to alleviate the influence of slime, and interactions among hydrocyclone de-sliming, reagent dispersion, and magnetic iron removal. Results show that under optimized operating conditions the entire beneficiation technology results in a flotation concentrate with a Zn grade of 34.66% and a recovery of 73.41%.