水热法制备Ag/TiO2纳米复合材料及其抗菌性能

采用水热晶化法制备Ag掺杂量不同的Ag/TiO2纳米复合抗菌材料.用XRD、SEM等手段表征Ag/TiO2复合材料的晶相和形貌.研究光源、Ag掺杂量、紫外光照时间、不同实验菌种等因素对Ag/TiO2纳米复合材料抗菌性能的影响.结果表明,通过不同水热温度制备出来的纳米Ag/TiO2复合材料中的TiO2都以锐钛矿晶型存在;在无光照的情况下,纳米Ag/TiO2复合材料有较强的抗菌性能,当n(Ti)∶n(Ag)=1∶0.2时,有最佳抗菌效果;长波紫外灯照射12 h后,由于Ag+被还原,复合材料总的抗菌性能有所下降.     

Ag/SiO2复合纳米粒子的超声化学合成

本文中首先利用正硅酸乙酯(TEOS)的碱性水解制备了均匀分散的S iO2微球(粒径约70 nm),然后采用超声辐射与红外辐射结合的方法在其表面包覆了一层分布均匀的Ag纳米粒子(粒径约8 nm).研究了实验条件对产物的影响,并通过透射电镜(TEM)、X射线衍射(XRD)、紫外可见吸收光谱(UV-vis)、差示扫描量热法(DSC)和红外吸收光谱(FT-IR)对产物的形貌及性质进行了表征.     

纳米Ag粉的显微结构和性能表征

采用自悬浮定向流法制备纳米Ag粉。用透射电镜(TEM)、X射线能量色散谱(EDAX)、X射线衍射(XRD)、紫外-可见光吸收光谱(UV-Vis)和差示扫描量热法(DSC)对纳米微晶形貌、粒度、结构和性能进行研究。结果表明:在He气和Ar气流中制备的纳米Ag粉的平均粒径分别为15 nm和80 nm;颗粒基本为球形,贮存在未密封的广口瓶中1 a后含氧量为1.04%,最大的吸收峰出现在波长为283 nm处,熔化焓为93.55 J/g,熔点为959.70℃,比粗晶银的熔点(961.93℃)低2.23℃。     

微波辅助加热层状液晶模板法制备钯纳米粒子

将微波加热法引入到液晶模板中, 探索微波辅助加热层状液晶模板法制备钯纳米粒子, 利用透射电镜和X-射线粉末衍射对产物进行表征. 微波加热下, 在Tween-80/n-C10H21OH/H2O形成的液晶模板体系中成功制备了分布均匀的钯金属纳米粒子, 大大缩短了反应时间; 改变反应物浓度和加热时间可将钯纳米粒子的粒径控制在3-6 nm.     

磷酸钴纳米粒子的微波辐射制备法

介绍用微波辐射法对磷酸钴纳米粒子的制备方法和分离方法.并对磷酸钴纳米粒子进行了结构和组成的测试,讨论了影响粒子形成的主要因素.通过实验得到了平均粒径为50.64nm的球形微粒的磷酸钴纳米粒子.     

Ag/CuMoO4纳米线的制备及其光催化活性的研究

采用水热技术获得了Cu Mo O4纳米线,通过光还原技术成功将Ag负载到Cu Mo O4纳米线材料上。利用罗丹明B模拟水中污染物,考察了Cu Mo O4和Ag/Cu Mo O4的光催化活性。研究结果表明：Ag均匀沉积在Cu Mo O4表面,提高了Cu Mo O4的光生电子-空穴对的分离效率,从而有效提高了催化剂的活性,对罗丹明B的降解率达95%。     

纳米Fe/Cu双金属的制备及其对水中亚甲基蓝的去除

利用液相还原法制备了纳米Fe/Cu颗粒,考察了其对水中亚甲基蓝的去除性能,研究了不同pH、亚甲基蓝初始浓度和反应时间对去除效果的影响.结果表明,酸性条件下Fe/Cu纳米双金属对亚甲基蓝去除效果良好,且在45min时反应达到平衡,对亚甲基蓝的去除过程符合准一级动力学方程和Langmuir吸附等温模型.     

三维Ag/ZnO中空微球的制备及其抗菌性能

在生物高分子海藻酸钠的辅助下,采用水热合成的方法制备了具有三维分层超结构的Ag/ZnO中空微球,利用场发射扫描电镜、高分辨透射电镜和光电子能谱等手段对其结构进行了表征,最后对其抗菌性能进行了研究。结构表征结果表明:所制的样品为直径3～5μm的中空微球,其球壁是由直径约100 nm、长度约1μm的Ag/ZnO纳米棒沿着其生长方向并垂直于微球表面的定向排列所组成。抗菌研究结果表明:Ag的质量分数为2.13%的Ag/ZnO中空微球复合材料表现出了协同的高效抗菌性能,其对大肠杆菌和金黄色葡萄球菌的M IC值分别为600μg/mL和400μg/mL。     

PS/Ag纳米复合粒子的制备与表征

目的 制备PS/Ag纳米复合粒子.方法 以二硫代苯甲酸异丙苯酯(CDB)为链转移剂,用可逆加成断裂链转移聚合(RAFT)的方法将硫代羰基引入到聚苯乙烯(PS)高分子链中,采用透射电子显微镜(TEM)对其进行了表征.利用PS高分子链中的硫代羰基有保护和稳定Ag纳米粒子的作用,制备了PS/Ag纳米复合粒子.结果 Ag纳米粒子具有良好的单晶结构,且均匀分散于PS胶体粒子中.结论 PS/Ag纳米复合粒子的结构与AgNO_3溶液的加入量有关.     

N2分压对抗菌TiN/Cu纳米复合涂层的综合性能影响

人体组织对植入物磨损碎片和腐蚀产物产生的异物反应以及细菌感染是导致植入物失败的主要因素。为了解决这些问题,本文采用电弧离子镀系统通过不同N₂分压的工艺参数设置,在304不锈钢上制备获得一系列抗菌TiN/Cu纳米复合涂层沉积,分别命名为TiN/Cu-x（x = 0.5,1.0,1.5 Pa）。X射线衍射分析、能量色散X射线光谱和扫描电镜分析结果表明,N₂分压决定了TiN/Cu纳米复合涂层的Cu含量、表面缺陷和微晶尺寸,进一步影响了其综合能力。TiN/Cu涂层的硬度和耐磨性随着微晶尺寸的增加而增强。在表面缺陷、微晶尺寸和铜含量的协同作用下,TiN/Cu-1.0和TiN/Cu-1.5涂层具有优异的耐腐蚀性。此外,生物试验证明,所有TiN/Cu涂层均无细胞毒性,抗菌能力强。其中,TiN/Cu-1.5涂层显著促进了细胞增殖,有望成为一种新型抗菌、耐腐蚀、耐磨的医疗植入物表面涂层。     

Fe3O4/Ag复合纳米颗粒的制备及其抑菌性能研究

首先用水热法制备了Fe₃O₄纳米球,然后以制备的磁性Fe₃O₄纳米粒子为磁核,在高温高压反应釜中与葡萄糖反应,使其表面包覆一层聚糖,利用聚糖的还原性,让包覆后的粒子与AgNO₃反应,制备出Fe₃O₄/Ag纳米复合粒子。用透射电镜（TEM）、X射线衍射仪（XRD）对所制备的材料的形貌和结构进行了表征。通过抑菌实验的测定,结果表明Fe₃O₄/Ag复合材料具有良好的抑菌活性。     

溶胶凝胶法和浸渍法制备的Cu/SiO2催化剂的表征与性能

以CuCl2为铜源,采用溶胶凝胶法和浸渍法制备了SG-Cu/SiO2和IM-Cu/SiO2催化剂,用XRD、BET、IR、TPR等手段对催化剂进行了表征,考察了2种催化剂对NO CO反应的催化性能.结果表明,不同方法制备的催化剂在孔容、比表面积和表面OH的分布上有很大差异, 金属粒子在催化剂中的分散程度和存在状态也有所不同.在NO CO反应中,SG-Cu/SiO2的催化性能高于IM-Cu/SiO2,在SG-Cu/SiO2催化剂中形成的难还原的铜物种对NO CO的催化性能较好.     

传统加热和微波加热下氧化锰矿的碳热还原行为研究

For the purpose of exploring a potential process to produce FeMn, the effects of microwave heating on the carbothermal reduction characteristics of oxidized Mn ore was investigated. The microwave heating curve of the mixture of oxidized Mn ore and coke was analyzed in association with the characterization of dielectric properties. The comparative experiments were conducted on the carbothermal reductions through conventional and microwave heatings at temperatures ranging from 973 to 1373 K. The thermogravimetric analysis showed that carbothermal reactions under microwave heating proceeded to a greater extent and at a faster pace compared with those under conventional heating. The metal phases were observed in the microstructures only under microwave heating. The carbothermal reduction process under microwave heating was discussed. The electric and magnetic susceptibility differences were introduced into the thermodynamics analysis for the formation of metal Mn. The developed thermodynamics considered that microwave heating could make the reduction of MnO to Mn more accessible and increase the reduction extent.     

Nucleation and crystallization of tailing-based glass-ceramics by microwave heating

The effect of microwave radiation on the nucleation and crystallization of tailing-based glass-ceramics was investigated using a 2.45 GHz multimode microwave cavity. Tailing-based glass samples were prepared from Shandong gold tailings and Guyang iron tailings utilizing a conventional glass melting technique. For comparison, the tailing-based glass samples were crystallized using two different heat-treatment meth-ods:conventional heating and hybrid microwave heating. The nucleation and crystallization temperatures were determined by performing a dif-ferential thermal analysis of the quenched tailing-based glass. The prepared glass-ceramic samples were further characterized by Fourier trans-form infrared spectroscopy, X-ray diffraction, Raman spectroscopy, thermal expansion coefficient measurements, and scanning electron micros-copy. The results demonstrated that hybrid microwave heating could be successfully used to crystallize the tailing-based glass, reduce the proc-essing time, and decrease the crystallization temperature. Furthermore, the results indicated that the nucleation and crystallization mechanism of the hybrid microwave heating process slightly differs from that of the conventional heating process.     

磁控溅射制备Ag/TiO2复合薄膜的光催化降解性能

为了提高TiO2薄膜的光催化效率,利用中频交流磁控溅射技术,采用Ti和Ag金属靶制备了Ag/TiO2复合薄膜.利用X射线光电子能谱、 X射线衍射和扫描电子显微镜分析了复合薄膜的成分、结构和表面形貌,并研究了其光催化降解性能.结果发现: Ag在厚度较薄时以聚集颗粒形式存在; 在Ag膜厚度为15 nm时, Ag/TiO2复合薄膜与TiO2薄膜相比其光催化效率可提高2倍; Ag/TiO2复合薄膜对亚甲基蓝的光催化降解效率与复合薄膜的透射率均随Ag膜厚度增加逐渐下降,其原因是Ag膜厚度不断增加,最终完全覆盖TiO2薄膜表面,阻挡了TiO2薄膜与污染物的有效接触, Ag作为光生电子捕获剂的有利影响消失.     

磁控溅射PP基氧化锌／铜层状膜性能研究

用磁控溅射法在PP非织造布表面沉积氧化锌/铜薄膜来增加抗静电、抗菌、抗紫外等性能．研究首先采用正交试验设计方法沉积铜薄膜,选择最优抗静电性效果的铜膜．铜膜参数为1Pa,20W,5min时,抗静电性能达到最好．接着在沉积最优铜膜的PP表面溅射不同参数氧化锌形成层状膜,并利用扫描电子显微镜进行表面分析．结果表明,ZnO／Cu层状膜比ZnO单层膜颗粒明显且更加致密．经过测试后,镀层状膜的PP具有良好的抗紫外透过性和良好的抗菌性．氧化锌参数为0．5Pa,75W,40min,铜膜参数为1Pa,20W,5min具有最好抗紫外性．     

Ag／Cu系的DIGM及迁移晶界扩散系数

用配有X－射线能谱的扫描电镜及光学显微镜观察了400，480度及580度，经不同时间，Ag膜／Cu块扩散对中Ag沿Cu晶界扩散诱发的晶界迁移（DIGM）现象，根据迁移晶界的特征，选用与其特征相适应的扩散方程数学解，计算了迁移晶界与一胸止晶界的扩散系数。     

微波辐射制备的TiO2/NaY膜结构及光催化活性研究

采用微波辐射加热方法制备出负载型TiO2/NaY光催化剂,采用X-射线粉末衍射(XRD)、红外光谱(IR)与紫外可见漫反射谱(UV-vis DRS)对催化剂结构进行了表征,以苯酚光催化降解与矿化对催化剂活性进行评价.结果表明,微波辐射加热方法促进了表面TiOx物种与载体NaY间的相互作用,TiO2在载体表面难以形成晶相结构,同时也导致了NaY分子筛结构的坍塌,因而催化剂对水体中苯酚的光催化降解与矿化活性较低.