铝电解用NiFe2O4尖晶石基惰性阳极

采用高温固相合成法制备铝电解用NiFe2O4尖晶石基惰性阳极,利用球形模型研究了烧结时气孔的变化规律,并研究了烧结温度对其微观形貌和基本物理性能的影响.结果表明:烧结温度能显著改变NiFe2O4尖晶石基惰性阳极的性能;Fe2O3与NiO的反应属于自发反应,从热力学角度讲,该反应在常温下就可进行,而升高温度是为了满足动力学条件;当烧结温度从1150℃升高至1400℃,气孔率由30.41%降低到1.72%,抗弯强度由14.62MPa增加至71.94MPa.     

合成工艺对NiFe_2O_4基惰性阳极性能的影响

为得到制备NiFe2O4基惰性阳极的最佳条件,利用正交实验法确定合适的工艺条件.考虑了影响惰性阳极制品的4个主要因素,每个因数又设计3个水平,通过正交实验极差分析研究了各因素对制品气孔率的影响,并确定了影响因素的主次.实验结果表明:对烧结后试样气孔率影响最大的因素是烧结温度,其次是纳米粉含量,再次是成型压力,最后是烧结时间;添加合适量的纳米粉,提高烧结温度和保温时间,增大成型压力等都有利于降低样品的气孔率.最佳工艺条件为:纳米粉质量分数20%,成型压力200 MPa,烧结温度1 400℃,烧结时间6 h.     

ZrO_2-Al_2O_3复相陶瓷材料的制备研究

采用水解ZrO（NO3）2·2H2O法制备出ZrO2,以α-Al2O3、ZrO（NO3）2·2H2O、氨水和去离子水为原料在不同温度下制备出ZrO2-Al2O3复相陶瓷,研究了ZrO2的物相组成,以及ZrO2和ZrO2-Al2O3的显微形貌,同时分析了烧结温度对ZrO2-Al2O3复相陶瓷体积密度和气孔率的影响。结果表明：水解ZrO（NO3）2·2H2O法制备出的ZrO2物相较为单一,以m-ZrO2为主,含有少量的t-ZrO2,并且ZrO2晶粒结晶度较好,具有一定的分散性。以α-Al2O3、ZrO（NO3）2·2H2O、氨水和去离子水为原料制备的ZrO2-Al2O3复相陶瓷,1500℃烧结温度下,体积密度最大,为3.81g/cm3;在1600℃下相对较高,为3.79g/cm3;陶瓷气孔率在1550℃下气孔率达到最低,为0.83%。     

ZrO2(3Y)增韧增强WC-20%Co金属陶瓷复合材料

采用热等静压真空烧结工艺制备了不同含量ZrO2(3Y)/WC-20%Co金属陶瓷复合材料.对复合材料进行了硬度、抗弯强度和冲击韧性等力学性能测试,用扫描电子显微镜(SEM)分析了微观组织及冲击断口成分,用X射线衍射定量分析计算了力学性能试验前后t→m相变量.实验表明:ZrO2(3Y)在WC-20%Co基体中呈球形,均匀分布在Co相和WC相中,该复合材料抗弯强度和冲击韧性明显提高,硬度指标提高不明显.     

ZrO2粒径对ZrO2/ZrW2O8复合材料性能的影响

分别采用Nano-ZrO2和Commercial-ZrO2制备ZrO2/ZrW2O8复合材料,并对所得复合材料的微观结构、烧结质量及其热膨胀性能进行了研究.结果表明,当ZrO2和ZrW2O8的质量比为2∶ 1时,ZrO2/ZrW2O8复合材料的热膨胀系数极低,接近于零.然而Commercial-ZrO2/ZrW2O8复合材料存在致密度不高,气孔率大的缺点.Nano-ZrO2的采用,可以降低基体的烧结温度,改善复合材料的烧结质量,Nano-ZrO2/ZrW2O8复合材料的相对密度达到94%,比Commercial-ZrO2/ZrW2O8的相对密度75%有明显提高.     

Al2O3对B4C-Al2O3-Al显微组织与力学性能的影响

在B4C-Al2O3预烧体中真空熔渗铝制备了B4C-Al2O3-Al复合材料,分析了w(Al2O3)对复合材料显微组织和力学性能的影响.结果表明:B4C-Al2O3-Al复合材料主要由B4C,Al2O3,Al,Al3BC和AlB2等相组成;随着w(Al2O3)的增加,复合材料的HRA硬度先增大后减小,材料的抗弯强度和断裂韧性均先减小后增大,当w(Al2O3)为25%时,复合材料具有较好的综合性能,它的气孔率、硬度、抗弯强度和断裂韧性分别为2.06%,84.4HRA,440.36 MPa和6.53 MPa.m1/2;延性铝的加入、裂纹的偏转和分叉、晶粒的细化、增韧相AlB2的生成及热膨胀的不匹配...     

Al2O3粉末对ZrO2-TiB2-Al2O3纳米复合陶瓷材料力学性能的影响

为了改善ZrO2陶瓷材料的综合力学性能,探讨了添加不同粒径和含量的Al2O3粉末对ZrO2-TiB2-Al2O3纳米复合陶瓷材料微观结构和力学性能的影响.采用真空热压烧结工艺制备了ZrO2纳米复合陶瓷材料,烧结温度为1 450℃,热压压力为30MPa,保温1h.结果表明:微米Al2O3粉末的体积分数为10%时,ZrO2-TiB2-Al2O3纳米复合陶瓷材料的抗弯强度最高,可达743MPa;添加纳米Al2O3粉末对材料的韧性提高明显,最高可达11.37MPa.m1/2,但不同粒径的Al2O3粉末对材料的硬度影响则不明显,材料的硬度随Al2O3含量的增加而增加.     

CuMn2O4/Ce(Zr)O2/cord催化剂对CO-O2和CO-NOx反应的研究

用共沉淀法和溶胶凝胶法制备了以CuMn2O4尖晶石为主相的Cu-Mn复合氧化物粉体,并制成负载型CuMn2O4/(Ce(Zr)O2)/cord催化剂,同时测定了CO-O2和CO-NOx的反应活性即λ特性和温度特性,发现空速≤3000 h-1情况下,富氧条件下(λ>1.02)溶胶凝胶法制备的CuMn2O4/(Ce(Zr)O2)/cord催化剂的NOx转化率高于Pd/Ce(Zr)O2/cord.     

MnO_2对镍铁尖晶石烧结行为及磁性的影响

通过两步固相反应法合成了不同MnO2质量分数的NiFe2O4尖晶石.利用扫描电镜、X射线衍射仪、差热分析仪、热膨胀仪和振动样品磁力计,分别对样品的结构、物相变化、烧结行为和磁性进行了研究.结果表明,添加的MnO2在烧结过程中发生了分解反应,Mn元素以Mn2+,Mn3+形式进入NiFe2O4尖晶石晶格中,样品无新相生成,材料仍是镍铁尖晶石结构.另外,MnO2能够促进烧结,添加1%MnO2后试样收缩速率达到最大时的温度比纯镍铁尖晶石低59°C.添加1%MnO2时,试样的饱和磁化强度(Ms)和矫顽力(Hc)分别为15.673 emu/g和48.316Oe.     

等离子分解锆英石制备ZrO2-SiO2-Al2O3系复相陶瓷

等离子分解锆英石(PDZ,plasmicalldecomposedZrO2)与Al2O3注浆成型反应烧结制备ZrO2SiO2Al2O3系复相陶瓷,与用锆英粉和Al2O3制备的该系复相陶瓷进行对比。采用XRD、OM、SEM等手段研究烧成后材料的物相组成、显微结构及物理性能。结果表明:ZrSiO4的分解先于莫来石形成;由PDZ制得的制品性能优于锆英粉制得的制品;n(Al2O3)/n(PDZ)=3/1、1540～1580℃为合适的原料配方和烧成温度范围     

In situ (α-Al2O3+ZrB2)/Al composites with network distribution fabricated by reaction hot pressing

In situ (α-Al2O3+ZrB2)/Al composites with network distribution were fabricated using low-energy ball milling and reaction hot pressing. Differential thermal analysis (DTA) was used to study the reaction mechanisms in the Al–ZrO2–B system. X-ray diffraction (XRD) and scanning electron microscopy (SEM) in conjunction with energy-dispersive X-ray spectroscopy (EDX) were used to investigate the composite phases, morphology, and microstructure of the composites. The effect of matrix network size on the microstructure and mechani-cal properties was investigated.The results show that the optimum sintering parameters to complete reactions in the Al–ZrO2–B system are 850℃ and 60 min.In situ-synthesizedα-Al2O3 and ZrB2 particles are dispersed uniformly around Al particles, forming a network micro-structure; the diameters of theα-Al2O3 and ZrB2 particles are approximately 1–3μm. When the size of Al powder increases from 60–110μm to 150–300μm, the overall surface contact between Al powders and reactants decreases, thereby increasing the local volume fraction of re-inforcements from 12% to 21%. This increase of the local volume leads to a significant increase in microhardness of thein situ (α-Al2O3–ZrB2)/Al composites from Hv 163 to Hv 251.     

ZrO2—SiC复合材料电性能的研究

本文对ZrO_2－SiC复合材料的导电性能进行了研究，结果表明：复合材料中SiC含量、热压烧结条件、使用温度等对材料的电阻率都有显著影响．     

Yb2O3、Al2O3、TiO2对Yb-TZP材料性能的影响

用超细ZrO2 、Yb2 O3粉末经机械混合、常压烧结制备Yb_TZP材料 ,实验显示2 .5% (摩尔分数 ,全文同 )Yb2 O3的掺量足以将ZrO2 稳定在四方相 ;8% (质量分数 ,全文同 )Al2 O3、0 .5% (质量分数 ,全文同 )TiO2 的添加剂使Yb_TZP的烧结温度下降 10 0℃ ,并且获得σf 提高 11%、KⅠc增加 16 %、Hv 增加 13%的好结果 .     

利用铁酸镍控制二氧化钛结构相变提高其光催化性能研究

分别采用共沉淀法和溶胶-凝胶法制备铁酸镍和二氧化钛纳米粉体,探讨了铁酸镍纳米掺杂对二氧化钛"锐钛矿"→"金红石"的晶体结构转变及其光催化活性的影响.结果表明,铁酸镍的掺杂可抑制二氧化钛由"锐钛矿"到"金红石"的结构相变,显著提高其光催化活性,在最佳掺杂浓度时,其光催化降解曙红的效率可以提高约2倍.     

复合多铁材料0.2NiFe2O4/0.8BaTiO3的制备及性能研究

采用溶胶-凝胶与固相反应相结合的方法制备0.2NiFe2O4/0.8BaTiO3复合多铁材料.X射线衍射结果表明,铁电相与铁磁相共存.扫描电子显微镜(SEM)和透射电子显微镜(TEM)对样品的形貌进行了分析.扫描电子显微镜结果表明材料内部是异质结构的,高分辨透射电子显微镜(HRTEM)结果分析复合材料由NiFe2O4和BaTiO3两相构成,并且两相之间存在明显的界面.电滞回线表明,样品具有铁电性,但存在着一定的漏电.利用振动样品磁强计(VSM)对样品的磁性能进行了测量,由于NiFe2O4的存在,样品具有磁性.     

镍铁氧体催化过硫酸氢钾对奥卡西平的降解研究

研究了通过水热合成法制备的镍铁氧体(NiFe_2O_4),催化过硫酸氢钾(PMS)产生自由基,在常温常压下降解奥卡西平(OXC).采用扫描电子显微镜(SEM)、X射线粉末衍射(XRD)及磁滞回线对镍铁氧体催化剂进行了表征;探究了PMS投加量、NiFe_2O_4投加量以及初始pH对OXC降解效率的影响,结果显示提高PMS和NiFe_2O_4的投量以及偏中性的初始pH均有利于OXC的降解.通过投加不同种类的猝灭剂(甲醇和叔丁醇),证实了OH·和SO_4~-·对OXC的降解起着重要作用,且SO_4~-·的作用更显著.此外,进一步的试验发现NiFe_2O_4具有较好的稳定性和重复利用性:经6次重复使用后,NiFe_2O_4对OXC的降解效率仍可以维持在88%左右;并且,PMS/NiFe_2O_4对滤后水和原水中的OXC也能进行高效催化去除.这些试验结果表明PMS/NiFe_2O_4催化氧化体系对OXC等PPCPs的降解具有良好的应用前景.     

ZrO2对Si3N4陶瓷烧结性能的影响

对添加ＺｒＯ伯Ｓｉ３Ｎ４陶瓷烧结性能的研究表明，一方面ＺｒＯ２可作为一种烧结助剂，促进液相烧结；另一方面它也以四方相形式弥散分布于Ｓｉ３Ｎ４晶粒间，以提高材料的强韧性，试验结果表明：常压烧结下，ＺｒＯ２的质量分数为０．１８时，材料强韧性最好。     

纳米结构ZrO_2(Y)和ZrO_2(Y)-Al_2O_3粉体低温退火前后的结构和性质

研究等离子体 -化学方法制备的纳米结构 Zr O2 -Y2 O3 和 Zr O2 -Y2 O3-Al2 O3 粉体及其不同温度退火前后的结构、性质变化 .结果表明 ,用这种方法制备的粉体 ,烧结后具有很好的聚合性能 ,聚合结构可达到 1～ 2 μm,且内部晶粒尺寸很小 (2 5～ 35 nm) ;在 12 0 0℃以下退火 ,X射线衍射图谱上没有 Al2 O3 的衍射峰 ;对于两种体系 ,主相 Zr O2 的结构虽大致相同 ,但当低温退火 (<12 0 0℃ )时其在 Zr O2 -Y2 O3 体系中的晶格畸变比在 Zr O2 -Y2 O3-Al2 O3 系统中的变化更大 ;晶粒尺寸 (D)为 10～ 15 nm的粉体几乎没有晶格畸变