选用Fe基非晶合金粉末(含有Cr、Mo、Ni、P、B、Si),采用等离子喷涂方法在Q235基体上制备了金属玻璃涂层.在自行设计的腐蚀实验装置中将Q235钢、1Cr18Ni9Ti不锈钢和覆有Fe基金属玻璃涂层的Q235钢浸入450,℃的高温液态无铅钎料Sn-3.5,Ag-0.5,Cu中进行腐蚀,利用扫描电子显微镜微观分析了腐蚀后的微观形貌及腐蚀产物.研究结果表明:相同实验条件下,Q235钢和1Cr18Ni9Ti不锈钢表面均腐蚀严重,断面微观组织分为钎料层、腐蚀层和基体层.其中Q235钢的腐蚀剧烈,腐蚀层成分为FeSn2;1Cr18Ni9Ti不锈钢腐蚀较严重,腐蚀层成分为(Fe,Cr)Sn2.Q235基体表面的Fe基金属玻璃涂层腐蚀前后断面微观形貌变化不大,没有出现明显的腐蚀分层,表现出了非常好的耐高温无铅钎料腐蚀的能力.     

Al3Ti和TiC/Al3Ti激光熔覆涂层的高温氧化和浸泡腐蚀性能

采用激光熔覆技术在铝合金表面制备了Al3Ti金属间化合物和TiC颗粒增强Al3Ti基复合材料涂层,对比分析了两种涂层的高温氧化和浸泡腐蚀性能。结果表明:在稍低于铝合金熔点(600℃)循环氧化70h后,两种涂层均没有明显的氧化增重,显示出较强的抗氧化性。氧化温度为900℃时,涂层的氧化增重呈抛物线规律增长,且复合材料涂层的抗氧化性低于Al3Ti涂层。在NaCl质量分数为3.5%的溶液中浸泡15天后,复合材料涂层的腐蚀程度最轻,涂层中的硬质相Al3Ti和TiC抑制了点蚀的扩展,但两种涂层均提高了铝合金的抗腐蚀性能。     

固态NaCl诱导的TiAlN多层涂层热腐蚀行为研究

采用高功率脉冲磁控溅射(HIPIMS)技术耦合多弧离子镀技术,在钛合金和304不锈钢基体表面沉积高致密TiAlN/Me多层纳米复合膜层,通过SEM、XRD、XPS等方法对涂层的宏微观结构进行表征,在500 ℃高温的固态盐膜环境下,研究不同金属子层种类对涂层高温热腐蚀能力的影响规律．结果表明:TiAlN/Ti多层涂层孔隙率低至0.049 %,以点蚀为主要腐蚀形式的涂层热腐蚀面积占比为2.948%,分别达到304不锈钢和Ti-6Al-4V钛合金基体耐腐蚀能力的24.046和23.041倍．TiAlN/TiAl涂层由于涂层表面缺陷和层间缺陷分布广泛,涂层腐蚀面积占比达到67.090 %．TiAlN/Ti比TiAlN/TiAl多层纳米复合膜层有更优的高温热腐蚀性能．      

溅射Ni16Cr2.5Al微晶涂层及其氧化行为

NiCrAl是NiCrAlY型包覆涂层的主要成分,对NiCrAl涂层的沉积形态及其氧化行为的研究具有重要科学意义.磁控溅射在不锈钢Fe18Cr9Ni0.1Ti基体上制备出Ni16Cr2.5Al微晶涂层(基体分倾斜45 和竖直90 两种方式悬挂),使用SEM/EDAX,X ray,对Ni16Cr2.5Al微晶涂层及其氧化膜进行了分析,以探索高温合金用涂层形成及其氧化膜形成机制.     

不锈钢热浸镀铝抗高温氧化腐蚀性能的研究

:钢材经热浸镀铝后 ,具有了良好的抗高温氧化腐蚀性能。为进一步提高 1Cr18Ni9Ti、1Cr13不锈钢的高温使用性能 ,本文对两种材料进行了热浸镀稀土铝合金处理和抗高温氧化性能的试验。高温氧化试验结果表明 ,1Cr18Ni9Ti、1Cr13不锈钢经热浸镀铝处理后抗高温氧化腐蚀性能明显提高 ,这主要取决于合金层中Al-Fe金属间化合物在高温氧化中的变化。 90 0℃氧化 5 0 0h ,1Cr18Ni9Ti钢浸镀件形成致密的α -Al2 O3氧化膜和 β -NiAl相层 ;1Cr13钢浸镀件形成Al2 O3氧化膜及Cr2 O3氧化物。研究表明 ,不锈钢中Cr、Ni元素对提高抗高温氧化性具有重要的影响作用。     

MA956 ODS合金微晶涂层对1Cr18Ni9Ti不锈钢氧化性能的改善

采用高频电脉冲沉积技术在1Cr18Ni9TI不锈钢表面上沉积了厚度约为50um的MA956 ODS合金纳米微晶涂层,涂层与基体之间呈现良好的冶金结合,在1000度静态空气中对1Cr18Ni9Ti试样与表面施加涂层试样进行了总计100h的恒温氧化实验,用AFM,SEM,EDX和XRD分别对涂层和氧化后试样的形貌,成分和组成进行了观察和分析,结果显示,1Cr18Ni9Ti表面沉积MA956ODS合金纳米微晶涂层促进了Cr的选择氧化,提高了1Cr19Ni9Ti表面氧化膜的粘附性,了1Cr18Ni9Ti抗高温氧化性能。     

镍基涂层和2种钢的冲刷腐蚀特性及其电化学行为

研究了2种超音速火焰喷涂Ni基涂层(Ni60JH与Delelo50)和2种钢(1Crl8Ni9Ti与20钢)在液固两相流中，冲刷腐蚀的交互作用及其电化学行为，并对其冲刷腐蚀机制进行了探索性分析．研究结果表明，Ni60JH和Delelo50涂层的腐蚀质量损失率分别为基体材料的1／30和1／16，Ni60JH涂层的耐冲刷腐蚀性能比基体高15倍多，并与1Crl8Ni9Ti不锈钢相当，且Delelo50涂层的耐冲刷腐蚀性能比基体高5倍多．Ni60JH涂层主要以切削、犁削冲蚀磨损机理为主，而Delel050涂层和2种钢主要以犁削、塑性变形、翻边冲蚀磨损机理为主．2种涂层和不锈钢在纯腐蚀时均处于钝化状态，在冲刷腐蚀时均处于活化溶解状态．     

溶胶-凝胶技术提高不锈钢抗高温氧化及铝合金阳极氧化膜的耐蚀性能

采用溶胶--凝胶法在不锈钢基体表面制备ZrO2和Al2O3涂层,并对铝合金阳极氧化膜进行封孔处理.采用高温循环氧化法研究ZrO2和Al2O3涂层抗高温氧化性能,通过电化学阻抗谱和剥蚀法分析溶胶--凝胶法封孔后铝合金氧化膜的耐腐蚀性能.结果表明:ZrO2和Al2O3涂层的抗高温氧化性能随涂层厚度增加而提高;铝合金阳极氧化膜的耐腐蚀性能也随封孔次数的增加而提高,但当封孔处理超过8次后,阻抗值和腐蚀程度基本不随封孔次数发生变化;实施相同次数封孔处理后,Al2O3溶胶的封孔效果略优于ZrO2溶胶的封孔效果.     

Q235钢热浸渗铝层的组织分析和性能

分析了Q235钢热浸渗铝层的组织,并对其抗高温氧化和耐高温腐蚀性能进行了研究.显微硬度试验结果表明渗层硬度可达1000 HV,并具有较大的脆性.经扩散退火后,渗层组织和显微硬度都发生了明显的变化.高温氧化和热腐蚀试验结果表明,渗铝Q235钢的抗高温氧化性能和1Cr18Ni9Ti奥氏体不锈钢相当,而耐热腐蚀性能明显优于后者.     

Ti60合金电弧离子镀Ti-Al-Cr防护涂层的抗循环热冲击性能

利用电弧离子镀技术在Ti60合金表面制备了Ti-48Al-5Cr和Ti-48Al-12Cr(原子分数,%)两种涂层.研究了Ti60及涂层样品在高温(900℃和950℃)和室温(强制水冷)之间的抗循环热冲击能力.分析了热冲击过程中样品的质量变化、相组成、表面及截面形貌的显微照片.结果显示Ti-48Al-12Cr涂层具有较好的抗循环热冲击性能,能有效地保护Ti60基体.而Ti-48Al-5Cr涂层不能有效地保护基体,这是因为Cr元素含量不同导致氧化机制的差异.热冲击实验加速了氧化物的剥落和破坏,因此加速了内氧化的发生和裂纹的萌生、扩展.     

热处理对硝酸熔盐中347H不锈钢腐蚀行为的影响

利用静态熔盐浸泡实验,研究了不同晶粒度的347H不锈钢在565 ℃混合硝酸熔盐(60%NaNO₃+40%KNO₃)中长达120 h的腐蚀行为.通过增重法绘制腐蚀动力学曲线,并研究347H不锈钢的表面腐蚀产物、物相、腐蚀表面微区成分,解释347H不锈钢在硝酸熔盐中的腐蚀机理.结果表明:经过固溶处理调控晶粒度的347H不锈钢在熔盐腐蚀中腐蚀速率有所降低,腐蚀动力学曲线变为线性增长趋势.通过XRD检测得到,347H不锈钢在硝酸熔盐中的腐蚀产物主要是Fe₂O₃和少量的Fe₃O₄及NaFeO₂.Fe₃O₄,结构致密,能有效减小硝酸熔盐对钢基体的腐蚀,导致347H不锈钢在腐蚀后期质量损失有所降低.腐蚀产物形貌和横截面厚度分析结果表明,经过1 160 ℃固溶处理1 h后不锈钢晶粒度达到7级时,腐蚀层厚度达到最低为0.661 μm,此时347H不锈钢在硝酸熔盐中的耐腐蚀性达到最好.     

Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel

The effects of chitosan inhibitor on the corrosion behavior of 2205 duplex stainless steel were studied by electrochemical measurements, immersion tests, and stereology microscopy. The influences of immersion time, temperature, and chitosan concentration on the corrosion inhibition performance of chitosan were investigated. The optimum parameters of water-soluble chitosan on the corrosion inhibition performance of 2205 duplex stainless steel were also determined. The water-soluble chitosan showed excellent corrosion inhibition performance on the 2205 duplex stainless steel. Polarization curves demonstrated that chitosan acted as a mixed-type inhibitor. When the stainless steel specimen was immersed in the 0.2 g/L chitosan solution for 4 h, a dense and uniform adsorption film covered the sample surface and the inhibition efficiency (IE) reached its maximum value. Moreover, temperature was found to strongly influence the corrosion inhibition of chitosan; the inhibition efficiency gradually decreased with increasing temperature. The 2205 duplex stainless steel specimen immersed in 0.4 g/L water-soluble chitosan at 30℃ displayed the best corrosion inhibition among the investigated specimens. Moreover, chitosan decreased the corrosion rate of the 2205 duplex stainless steel in an FeCl₃ solution.     

正压水煤气余热锅炉防磨瓦腐蚀失效分析

1Cr20Ni14Si2不锈钢防磨瓦在水煤气余热锅炉中运行被腐蚀甚至断裂,对正压水煤气立式余热锅炉过热器不锈钢防磨瓦断裂失效进行研究。采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和电子能谱分析仪(EDS)设备对锅炉1Cr20Ni14Si2不锈钢失效防磨瓦的表面腐蚀褐色粉末、不锈钢表面和人为断面成分进行测试。XRD测试结果表明表面褐色粉末存在多种金属氧化物和硫化物;EDS实验检测结果表明：不锈钢表面含大量S和O。这说明1Cr20Ni14Si2不锈钢在焦化炉中易被S腐蚀而失去不锈钢特性。EDS结果分析发现不锈钢Ni含量明显低于国标要求含量,降低了不锈钢韧性并降低其防腐蚀性能。烟气中S、C和O经腐蚀孔隙进入材料内部加速不锈钢内部腐蚀。研究结果对水煤气余热锅炉防磨瓦材料选型和防磨结构优化具有指导意义。     

SiO2-B2O3-ZrO2陶瓷涂层的制备及性能

采用料浆法以水玻璃为粘结剂在不锈钢基体表面制备了主要组成为SiO₂-B₂O₃-ZrO₂的陶瓷涂层。利用XRD、TG-DTA、SEM分析了陶瓷涂层的相组成及显微组织，并测试了涂层的抗热震性能和显微硬度。结果表明，当陶瓷骨料(g)与水玻璃(mL)的比例为1∶20时,在850℃下保温30min可得到结构致密的陶瓷涂层；在800℃下涂层经热震31次无裂纹，无脱落，表面显微硬度达到456.8MPa；所制备的陶瓷涂层与不锈钢基体之间不仅有机械物理的嵌合，还存在元素扩散，涂层与基体密着性好，结合紧密。     

347H不锈钢电化学腐蚀行为研究

使用电化学工作站检测热轧态347H不锈钢、固溶态酸洗347H不锈钢和固溶处理态347H不锈钢在3.5wt.%NaCl、5wt.%H₂SO₄和5wt.%NaOH腐蚀介质中的电化学腐蚀行为,绘制极化曲线和电化学阻抗谱研究固溶处理对347H不锈钢电化学腐蚀行为的影响.结果表明:在3.5wt.%NaCl腐蚀介质中,固溶态酸洗347H不锈钢表现出最佳的耐腐蚀性,而固溶处理会降低热轧态347H不锈钢的耐腐蚀性能.在5wt.%H₂SO₄腐蚀介质中,通过1 160 ℃固溶处理2 h,347H不锈钢的耐腐蚀性有所提高.在5wt.%NaOH腐蚀介质中,热轧态347H不锈钢的自腐蚀电流密度和其他状态的347H不锈钢相比要小一个数量级,因此,热轧态347H不锈钢更耐5wt.%NaOH腐蚀介质的腐蚀.     

不同生物炭进入土壤后对304不锈钢腐蚀的影响

生物炭在土壤应用过程,不可避免地会对与土壤之间接触的机械设备部分产生腐蚀作用。为探究生物炭应用于农业生产中对机械设备以及金属工具损耗的影响,采用分别在700、400和100℃温度下裂解制备的小麦秸秆生物炭(WB)、水稻秸秆生物炭(RB)和松木生物炭(PB)的生物炭对304不锈钢板材进行腐蚀处理,并测量其极化曲线和电化学阻抗谱和腐蚀表现。结果表明:与空白组(CK)对比,相较于304不锈钢的腐蚀速率,在施入WB的土壤中,腐蚀速率会随着WB裂解温度的增大而增大;而加入RB的土壤会加剧不锈钢的腐蚀,其中在加入400℃RB的土壤中腐蚀速率达到最大;这是因为WB和RB的加入会提升土壤中的Cl~-含量至足以达到点蚀效应的程度加速了不锈钢板材的腐蚀。与此同时,发现100℃制备的PB生物炭可以抑制不锈钢的腐蚀。总而言之,不同生物质和制备温度的生物炭在土壤实际应用中表现出不同的腐蚀和抗腐蚀特性,因此深入研究这些方面将为其农业应用具有深远影响。     

压力管道金属材料焊接接头的流动加速腐蚀性能

通过温度、压力、流速可控的流动加速腐蚀实验机,模拟某冷凝水管线工况,对20钢分别与20钢、Q345R钢和304不锈钢焊接接头的流动加速腐蚀性能进行研究。通过扫描电镜(SEM)和能谱仪(EDS)对腐蚀产物进行表征。结果表明:腐蚀速率从大到小依次为20钢-20钢、20钢-Q345R钢、20钢-304不锈钢;相对于20钢母材,3种焊接接头的腐蚀电流均变小,腐蚀电位均向正方向偏移,构成电偶腐蚀时加速了母材的腐蚀速度。在介质流动的状态下,20钢-20钢焊接接头腐蚀产物膜为柱状,20钢-Q345R钢焊接接头腐蚀产物膜为分层片状结构,20钢-304不锈钢焊接接头腐蚀产物为网状结构,其覆盖率从大到小依次为20钢-Q345R,20钢-304不锈钢,20钢-20钢。     

南海东部海域不锈钢紧固件的腐蚀失效分析

【目的】为配合南海东部海区的海洋环境调查,研究该海区不锈钢紧固件发生的腐蚀现象。【方法】使用奥氏体不锈钢紧固件,利用海洋平台钢桩和不锈钢钢缆紧固相应的调查设备,通过一年的海试,检查该类不锈钢紧固件的腐蚀情况。【结果】不锈钢紧固件腐蚀严重,不同形状的材料腐蚀部位和程度不同。不锈钢的腐蚀主要表现为点蚀和隙缝腐蚀等局部腐蚀,严重时穿孔、断裂失效。【结论】建议在海洋金属结构中尽量使用同牌号同批次的同种金属材料,以确保材料电极电势相同,减小宏观电池的形成;若确实需要使用异种金属,必须对异种材料间进行电绝缘。     

铁素体不锈钢在盐酸溶液中的缓蚀行为控制

通过电化学方法、失重曲线和SEM分析，考察了铁素体不锈钢在盐酸溶液中的腐蚀过程，重点分析了SDS和SAD两种缓蚀剂对盐酸溶液中不锈钢腐蚀行为的控制作用.研究结果表明:不锈钢在单一盐酸溶液中始终保持活性溶解状态，腐蚀方式以均匀腐蚀为主，沿晶界处易发生晶间腐蚀.SDS和SAD缓蚀剂均为界面型缓蚀剂，其缓蚀效率存在极大值.当缓蚀剂质量分数为0015%时，两种缓蚀剂均表现出良好的缓蚀性能，可降低不锈钢在盐酸溶液中的腐蚀速度.在相同浓度条件下，SAD缓蚀效率高于SDS缓蚀剂.     

316L不锈钢应力腐蚀研究进展

316L不锈钢具备良好的力学性能、焊接性能、耐蚀性能,被广泛应用于化工管道、船舶及核电等领域。因其应用环境复杂,316L不锈钢在特定介质环境和拉应力的协同作用下,易发生应力腐蚀开裂,导致严重事故。概述了316L不锈钢应力腐蚀裂纹萌生及扩展的规律,总结了其应力腐蚀的阳极溶解和氢致开裂两种微观主导机制的特点。在此基础上,针对介质环境、材料、表面应力状态3个影响因素,综述了近年来通过调节介质环境的pH、溶液浓度、引入压应力、优化微观结构及涂层工艺等方面,改善316L不锈钢应力腐蚀性能的研究进展。最后,基于316L不锈钢面临的应力腐蚀问题,从应力腐蚀机制和防护措施两方面展望了316L不锈钢应力腐蚀的研究热点和方向。