CeO2对等离子喷涂Cr2O3涂层组织和滑动磨损性能的影响

通过在Cr2 O3 材料中加入不同含量的CeO2 添加剂 ,探讨了稀土对等离子喷涂Cr2 O3 涂层组织、抗拉结合强度和滑动磨损性能的影响。研究结果表明 ,添加适量CeO2 可以提高Cr2 O3 涂层的致密性、抗拉结合强度和耐磨性。在滑动磨损条件下 ,Cr2 O3 涂层的磨损为疲劳磨损 ,CeO2 的加入不会改变涂层的磨损失效机制。涂层的耐磨性与涂层的抗拉结合强度成正比。     

等离子喷涂氧化铝陶瓷涂层组织

用X射线衍射、扫描电镜和显微硬度计研究了45钢表面等离子喷涂Al2O3陶瓷涂层的微观组织结构、显微硬度,同时对涂层的界面结合特性进行了考察。结果表明,喷涂前的α-Al2O3相粉末,经喷涂后,存在α-Al2O3相向γ-Al2O3相的转变,且以γ-Al2O3相为主相。在金属基体与陶瓷层之间加入NiCrAl层后热膨胀系数不匹配性得到一定程度的改善,从而使涂层内应力降低,结合强度得以提高。     

等离子喷涂Al2O3-TiO2涂层的干摩擦磨损特性

利用等离子喷涂方法制备了Al2O3-TiO2涂层,测定了涂层的显微硬度和表观气孔率,并对涂层与GCr15钢配副,在不同P-V值及无润滑情况下进行了球-盘式摩擦磨损试验。试验结果表明：Al2O3-TiO2（w（TiO2）=13%）涂层在低速低载条件下具有显著的减摩抗磨性能;Al2O3-TiO2（w（TiO2）=20%）和Al2O3-TiO2（w（TiO2）=40%）涂层在高压力、转速工况下,具有优良的干摩擦特性。研究结果为实际生产选择涂层提供了依据。     

HVOF制备的Ni60/WC-10Co4Cr涂层组织和滑动磨损性能研究

为了降低超音速火焰(HVOF)喷涂金属陶瓷涂层的材料和加工成本,使其在更大范围内替代会给环境带来严重污染的电镀硬铬(EHC)涂层,本文将不同比例的Ni60与WC-10Co4Cr相混合,并采用HVOF喷涂工艺分别制备了5种金属陶瓷复合涂层.研究了这些涂层的显微组织、基本性能和滑动磨损性能,并将其与EHC涂层进行对比.结果表明:所有HVOF喷涂工艺制备的Ni60/WC-10Co4Cr涂层都很致密(孔隙率小于1%),随着WC-10Co4Cr比例的增加,Ni60/WC-10Co4Cr涂层的硬度从688.3 HV0.3增加到1 203.4HV0.3,磨损率由2.75×10~(-5) mm~3/N·m降低到7.29×10~(-7) mm~3/N·m.并且,所有HVOF喷涂工艺制备的涂层和与其配对的摩擦副的磨损率以及磨擦系数均低于EHC涂层,表现出良好的抗滑动磨损性能.     

等离子喷涂Mo涂层在常温至300 ℃的干摩擦磨损性能

采用大气等离子喷涂在45钢表面制备了Mo涂层,研究了Mo涂层的微观结构和力学性能,并考察了涂层与GCr15球对摩时在常温至300℃时的干摩擦磨损性能.结果表明:等离子喷涂制备的Mo涂层较致密,涂层与基体结合良好,涂层的平均硬度为329.0 HV.随着环境温度的升高,涂层的摩擦因素和体积磨损率均逐渐增加.Mo涂层在室温和300℃时的摩擦因素分别为0.52和1.14.涂层在300℃时的体积磨损率为11.2×10~(-5)mm~3/N·m是常温下的5倍.随着环境温度的增加,等离子喷涂Mo涂层的层间剥落、氧化和粘着磨损逐渐加剧.     

高温球阀喷涂Al2-O3-TiO2和WC-Co涂层的耐磨粒磨损性能

采用激光等离子喷涂技术在已失效的高温球阀基体材料上制备Al2O3-TiO2与WC-Co金属陶瓷涂层,在摩擦磨损试验机上对涂层的耐磨粒磨损性能进行研究,利用扫描电镜、光学显微镜对涂层的显微组织结构、磨损表面及其相组进行分析,并采用维氏显微硬度计、WE-50型液压拉伸验机和箱式电热炉对涂层的显微硬度、结合强度及抗热震性进行测试.结果表明,Al2O3-TiO2金属陶瓷涂层的综合性能最好,可以用于失效高温球阀的再制造.     

等离子喷涂纳米和微米Al_2O_3-TiO_2涂层摩擦磨损性能研究

采用大气等离子喷涂的方法制备了纳米和微米Al2O3-TiO2涂层,其中w(TiO2)=13%.分析了涂层组织形貌特征和结合强度等性能,研究了两种涂层在不同载荷下的摩擦磨损性能.结果表明,纳米Al2O3-TiO2涂层是由未熔或半熔纳米颗粒区域与完全熔融粒子铺展区域共同构成的,孔隙率低,显微硬度、结合强度均高于层状结构的微米涂层,且纳米涂层磨损量明显小于微米涂层.高载荷下磨屑均匀细化、圆整,形成微滚珠效应,纳米涂层稳态摩擦系数随载荷增大而下降,而微米涂层摩擦系数随载荷变化不明显.     

等离子喷涂Al2O3涂层内粒子间结合的研究

论述了通过对等离子喷涂Ａｌ２Ｏ３涂层内电镀铜，利用镀入的铜在涂层断面上的分布，定量地测定涂层内粒子间结合的方法及结果。结果表明，粒子间最大的平均结合率占所有界面的３２％。这种有限的结合被认炎是受熔化粒子的温度及熔滴与涂层的作用时间影响所致。     

等离子喷涂氧化铝陶瓷涂层的组织与相结构分析

本文利用等离子喷涂设备,制备了以镍包铝粉末作为打底层,以Ni60混合不同重量百分比的Al2O3陶瓷粉末作为工作涂层的不同试样,通过扫描电镜、X射线衍射仪、显微硬度计和VIDAS图像分析仪等仪器,研究了涂层的组织和相结构,结果表明,涂层为Ni奥氏体相上弥散分布Ni3B、NiB、Cr3B、Cr23B6等硬质相,另一硬质相Al2O3则主要以亚稳相γ-Al2O3存在,且涂层相结构不单一,为Ni基晶态/非晶态结构。     

等离子喷涂Al_2O_3-TiO_2涂层的干摩擦磨损特性

利用等离子喷涂方法制备了Al2O3-TiO2涂层,测定了涂层的显微硬度和表观气孔率,并对涂层与GCr15钢配副,在不同P-V值及无润滑情况下进行了球 - 盘式摩擦磨损试验.试验结果表明:Al2O3-TiO2(w(TiO2)=13%)涂层在低速低载条件下具有显著的减摩抗磨性能;Al2O3-TiO2(w(TiO2)=20%)和Al2O3-TiO2(w(TiO2)=40%)涂层在高压力、转速工况下,具有优良的干摩擦特性.研究结果为实际生产选择涂层提供了依据.     

Ce对高铝青铜超音速等离子喷涂层组织结构的影响

将稀土Ce和高铝青铜粉体通过研磨混合,采用超音速等离子喷涂技术制备含稀土Ce的高铝青铜合金粉体涂层,采用XRD、SEM、EDS等手段对不同铈含量的高铝青铜合金粉体喷涂层表面组织、微观应力和界面元素扩散进行观察和分析,研究微量稀土元素铈对高铝青铜合金粉体涂层组织结构和界面元素扩散的影响.结果表明:粉体研磨后,铈粉以片状和碎块状方式粘结在高铝青铜粉体颗粒表面,并且出现微合金化现象.高铝青铜合金粉体的喷涂流动性和熔覆性随含铈量的增加而变大,涂层表面存在微观压应力,并随着含铈量的增加压应力呈现先降低后增加的趋势.随铈含量的增加,涂层合金与基体表面润湿性能增强,界面处Cu、Al元素贫化现象减弱.     

CeO2对激光熔覆生物陶瓷涂层组织形貌的影响

采用激光熔覆技术在Ti-6Al-4V合金基体上制备生物陶瓷复合涂层,研究稀土氧化物CeO2的加入对生物陶瓷涂层组织的影响.结果表明,CeO2对合成HA、β-Ca3(PO4)2和其它钙磷基活性生物陶瓷具有明显的催化作用,且可抑制基体元素对表层组成的干扰;改善熔覆层的组织,使其均匀化,细化;熔覆层与基体结合紧密,能实现良好的冶金结合.     

Effect of Gd2O3 on the microstructure and thermal properties of nanostructured thermal barrier coatings fabricated by air plasma spraying

The nanostructured 4–8 mol% Gd_2O_3-4.5 mol% Y_2O_3-ZrO_2(4–8 mol% Gd YSZ) coatings were developed by the atmospheric plasma spraying technique. The microstructure and thermal properties of plasmasprayed 4–8 mol% Gd YSZ coatings were investigated. The experimental results indicate that typical microstructure of the as-sprayed coatings were consisted of melted zones, nano-zones, splats, nano-pores,high-volume spheroidal pores and micro-cracks. The porosity of the 4, 6 and 8 mol% Gd YSZ coatings was about 9.3%, 11.7% and 13.3%, respectively. It was observed that the addition of gadolinia to the nano-YSZ could significantly reduce the thermal conductivity of nano-YSZ. The thermal conductivity of Gd YSZ decreased with increasing Gd_2O_3 addition. And the reduction in thermal conductivity is mainly attributed to the addition of Gd_2O_3, which results in the increase in oxygen vacancies, lattice distortion and porosity.     

Cr2O3掺杂对ZnO陶瓷薄膜低压压敏性能的影响

为了制备高性能ZnO陶瓷薄膜低压压敏电阻器,利用新型Sol-Gel方法研究了Cr2O3掺杂对ZnO陶瓷薄膜低压压敏性能的影响．复合先驱体溶液由Bi2O3,Sb2O3,MnO及Cr2O3掺杂的ZnO纳米粉体均匀分散于含有Zn(CH3COO)2,Bi2O3,Sb2C3,MnO及Cr2O3的溶胶中制成．研究结果表明：利用新型Sol-Gel方法制备的ZnO陶瓷薄膜中,ZnCr2O4相在较低的Cr2O3添加量时出现,当Cr2O3的摩尔分数为0．75％时,ZnO陶瓷薄膜的非线性系数α为7,压敏电压为6V,漏电流密度为0．7μA/mm^2。     

SiO2-B2O3-ZrO2陶瓷涂层的制备及性能

采用料浆法以水玻璃为粘结剂在不锈钢基体表面制备了主要组成为SiO₂-B₂O₃-ZrO₂的陶瓷涂层。利用XRD、TG-DTA、SEM分析了陶瓷涂层的相组成及显微组织,并测试了涂层的抗热震性能和显微硬度。结果表明,当陶瓷骨料(g)与水玻璃(mL)的比例为1∶20时,在850℃下保温30min可得到结构致密的陶瓷涂层;在800℃下涂层经热震31次无裂纹,无脱落,表面显微硬度达到456.8MPa;所制备的陶瓷涂层与不锈钢基体之间不仅有机械物理的嵌合,还存在元素扩散,涂层与基体密着性好,结合紧密。     

镁合金等离子喷 Al/Al2 O3涂层配比及参数优化

用等离子弧在 AZ31镁合金表面喷涂 Al＋Al2 O3粉末,制备 Al／Al2 O3复合材料涂层。观察分析不同粉末配比时涂层的划痕试验结果、SEM 照片以及 XRD 衍射数据,确定 Al＋Al2 O3的合理配方。通过正交试验设计,分别对涂层密度、显微硬度和沉积率等指标进行分析,最后确定制备复合材料涂层的最优工艺参数。     

Cu-Zn-Al2O3 nanocomposites: study of microstructure,corrosion, and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechan-ically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

纳米级TiO2添加剂对Al2O3陶瓷微观结构与烧结性能的影响

用微米级和纳米级两种不同的TiO2作为烧结助剂加入Al2O3陶瓷中，研究其对Al2O3陶瓷微观结构和烧结性能的影响。结果表明，纳米TiO2能更好的提高Al2O3陶瓷的烧结活性，降低烧结温度，Al2O3陶瓷在1600℃以下就可致密烧结。另外，纳米TiO2的加入，对Al2O3陶瓷的微观结构也产生影响，加入纳米TiO2的试样其晶粒尺寸比加入微米TiO2的大，TiO2与A12O3形成固溶体。     

纳米级TiO2添加剂对Al2O3陶瓷微观结构与烧结性能的影响

用微米级和纳米级两种不同的TiO2作为烧结助剂加入Al2O3陶瓷中,研究其对Al2O3陶瓷微观结构和烧结性能的影响.结果表明,纳米TiO2能更好的提高Al2O3陶瓷的烧结活性,降低烧结温度,Al2O3陶瓷在1 600 ℃以下就可致密烧结.另外,纳米TiO2的加入,对Al2O3陶瓷的微观结构也产生影响,加入纳米TiO2的试样其晶粒尺寸比加入微米TiO2的大,TiO2与Al2O3形成固溶体.