利用临汾1962年～2007年0cm～20em各层逐月平均地温,采用气候倾向率、滑动t检验等气候统计方法,研究了近46年临汾浅层平均地温的变化趋势、异常年份和气候突变等．结果表明：近46年来临汾各季节浅层平均地温均呈现为显著的变化趋势（-0．07 ℃／10a～0．53℃／10a）,春季最大,夏季最小;各浅层年平均地温均呈明显的升高趋势,平均每1-年升高0．15℃-0．26℃,以表层地温增温率最大;春季、秋季和年浅层平均地温表现为“暖-冷-暖”的变化趋势;浅层地温春季、冬季多异常年份,年平均地温异常偏高发生在2000年后,异常偏低发生在1996年;用滑动t检验法和Yarnamoto法发现地温在1996年附近发生了突变,用M—k法发现地温在2002年附近发生了突变;气温升高是导致地温上升的主要原因．     

定向凝固合金DZ466在涂 NaCl/Na2 SO4盐条件下热腐蚀行为

采用涂NaCl/Na2 SO4盐方法研究了DZ466合金在850℃和950℃条件下热腐蚀行为.结果表明：合金的腐蚀层包括三个区域,最外层为( Ni,Co) O氧化物层,次外层为尖晶石结构氧化层( Ni,Co) Cr2 O4,内层为内腐蚀层,850℃时该层为Ni3 S2,而950℃时除Ni3 S2外,在靠近次外层还形成内氧化Al2 O3;在850℃和950℃时合金的热腐蚀机制相同,氧化膜连续性的破坏,是合金遭受热腐蚀的主要原因;热腐蚀增重曲线均符合抛物线规律,其速率常数分别为3.1×10-11 g2·cm-4·s-1和1.5×10-9 g2·cm-4·s-1,热腐蚀激活能分别为179.2 kJ·mol-1和138.3 kJ·mol-1.     

非晶FeCuNbSiB多层膜的巨磁阻抗效应(英)

研究在250℃退火温度下非晶FeCuNbSiB薄膜的巨磁阻抗效应.X-ray谱和Mössbauer谱显示样品为非晶状态.导电层的厚度为2μm，磁性层的厚度为1μm.三明治结构的最大阻抗效应为20%.为了提高巨磁阻抗效应，在两磁性层之间加入了绝缘层SiO₂，在250℃退火温度下最大阻抗效应为62%.随着驱动电流频率的增大，磁阻抗效应曲线由随磁场的单调下降变为出现峰的结构.     

非晶FeCuNbSiB多层膜的巨磁阻抗效应

研究在250℃退火温度下非晶FeCuNbSiB薄膜的巨磁阻抗效应.X-ray谱和Mossbauer谱显示样品为非晶状态.导电层的厚度为2 μm,磁性层的厚度为1 μm.三明治结构的最大阻抗效应为20%.为了提高巨磁阻抗效应,在两磁性层之间加入了绝缘层SiO2,在250℃退火温度下最大阻抗效应为62%.随着驱动电流频率的增大,磁阻抗效应曲线由随磁场的单调下降变为出现峰的结构.     

不同缓冲层对Ni_(81)Fe_(19)薄膜性能影响和微结构分析

采用磁控溅射方法制备分别以Ta和NiFeCr为缓冲层的Ta(NiFeCr)/NiFe/Ta薄膜材料.对于相同厚度的NiFe薄膜,与传统材料Ta相比,用NiFeCr作缓冲层薄膜的各向异性磁电阻有显著的提高.X射线衍射结果表明,与Ta缓冲层相比NiFeCr缓冲层可以诱导更强的NiFe(111)织构.高分辨透射电子显微镜结果表明,NiFeCr缓冲层和NiFe层的晶格匹配非常好,NiFe沿着NiFeCr外延生长,以NiFeCr为缓冲层的NiFe薄膜具有良好的晶体结构.对薄膜进行热处理,以NiFeCr缓冲层为缓冲薄膜的各向异性磁电阻值在350℃以下基本保持不变,当退火温度超过350℃后,其值会明显下降.以NiFeCr缓冲层的薄膜在350℃以下退火具有良好的热稳定性.     

电磁出钢系统中感应加热线圈工况温度分析

为了将电磁出钢系统应用于实际生产,提出一种能让该系统使用的感应加热线圈在高温水口砖内正常工作的隔热方法.利用数值模拟方法考察了300t电磁出钢系统用钢包水口座砖的热流密度以及有无隔热层条件下置入在水口座砖内的感应加热线圈的工况温度.结果表明,无隔热层条件下线圈在高温水口座砖内无法使用,而在线圈的顶部及内外两侧布置一层隔热材料可以有效地降低线圈的工况温度;隔热层的厚度和导热系数均影响线圈的工况温度,当隔热层厚度为40mm,导热系数为003W/(m·℃)时,线圈的最高工况温度由原来的1187℃降至467℃,满足线圈的工况温度要求.     

催化发光传感器纳米薄膜制备条件的优化

本研究用溶胶-凝胶法制备MgO和In2O3纳米薄膜材料前躯体,用浸渍镀膜法制备纳米薄膜．讨论了MgO和In2O3薄膜在不同的胶体制备pH值、煅烧温度和镀膜层数下,对一些有机气体的催化发光信号强度的影响．通过实验数据分析得出,MgO纳米薄膜在胶体制备pH为8、镀膜层数为5层、煅烧温度为550℃的条件下对乙二醇甲醚等蒸气具有最佳的催化发光信号．In2O3纳米薄膜在胶体制备pH为5、镀膜层数为5层、煅烧温度为550℃的条件下,对乙酸等蒸气具有最佳的催化发光信号．     

Comparison of Effects of Different Organo-montmorillonites on PA 66/Clay Nanocomposites

Different organo-montmorillonites （OMMTs） are prepared by modifying montmorillonites （MMTs） with CTAB, PA 1010 salts/CTAB, PEG/CTAB, PVA/CTAB, PVP, PVP/ CTAB and PA 6/CTAB, respectively. These OMMTs were studied by X-ray diffraction and TG. The gallery sizes of them are all larger than that of sodium MMTs. And the decomposition temperatures of them are all much higher than that of MMT and the processing temperature of PA 66, especially OM - 6 and OM - 7, the decomposition temperatures of which are 451.6℃ and 439.1℃, almost the collapse temperature of the native MMT crystal lattice which is more than 5080C. Then PA 66/Clay nanocomposites were synthesized by mixing these OMMTs with PA 66 matrix via melt intercalation. Experimental results indicate that the tensile and flexural properties increase significantly, especially those of PCN - 08. The combination property of PCN- 08 is the best. TEaM photos show that some clay platelets are present in the matrix as exfollated layers, while most of the clay platelets are present as intercalated layers.     

进水塔施工期温度仿真分析

结合燕山水库进水塔施工方案,应用有限元软件ANSYS,对其施工过程进行了仿真分析.分析表明：施工期混凝土最大温升为29.934℃,浇注后3-4 d即达到峰值,最大温差均不超过24℃.温度应力随着温差的增大而增大,温度应力最大值1.68 MPa,出现在两层混凝土浇筑的接触面,由浇筑时产生的瞬时温差引起.     

MOD法在不同种子层上制备La_(0.4)Sr_(0.6)TiO_3缓冲层的研究

采用金属有机沉积法(MOD)在双轴织构的Ni-5%W基带上制备了La0.4Sr0.6TiO3,LaTiO3和SrTiO3三种种子层,然后再在种子层上沉积La0.4Sr0.6TiO3薄膜.SEM图像显示种子层颗粒分布均匀,大小基本一致.通过XRD和SEM研究了不同种子层对La0.4Sr0.6TiO3薄膜取向和表面形貌的影响.结果显示,在LaTiO3种子层上Ar-4%H2气氛下950℃制备的薄膜取向良好,表面光滑致密,无裂纹和孔洞出现.     

Paleo-environmental study on the growth of magnetotactic bacteria and precipitation of magnetosomes in Chinese loess-paleosol sequences

405 samples were collected from L5-S5-L6 in consideration of obvious variations in susceptibility of the geological sections, which are section Xifeng in Gansu Province and section Duanjiapo in Shaanxi Province for study of magnetotactic bacteria (MB) and magnetosomes (MS) in Chinese loess-paleosol sequences. MB in each sample were observed by TEM after being cultured under 8-18℃, room temperature (RT), 25℃, 26℃ and 30℃ conditions. In general, MB are distributed widely in loess-paleosol sequences, fewer in loess layers with predomination of vibriod in shape. However, there are more MB in paleosol layers with morphological varieties such as roddish, vibriod and occasionally approximately coccus. The magnetosomes (MS) in MB of paleosol are usually arranged in chains along the cells. It was also found that MB growth and MS formation are associated with the environment in which MB live. It can be inferred from the distributions of MB and MS that the paleoclimates fluctuated during the formation of loess-paleosol sequences in the Chinese Loess Plateau. The climate became gradually warmer but displayed more frequent fluctuations from the northwest to the southeast of the Plateau .     

纯钛TA1和钛合金TC4表面固体渗硼

采用固体粉末法分别对基体组织为α-Ti的TA1和基体组织为(α+β)-Ti的TC4钛合金表面进行了渗硼,在偏光显微镜和扫描电镜(SEM)下观察了渗层的形貌,用X射线衍射(XRD)分析了渗层的物相组成.实验结果表明,渗硼温度在850~1000℃范围内,TA1表面渗层为平行于基体表面的多层结构,为Ti3O相和TiB相;当渗硼温度高于920℃时TiB为主要组成并出现了TiB2相,且硼钛化合物的含量随温度升高而增加.当渗硼温度低于1000℃时,TC4表面渗层为Ti3O相和TiB相,在渗硼温度高于1000℃时,渗层为TiB2+TiB晶须结构.渗硼温度高于1000℃是TA1和TC4表面形成硼钛化合物的充分条件.     

神经网络模型在锂离子电池表面温度预测中的应用研究

基于人工神经网络构建了锂离子电池表面温度的预测模型. 该模型为3层网络结构,其中输入层中有4个节点,隐含层中有9个神经元,输出层中有1个节点. 训练结果表明,模型具有较快的收敛速度和优秀的训练质量,从而保证了预测的精确度. 模型的预测值与实验值吻合程度高,说明了模型工作的有效性. 模型预测电池在较高环境温度(80 ℃)下以10C倍率放电结束时的表面温度为86.71℃,仅比环境温度高出6.71 ℃. 该模型有助于电池热管理系统的研究与开发.      

单道次热轧对Fe-15Si硅钢氧化层形貌的影响

将Fe-15Si硅钢试样分别在1000~1200℃空气条件下氧化30min，观察发现在1000℃和1100℃时，氧化层与基体界面处存在硅酸亚铁，而当温度为1200℃时，硅酸亚铁不但存在于界面处，同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验，压下率分别为10%和30%，发现1000℃和1100℃时，较高的压下率使氧化层破碎更加严重，但是单道次热轧未能改变氧化层的结构；当温度为1200℃时，由于液态的硅酸亚铁的出现，单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中，消除了硅酸亚铁层的钉扎基体的效应，改善了氧化层与基体界面的平直度.     

预退火工艺对Bi3.15Nd0.85Ti3O12铁电薄膜性质的影响

采用溶胶一凝胶法在Pt／Ti／SiO2/Si基片上制备了Bi3.15Nd0.85Ti3O12铁电薄膜。将薄膜分别进行每一层预退火、每二层预退火、每三层空气中500℃预退火10min，分别称为a．b、c组薄膜，最后都于氮气氛中680℃总退火0．5h。结果表明，预退火工艺对薄膜的铁电性能影响较大，而对取向基本没有影响。同时，a,b两组薄膜的铁电性能（2Pr分别为47．8μC／cm2。和51．9μC／cm2）远远优于c组薄膜的铁电性（2Pr=28．7 μC／cm2）。所有Bi3.15Nd0.85Ti3O12薄膜都呈现良好的抗疲劳特性。     

CdS/TiO2复合纳米管制备和光催化性能的研究

采用阳极氧化法在纯钛箔上制备TiO2纳米管,再通过连续离子层沉积法在TiO2纳米管上沉积CdS粒子,沉积3层CdS后,进行退火处理,退火后再沉积3层CdS.利用透射电子显微镜(TEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)和拉曼光谱对纳米管的形貌、物相结构和元素价态等特性进行分析.结果表明:经阳极氧化法制备的TiO2纳米管为锐钛矿结构,随后沉积的CdS同时出现了立方相与六方相晶格结构,400℃退火可以显著增加立方相CdS的结晶程度;纳米管中CdS粒子的直径均小于5 nm,CdS粒子由一大一小2个纳米粒子组成,大粒子由退火过程形成.光催化实验表明:经过退火处理的CdS/TiO2复合纳米管的可见光光催化能力约是未退火样品的3倍,说明退火处理可以有效提高TiO2可见光光催化能力.     

青藏高原当雄错晚更新世末期-全新世早期叠层石新发现

 在青藏高原首次发现当雄错第四纪晚期叠层石群,其发现对于阐明高原第四纪晚期古环境演化有重要意义。通过对当雄错第四纪晚期发育的3层叠层石的地球化学特征以及14C年龄研究发现：叠层石发育最佳温度20~30℃,当温度低于12~15℃时,蓝藻停止生长。目前,当雄错湖水年均温度为4.8℃,可知当时水温高于现代10℃;这3层叠层石的¹⁴C年龄分别与同布林（Bölling）和阿路罗德（Allevöd）两次暖期事件,及10.5 ka~9 kaBP全新世早期转暖期一致,并且叠层石中δ¹⁸O均值在-7.23~-6.6之间,δ¹³C均值在4.75~5.65之间,两者均较高,可知当雄错当时气温较高。该时段3个暖期的发现,对详细建立划分青藏高原第四纪晚期气候-年代学标尺有重要价值。     

褐铁矿的热分解特性及其对烧结过程的影响

利用热重分析的方法对褐铁矿FMG粉(简称FMGF)在受热升温过程的热分解特性进行了详细的研究.结果表明:FMGF中的结晶水在200~400℃温度区间内即完成了分解挥发,这样可以改善烧结料层透气性,使料层上部热量有效传递到下部;分解其中的结晶水,就能减少褐铁矿中的结晶水分解对烧结固体燃料消耗和烧结热平衡影响.烧结杯试验和工业应用结果验证了热分解特性研究的结论:在高比例褐铁矿条件下,通过提高难熔矿配比,可改善烧结料层透气性,改善料层传热条件,最终降低烧结固体燃耗,提高烧结成品率.     

Ni系低温钢的高温氧化行为研究

为研究Ni系低温钢的高温氧化行为,利用Setsys Evolution型高温同步热分析仪对Fe-3.5Ni和Fe-9Ni钢在700~1200℃的氧化行为进行了研究,采用电子探针(EPMA)、场发射扫描电镜(SEM)和X射线衍射(XRD)等手段表征了氧化物微观形貌和物相组成.结果表明:700~1200℃条件下氧化2h后,Fe-3.5Ni钢和Fe-9Ni钢的氧化增重曲线规律相似,相同氧化温度条件下,单位面积Fe-9Ni钢的增重量低于Fe-3.5Ni钢.随氧化温度的升高,试样表面依次出现团絮状、晶须状和不规则多边形状Fe₂O₃.氧化分为内氧化和外氧化,内、外氧化层厚度随氧化温度的提高逐渐增加,且900℃是两种钢外氧化层厚度发生突变的临界温度.内氧化层由FeNi₃和混合物(FeO+Fe₃O₄)组成,外氧化层由Fe₂O₃,Fe₃O₄和FeO组成,且外氧化层内包裹着尖晶石相NiFe₂O₄;随着Ni含量增加,NiFe₂O₄增多并形成连续的薄带.     

温差法制备纳米气泡及温度的影响

通过一系列的实验建立了利用冷水（4±0.1℃）和热水（25～40℃）进行替换即温差法制备界面纳米气泡的方法.原子力显微镜（AFM）观察显示：温差法也能在疏水的高序热解石墨（HOPG）表面上产生稳定的纳米气泡.统计结果显示：热水温度在25～38℃范围内,产生纳米气泡的数量随着热水温度的升高而增多,当热水温度为38℃左右时达到最大值,之后随着热水温度的升高反而减少;每平方微米纳米气泡气体的总体积在37℃时达到最大值;温差法也能产生纳米气层和双层结构,其性质与前人发现的一致.