纳米Al2O3颗粒对Cu-Al2O3性能的影响

采用溶胶-凝胶法制备纳米Al₂O₃颗粒,通过粉末冶金法制备氧化铝铜（Cu-Al₂O₃）。采用X射线光电子能谱仪、扫描电子显微镜、洛氏硬度仪和涡流计分别测试了Cu-Al₂O₃的结合能、微观组织、硬度和导电率。结果表明：随Al₂O₃颗粒含量的增加,Cu-Al₂O₃的硬度先升高后降低,当Al₂O₃颗粒的质量分数达到0.084%时,Cu-Al₂O₃的硬度达到最大值75.73（HRB）。Cu-Al₂O₃的导电率随着Al₂O₃颗粒含量的增加逐渐下降。Al₂O₃颗粒的质量分数为0.084%时为最佳值,Cu-Al₂O₃的硬度达到最大值,导电率达到69.1% IACS。     

稀土Sm2O3对WCoB-TiC复相陶瓷组织的影响

以WC、TiB₂、Co粉末为基本原料,添加稀土Sm₂O₃为抑制剂,采用真空液相反应烧结技术制备WCoB-TiC复相陶瓷材料,利用XRD、SEM和EDS对其微观形貌和相组成进行表征。结果表明,添加一定量稀土Sm₂O₃后,WCoB-TiC复相陶瓷晶粒细小且分布均匀,晶粒的长大得到抑制;随着稀土Sm₂O₃的过量加入,复相陶瓷中有棒状晶粒出现,晶粒有粗化的趋势。在1400℃下烧结时,当Sm₂O₃添加量为0.3%时,制成的WCoB-TiC复相陶瓷材料密度达到10.01g/cm³,硬度HRA达到 91。     

A12O3在一次烧结BaTiO3中的作用探讨

 探索了掺微量Al₂O₃和SiO₂的BaTiO₃的一次烧结工艺,该工艺有效降低了烧结温度.应用电子探针、光学显微镜、X射线衍射仪,TN-524能谱等设备对样品进行分析.BaTiO₃瓷体电阻随Al₂O₃掺杂量的变化关系及Al在BaTiO₃中分布情况等实验事实,表明在BaTiO₃烧结过程中Al可能是一种半导化元素,起施主的作用.通过新工艺,得到了性能较好的BaTiO₃热敏电阻.     

Al3+掺杂LiMn2O4的制备及高温循环性能研究

采用沉淀法合成LiMn_2-xAl_xO₄（x=0.01,0.05,0.10,0.20）,pH的范围为10.5～10.6,搅拌速度为350 r/min,水浴温度为55℃,分两次烧结.首次煅烧温度为680℃,保温时间为18 h;第二次煅烧温度为850℃,保温时间为18 h.利用X射线衍射、扫描电子显微镜和电化学方法测试最终产物.测试结果表明：Al³⁺的掺入有效地改善了LiMn₂O₄的高温循环性能,使其高温循环容量衰减得到了有效的抑制,尤其当Al³⁺的掺入量为0.05时,有比其他掺杂量更优的性能.     

Al2O3/WO3/ZrO2催化剂的制备及在酯交换反应中的研究

以松木为模板,采用模板法将不同含量的Al₂O₃添加到WO₃/ZrO₂复合氧化物中,采用X射线衍射、BET比表面积分析、拉曼光谱和NH₃等温吸附测试等手段对其进行表征,以评估其改进结果。将Al₂O₃/WO₃/ZrO₂催化剂应用到甲醇与乌桕油（非食用油）的酯交换反应中,在其他反应条件相同,Al₂O₃质量分数为3%时,生物柴油最高产率达到83.1%。结果表明：添加Al₂O₃稳定了ZrO₂的四方相结构,使得催化剂比表面积更大、孔数量增加;模板法制备的催化剂孔径分布均匀,WO₃呈高度分散无定型状态;引入Al₂O₃增加了WO₃/ZrO₂催化剂的中强酸性,对弱酸性和强酸性无明显改变。     

CoFe2O4-Al2O3复合材料的制备及其在含日落黄废水处理中的应用

制备了铁酸钴-氧化铝（CoFe₂O₄-Al₂O₃）复合材料,并采用扫描电子显微镜（SEM）、X射线衍射（XRD）、比表面积和孔径分析仪对多孔CoFe₂O₄-Al₂O₃复合材料的物相和形貌进行了分析. 利用制备的CoFe₂O₄-Al₂O₃复合材料活化过硫酸氢钾（PMS）来降解废水溶液中的日落黄（SY）,通过研究CoFe₂O₄-Al₂O₃材料制备过程中Co²⁺,Fe³⁺和Al³⁺的物质的量之比、煅烧温度和时长对材料催化性能的影响,发现Co²⁺,Fe³⁺和Al³⁺的最佳物质的量之比为1:2:12,最佳煅烧温度为400 ℃和最佳煅烧时长为3 h. 对采用在最优条件下制得的CoFe₂O₄-Al₂O₃复合材料作为催化剂,PMS氧化降解含日落黄废水进行研究,考察了pH值、温度、不同体系、PMS用量、CoFe₂O₄-Al₂O₃材料用量和一些阴离子对日落黄降解的影响. 结果表明：在pH=7,温度为55 ℃条件下,用0.1 g催化剂和0.125 g PMS能使100 mL质量浓度为0.6 g·L^-1的日落黄溶液在30 min内降解率达到99.5%. 同时,碳酸氢根负离子（HCO₃^-）和硝酸根负离子（NO₃^-）的加入抑制了日落黄的降解,而Cl^-则能促进日落黄的降解. 此外,在进行4次循环使用后,CoFe₂O₄-Al₂O₃仍表现出很好的催化性能,日落黄去除效果仍能达到90%以上.     

真空热压烧结Cu-Al2O3热变形行为研究

采用真空热压烧结法制备Cu-Al₂O₃复合材料,并在Gleeble-1500D热模拟机上对其进行高温压缩试验.阐述了内氧化原理,分析了真空热压烧结制备的铜基复合材料的微观组织和材料性能,研究了在变形温度为650~950℃,变形速率为0.01~5 s^-1,最大真应变为0.7时的流变应力行为.结果表明：变形温度和变形速率对流变应力的影响较大,随着变形温度的升高和应变速率的减小,峰值应力逐渐减小.采用双曲线正弦模型建立了材料高温变形时的流变应力本构方程,确定热变形激活能为220.7 kJ/mol.     

原位合成CNTs/Cu-Al2O3复合材料的性能研究

对Al的质量分数分别为0.20%,0.35%,0.60%的Cu-Al合金粉末进行内氧化,得到Cu-Al₂O₃粉末。采用化学气相沉积法在Cu-Al₂O₃粉末表面原位生长碳纳米管(carbon nano tubes, CNTs),采用放电等离子烧结工艺成功制备了CNTs/Cu-Al₂O₃复合材料。采用扫描电子显微镜和透射电子显微镜观察了CNTs/Cu-Al₂O₃复合粉末、复合材料断口的形貌。采用显微硬度计、微拉伸试验机、摩擦磨损试验机分别对纯Cu及复合材料的维氏硬度、抗拉强度、摩擦因数进行测试。采用电化学工作站测试复合材料在3.5%NaCl (质量分数)水溶液中的耐腐蚀性能。结果表明,随着Al的质量分数的增加,粉末表面合成的CNTs的数量也增多。Al的质量分数为0.35%时,CNTs/Cu-Al₂O₃复合材料的综合性能最佳,与纯Cu相比,复合材料的抗拉强度和腐蚀电势分别提高了86.4%和43.2%,分别为315 MPa和-0.268 V,摩擦因数降低了53.3%,仅为0.28。     

纳米Al2O3分离富集环境样品中的铊

 研究了纳米Al₂O₃对铊的吸附性能,考察了吸附热力学,最佳酸度和吸附容量.实验结果表明:在最佳pH条件下,铊定量、快速地被吸附在纳米Al₂O₃材料上;其2,20,40 ℃时最大吸附容量分别为4.44, 5.78, 6.28 mg·g^-1;等温吸附线呈现可逆的Langmuir吸附形式.吸附反应的焓变ΔH⁰和熵ΔS⁰均为正值,ΔG⁰为负值,说明该过程是自发的吸热反应.被吸附在纳米Al₂O₃上的金属离子能采用1.00 mL 0.25 mol·L^-1 HCl溶液定量洗脱, 其回收率达到98%.该法对铊的检出限为0.84 μg·L^-1,相对标准偏差(RSD)为2.4%, 已成功地应用于实际水样和多金属结核样品GBW07296的测定,分析结果令人满意.     

TiO2/CB-NiCo2O4修饰玻碳电极的制备及其对葡萄糖的电化学测定

利用低温下的水化学生长法合成了镍钴氧化物（NiCo₂O₄）纳米针,因其自组装而表现出立方晶相,再用二氧化钛/炭黑（TiO₂/CB）对NiCo₂O₄表面进行了改性,合成了TiO₂/CB-NiCo₂O₄复合纳米材料.用X射线光电子能谱仪（XPS）、扫描电子显微镜（SEM）、能量色散X射线光谱仪（EDX）图谱对材料的形貌进行了表征,运用循环伏安法（CV）、时间-电流（i-t）曲线法考察了TiO₂/CB-NiCo₂O₄修饰玻碳电极的电化学行为.实验发现：TiO₂/CB-NiCo₂O₄修饰电极对葡萄糖的氧化有良好的电催化性能,其线性范围为0.001~1.780 mmol·L^-1,检测限为0.53 μmol·L^-1（信噪比S/N=3）.将该法用于实际样品中葡萄糖的测定,结果令人满意.     

Single-negative properties of Ba2Co1.8Cu0.2Fe12O22 and Ba3Co2Fe23.4Zn0.6O41 hexagonal ferrites

The electromagnetic properties of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂ (Co₂Y) and Ba₃Co₂Fe_23.4Zn_0.6O₄₁ (Co₂Z) were studied by measuring microwave scattering parameters. In the transmission spectra of Ba₂Co_1.8Cu_0.2Fe₁₂O₂₂, a forbidden band emerges due to ferromagnetic resonance, and the permeability will turn to negative in the vicinity of the ferromagnetic resonance frequency. In the complex permittivity spectra of Ba₃Co₂Fe_23.4Zn_0.6O₄₁, the negative permittivity can be obtained due to dielectric resonance. Therefore, Co₂Y and Co₂Z can be used to construct left-handed materials possessing negative permeability and negative permittivity simultaneously.     

Lead-bismuth-free piezoceramics （Na0.5K0.44Li0.06）Nb0.95Sb0.05O3-Na5.6Cu1.2Sb10O29

Newly developed sintering aid Na5.6Cu1.2Sb10O29 (NCS) and lead-bismuth-free piezoceramics (Na0.5K0.44Li0.06) Nb0.95Sb0.05O3 (NKLNS) were prepared by the conventional solid state reaction. The effects of sintering aid NCS on the electrical properties of NKLNS were investigated. It was found that the addition of a proper amount of sintering aid NCS to NKLNS is effective not only on improving the density and the piezoelectric activity, but also on reducing the dielectric loss of NKLNS. The NKLNS doped with 0.4 mol% NCS has a piezoelectric constant d33 as high as 261pC/N and an electromechanical coupling factor k33 above 60%. These results show that NCS-doped NKLNS is a promising and practicable candidate for lead-bismuth-free piezoceramics.     

CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2玻璃陶瓷的制备及化学稳定性研究

玻璃陶瓷是固化处理中、高放废物和α废物较为理想的候选材料之一。研究了特定条件下制备的CaO-ZrO2-TiO2-Al2O3-B2O3-SiO2体系玻璃陶瓷在水淬和空气中自然冷却的两种冷却制度对其结晶行为和显微结构的影响,用粉末浸泡实验方法测试了其化学稳定性。结果表明:自然冷却形成的玻璃陶瓷晶相主要是ZrSiO4和ZrTiO4;在25～70℃范围内,温度对玻璃陶瓷浸出率无明显影响,90℃下浸出率比25℃,40℃,70℃的浸出率高一个数量级;7 d元素总的归一化浸出为1.87 g/m2。     

TiO2/Al2O3-Al2O3-TiO2/Al2O3绝缘结构的真空沿面闪络特性

基于变插入层介电常数的多层绝缘结构能改善电场分布、提高真空沿面闪络特性.通过真空热压烧结制备了TiO2/Al2O3-Al2O3-TiO2/Al2O3(A-B-A)3层绝缘结构,A层w(TiO2)为0.5%到20%.测量了该绝缘结构的真空沿面闪络特性,发现闪络特性随w(TiO2)的增加而提高,当w(TiO2)为20%时,其脉冲初次闪络电压较同等厚度的Al2O3陶瓷提高了63%.研究发现:A层的介电常数可由w(TiO2)调控,介电常数的增大能有效降低真空-绝缘子-阴极三结合点处的电场强度;A层表面存在的TiO2颗粒可以减小二次电子发射系数并改善表面电荷分布;TiO2的电导率虽比Al2O3高,但其仍为绝缘体,即使TiO2含量较高时也不会形成贯穿的导电通道.     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F- Glass Containing Cr2O3

The effect of Cr₂O₃ on the nucleation and crystallization of Na₂O-CaO-Al₂O₃-SiO₂-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1.5 % (mass fraction) Cr₂O₃ can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr₂O₄] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO₃ grew epitaxially.     

二维磁性NbSi2N4-WSi2N4-NbSi2N4异质结的光生电流效应

采用量子输运方法研究了二维(2D)磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄面内异质结的光生电流效应.该异质结具有C2v非空间反演对称性,在可见光范围内,用线偏光垂直及倾斜照射时,均能激发显著的光生电流效应,产生自旋极化且偏振敏感的光电流.光电流与偏振角(θ)和入射角(α)均为余弦依赖(cos(2θ),cos(2α))关系.两种照射方式下均能产生纯自旋流及完全自旋极化的光电流.在垂直照射时,能取得完美的自旋阀效应.这些结果表明,二维磁性NbSi₂N₄-WSi₂N₄-NbSi₂N₄异质结在低能耗自旋电子学及低维光电探测领域具有应用潜力.     

层状化合物K0.81Li0.27Ti1.73O4的合成

研究以K₂CO₃,Li₂CO₃和TiO₂为反应原料合成层状钛酸盐K_0.81Li_0.27Ti_1.73O₄过程中合成条件对产物的影响. 结果表明: 反应温度在
1 000~1 200 ℃, 反应原料配比为n(K₂CO₃) ∶n(Li₂CO₃) ∶n(TiO₂)=(0.405~0.42) ∶(0.135~0.165) ∶1.73时, 均可以得到产物K_0.81Li_0.27Ti_1.73O₄, 延长反应时间及升高反应温度均有利于产物的生成; 在1 200 ℃高温条件下, 使用刚玉坩埚为反应容
器时, 最佳的反应条件是： 反应温度为1 100 ℃, 反应原料配比为n(K₂CO₃) ∶n(Li₂CO₃) ∶n(TiO₂)=0.405 ∶0.135 ∶1.73, 反应24 h.     

纳米Fe2O3-Al2O3复合材料的制备

采用溶胶-凝胶表面包覆法制备了纳米Fe₂O₃-Al₂ O₃复合材料, 利用X射线衍射和透射电镜对样品的物相、 粒度和形貌进行了研 究. 结果表明, α-Fe₂O₃掺杂降低了Al₂O₃相变温度, 在900 ℃可以得到稳定的α-Al₂O₃相.